CN104917019A - Tetrapod-like zinc oxide whisker doped carbon brush for noise reduction wear-resisting motor and preparation method of carbon brush - Google Patents

Tetrapod-like zinc oxide whisker doped carbon brush for noise reduction wear-resisting motor and preparation method of carbon brush Download PDF

Info

Publication number
CN104917019A
CN104917019A CN201510253795.1A CN201510253795A CN104917019A CN 104917019 A CN104917019 A CN 104917019A CN 201510253795 A CN201510253795 A CN 201510253795A CN 104917019 A CN104917019 A CN 104917019A
Authority
CN
China
Prior art keywords
carbon brush
zinc oxide
noise reduction
wear
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201510253795.1A
Other languages
Chinese (zh)
Inventor
夏保东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui A Nail Trade Co Ltd
Original Assignee
Anhui A Nail Trade Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui A Nail Trade Co Ltd filed Critical Anhui A Nail Trade Co Ltd
Priority to CN201510253795.1A priority Critical patent/CN104917019A/en
Publication of CN104917019A publication Critical patent/CN104917019A/en
Pending legal-status Critical Current

Abstract

The invention belongs to the carbon brush technical field and relates to a tetrapod-like zinc oxide whisker doped carbon brush for a noise reduction wear-resisting motor and a preparation method of the carbon brush. According to the carbon brush, middle-temperate coal tar pitch, epoxy resin and polyvinyl butyral are mixed together so as to be adopted as an adhesive; and the composite adhesive has strong adhesion for raw materials, high tension and little possibility of cracking, and doped tetrapod-like zinc oxide whiskers has wear resistance, vibration reduction, noise reduction and toughening effects, and therefore, the use performance of the carbon brush can be effectively improved; nano-carbon sol is adopted, and therefore, the electric conductivity of the carbon brush can be improved, and the wear resistance of the carbon brush can be increased. The carbon brush prepared by adopting the method of the invention has the advantages of excellent abrasion resistance in operation, stable operation, low noise, excellent electric conduction performance and no damage to a rotor and a stator.

