CN104513614B - Timber nursing agent and preparation method thereof - Google Patents
Timber nursing agent and preparation method thereof Download PDFInfo
- Publication number
- CN104513614B CN104513614B CN201310452227.5A CN201310452227A CN104513614B CN 104513614 B CN104513614 B CN 104513614B CN 201310452227 A CN201310452227 A CN 201310452227A CN 104513614 B CN104513614 B CN 104513614B
- Authority
- CN
- China
- Prior art keywords
- timber
- reactor
- nursing
- octadecanol
- sodium benzoate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A provided timber nursing agent comprises the compositions in percent by weight: 10-30% of lemon oil, 10-30% of olive oil, 0.5-5% of beeswax, 2-4.7% of span 60, 2-3.6% of tween 60, 0.5-10% of octadecanol, 3-20% of soybean amine, 5-20% of lignin, 0.5-3% of dodecyl trimethyl ammonium chloride, 30-60% of deionized water, and 0.5-5% of sodium benzoate. The invention also discloses a preparation method for the above timber nursing agent. The timber nursing agent has the characteristics of being environment-friendly, nontoxic, smooth, slippery, resistant to dust, resistant to water, and capable of deeply nursing timber, and is capable of solving problems existing in a conventional timber nursing product. The production technology is simple and easy to enforce, and has good generalization performance.
Description
Technical field
The present invention relates to a kind of nursing agent, particularly to a kind of timber nursing agent, the invention still further relates to this timber nursing
The preparation method of agent.
Background technology
In many building types, timber is affected by the construction material that people like for a long time.In wooden building, timber structure
House is always traditional main flow.The builders of many countries are doing commercial building, communal facility and amusement using timber
Facility and industrial building, timber is also regarded as the mark of the even luxurious degree of only family homes quality.Timber floor increases house
Beautiful and warm, for carpet, timber floor is more easy to keep cleaning, does not attract dust not hide and receives acarid.In outdoor, just like
The wooden finishing of its point, such as stair, railing, panel and lath fence can durable for many years, and increase aesthetic feeling and there is increment make
With.But, timber product is easily affected by weather and environment, and the increase with use time, is easily deformed, so needing
Nursed using timber nursing agent.And existing timber care product universal not environmentally it is impossible to nurse wooden from deep layer.
Content of the invention
In view of this, an object of the present invention it is simply that supply a kind of timber nursing agent, this timber nursing agent environment-protecting asepsis,
Light smooth, dustproof and waterproof, deep layer nursing is wooden, can solve that existing timber care product exists not environmentally be unable to deep layer and protect
The problems such as manage wooden.
The second object of the present invention is the preparation method providing above-mentioned timber nursing agent, the method process is simple, low cost,
There is good generalization.
First purpose of the present invention is to be achieved through the following technical solutions:
A kind of timber nursing agent, its constituent and percentage by weight are as follows:
Fructus Citri Limoniae oil: 10～30%；Olive oil: 10～30%；Cera Flava: 0.5～5%；Emulsifying agent: 2～4.7%；Surfactant:
2～3.6%；Octadecanol: 0.5～10%；Semen sojae atricolor amine: 3～20%；Lignin: 5～20%；Dodecyl trimethyl ammonium chloride: 0.5
～3%；Deionized water: 30～60%；Sodium benzoate: 0.5～5%.
Described emulsifying agent is sorbester p18.
Described surfactant is polysorbate60.
