CN105153929A - Adhesive of primer paint of household aluminium alloy sliding doors and preparation method thereof - Google Patents

Abstract

The invention provides an adhesive of primer paint of household aluminium alloy sliding doors and a preparation method thereof, relating to the technical field of production of home decoration materials. The adhesive is characterized by being prepared from the following materials in parts by weight: 14 parts of polydimethylsiloxane, 7 parts of acrylic resin, 9 parts of triethylene tetramine, 6 parts of hexamethylenetetramine, 7 parts of n-butyl methacrylate, 4 parts of modified nano carbon, 3 parts of aluminium sulfate, 3 parts of citric acid, 3 parts of di-tetradecanol ester and 7 parts of butane coupling agent KH510. The method is reasonable, is reasonable in proportioning and is convenient to operate.

Description

Tackiness agent of a kind of priming paint of Domestic aluminium alloy sliding door and preparation method thereof

Technical field:

The present invention relates to house decoration material produce technical field, be specifically related to tackiness agent of a kind of priming paint of Domestic aluminium alloy sliding door and preparation method thereof.

Background technology:

Sliding door comes from China, reaches Korea, Japan through Chinese culture.From word meaning: promote the door pulled; Have from material: have timber, metal, organic and inorganic material (as: glass) point; Purposes: the door that can be used for wardrobe, bookcase, built-in wardrobe, bedroom, parlor, showroom.

Initial sliding door is only for the sliding door of bedroom or changing rooms wardrobe, but along with the development of technology and the variation of finishing means, from traditional plate surface, to glass, cloth art, rattan plaited, aluminium alloy extrusions, from sliding door, accordion door to partition door, the function of sliding door and use range are in continuous expansion.In this case, the utilization of sliding door starts to become various and abundant.Except modal partition door, sliding door is widely used in bookcase, built-in wardrobe, parlor, showroom, plug-type family door etc.

In life now, sliding door not only wants excellent property, and its outward appearance is all very important with being convenient to degree of cleaning, has the many sliding door time for a long time easily to fall paint, or wiping after touching and just have very serious scratch, is also unacceptable so for consumers.

Summary of the invention:

Technical problem to be solved by this invention be to overcome existing technological deficiency provide a kind of method rationally, the tackiness agent of the priming paint of reasonable ratio, easy to operate a kind of Domestic aluminium alloy sliding door and preparation method thereof.

Technical problem to be solved by this invention adopts following technical scheme to realize:

Tackiness agent of a kind of priming paint of Domestic aluminium alloy sliding door and preparation method thereof, is characterized in that: be made up of the material of following weight part,

Polydimethylsiloxane 14 parts, acrylic resin 7 parts, triethylene tetramine 9 parts, vulkacit H 6 parts, n-BMA 7 parts, 4 parts, modified Nano carbon, 3 parts, Tai-Ace S 150, citric acid 3 parts, two ten four carbon alcohols ester 3 parts, butane coupling agent KH5107 part;

Its preparation method comprises,

Polydimethylsiloxane, acrylic resin, triethylene tetramine, vulkacit H, modified Nano carbon are put into stainless steel cauldron by being warming up to 220 DEG C, stirring reaction 3.5 hours by I;

N-BMA, Tai-Ace S 150, citric acid, two ten four carbon alcohols esters are put into stainless steel cauldron by being warming up to 205 DEG C, stirring reaction 3 hours by II;

III starts working II after 0.5 hour in I work, after then completing at the same time, the material in I and II is put into a new reactor, and with the intensification stirring reaction 5 hours of 45 DEG C/h, the 2nd little adds butane coupling agent KH510 constantly;

IV after III step completes, and is taken out by material, and shakes mixing 20 minutes, then extruded by twin screw extruder, temperature controls at 100 DEG C, has then extruded rear material left 10 minutes, then put into pulverizer lapping powder and be broken into 130-165 object powder, packaging warehouse-in.

Beneficial effect of the present invention is: the more convenient and result of use of the processing of particle or pulverulence very good; and different materials is processed by various steps such as reaction, concussion, mixing; make the performance of product more excellent; and the service efficiency of material also can improve, so just make product more outstanding.The inventive method rationally, reasonable ratio, easy to operate.

Embodiment:

The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, setting forth the present invention further below.

More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.

Claims (1)

1. the tackiness agent and preparation method thereof of the priming paint of a Domestic aluminium alloy sliding door, is characterized in that: be made up of the material of following weight part,

Polydimethylsiloxane 14 parts, acrylic resin 7 parts, triethylene tetramine 9 parts, vulkacit H 6 parts, n-BMA 7 parts, 4 parts, modified Nano carbon, 3 parts, Tai-Ace S 150, citric acid 3 parts, two ten four carbon alcohols ester 3 parts, butane coupling agent KH5107 part;

Its preparation method comprises,

Polydimethylsiloxane, acrylic resin, triethylene tetramine, vulkacit H, modified Nano carbon are put into stainless steel cauldron by being warming up to 220 DEG C, stirring reaction 3.5 hours by I;

N-BMA, Tai-Ace S 150, citric acid, two ten four carbon alcohols esters are put into stainless steel cauldron by being warming up to 205 DEG C, stirring reaction 3 hours by II;

III starts working II after 0.5 hour in I work, after then completing at the same time, the material in I and II is put into a new reactor, and with the intensification stirring reaction 5 hours of 45 DEG C/h, the 2nd little adds butane coupling agent KH510 constantly;

IV after III step completes, and is taken out by material, and shakes mixing 20 minutes, then extruded by twin screw extruder, temperature controls at 100 DEG C, has then extruded rear material left 10 minutes, then put into pulverizer lapping powder and be broken into 130-165 object powder, packaging warehouse-in.