CN105036650A - Polymer mortar terrace and preparing method thereof - Google Patents
Polymer mortar terrace and preparing method thereof Download PDFInfo
- Publication number
- CN105036650A CN105036650A CN201510435456.5A CN201510435456A CN105036650A CN 105036650 A CN105036650 A CN 105036650A CN 201510435456 A CN201510435456 A CN 201510435456A CN 105036650 A CN105036650 A CN 105036650A
- Authority
- CN
- China
- Prior art keywords
- polymer mortar
- major ingredient
- mortar terrace
- terrace
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a polymer mortar terrace and a preparing method thereof. The polymer mortar terrace comprises a bottom material layer, a main material layer and a surface material layer which are sequentially laid on a concrete base body. The bottom material layer is composed of, by weight, 2-20% of emulsion, 1-10% of water reducing agents, 2-20% of silica fume, 0.1-1% of cellulose ether, 2-20% of fine sand and 30-70% of white cement; the main material layer comprises, by weight, 1-10% of emulsion, 1-10% of water reducing agents, 1-10% of silica fume, 0.02-0.2% of cellulose ether, 1-10% of fine sand, 0.1-1% of pigment, 4-40% of white cement and 20-70% of graded joint sand; the surface material layer is formed by mixing a polymer and water, wherein the weight content of the polymer is 30-70%. Compared with the prior art, the polymer mortar terrace obtained through preparation is high in strength and low in cost, and has excellent anti-corrosion, temperature resistant, permeation resistant, antiskid and self-cleaning properties, and the preparing technology is simple, easy to implement and suitable for industrial production application.
Description
Technical field
The present invention relates to a kind of terrace and preparation method thereof, especially relate to a kind of polymer mortar terrace and preparation method thereof.
Background technology
Terrace is the part that industrial ground contacts with bottom, and it bears the load of industrial ground, requires to have certain strength and stiffness, and has protection against the tide, waterproof, warming, wear-resisting performance.There is close relationship in bottom and outdoor buildings place, handle terrace and platform, step and the buildings relation along place, limit well, Building And Grounds are joined clear and definite, whole harmonious.
Terrace is applicable to some for the higher place of health conditions requiring such as hospital ground, food factory's mill floor, pharmaceutical factory's mill floor, laboratory building ground, machine room ground etc.; Require the anti-impact anticorrosive wear-resisting ground of pressure such as underground parking, factory's storehouse (crossing fork truck region) etc.Floor material main at present has inorganic abrasion proof ground material, epoxy mortar earth material, brick plate paving, polyurethane cement earth material etc., have the industries such as the food of very high request in the anti-skidding of ground and health, above-mentioned floor material has such or such shortcoming.Be not suitable for wet environment as inorganic abrasion-resistant ground and do not reach foodstuff production hygienic requirements; Epoxy mortar earth material non-refractory rinses, fragile; The easy breed bacteria in brick plate pavement joint place, difficulty reaches hygienic standard; Polyurethane cement ground cost is higher.
Chinese patent 201310286930.3 discloses a kind of abrasion-proof terrace, comprises wearproof paint layer, tack coat, fine sand layer, basic unit, protective layer and film layer, and described wearproof paint layer is in the superiors; Described protective layer is below wearproof paint layer; Described film layer is in the middle of protective layer and tack coat; Described fine sand layer is in the middle of tack coat and basic unit.Although this patent has good erosion resistance and skid resistance, its automatically cleaning ability, is difficult to the hygienic requirements reaching food factory's room earth material.
Summary of the invention
Object of the present invention be exactly in order to overcome above-mentioned prior art exist defect and a kind of polymer mortar terrace and preparation method thereof is provided.
Object of the present invention can be achieved through the following technical solutions:
A kind of polymer mortar terrace, this terrace comprises the initial bed be laid on successively on concrete substrate, major ingredient layer and precoat,
Described initial bed is made up of the component of following weight percentage:
Described major ingredient layer comprises the component of following weight percentage:
Described precoat is mixed by polyurethane acroleic acid and water, and wherein, the weight content of polyurethane acroleic acid is 30 ~ 70%.
The thickness of described initial bed is 0.1-0.9mm, and the thickness of described major ingredient layer is 6-18mm, and the thickness of described precoat is 0.1-0.5mm.
Described emulsion is mixed by acrylate copolymer and water, and wherein, the weight content of acrylate copolymer is 30 ~ 70%.
Described acrylate copolymer is polyethyl acrylate or polymethylmethacrylate.
Described water reducer is melmac water reducer or polycarboxylate dehydragent.
Described ether of cellulose is methylcellulose gum.
Described graded sand is prototype gradation sand.