Second object of the present invention is to be achieved through the following technical solutions:
A kind of preparation method of timber nursing agent, comprises the following steps:
(1) Fructus Citri Limoniae oil, olive oil, Cera Flava are put in reactor a, open to do and mix, be warming up to 90 DEG C, keep 2 hours；
(2) by deionized water, emulsifying agent, surfactant, octadecanol, Semen sojae atricolor amine, lignin, trimethyl chlorine
It is sufficiently stirred in change ammonium, sodium benzoate addition reactor b, react 2 hours；
(3) material in reactor a is added in reactor b, fully reaction 2 hours, go out finished product after being cooled to 30 DEG C；
Wherein, the percentage by weight that each component accounts for is: Fructus Citri Limoniae oil: 10～30%；Olive oil: 10～30%；Cera Flava: 0.5～
5%；Emulsifying agent: 2～4.7%；Surfactant: 2～3.6%；Octadecanol: 0.5～10%；Semen sojae atricolor amine: 3～20%；Lignin: 5～
20%；Dodecyl trimethyl ammonium chloride: 0.5～3%；Deionized water: 30～60%；Sodium benzoate: 0.5～5%.
In described step (2), emulsifying agent is sorbester p18.
In described step (2), surfactant is polysorbate60.
The present invention compared with prior art, has the beneficial effect that
1) the raw material health green used by the present invention, product will not be to human body and environmental effects, environment-protecting asepsis；2) produce
Product nurse timber-work, wood surface light can be made smooth, have good sense of touch and visual effect；3) product of the present invention
One layer of overcoat can be produced to timber-work surface product, play the effect of dustproof and waterproof；4) product of the present invention being capable of deep layer
Nursing is wooden, and step is simple, great marketing.
Specific embodiment
Embodiment 1
A kind of timber nursing agent, its constituent and percentage by weight are as follows:
Fructus Citri Limoniae oil: 10%；Olive oil: 10%；Cera Flava: 1.5%；Sorbester p18: 3%；Polysorbate60: 3%；Octadecanol: 1.5%；Semen sojae atricolor
Amine: 3%；Lignin: 5%；Dodecyl trimethyl ammonium chloride: 1.5%；Deionized water: 60%；Sodium benzoate: 1.5%.
The preparation method of above-mentioned timber nursing agent, comprises the following steps:
(1) Fructus Citri Limoniae oil, olive oil, Cera Flava are put in reactor a, open to do and mix, be warming up to 90 DEG C, keep 2 hours；
(2) by deionized water, sorbester p18, polysorbate60, octadecanol, Semen sojae atricolor amine, lignin, trimethyl chlorination
It is sufficiently stirred in ammonium, sodium benzoate addition reactor b, react 2 hours；
(3) material in reactor a is added in reactor b, fully reaction 2 hours, go out finished product after being cooled to 30 DEG C；
Wherein, the percentage by weight that each component accounts for is: Fructus Citri Limoniae oil: 10%；Olive oil: 10%；Cera Flava: 1.5%；Sorbester p18:
3%；Polysorbate60: 3%；Octadecanol: 1.5%；Semen sojae atricolor amine: 3%；Lignin: 5%；Dodecyl trimethyl ammonium chloride: 1.5%；Deionization
Water: 60%；Sodium benzoate: 1.5%.
Embodiment 2
A kind of timber nursing agent, its constituent and percentage by weight are as follows:
Fructus Citri Limoniae oil: 14%；Olive oil: 14%；Cera Flava: 2%；Sorbester p18: 3%；Polysorbate60: 2.5%；Octadecanol: 4.5%；Semen sojae atricolor
Amine: 13%；Lignin: 12%；Dodecyl trimethyl ammonium chloride: 2%；Deionized water: 30%；Sodium benzoate: 3%.
The preparation method of above-mentioned timber nursing agent, comprises the following steps:
(1) Fructus Citri Limoniae oil, olive oil, Cera Flava are put in reactor a, open to do and mix, be warming up to 90 DEG C, keep 2 hours；
(2) by deionized water, sorbester p18, polysorbate60, octadecanol, Semen sojae atricolor amine, lignin, trimethyl chlorination
It is sufficiently stirred in ammonium, sodium benzoate addition reactor b, react 2 hours；
(3) material in reactor a is added in reactor b, fully reaction 2 hours, go out finished product after being cooled to 30 DEG C；
Wherein, the percentage by weight that each component accounts for is: Fructus Citri Limoniae oil: 14%；Olive oil: 14%；Cera Flava: 2%；Sorbester p18: 3%；
Polysorbate60: 2.5%；Octadecanol: 4.5%；Semen sojae atricolor amine: 13%；Lignin: 12%；Dodecyl trimethyl ammonium chloride: 2%；Deionization
Water: 30%；Sodium benzoate: 3%.
