CN105885560A - Nano antifouling fiber coating - Google Patents
Nano antifouling fiber coating Download PDFInfo
- Publication number
- CN105885560A CN105885560A CN201610337556.9A CN201610337556A CN105885560A CN 105885560 A CN105885560 A CN 105885560A CN 201610337556 A CN201610337556 A CN 201610337556A CN 105885560 A CN105885560 A CN 105885560A
- Authority
- CN
- China
- Prior art keywords
- parts
- fiber coating
- nano antifouling
- stannous chloride
- alumina silicate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a nano antifouling fiber coating which comprises the following raw materials in parts by weight: 50-55 parts of resin liquid, 20-30 parts of waterproof agent, 5-10 parts of cellulose polymer, 10-20 parts of stannous chloride, 10-20 parts of cuprous oxide, 10-15 parts of alumina silicate fiber, 10-20 parts of short fiber and 5-10 parts of acidized graphite. The nano antifouling fiber coating provided by the invention has the characteristics of fouling resistance, water resistance, low price and long service life.
Description
Technical field
The invention belongs to building field, relate to a kind of nano antifouling fiber coating.
Background technology
At present, in building industry, the top in many houses or side are many due to its body plan part, figure is complicated, so its tightness is poor, easy any standing water on top, interior wall get damp, mouldy, brings the biggest puzzlement to resident family, common waterproof material, although solving a problem promptly, but it being the most aging, heat-resisting tolerance to cold is poor, water resistance is poor, often needs repeatedly to brush.
House is stained and refers to house and stand all day to expose to the weather and by corroding and dirt is adhered to, make house tarnish.House is stained and can bring the biggest puzzlement to resident family.Such as traditional Organotin antifouling paints because poisonous, it is prohibited from using.The loss caused for preventing house to be stained, hereby have developed a kind of nano antifouling fiber coating and be coated on room body to increase house fouling resistance ability, specific function in conjunction with nano-fiber material, on the premise of coatings industry needs environmental protection, the soil resistant fibre coating of long-acting nontoxic soil resistant fibre coating containing some nano-scale component and nanometer scale will become the main development direction of soil resistant fibre coating.
Summary of the invention
The technical problem to be solved in the present invention is: overcome anti-fouling material anti-fouling effect in prior art to be difficult to meet house moulding changeable, structure is complicated, make waterproof construction tolerance to cold the most aging, heat-resisting in house poor, water resistance is poor, often need the technical problem repeatedly brushed, it is provided that a kind of antifouling, waterproof, nano antifouling fiber coating of low price, materials'use life-span length.
The technical solution adopted for the present invention to solve the technical problems is: provides a kind of nano antifouling fiber coating, it is characterized in that: include resin liquid, waterproofing agent, cellulosic polymer, stannous chloride, Red copper oxide, alumina silicate fibre, chopped fiber, acidifying graphite；Its feed components includes resin liquid 50-55, waterproofing agent 20-30, cellulosic polymer 5-10, stannous chloride 10-20, Red copper oxide 10-20, alumina silicate fibre 10-15, chopped fiber 10-20, acidifying graphite 5-10 by weight.
As preferably, described nano antifouling fiber coating, it is characterized in that: its feed components by weight, including resin liquid 55, waterproofing agent 20, cellulosic polymer 5, stannous chloride 20, Red copper oxide 20, alumina silicate fibre 15, chopped fiber 10, acidifying graphite 10.
As preferably, described nano antifouling fiber coating, it is characterized in that: contained resin liquid by 15～the PVC resin powder of 20% and 85～90% Ketohexamethylene constitute.
As preferably, described nano antifouling fiber coating, feature is: it is prepared by following method:
(1) according to formula composition, the PVC resin powder of 20% and the Ketohexamethylene of 85% are stirred；
(2) in described step (1), add stannous chloride, Red copper oxide, be again stirring for uniformly；
(3) by cellulosic polymer, alumina silicate fibre, chopped fiber mixing, stir；
(4) waterproofing agent, acidifying graphite are poured in the mixture that described step (3) prepares, be again stirring for uniformly, preparing nano antifouling fiber coating.
The invention has the beneficial effects as follows that a kind of nano antifouling fiber coating of the present invention has antifouling, waterproof, low price, the feature of materials'use life-span length.
Detailed description of the invention
A kind of nano antifouling fiber coating of the present invention, is characterized in that: include resin liquid, waterproofing agent, cellulosic polymer, stannous chloride, Red copper oxide, alumina silicate fibre, chopped fiber, acidifying graphite；Its feed components includes resin liquid 50-55, waterproofing agent 20-30, cellulosic polymer 5-10, stannous chloride 10-20, Red copper oxide 10-20, alumina silicate fibre 10-15, chopped fiber 10-20, acidifying graphite 5-10 by weight.
As preferably, described nano antifouling fiber coating, it is characterized in that: its feed components by weight, including resin liquid 55, waterproofing agent 20, cellulosic polymer 5, stannous chloride 20, Red copper oxide 20, alumina silicate fibre 15, chopped fiber 10, acidifying graphite 10.
As preferably, described nano antifouling fiber coating, it is characterized in that: contained resin liquid by 15～the PVC resin powder of 20% and 85～90% Ketohexamethylene constitute.
As preferably, described nano antifouling fiber coating, feature is: it is prepared by following method:
(1) according to formula composition, the PVC resin powder of 20% and the Ketohexamethylene of 85% are stirred；
(2) in described step (1), add stannous chloride, Red copper oxide, be again stirring for uniformly；
(3) by cellulosic polymer, alumina silicate fibre, chopped fiber mixing, stir；
(4) waterproofing agent, acidifying graphite are poured in the mixture that described step (3) prepares, be again stirring for uniformly, preparing nano antifouling fiber coating.
The above is only the preferred embodiment of the present invention, is not limited to the present invention, it is noted that
For those skilled in the art, on the premise of without departing from the technology of the present invention principle, it is also possible to make some improvement and modification, these improve and modification also should be regarded as protection scope of the present invention.
Claims (4)
1. a nano antifouling fiber coating, is characterized in that: include resin liquid, waterproofing agent, cellulosic polymer, stannous chloride, Red copper oxide, alumina silicate fibre, chopped fiber, acidifying graphite；Its feed components includes resin liquid 50-55, waterproofing agent 20-30, cellulosic polymer 5-10, stannous chloride 10-20, Red copper oxide 10-20, alumina silicate fibre 10-15, chopped fiber 10-20, acidifying graphite 5-10 by weight.
2. nano antifouling fiber coating as claimed in claim 1, it is characterized in that: its feed components by weight, including resin liquid 55, waterproofing agent 20, cellulosic polymer 5, stannous chloride 20, Red copper oxide 20, alumina silicate fibre 15, chopped fiber 10, acidifying graphite 10.
3. the nano antifouling fiber coating as described in claim 1-2, is characterized in that: contained resin liquid by 15～the PVC resin powder of 20% and 85～90% Ketohexamethylene constitute.
4. the nano antifouling fiber coating as described in claim 1-3, feature is: it is prepared by following method:
(1) according to formula composition, the PVC resin powder of 20% and the Ketohexamethylene of 85% are stirred；
(2) in described step (1), add stannous chloride, Red copper oxide, be again stirring for uniformly；
(3) by cellulosic polymer, alumina silicate fibre, chopped fiber mixing, stir；
(4) waterproofing agent, acidifying graphite are poured in the mixture that described step (3) prepares, be again stirring for uniformly, preparing nano antifouling fiber coating.