A preparation method for polymer mortar terrace, comprises the following steps:
(1) by concrete substrate matte finish, then use high pressure water flushing wash clean, and keep concrete substrate surface moisture and not ponding;
(2) emulsion 2-20%, water reducer 1-10%, silicon ash 2-20%, ether of cellulose 0.1-1%, fine sand 2-20% and white cement 30-70% is taken by mass percentage, be uniformly mixed, obtained bed material, and by its evenly brushing concrete substrate after treatment, obtain initial bed;
(3) content takes emulsion 1-10%, water reducer 1-10%, silicon ash 1-10%, ether of cellulose 0.02-0.2%, fine sand 1-10%, pigment 0.1-1%, white cement 4-40% and graded sand 20-70% by mass percentage, be uniformly mixed, obtained major ingredient, and it is evenly paved on initial bed, obtain major ingredient layer after floating;
(4) content takes polymkeric substance 30 ~ 70% by mass percentage, and surplus is water, is uniformly mixed, obtained fabric, and by its even application on major ingredient layer, obtained precoat;
Above-mentioned steps is all 10 ~ 35 DEG C in temperature, carries out under condition of normal pressure, in addition, needs to keep calm, without rain, without direct sunlight in construction process.
Inventive polymers mortar terrace comprises the initial bed be laid on concrete substrate, major ingredient layer and precoat and obtained polymer mortar terrace, the first hacking of concrete substrate also keeps moistening, initial bed can be made to be combined with concrete substrate better, simultaneously, initial bed adopts the polymer mortar material similar to major ingredient Rotating fields performance, thus greatly can increase the bonding of major ingredient layer and concrete substrate, major ingredient layer adopts acrylate copolymer emulsion mortar, there is after shaping very high strength and excellent corrosion-resistant, resistance to elevated temperatures, simultaneously, major ingredient layer can according to the demand of different client, add the pigment of different colours, make product resolution attractive in appearance higher, precoat adopts polyurethane acrylic acid paint, the impervious of surface can be increased, wear resisting property, make surface easily cleaning.The environmental protection of this terrace raw materials, nontoxic, the grating of sand ensures the high strength of system and anti-skidding, and the apolegamy of admixture is considered system densification, flawless, impervious etc. to add the selection of emulsion, improves heatproof, the performance such as durable.
Compared with prior art, the present invention has the following advantages:
1) intensity is high, cost is low: the shaping rear intensity of the polymer mortar terrace that the present invention obtains is high, thus saves terrace materials, and cost is reduced;
2) anti-corrosion, heatproof, anti-permeability performance excellence: polymer mortar terrace adopts acrylate copolymer emulsion, graded sand and extraordinary admixture, forms the tridimensional network of densification after solidification;
3) anti-skidding, self-cleaning performance is excellent: the roughness that the employing of graded sand makes surperficial self-assembling formation certain, so anti-skidding, the employing polyurethane acrylic acid paint of coating materials, makes surface compact impermeabilisation, not easily contaminated, pollutes also easy cleaning even if having;
4) preparation process is simple: operation is simple for the preparation method of polymer mortar terrace of the present invention, and the work group of 6 ~ 8 people can complete the workload of the terrace of 300 square meter every day.
Accompanying drawing explanation
Fig. 1 is the structural representation of polymer mortar terrace prepared by the present invention;
In figure, 1-concrete substrate, 2-initial bed, 3-major ingredient layer, 4-precoat.
Embodiment
Below in conjunction with the drawings and specific embodiments, the present invention is described in detail.The present embodiment is implemented premised on technical solution of the present invention, give detailed embodiment and concrete operating process, but protection scope of the present invention is not limited to following embodiment.
Embodiment 1
A kind of polymer mortar terrace, comprise the initial bed be successively set on concrete substrate, major ingredient layer and precoat, as shown in Figure 1, this terrace is prepared from by following steps its structure:
(1) by concrete substrate matte finish, then use high pressure water flushing wash clean, and keep concrete substrate surface moisture and not ponding;
(2) by mass percentage take mass concentration be 70% polyethyl acrylate emulsion 2%, melmac water reducer 10%, silicon ash 2%, methylcellulose gum 0.1%, fine sand 20% and white cement 65.9%, be uniformly mixed, obtained bed material, and by its evenly brushing concrete substrate after treatment, obtain the initial bed that thickness is 0.5mm;
(3) by mass percentage content take concentration be 60% polyethyl acrylate emulsion 10%, polycarboxylate dehydragent 10%, silicon ash 10%, methylcellulose gum 0.2%, fine sand 5%, red pigment 1%, white cement 20% and prototype gradation sand 43.8%, be uniformly mixed, obtained major ingredient, and it is evenly paved on initial bed, obtain the major ingredient layer that thickness is 18mm after floating;
(4) content takes polyurethane acroleic acid 30% by mass percentage, and surplus is water, is uniformly mixed, obtained fabric, and by its even application on major ingredient layer, obtained thickness is the precoat of 0.4mm, i.e. obtained polymer mortar terrace;
Above-mentioned steps is all 25 DEG C in temperature, carries out under condition of normal pressure, in addition, needs to keep calm, without rain, without direct sunlight in construction process.
