CN105086576A - Mixed stuffing for oil paint and preparing method thereof - Google Patents
Mixed stuffing for oil paint and preparing method thereof Download PDFInfo
- Publication number
- CN105086576A CN105086576A CN201510487438.1A CN201510487438A CN105086576A CN 105086576 A CN105086576 A CN 105086576A CN 201510487438 A CN201510487438 A CN 201510487438A CN 105086576 A CN105086576 A CN 105086576A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- mixed
- solvent
- stuffing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a mixed stuffing for oil paint and relates to the technical field of chemistry painting preparation. The mixed stuffing is prepared from 8-10 parts of calcium carbonate, 6-8 parts of calcium phosphate, 3-5 parts of mica powder, 5-7 parts of barium sulfate, 8-10 parts of talcum powder, 6-8 parts of kieselguhr, 5-7 parts of porous quartz powder, 6-8 parts of kaolin, 6-8 parts of silicon dioxide, 6-8 parts of inorganic water absorption particles, 6-8 parts of stain-inhibiting powder, and 10-20 parts of mixed solvent. The mixed stuffing has the advantages that by mixing different stuffing materials available in the market correspondingly, functional diversity of the stuffing is guaranteed; by taking the stuffing as the raw material for preparing oil paint, the advantages of the oil paint are guaranteed, and the oil paint is uniform in texture; the mixed stuffing is environment-friendly, free of toxicity, high in efficiency, high in market value and convenient to use and popularize.
Description
Technical field
The present invention relates to chemistry painting industry preparing technical field, be specifically related to mixed fillers of a kind of paint and preparation method thereof.
Background technology
Paint is that one firmly can cover body surface, plays protection, decoration, mark and the chemical mixture coating of other special purposes.China's coating circle more authoritative " coating process " book is definition like this: " coating is a kind of material, and this material can be coated in article surface by different construction technologies, forms adhere well, has some strength, continuous print solid film.The film common name film of such formation, also known as paint film or coating.”
The formula comprised in paint is a lot, in paint, filler is the one formula of outbalance, mainly increase the filling power of paint, the filler painted in market is comparatively general, but the selection of its filler not science, general is all that single raw material directly uses, and the texture of paint can be caused so low, and impact uses.
Summary of the invention:
Technical problem to be solved by this invention is to provide a kind of formula rationally, and production technique is simple, increases mixed fillers of the paint of paint homogeneity and preparation method thereof.
Technical problem to be solved by this invention realizes by the following technical solutions:
A mixed fillers for paint, is characterized in that: be made up of following raw material:
Calcium carbonate 8-10 part, calcium phosphate 6-8 part, mica powder 3-5 part, barium sulfate 5-7 part, talcum powder 8-10 part, diatomite 6-8 part, cellular quartz powder 5-7 part, kaolin 6-8 part, silicon-dioxide 6-8 part, inorganic water-absorption particle 6-8 part, mildew-resistant powder 6-8 part, the solvent 10-20 part that is in harmonious proportion.
The preferred component of each raw material is:
9 parts, calcium carbonate, 7 parts, calcium phosphate, mica powder 4 parts, 6 parts, barium sulfate, talcum powder 9 parts, 7 parts, diatomite, 6 parts, cellular quartz powder, kaolin 7 parts, silicon-dioxide 7 parts, inorganic water-absorption particle 7 parts, 7 parts, mildew-resistant powder, the solvent 15 parts that is in harmonious proportion.
Described mildew-resistant powder is: phenol and tributyl tin carry out common being mixed according to the amount of mass ratio 2:1.
Described mediation solvent is dropped in stirring tank by dimethylbenzene 3 parts, 2 parts, turps, alcohol 1 part, vinylbenzene 4 parts, and after 120-140 DEG C of high-temperature stirring 2-3h, cooling discharging obtains.
Described inorganic water-absorption particle is ion exchange resin ball grain or superabsorbent gels, potassium type resin cation (R.C.) spherolite.
Another object of the present invention is to provide a kind of method preparing the mixed fillers of the present invention's paint:
First all raw materials in raw material except mediation solvent are mixed, and then grind accordingly, until particle fineness is after 20um-30um, it is all dropped in stirred pot, then the mediation solvent in raw material is all poured into wherein, stir, until be after paste, take out and dry at abrasive dust, can obtain.
The present invention is by the interpolation of inorganic water-absorption particle, and ensure the uniform color in marking paint, consolidation, makes moisture content in marking paint little to greatest extent, improves sticking power;
Various different monomer filler mixes by the present invention accordingly, ensure that the reservation of the advantage of each filler, adopts simultaneously and is in harmonious proportion solvent as stirring liquid, avoids producing inferior position to filler, ensures filler work reliability.
Beneficial effect of the present invention is: the present invention is by carrying out corresponding combination treatment by filler individuality different on market, ensure that the functional diversity of filler, adopt this product filler as the starting material of paint preparation, ensure that the advantage of paint, homogeneous, environment-protecting asepsis, efficient, marketable value is high, is convenient to promote and use.
