CN105544037A - Waterproof tension-resistant blended yarn - Google Patents

Waterproof tension-resistant blended yarn Download PDF

Info

Publication number
CN105544037A
CN105544037A CN201610055223.7A CN201610055223A CN105544037A CN 105544037 A CN105544037 A CN 105544037A CN 201610055223 A CN201610055223 A CN 201610055223A CN 105544037 A CN105544037 A CN 105544037A
Authority
CN
China
Prior art keywords
fiber
mix
blend
parts
blended yarn
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201610055223.7A
Other languages
Chinese (zh)
Inventor
陈昶
刘守串
陈瑞兵
孙玉童
童朝俊
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI WUWEI TIANCHENG TEXTILE Co Ltd
Original Assignee
ANHUI WUWEI TIANCHENG TEXTILE Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI WUWEI TIANCHENG TEXTILE Co Ltd filed Critical ANHUI WUWEI TIANCHENG TEXTILE Co Ltd
Priority to CN201610055223.7A priority Critical patent/CN105544037A/en
Publication of CN105544037A publication Critical patent/CN105544037A/en
Pending legal-status Critical Current

Abstract

The invention discloses a waterproof tension-resistant blended yarn. The waterproof tension-resistant blended yarn is prepared from, by weight, 60-80 parts of modified rice fibers, 10-18 parts of acrylic fibers, 5-15 parts of viscose, 10-18 parts of flax fibers and 5-18 parts of tencel fibers. A blending process is adopted for spinning the raw materials into the yarn. The waterproof tension-resistant blended yarn is waterproof, good in durability and excellent in tension resistance.

Description

A kind of waterproof stretch-proof blended yarn
Technical field
The present invention relates to blended yarn technical field, particularly relate to a kind of waterproof stretch-proof blended yarn.
Background technology
Along with growth in the living standard, the requirement for garment material is more and more higher, and the Functional Requirement especially for fabric is more and more higher.Waterproof, stretch-proof, good endurance functional fabric be more and more subject to liking of consumer, current clothes braided wire, to Exposure to Sunlight, drench with rain, performance requirement that brute force is torn is higher, and general side realizes due to its waterproof, durability, stretch-proof performance is not enough, easily to rupture, play first order issue, have a strong impact on the quality of clothes, simultaneously, because fracture also easily allows outside water be splashed in clothes, have a strong impact on and wear effect.
Summary of the invention
The present invention proposes a kind of waterproof stretch-proof blended yarn, waterproof, good endurance, stretch-proof excellent performance.
A kind of waterproof stretch-proof blended yarn that the present invention proposes, its raw material comprises by weight: modification rice fiber 60-80 part, acrylic fiber 10-18 part, gluing fiber 5-15 part, linen fibre 10-18 part, tencel fiber 5-18 part, and adopt blended weave spun yarn.
Preferably, modification rice fiber adopts following technique to prepare: by cottonseed oil, rice starch mix and blend, mix and blend temperature is 92-98 DEG C, obtains the first prefabricated material; By castor oil, poly methyl diphenylene diisocyanate mix and blend, mix and blend temperature is 35-45 DEG C, adds the first prefabricated material, ethanolic solution mixes, and filters, washing, and fermentation, spinning, obtains modification rice fiber.
Preferably, the weight ratio of cottonseed oil, rice starch is 5-15:20-40.
Preferably, the weight ratio of castor oil, poly methyl diphenylene diisocyanate is 2-10:3-8.
Preferably, modification rice fiber adopts following technique to prepare: by weight by 5-15 part cottonseed oil, 20-40 part rice starch mix and blend 20-50min, mix and blend temperature is 92-98 DEG C, obtains the first prefabricated material; By 2-10 part castor oil, 3-8 part poly methyl diphenylene diisocyanate mix and blend 10-30min, mix and blend temperature is 35-45 DEG C, adds the first prefabricated material, 55-75% ethanolic solution mixes, filter, washing, fermentation, spinning, obtains modification rice fiber.
Preferably, described waterproof stretch-proof blended yarn, its raw material comprises by weight: modification rice fiber 70-76 part, acrylic fiber 12-16 part, gluing fiber 8-12 part, linen fibre 12-14 part, tencel fiber 10-14 part, and adopts blended weave spun yarn.
In the present invention, castor oil and the effect of poly methyl diphenylene diisocyanate obtain base polyurethane prepolymer for use as, fatty glyceride in cottonseed oil not only can and rice starch between form hydrogen bond, rice starch plasticity is fabulous, height of formation network-like structure is acted on further further with the base polyurethane prepolymer for use as of above-mentioned synthesis, it is fabulous that not only ageing-resistant performance adopted by modification rice fiber, and hydrophobic performance and mechanical property are very excellent, and tear-resistant performance is fabulous; The groove that modification rice fiber gluing fiber, linen fibre, tencel fiber and acrylic fiber indulge face cooperatively interacts cohesive force by force, and goods good waterproof performance, tear-resistant performance strengthens further.
Detailed description of the invention
Below, by specific embodiment, technical scheme of the present invention is described in detail.
Embodiment 1
A kind of waterproof stretch-proof blended yarn, its raw material comprises by weight: modification rice fiber 60 parts, acrylic fiber 18 parts, gluing fiber 5 parts, linen fibre 18 parts, tencel fiber 5 parts, and adopts blended weave spun yarn.
Embodiment 2
A kind of waterproof stretch-proof blended yarn, its raw material comprises by weight: modification rice fiber 80 parts, acrylic fiber 10 parts, gluing fiber 15 parts, linen fibre 10 parts, tencel fiber 18 parts, and adopts blended weave spun yarn.
Embodiment 3
A kind of waterproof stretch-proof blended yarn, its raw material comprises by weight: modification rice fiber 70 parts, acrylic fiber 16 parts, gluing fiber 8 parts, linen fibre 14 parts, tencel fiber 10 parts, and adopts blended weave spun yarn.
Modification rice fiber adopts following technique to prepare: by weight by 15 portions of cottonseed oils, 20 parts of rice starch mix and blend 50min, mix and blend temperature is 92 DEG C, obtains the first prefabricated material; By 10 parts of castor oil, 3 parts of poly methyl diphenylene diisocyanate mix and blend 30min, mix and blend temperature is 35 DEG C, adds the first prefabricated material, 75% ethanolic solution mixes, and filters, washing, and fermentation, spinning, obtains modification rice fiber.
Embodiment 4
A kind of waterproof stretch-proof blended yarn, its raw material comprises by weight: modification rice fiber 76 parts, acrylic fiber 12 parts, gluing fiber 12 parts, linen fibre 12 parts, tencel fiber 14 parts, and adopts blended weave spun yarn.
Modification rice fiber adopts following technique to prepare: by weight by 5 portions of cottonseed oils, 40 parts of rice starch mix and blend 20min, mix and blend temperature is 98 DEG C, obtains the first prefabricated material; By 2 parts of castor oil, 8 parts of poly methyl diphenylene diisocyanate mix and blend 10min, mix and blend temperature is 45 DEG C, adds the first prefabricated material, 55% ethanolic solution mixes, and filters, washing, and fermentation, spinning, obtains modification rice fiber.
Embodiment 5
A kind of waterproof stretch-proof blended yarn, its raw material comprises by weight: modification rice fiber 74 parts, acrylic fiber 14 parts, gluing fiber 10 parts, linen fibre 13 parts, tencel fiber 12 parts, and adopts blended weave spun yarn.
Modification rice fiber adopts following technique to prepare: by weight by 12 portions of cottonseed oils, 36 parts of rice starch mix and blend 30min, mix and blend temperature is 95 DEG C, obtains the first prefabricated material; By 8 parts of castor oil, 6 parts of poly methyl diphenylene diisocyanate mix and blend 20min, mix and blend temperature is 42 DEG C, adds the first prefabricated material, 68% ethanolic solution mixes, and filters, washing, and fermentation, spinning, obtains modification rice fiber.
The above; be only the present invention's preferably detailed description of the invention; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.