Embodiment 2
A kind of polymer mortar terrace, comprise the initial bed be successively set on concrete substrate, major ingredient layer and precoat, this terrace is prepared from by following steps:
(1) by concrete substrate matte finish, then use high pressure water flushing wash clean, and keep concrete substrate surface moisture and not ponding;
(2) by mass percentage take mass concentration be 30% polymethylmethacrylate emulsion 20%, polycarboxylate dehydragent 10%, silicon ash 20%, methylcellulose gum 1%, fine sand 19% and white cement 30%, be uniformly mixed, obtained bed material, and by its evenly brushing concrete substrate after treatment, obtain the initial bed that thickness is 0.1mm;
(3) by mass percentage content take concentration be 70% polymethylmethacrylate emulsion 5%, polycarboxylate dehydragent 3.8%, silicon ash 1%, methylcellulose gum 0.1%, fine sand 10%, veridian 0.1%, white cement 10% and prototype gradation sand 70%, be uniformly mixed, obtained major ingredient, and it is evenly paved on initial bed, obtain the major ingredient layer that thickness is 6mm after floating;
(4) content takes polyurethane acroleic acid 70% by mass percentage, and surplus is water, is uniformly mixed, obtained fabric, and by its even application on major ingredient layer, obtained thickness is the precoat of 0.1mm, i.e. obtained polymer mortar terrace;
Above-mentioned steps is all 35 DEG C in temperature, carries out under condition of normal pressure, in addition, needs to keep calm, without rain, without direct sunlight in construction process.
Embodiment 3
A kind of polymer mortar terrace, comprise the initial bed be successively set on concrete substrate, major ingredient layer and precoat, this terrace is prepared from by following steps:
(1) by concrete substrate matte finish, then use high pressure water flushing wash clean, and keep concrete substrate surface moisture and not ponding;
(2) by mass percentage take mass concentration be 40% polyethyl acrylate emulsion 10%, melmac water reducer 1%, silicon ash 16.5%, methylcellulose gum 0.5%, fine sand 2% and white cement 70%, be uniformly mixed, obtained bed material, and by its evenly brushing concrete substrate after treatment, obtain the initial bed that thickness is 0.9mm;
(3) by mass percentage content take concentration be 30% polymethylmethacrylate emulsion 1%, melmac water reducer 1%, silicon ash 5%, methylcellulose gum 0.02%, fine sand 1%, yellow ultramarine 0.5%, white cement 40% and prototype gradation sand 51.48%, be uniformly mixed, obtained major ingredient, and it is evenly paved on initial bed, obtain the major ingredient layer that thickness is 16mm after floating;
(4) content takes polyurethane acroleic acid 50% by mass percentage, and surplus is water, is uniformly mixed, obtained fabric, and by its even application on major ingredient layer, obtained thickness is the precoat of 0.5mm, i.e. obtained polymer mortar terrace;
Above-mentioned steps is all 10 DEG C in temperature, carries out under condition of normal pressure, in addition, needs to keep calm, without rain, without direct sunlight in construction process.
Embodiment 4
A kind of polymer mortar terrace, comprise the initial bed be successively set on concrete substrate, major ingredient layer and precoat, this terrace is prepared from by following steps:
(1) by concrete substrate matte finish, then use high pressure water flushing wash clean, and keep concrete substrate surface moisture and not ponding;
(2) by mass percentage take mass concentration be 50% polyethyl acrylate emulsion 12%, polycarboxylate dehydragent 5%, silicon ash 12.5%, methylcellulose gum 0.5%, fine sand 10% and white cement 60%, be uniformly mixed, obtained bed material, and by its evenly brushing concrete substrate after treatment, obtain the initial bed that thickness is 0.4mm;
(3) by mass percentage content take concentration be 50% polymethylmethacrylate emulsion 8%, melmac water reducer 8%, silicon ash 10%, methylcellulose gum 0.2%, fine sand 8%, red pigment 0.1%, white cement 4% and prototype gradation sand 61.7%, be uniformly mixed, obtained major ingredient, and it is evenly paved on initial bed, obtain the major ingredient layer that thickness is 12mm after floating;
(4) content takes polyurethane acroleic acid 50% by mass percentage, and surplus is water, is uniformly mixed, obtained fabric, and by its even application on major ingredient layer, obtained thickness is the precoat of 0.5mm, i.e. obtained polymer mortar terrace;
Above-mentioned steps is all 25 DEG C in temperature, carries out under condition of normal pressure, in addition, needs to keep calm, without rain, without direct sunlight in construction process.