Description

Wear-resisting carbon brush used for electric engine of noise reduction of a kind of blending four acicular type zinc oxide crystal whisker and preparation method thereof
Technical field
The present invention relates to carbon brush technical field, wear-resisting carbon brush used for electric engine of noise reduction being specifically related to a kind of blending four acicular type zinc oxide crystal whisker and preparation method thereof.
Background technology
Carbon brush is a class slide contact member, be widely used in many electric equipments, it is motor, the device of transferring energy and signal between the standing part of engine or other rotating machineries and rotating part, its composition material is primarily of graphite, Resin adhesive and other auxiliary agents, then make through sinter molding, conventional carbon brush in use ubiquity wears no resistance, loss is large, the problems such as useful life is short, and there is pollution in process of production, therefore research and development service efficiency is badly in need of high, the carbon brush material of Environmental Safety, to adapt to the demand in market.
Summary of the invention
The object of the invention is to, wear-resisting carbon brush used for electric engine of noise reduction providing a kind of blending four acicular type zinc oxide crystal whisker and preparation method thereof, to achieve these goals, the technical solution used in the present invention is as follows:
A kind of wear-resisting carbon brush used for electric engine of noise reduction of blending four acicular type zinc oxide crystal whisker, it is characterized in that, this carbon brush is made up of the raw material of following weight portion: four acicular type zinc oxide crystal whisker 4-5, polyvinyl butyral resin 2-3, high purity graphite 50-60, medium temperature coal pitch 30-35, conductive carbon black 5-8, nano carbon sol 10-12, castor oil 8-10, epoxy resin 10-12, dodecyl sodium sulfate 0.1-0.2, nano-aluminium oxide 2-3, titanate coupling agent 1-2.
The preparation method of the wear-resisting carbon brush used for electric engine of noise reduction of described a kind of blending four acicular type zinc oxide crystal whisker is: first each component dropped into after mixing in mixer, be heated to 60-80 DEG C, continue to be uniformly mixed 30-40min, subsequently gained material is cooled, drop into backflow in pulverizer to pulverize, make gained powder cross 100 mesh sieves, then by compressing for gained micro mist band line, product after shaping is sent in blanket of nitrogen sintering furnace and is sintered, and gets product after terminating through cooling, electric welding, packaging.
Described sintering condition is: sintering temperature: 300-350 DEG C; Sintering time 6-10h.
Beneficial effect: the present invention utilizes medium temperature coal pitch to mix as bonding agent with epoxy resin, polyvinyl butyral resin, the bonding force of this composite caking agent to raw material is strong, tension force is good, not easy to crack, the four acicular type zinc oxide crystal whisker of blending has wear-resisting, vibration damping, noise reduction, the effect such as toughness reinforcing, effectively improve the serviceability of carbon brush, nano carbon sol add the conductivity that improve carbon brush, strengthen resistance to wear, the carbon brush that the present invention prepares in use resistance to wear is good, smooth running, and noise is little, conduct electricity efficiently excellent, do not hinder rotor and stator.
Embodiment
Embodiment
The carbon brush of the present embodiment is made up of the raw material of following weight portion: four acicular type zinc oxide crystal whisker 4.5, polyvinyl butyral resin 2.5, high purity graphite 58, medium temperature coal pitch 32, conductive carbon black 6, nano carbon sol 10, castor oil 9, epoxy resin 12, dodecyl sodium sulfate 0.2, nano-aluminium oxide 2.5, titanate coupling agent 1.8.
Its preparation method is: first each component dropped into after mixing in mixer, be heated to 60-80 DEG C, continue to be uniformly mixed 35min, subsequently gained material is cooled, drop into backflow in pulverizer to pulverize, make gained powder cross 100 mesh sieves, then by compressing for gained micro mist band line, product after shaping is sent in blanket of nitrogen sintering furnace and is sintered, and gets product after terminating through cooling, electric welding, packaging.
Wherein sintering condition is: sintering temperature: 300-350 DEG C; Sintering time 8h.
The carbon brush the performance test results that the present embodiment obtains is as follows:
Test item Detected value
Size 5mm*5mm*15mm
Shore hardness 18
Abrasion loss mm/100H 0.42
Slip noise (dB) ≤40
Useful life (H) ≥1225
Spark situation Stable
Resistivity μ Ω .m 420

Claims (3)

1. the wear-resisting carbon brush used for electric engine of the noise reduction of a blending four acicular type zinc oxide crystal whisker, it is characterized in that, this carbon brush is made up of the raw material of following weight portion: four acicular type zinc oxide crystal whisker 4-5, polyvinyl butyral resin 2-3, high purity graphite 50-60, medium temperature coal pitch 30-35, conductive carbon black 5-8, nano carbon sol 10-12, castor oil 8-10, epoxy resin 10-12, dodecyl sodium sulfate 0.1-0.2, nano-aluminium oxide 2-3, titanate coupling agent 1-2.
2. the preparation method of the wear-resisting carbon brush used for electric engine of noise reduction of a kind of blending four acicular type zinc oxide crystal whisker as claimed in claim 1, it is characterized in that, described preparation method is: first each component dropped into after mixing in mixer, be heated to 60-80 DEG C, continue to be uniformly mixed 30-40min, subsequently gained material is cooled, drop into backflow in pulverizer to pulverize, gained powder is made to cross 100 mesh sieves, again by compressing for gained micro mist band line, product after shaping is sent in blanket of nitrogen sintering furnace and is sintered, and gets product after terminating through cooling, electric welding, packaging.
3. the preparation method of the wear-resisting carbon brush used for electric engine of noise reduction of a kind of blending four acicular type zinc oxide crystal whisker as claimed in claim 2, it is characterized in that, in described sintering process, sintering condition is: sintering temperature: 300-350 DEG C; Sintering time 6-10h.
CN201510253795.1A 2015-05-18 2015-05-18 Tetrapod-like zinc oxide whisker doped carbon brush for noise reduction wear-resisting motor and preparation method of carbon brush Pending CN104917019A (en)