Claims (6)

1. a waterproof stretch-proof blended yarn, is characterized in that, its raw material comprises by weight: modification rice fiber 60-80 part, acrylic fiber 10-18 part, gluing fiber 5-15 part, linen fibre 10-18 part, tencel fiber 5-18 part, and adopt blended weave spun yarn.
2. waterproof stretch-proof blended yarn according to claim 1, is characterized in that, modification rice fiber adopts following technique to prepare: by cottonseed oil, rice starch mix and blend, mix and blend temperature is 92-98 DEG C, obtains the first prefabricated material; By castor oil, poly methyl diphenylene diisocyanate mix and blend, mix and blend temperature is 35-45 DEG C, adds the first prefabricated material, ethanolic solution mixes, and filters, washing, and fermentation, spinning, obtains modification rice fiber.
3. waterproof stretch-proof blended yarn according to claim 2, is characterized in that, the weight ratio of cottonseed oil, rice starch is 5-15:20-40.
4. the waterproof stretch-proof blended yarn according to claim 2-3 mono-, is characterized in that, the weight ratio of castor oil, poly methyl diphenylene diisocyanate is 2-10:3-8.
5. the waterproof stretch-proof blended yarn according to any one of claim 2-4, it is characterized in that, modification rice fiber adopts following technique to prepare: by weight by 5-15 part cottonseed oil, 20-40 part rice starch mix and blend 20-50min, mix and blend temperature is 92-98 DEG C, obtains the first prefabricated material; By 2-10 part castor oil, 3-8 part poly methyl diphenylene diisocyanate mix and blend 10-30min, mix and blend temperature is 35-45 DEG C, adds the first prefabricated material, 55-75% ethanolic solution mixes, filter, washing, fermentation, spinning, obtains modification rice fiber.
6. the waterproof stretch-proof blended yarn according to any one of claim 1-5, it is characterized in that, its raw material comprises by weight: modification rice fiber 70-76 part, acrylic fiber 12-16 part, gluing fiber 8-12 part, linen fibre 12-14 part, tencel fiber 10-14 part, and adopt blended weave spun yarn.
CN201610055223.7A 2016-01-26 2016-01-26 Waterproof tension-resistant blended yarn Pending CN105544037A (en)