CN105755661B - A kind of fancy polyester fibre cotton knitting fabric and its production technology - Google Patents
A kind of fancy polyester fibre cotton knitting fabric and its production technology Download PDFInfo
- Publication number
- CN105755661B CN105755661B CN201610250616.3A CN201610250616A CN105755661B CN 105755661 B CN105755661 B CN 105755661B CN 201610250616 A CN201610250616 A CN 201610250616A CN 105755661 B CN105755661 B CN 105755661B
- Authority
- CN
- China
- Prior art keywords
- fabric
- polyester fibre
- yarn
- dyeing
- fibre cotton
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of fancy polyester fibre cotton knitting fabric is carved yarn and cotton yarn weaving into polyester fibre cotton institutional framework by terylene cloud, is successively produced through weaving, pre-treatment, dyeing, post-processing, drying and sizing.Fancy polyester fibre cotton knitting fabric outer layer of the invention shows deep mixed, in picturesque disorder, the apparent differentiation striped of plastic relief sense, internal layer is smooth, smooth, soft, there is the feel and wearability of cotton simultaneously, realize the perfect combination of appearance and wearability, it breaches existing terylene fancy fabric style and shows slightly single situation, and better wearability is played, there is good market prospects and economical, societal benefits, and energy-saving production technology environmental protection.
Description
Technical field
The present invention relates to technical field of textile fabric, especially a kind of fancy polyester fibre cotton knitting fabric and its production technology.
Background technique
Synthetic fibers are quickly grown in recent years, and various functional, differential terylene also come into being.Such as imitative fiber crops, are imitated imitative cotton
The imitated natural fabrics such as silk, the main structure by changing yarn, to form the product of unique style, while improving fabric
People's lives are interspersed and beautified to feel.Emulation class yarn is at home and abroad occupied important in the market with its unique style
Status.The advantages of terylene flame, also referred to as terylene cloud carve yarn, combine natural fiber and chemical fibre is reduced to nature
The dependence of resource and environment forms plastic relief sense using different contraction principle.Currently, commonly terylene cloud on domestic and international market
The terylene fancy fabric of yarn and the braiding of ordinary polyester processed filament is carved, style shows slightly single with purposes.
Summary of the invention
The main object of the present invention is to provide a kind of perfection for realizing appearance and wearability the shortcomings that overcoming the prior art
In conjunction with breaching existing terylene fancy fabric style and show slightly single situation, there is good market prospects and economy, society's effect
Benefit, and the fancy polyester fibre cotton knitting fabric and its production technology of energy-saving production technology environmental protection.
The present invention adopts the following technical scheme:
A kind of fancy polyester fibre cotton knitting fabric is carved yarn and cotton yarn weaving by terylene cloud and is formed at polyester fibre cotton institutional framework.
Further, the terylene cloud carving yarn carves yarn using T90D terylene cloud, and cotton yarn uses JC40S cotton yarn, terylene cloud carving
A length of 28~the 32cm/100G of yarn, a length of 27~29cm/100G of cotton.
A kind of production technology of fancy polyester fibre cotton knitting fabric, successively includes following technique:
1. weaving, yarn and cotton yarn weaving are carved by terylene cloud and formed at polyester fibre cotton institutional framework；
2. pre-treatment carries out pre-treatment to fabric before dyeing and deoils；
3. dyeing, to treated before menstruation, fabric is dyed；
4. post-processing, reduction cleaning and neutralization are carried out to the fabric after dyeing；
5. drying, post-treated fabric is dried；
6. being formed, finished product sizing is carried out to the fabric after drying.
Further, in the weaving process, terylene cloud carves yarn and carves yarn using T90D terylene cloud, and cotton yarn uses JC40S cotton
Yarn, terylene cloud carve a length of 28~32cm/100G of yarn, a length of 27~29cm/100G of cotton.
Further, in the pre-treating technology, by fabric be placed in liquid alkaline containing 3~4g/L, 4~6g/L hydrogen peroxide,
In the treatment fluid of the deoxyenzyme of 0.4~0.6% refining degreaser, the glacial acetic acid of 0.4~0.6g/L and 0.1~0.2g/L,
20~40min is handled at a temperature of 110~150 DEG C.
Further, in the dyeing, dye bath ratio 1:10, by treated before menstruation, fabric is set in overflow dyeing machine
In levelling agent, the glacial acetic acid of 0.5~0.7g/L and the dyeing liquor of dyestuff containing 0.4~0.6g/L, in 125~140 DEG C of temperature
Lower processing 20~40min, 0.8~1.2 DEG C/min of heating rate, 0.8~1.2 DEG C/min of rate of temperature fall.