Embodiment 5
A kind of polymer mortar terrace, comprise the initial bed be successively set on concrete substrate, major ingredient layer and precoat, this terrace is prepared from by following steps:
(1) by concrete substrate matte finish, then use high pressure water flushing wash clean, and keep concrete substrate surface moisture and not ponding;
(2) by mass percentage take mass concentration be 50% polyethyl acrylate emulsion 12%, polycarboxylate dehydragent 5%, silicon ash 12.5%, methylcellulose gum 0.5%, fine sand 10% and white cement 60%, be uniformly mixed, obtained bed material, and by its evenly brushing concrete substrate after treatment, obtain the initial bed that thickness is 0.4mm;
(3) by mass percentage content take concentration be 50% polymethylmethacrylate emulsion 10%, melmac water reducer 10%, silicon ash 10%, methylcellulose gum 0.1%, fine sand 10%, red pigment 0.1%, white cement 39.8% and prototype gradation sand 20%, be uniformly mixed, obtained major ingredient, and it is evenly paved on initial bed, obtain the major ingredient layer that thickness is 12mm after floating;
(4) content takes polyurethane acroleic acid 50% by mass percentage, and surplus is water, is uniformly mixed, obtained fabric, and by its even application on major ingredient layer, obtained thickness is the precoat of 0.5mm, i.e. obtained polymer mortar terrace;
Above-mentioned steps is all 25 DEG C in temperature, carries out under condition of normal pressure, in addition, needs to keep calm, without rain, without direct sunlight in construction process.
Following table is that the correlated performance of preparation-obtained polymer mortar terrace in above-described embodiment detects data, specific as follows:
Ultimate compression strength in above table measures according to People's Republic of China (PRC) industry standard JG/T23-2011 " inspection by rebound method concrete compressive strength technical regulation ".
Claims (8)
1. a polymer mortar terrace, is characterized in that, this terrace comprises the initial bed be laid on successively on concrete substrate, major ingredient layer and precoat,
Described initial bed is made up of the component of following weight percentage:
Described major ingredient layer comprises the component of following weight percentage:
Described precoat is mixed by polyurethane acroleic acid and water, and wherein, the weight content of polyurethane acroleic acid is 30 ~ 70%.
2. a kind of polymer mortar terrace according to claim 1, is characterized in that, the thickness of described initial bed is 0.1-0.9mm, and the thickness of described major ingredient layer is 6-18mm, and the thickness of described precoat is 0.1-0.5mm.
3. a kind of polymer mortar terrace according to claim 1, it is characterized in that, described emulsion is mixed by acrylate copolymer and water, and wherein, the weight content of acrylate copolymer is 30 ~ 70%.
4. a kind of polymer mortar terrace according to claim 3, is characterized in that, described acrylate copolymer is polyethyl acrylate or polymethylmethacrylate.
5. a kind of polymer mortar terrace according to claim 1, is characterized in that, described water reducer is melmac water reducer or polycarboxylate dehydragent.
6. a kind of polymer mortar terrace according to claim 1, is characterized in that, described ether of cellulose is methylcellulose gum.
7. a kind of polymer mortar terrace according to claim 1, is characterized in that, described graded sand is prototype gradation sand.
8. a preparation method for the polymer mortar terrace as described in as arbitrary in claim 1 ~ 7, is characterized in that, comprise the following steps:
(1) by concrete substrate matte finish, then use high pressure water flushing wash clean, and keep concrete substrate surface moisture and not ponding;
(2) emulsion 2-20%, water reducer 1-10%, silicon ash 2-20%, ether of cellulose 0.1-1%, fine sand 2-20% and white cement 30-70% is taken by mass percentage, be uniformly mixed, obtained bed material, and by its evenly brushing concrete substrate after treatment, obtain initial bed;
(3) content takes emulsion 1-10%, water reducer 1-10%, silicon ash 1-10%, ether of cellulose 0.02-0.2%, fine sand 1-10%, pigment 0.1-1%, white cement 4-40% and graded sand 20-70% by mass percentage, be uniformly mixed, obtained major ingredient, and it is evenly paved on initial bed, obtain major ingredient layer after floating;
(4) content takes polymkeric substance 30 ~ 70% by mass percentage, and surplus is water, is uniformly mixed, obtained fabric, and by its even application on major ingredient layer, obtained precoat;
Above-mentioned steps is all 10 ~ 35 DEG C in temperature, carries out under condition of normal pressure.