Embodiment 3
A kind of timber nursing agent, its constituent and percentage by weight are as follows:
Fructus Citri Limoniae oil: 10%；Olive oil: 10%；Cera Flava 1.5%；Sorbester p18: 2%；Polysorbate60: 2%；Octadecanol: 1.5%；Semen sojae atricolor
Amine: 20%；Lignin: 20%；Dodecyl trimethyl ammonium chloride: 1.5%；Deionized water: 30%；Sodium benzoate: 1.5%.
The preparation method of above-mentioned timber nursing agent, comprises the following steps:
(1) Fructus Citri Limoniae oil, olive oil, Cera Flava are put in reactor a, open to do and mix, be warming up to 90 DEG C, keep 2 hours；
(2) by deionized water, sorbester p18, polysorbate60, octadecanol, Semen sojae atricolor amine, lignin, trimethyl chlorination
It is sufficiently stirred in ammonium, sodium benzoate addition reactor b, react 2 hours；
(3) material in reactor a is added in reactor b, fully reaction 2 hours, go out finished product after being cooled to 30 DEG C；
Wherein, the percentage by weight that each component accounts for is: Fructus Citri Limoniae oil: 10%；Olive oil: 10%；Cera Flava 1.5%；Sorbester p18: 2%；
Polysorbate60: 2%；Octadecanol: 1.5%；Semen sojae atricolor amine: 20%；Lignin: 20%；Dodecyl trimethyl ammonium chloride: 1.5%；Deionization
Water: 30%；Sodium benzoate: 1.5%.
The foregoing is only presently preferred embodiments of the present invention, not in order to limit the present invention, all essences in the present invention
Within god and principle, any modification, equivalent substitution and improvement made etc., should be included within the scope of the present invention.
Claims (2)
1. a kind of timber nursing agent it is characterised in that: its constituent and percentage by weight are as follows:
Fructus Citri Limoniae oil: 10～30%；Olive oil: 10～30%；Cera Flava: 0.5～5%；Emulsifier span 60:2～4.7%；Surface
Active agent tween 60:2～3.6%；Octadecanol: 0.5～10%；Semen sojae atricolor amine: 3～20%；Lignin: 5～20%；Dodecyl
Trimethyl ammonium chloride: 0.5～3%；Deionized water: 30～60%；Sodium benzoate: 0.5～5%.
2. a kind of preparation method of timber nursing agent according to claim 1 is it is characterised in that comprise the following steps:
(1) Fructus Citri Limoniae oil, olive oil, Cera Flava are put in reactor a, open to do and mix, be warming up to 90 DEG C, keep 2 hours；
(2) by deionized water, emulsifier span 60, surface active agent tween 60, octadecanol, Semen sojae atricolor amine, lignin, dodecyl
It is sufficiently stirred in trimethyl ammonium chloride, sodium benzoate addition reactor b, react 2 hours；
(3) material in reactor a is added in reactor b, fully reaction 2 hours, go out finished product after being cooled to 30 DEG C；
Wherein, the percentage by weight that each component accounts for is: Fructus Citri Limoniae oil: 10～30%；Olive oil: 10～30%；Cera Flava: 0.5～
5%；Emulsifying agent: 2～4.7%；Surfactant: 2～3.6%；Octadecanol: 0.5～10%；Semen sojae atricolor amine: 3～20%；Wooden
Element: 5～20%；Dodecyl trimethyl ammonium chloride: 0.5～3%；Deionized water: 30～60%；Sodium benzoate: 0.5～5%.