Further, in the dyeing, the dispersion that the dyestuff added in dyeing liquor is 0.08~0.16% is dark red
SPW-3BS dyestuff, 0.1~0.2% dispersion phloxine BG dyestuff and 0.25~0.3% dispersion rhodo HSF dyestuff.
Further, in the aftertreatment technology, first by the fabric after dyeing be placed in liquid alkaline containing 3~5g/L and 2~
In the treatment fluid of the sodium hydrosulfite of 4g/L, 20~40min of reduction cleaning is carried out at a temperature of 70~90 DEG C, then fabric is placed in and is contained
In the treatment fluid of the glacial acetic acid of 0.4~0.6g/L, 8~12min of neutralisation treatment at a temperature of 40~60 DEG C.
Further, in the stoving process, post-treated fabric is dried by dryer, drying temperature is
130~135 DEG C, machine speed is 15~20m/min.
Further, in the setting process, in forming machine by fabric be placed in containing 0.8~1.2% hydrophilic silicone oil and
Arrangement is carried out shaping in the treatment fluid of 0.1~0.3% moisture absorbing and sweat releasing auxiliary agent, setting temperature is 130~170 DEG C, speed 15
~19m/min.
By the above-mentioned description of this invention it is found that compared with prior art, the invention has the following beneficial effects:
First, terylene cloud carving yarn and cotton yarn are organically combined, weaving is presented at polyester fibre cotton institutional framework, finished fabric outer layer
Deep mixed out, in picturesque disorder, the apparent differentiation striped of plastic relief sense, internal layer is smooth, smooth, soft, while having cotton
Feel and wearability, realize appearance and wearability perfect combination, breach existing terylene fancy fabric style and show slightly
Single situation, and play better wearability can better meet consumer and follow the fashion, tell immediately following the psychology of trend
It asks, more the market competitiveness；
Second, in weaving process, terylene cloud carves that yarn is long to use 28~32cm/100G, and cotton yarn wire length uses 27~29cm/
100G, it is ensured that terylene cloud carving yarn full and uniform can be shunk under high-temperature and high-pressure conditions, and the effect as similar cloud carving is presented；
Third, control by stages heating and soaking time in dyeing, and strict control temperature rate, it can be ensured that boiling
The big terylene cloud of water shrinking percentage carves yarn full and uniform contraction under high-temperature and high-pressure conditions, and the differentiation striped of presentation is in picturesque disorder,
Guarantee cloth cover even dyeing, it is wrinkle resistant, without folding line, cloud carving effect it is obvious；
4th, moisture absorbable and breathable finishing is carried out to fabric by addition moisture absorbing and sweat releasing auxiliary agent in setting process, improves fabric
Moisture absorbing and sweat releasing performance, thus make fabric have both water suction, moisture-inhibiting, quick-drying characteristic, wear it is more comfortable；
In short, fancy polyester fibre cotton knitting fabric outer layer of the invention shows deep mixed, in picturesque disorder, plastic relief sense
Apparent differentiation striped, internal layer is smooth, smooth, soft, while having the feel and wearability of cotton, realizes appearance and takes
The perfect combination of performance breaches existing terylene fancy fabric style and shows slightly single situation, and plays better taking
Can, there is good market prospects and economical, societal benefits, and energy-saving production technology environmental protection.
Specific embodiment
Below by way of specific embodiment, the invention will be further described.
Embodiment one
A kind of production technology of fancy polyester fibre cotton knitting fabric of the invention, successively includes following technique:
1. weaving, yarn and the weaving of JC40S cotton yarn are carved by T90D terylene cloud and formed at polyester fibre cotton institutional framework, terylene cloud carves yarn
Wire length is 30cm/100G, a length of 28cm/100G of cotton.
2. pre-treatment carries out pre-treatment to fabric before dyeing and deoils；By fabric be placed in liquid alkaline containing 3.5g/L, 5g/L it is double
In the treatment fluid of the deoxyenzyme of oxygen water, 0.5% refining degreaser, the glacial acetic acid of 0.5g/L and 0.15g/L, in 130 DEG C of temperature
Lower processing 30min.
3. dyeing, dye bath ratio 1:10, by treated before menstruation, fabric is placed in the level dyeing containing 0.5g/L in overflow dyeing machine
Agent, the glacial acetic acid of 0.6g/L, the 0.12% dark red SPW-3BS dyestuff of dispersion, 0.15% dispersion phloxine BG dyestuff and
In the dyeing liquor of 0.275% dispersion rhodo HSF dyestuff, 30min, 1 DEG C/min of heating rate are handled at a temperature of 133 DEG C, is dropped
Warm 1 DEG C/min of rate.