Embodiment
The technique means realized to make the present invention, creation characteristic, reaching object and effect is easy to understand, below in conjunction with specific embodiment, setting forth the present invention further.
Embodiment 1
Take calcium carbonate 8kg, calcium phosphate 6kg, mica powder 3kg, barium sulfate 5kg, talcum powder 8kg, diatomite 6kg, cellular quartz powder 5kg, kaolin 6kg, silicon-dioxide 6kg, inorganic water-absorption particle 6kg, mildew-resistant powder 6kg, the solvent 10kg that is in harmonious proportion;
Described mildew-resistant powder is: phenol and tributyl tin carry out common being mixed according to the amount of mass ratio 2:1.
Described mediation solvent is dropped in stirring tank by dimethylbenzene 3 parts, 2 parts, turps, alcohol 1 part, vinylbenzene 4 parts, and after 120-140 DEG C of high-temperature stirring 2-3h, cooling discharging obtains.
Described inorganic water-absorption particle is ion exchange resin ball grain or superabsorbent gels, potassium type resin cation (R.C.) spherolite.
Preparation method is:
First all raw materials in raw material except mediation solvent are mixed, and then grind accordingly, until particle fineness is after 20um-30um, it is all dropped in stirred pot, then the mediation solvent in raw material is all poured into wherein, stir, until be after paste, take out and dry at abrasive dust, can obtain.
Embodiment 2
Take calcium carbonate 9kg, calcium phosphate 7kg, mica powder 4kg, barium sulfate 6kg, talcum powder 9kg, diatomite 7kg, cellular quartz powder 6kg, kaolin 7kg, silicon-dioxide 7kg, inorganic water-absorption particle 7kg, mildew-resistant powder 7kg, the solvent 15kg that is in harmonious proportion;
Described mildew-resistant powder is: phenol and tributyl tin carry out common being mixed according to the amount of mass ratio 2:1.
Described mediation solvent is dropped in stirring tank by dimethylbenzene 3 parts, 2 parts, turps, alcohol 1 part, vinylbenzene 4 parts, and after 120-140 DEG C of high-temperature stirring 2-3h, cooling discharging obtains.
Described inorganic water-absorption particle is ion exchange resin ball grain or superabsorbent gels, potassium type resin cation (R.C.) spherolite.
Preparation method is:
First all raw materials in raw material except mediation solvent are mixed, and then grind accordingly, until particle fineness is after 20um-30um, it is all dropped in stirred pot, then the mediation solvent in raw material is all poured into wherein, stir, until be after paste, take out and dry at abrasive dust, can obtain.
More than show and describe ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; what describe in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.Application claims protection domain is defined by appending claims and equivalent thereof.
Claims (6)
1. a mixed fillers for paint, is characterized in that: be made up of following raw material:
Calcium carbonate 8-10 part, calcium phosphate 6-8 part, mica powder 3-5 part, barium sulfate 5-7 part, talcum powder 8-10 part, diatomite 6-8 part, cellular quartz powder 5-7 part, kaolin 6-8 part, silicon-dioxide 6-8 part, inorganic water-absorption particle 6-8 part, mildew-resistant powder 6-8 part, the solvent 10-20 part that is in harmonious proportion.
2. the mixed fillers of a kind of paint according to claim 1, it is characterized in that, the preferred component of each raw material is: 9 parts, calcium carbonate, 7 parts, calcium phosphate, mica powder 4 parts, 6 parts, barium sulfate, talcum powder 9 parts, 7 parts, diatomite, 6 parts, cellular quartz powder, kaolin 7 parts, silicon-dioxide 7 parts, inorganic water-absorption particle 7 parts, 7 parts, mildew-resistant powder, the solvent 15 parts that is in harmonious proportion.
3. the mixed fillers of a kind of paint according to claim 1, is characterized in that: described mildew-resistant powder is: phenol and tributyl tin carry out common being mixed according to the amount of mass ratio 2:1.
4. the mixed fillers of a kind of paint according to claim 1, is characterized in that: described mediation solvent is dropped in stirring tank by dimethylbenzene 3 parts, 2 parts, turps, alcohol 1 part, vinylbenzene 4 parts, and after 120-140 DEG C of high-temperature stirring 2-3h, cooling discharging obtains.
5. the mixed fillers of a kind of paint according to claim 1, is characterized in that: described inorganic water-absorption particle is ion exchange resin ball grain or superabsorbent gels, potassium type resin cation (R.C.) spherolite.
6. prepare the method for the mixed fillers of a kind of paint in claim 1 or 2, it is characterized in that:
First all raw materials in raw material except mediation solvent are mixed, and then grind accordingly, until particle fineness is after 20um-30um, it is all dropped in stirred pot, then the mediation solvent in raw material is all poured into wherein, stir, until be after paste, take out and dry at abrasive dust, can obtain.