CN104817960A - Waterproof abrasion-resisting coating for planting machine - Google Patents
Waterproof abrasion-resisting coating for planting machine Download PDFInfo
- Publication number
- CN104817960A CN104817960A CN201510215511.XA CN201510215511A CN104817960A CN 104817960 A CN104817960 A CN 104817960A CN 201510215511 A CN201510215511 A CN 201510215511A CN 104817960 A CN104817960 A CN 104817960A
- Authority
- CN
- China
- Prior art keywords
- parts
- planting machine
- coating
- kaolin
- propylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a waterproof abrasion-resisting coating for a planting machine. The coating consists of, by mass, 15-25 parts of polytetrafluoroethylene resin, 3-5 parts of trioctyl phosphate, 7-10 parts of talcum powder, 20-30 parts of chlorosulfonated polyethylene, 30-45 parts of coal tar, 8-20 parts of maleic anhydride, 3-5 parts of kaolin, 2-5 parts of light calcium carbonate and 6-11 parts of propylene glycol. The waterproof abrasion-resisting coating for the planting machine is good in waterproof performance, abrasion-resisting performance and mechanical performance.
Description
Technical field
The present invention relates to paint field, especially, relate to a kind of planting machine waterproof antiwear coating.
Background technology
Mechanical means (such as planting machine) is present in all trades and professions, has brought a lot of products and facility, plays very important effect in the life of people.
Mechanical means generally uses metal to make, and therefore needs to do WATER REPELLENT.Meanwhile, mechanical means is in use easily worn.
One of method addressed these problems at present is exactly at planting machine top layer coating coating.But the water resistance of existing planting machine coating is not high, easily weares and teares.
Summary of the invention
The object of the invention is to provide a kind of planting machine waterproof antiwear coating, not high with the water resistance solving planting machine coating in prior art, the problem of easily wearing and tearing.
For achieving the above object, the invention provides a kind of planting machine waterproof antiwear coating, wherein, this coating is made up of the component of following massfraction:
Teflon resin 15-25 part;
Trioctyl phosphate 3-5 part;
Talcum powder 7-10 part;
Chlorosulfonated polyethylene 20-30 part;
Coal tar 30-45 part;
MALEIC ANHYDRIDE MIN 99.5 8-20 part;
Kaolin 3-5 part;
Light calcium carbonate 2-5 part; And
Propylene glycol 6-11 part.
Further, the invention provides a kind of planting machine waterproof antiwear coating, wherein, this coating is made up of the component of following massfraction: teflon resin 15 parts; Trioctyl phosphate 3 parts; Talcum powder 8 parts; Chlorosulfonated polyethylene 25 parts; 35 parts, coal tar; MALEIC ANHYDRIDE MIN 99.5 8 parts; Kaolin 3 parts; Light calcium carbonate 3 parts; And propylene glycol 6 parts.
Further, the invention provides a kind of planting machine waterproof antiwear coating, wherein, this coating is made up of the component of following massfraction: teflon resin 25 parts; Trioctyl phosphate 5 parts; Talcum powder 10 parts; Chlorosulfonated polyethylene 30 parts; 35 parts, coal tar; MALEIC ANHYDRIDE MIN 99.5 18 parts; Kaolin 3 parts; Light calcium carbonate 5 parts; And propylene glycol 10 parts.
The present invention has following beneficial effect: the invention provides a kind of planting machine coating, not only water resistance is high, and wear resistance is good, and mechanical property is high.
Embodiment
The planting machine waterproof antiwear coating that this preferred embodiment provides, its specific implementation process is as follows:
Wherein, this planting machine waterproof antiwear coating is made up of the component of following massfraction:
Teflon resin 15-25 part;
Trioctyl phosphate 3-5 part;
Talcum powder 7-10 part;
Chlorosulfonated polyethylene 20-30 part;
Coal tar 30-45 part;
MALEIC ANHYDRIDE MIN 99.5 8-20 part;
Kaolin 3-5 part;
Light calcium carbonate 2-5 part; And
Propylene glycol 6-11 part.
Embodiment 1:
Wherein, this planting machine waterproof antiwear coating is made up of the component of following massfraction: teflon resin 15 parts; Trioctyl phosphate 3 parts; Talcum powder 8 parts; Chlorosulfonated polyethylene 25 parts; 35 parts, coal tar; MALEIC ANHYDRIDE MIN 99.5 8 parts; Kaolin 3 parts; Light calcium carbonate 3 parts; And propylene glycol 6 parts.
Embodiment 2:
Wherein, this planting machine waterproof antiwear coating is made up of the component of following massfraction: teflon resin 25 parts; Trioctyl phosphate 5 parts; Talcum powder 10 parts; Chlorosulfonated polyethylene 30 parts; 35 parts, coal tar; MALEIC ANHYDRIDE MIN 99.5 18 parts; Kaolin 3 parts; Light calcium carbonate 5 parts; And propylene glycol 10 parts.
As can be seen from the above description, the above embodiments of the present invention achieve following technique effect:
The invention provides a kind of planting machine coating, not only water resistance is high, and wear resistance is good, and mechanical property is high.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention; For a person skilled in the art, the present invention can have various modifications and variations.Within the spirit and principles in the present invention all, any amendment done, equivalent replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (3)
1. a planting machine waterproof antiwear coating, is characterized in that, this coating is made up of the component of following massfraction:
Teflon resin 15-25 part;
Trioctyl phosphate 3-5 part;
Talcum powder 7-10 part;
Chlorosulfonated polyethylene 20-30 part;
Coal tar 30-45 part;
MALEIC ANHYDRIDE MIN 99.5 8-20 part;
Kaolin 3-5 part;
Light calcium carbonate 2-5 part; And
Propylene glycol 6-11 part.
2. planting machine waterproof antiwear coating according to claim 1, it is characterized in that, this coating is made up of the component of following massfraction: teflon resin 15 parts; Trioctyl phosphate 3 parts; Talcum powder 8 parts; Chlorosulfonated polyethylene 25 parts; 35 parts, coal tar; MALEIC ANHYDRIDE MIN 99.5 8 parts; Kaolin 3 parts; Light calcium carbonate 3 parts; And propylene glycol 6 parts.
3. planting machine waterproof antiwear coating according to claim 1, it is characterized in that, this coating is made up of the component of following massfraction: teflon resin 25 parts; Trioctyl phosphate 5 parts; Talcum powder 10 parts; Chlorosulfonated polyethylene 30 parts; 35 parts, coal tar; MALEIC ANHYDRIDE MIN 99.5 18 parts; Kaolin 3 parts; Light calcium carbonate 5 parts; And propylene glycol 10 parts.