4. post-processing, reduction cleaning and neutralization are carried out to the fabric after dyeing；First the fabric after dyeing is placed in containing 4g/
In the treatment fluid of the sodium hydrosulfite of the liquid alkaline and 3g/L of L, reduction cleaning 30min is carried out at a temperature of 80 DEG C, then fabric is placed in and is contained
In the treatment fluid of the glacial acetic acid of 0.5g/L, neutralisation treatment 10min at 50 °C.
5. drying, post-treated fabric is dried by dryer, drying temperature is 130~135 DEG C, and machine speed is
17m/min, the door width of fabric are 190cm, and grammes per square metre is 208g/ ㎡.
6. being formed, arrangement is carried out shaping to the fabric after drying in forming machine, fabric is placed in the hydrophilic silicone oil containing 1%
And 0.2% moisture absorbing and sweat releasing auxiliary agent treatment fluid in carry out shaping arrangement, setting temperature is 150 DEG C, speed 17m/min, on
Lower overfeeding 5%/17%.
It is 204cm × 184g/ ㎡, performance parameter by the fancy polyester fibre cotton knitted side gauge lattice that above-mentioned technique is produced
Are as follows:
The fancy polyester fibre cotton knitting fabric items physical index produced by above-mentioned technique reaches Q/FZFZ009-2014
" cloud carves polyester composite filament knitwear " company standard, GB18401 " National Textile basic security technical specification ", GB/T22848
Requirements of the national standard such as " knitting finished fabrics ".
Embodiment two
A kind of production technology of fancy polyester fibre cotton knitting fabric of the present embodiment, successively includes following technique:
1. weaving, yarn and the weaving of JC40S cotton yarn are carved by T90D terylene cloud and formed at polyester fibre cotton institutional framework, terylene cloud carves yarn
Wire length is 28cm/100G, a length of 27cm/100G of cotton.
2. pre-treatment carries out pre-treatment to fabric before dyeing and deoils；Fabric is placed in the dioxygen of liquid alkaline containing 3g/L, 4g/L
Water, 0.4% refining degreaser, 0.4g/L glacial acetic acid and 0.1g/L deoxyenzyme treatment fluid in, at a temperature of 110 DEG C at
Manage 20min.
3. dyeing, dye bath ratio 1:10, by treated before menstruation, fabric is placed in the level dyeing containing 0.4g/L in overflow dyeing machine
Agent, the glacial acetic acid of 0.5g/L, the 0.08% dark red SPW-3BS dyestuff of dispersion, 0.1% dispersion phloxine BG dyestuff and
In the dyeing liquor of 0.25% dispersion rhodo HSF dyestuff, 20min, 0.8 DEG C/min of heating rate are handled at a temperature of 125 DEG C, is dropped
Warm 0.8 DEG C/min of rate.
4. post-processing, reduction cleaning and neutralization are carried out to the fabric after dyeing；First the fabric after dyeing is placed in containing 3g/
In the treatment fluid of the sodium hydrosulfite of the liquid alkaline and 2g/L of L, reduction cleaning 20min is carried out at a temperature of 70 DEG C, then fabric is placed in and is contained
In the treatment fluid of the glacial acetic acid of 0.4g/L, neutralisation treatment 8min at a temperature of 40 DEG C.
5. drying, post-treated fabric is dried by dryer, drying temperature is 130~135 DEG C, and machine speed is
15m/min, the door width of fabric are 190cm, and grammes per square metre is 208g/ ㎡.
6. being formed, arrangement is carried out shaping to the fabric after drying in forming machine, fabric is placed in the hydrophilic silicon containing 0.8%
Oil and 0.1% moisture absorbing and sweat releasing auxiliary agent treatment fluid in carry out shaping arrangements, setting temperature is 130 DEG C, speed 15m/min,
Upper and lower overfeeding 5%/17%.
Embodiment three
A kind of production technology of fancy polyester fibre cotton knitting fabric of the present embodiment, successively includes following technique:
1. weaving, yarn and the weaving of JC40S cotton yarn are carved by T90D terylene cloud and formed at polyester fibre cotton institutional framework, terylene cloud carves yarn
Wire length is 32cm/100G, a length of 29cm/100G of cotton.
2. pre-treatment carries out pre-treatment to fabric before dyeing and deoils；Fabric is placed in the dioxygen of liquid alkaline containing 4g/L, 6g/L
Water, 0.6% refining degreaser, 0.6g/L glacial acetic acid and 0.2g/L deoxyenzyme treatment fluid in, at a temperature of 150 DEG C at
Manage 40min.
3. dyeing, dye bath ratio 1:10, by treated before menstruation, fabric is placed in the level dyeing containing 0.6g/L in overflow dyeing machine
Agent, the glacial acetic acid of 0.7g/L, the 0.16% dark red SPW-3BS dyestuff of dispersion, 0.2% dispersion phloxine BG dyestuff and
In the dyeing liquor of 0.3% dispersion rhodo HSF dyestuff, 40min, 1.2 DEG C/min of heating rate are handled at a temperature of 140 DEG C, is dropped
Warm 1.2 DEG C/min of rate.
4. post-processing, reduction cleaning and neutralization are carried out to the fabric after dyeing；First the fabric after dyeing is placed in containing 5g/
In the treatment fluid of the sodium hydrosulfite of the liquid alkaline and 4g/L of L, reduction cleaning 40min is carried out at a temperature of 90 DEG C, then fabric is placed in and is contained
In the treatment fluid of the glacial acetic acid of 0.6g/L, neutralisation treatment 12min at a temperature of 60 DEG C.
5. drying, post-treated fabric is dried by dryer, drying temperature is 130~135 DEG C, and machine speed is
20m/min, the door width of fabric are 190cm, and grammes per square metre is 208g/ ㎡.
6. being formed, arrangement is carried out shaping to the fabric after drying in forming machine, fabric is placed in the hydrophilic silicon containing 1.2%
Oil and 0.3% moisture absorbing and sweat releasing auxiliary agent treatment fluid in carry out shaping arrangements, setting temperature is 170 DEG C, speed 19m/min,
Upper and lower overfeeding 5%/17%.
It above are only three specific embodiments of the invention, but the design concept of the present invention is not limited to this, all benefits
It is made a non-material change to the present invention, should all be belonged to behavior that violates the scope of protection of the present invention with this design.
Claims (6)
1. a kind of production technology of fancy polyester fibre cotton knitting fabric, it is characterised in that:
1. weaving, yarn and cotton yarn weaving are carved by terylene cloud and formed at polyester fibre cotton institutional framework；
2. pre-treatment carries out pre-treatment to fabric before dyeing and deoils；
3. dyeing, to treated before menstruation, fabric is dyed；
4. post-processing, reduction cleaning and neutralization are carried out to the fabric after dyeing；
5. drying, post-treated fabric is dried；
6. being formed, finished product sizing is carried out to the fabric after drying；
In the weaving process, terylene cloud carves yarn and carves yarn using T90D terylene cloud, and cotton yarn uses JC40S cotton yarn, and terylene cloud carves yarn
Wire length is 28~32cm/100G, a length of 27~29cm/100G of cotton；
In the setting process, fabric is placed in containing 0.8~1.2% hydrophilic silicone oil and 0.1~0.3% suction in forming machine
Arrangement is carried out shaping in the wet treatment fluid for perspiring auxiliary agent, setting temperature is 150 DEG C, and speed is 15~19m/min.
2. a kind of production technology of fancy polyester fibre cotton knitting fabric as described in claim 1, it is characterised in that: the pre-treatment
In technique, by fabric be placed in liquid alkaline containing 3~4g/L, the hydrogen peroxide of 4~6g/L, 0.4~0.6% refining degreaser, 0.4~
In the treatment fluid of the deoxyenzyme of the glacial acetic acid and 0.1~0.2g/L of 0.6g/L, at a temperature of 110~150 DEG C handle 20~
40min。
3. a kind of production technology of fancy polyester fibre cotton knitting fabric as described in claim 1, it is characterised in that: the dyer
In skill, dye bath ratio 1: 10, by premenstrual treated fabric is placed in containing 0.4~0.6g/L levelling agent, 0.5 in overflow dyeing machine
In the glacial acetic acid of~0.7g/L and the dyeing liquor of dyestuff, 20~40min, heating rate 0.8 are handled at a temperature of 125~140 DEG C
~1.2 DEG C/min, 0.8~1.2 DEG C/min of rate of temperature fall.
4. a kind of production technology of fancy polyester fibre cotton knitting fabric as claimed in claim 3, it is characterised in that: the dyer
In skill, the dyestuff added in dyeing liquor is 0.08~0.16% dark red SPW-3BS dyestuff of dispersion, 0.1~0.2% dispersion is glimmering
The pink BG dyestuff of light and 0.25~0.3% dispersion rhodo HSF dyestuff.
5. a kind of production technology of fancy polyester fibre cotton knitting fabric as described in claim 1, it is characterised in that: the post-processing
In technique, first the fabric after dyeing is placed in the treatment fluid of the liquid alkaline containing 3~5g/L and the sodium hydrosulfite of 2~4g/L, 70
20~40min of reduction cleaning is carried out at a temperature of~90 DEG C, then fabric is placed in the treatment fluid of the glacial acetic acid containing 0.4~0.6g/L
In, 8~12min of neutralisation treatment at a temperature of 40~60 DEG C.
6. a kind of production technology of fancy polyester fibre cotton knitting fabric as described in claim 1, it is characterised in that: the drying work
In skill, post-treated fabric is dried by dryer, drying temperature is 130~135 DEG C, and machine speed is 15~20m/
min。