CN104497935A - Reactive-type plasticizer-free SIS hot-melt pressure-sensitive adhesive - Google Patents
Reactive-type plasticizer-free SIS hot-melt pressure-sensitive adhesive Download PDFInfo
- Publication number
- CN104497935A CN104497935A CN201410783631.5A CN201410783631A CN104497935A CN 104497935 A CN104497935 A CN 104497935A CN 201410783631 A CN201410783631 A CN 201410783631A CN 104497935 A CN104497935 A CN 104497935A
- Authority
- CN
- China
- Prior art keywords
- tackifier
- sensitive adhesive
- softening agent
- response type
- functional polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a reactive-type plasticizer-free SIS hot-melt pressure-sensitive adhesive. The reactive-type plasticizer-free SIS hot-melt pressure-sensitive adhesive comprises the following components in parts by weight: 23-39 parts of thermoplastic elastomer, 4-10 parts of a first functional polymer, 5-30 parts of a second functional polymer, 15-34 parts of a first tackifier, 15-30 parts of a second tackifier, 41-80 parts of a third tackifier, 0.5-2 parts of an anti-aging agent, 0.5-1 part of an antioxidant and 0.5-1 part of a light stabilizer. Since the formula system is free of small-molecule plasticizer and when the formula system is compounded with HDPE polymer sheets, the phenomenon that the plasticizer is dispersed in the polymer sheets cannot be caused and thus the reduction in the tensile property of the sheets and the loss in the property of the adhesive can be effectively avoided.
Description
Technical field
The present invention relates to the hot-fusible high-molecular pressure sensitive adhesive of field of waterproof materials, specifically a kind of a kind of response type being mainly used to make non-bituminous based high molecular self-adhesion glued membrane waterproof roll is without softening agent SIS hot-fusible pressure-sensitive adhesive.
Background technology
The pressure-sensitive adhesive layer that Macromolecular self-adhesive membrane waterproof roll adopts is divided into two large classes, is modifying asphalt class self-adhesive and non-bituminous based high molecular hot-fusible pressure-sensitive adhesive respectively.No matter consider production cost and performance, be all containing small molecules softening agent in which class formula in commercially available coiled material.After glue and macromolecular sheet material compound, this kind of component can enter into sheet material by diffusion thus its tensile property is declined, and elongation at break increases, and simultaneously glue-line a kind of component that runs off also can make the degradation of glue and then affect the normal service life of coiled material.
Usually the hot-fusible high-molecular pressure sensitive adhesive being used in field of waterproof materials generally comprises the components such as polymkeric substance, tackifier, softening agent and protection system, the force of cohesion of glue, by regulating the relative quantity of each component to control, rarely has and utilizes with the force of cohesion of composition regulation glue of functional group and the patent of viscosity or paper.Chinese patent: 93100058.0 disclose a kind of reaction type hot-fusible pressure-sensitive adhesive being applied to tape and mark paper, what he utilized is a kind of method of adding Four composition be made up of phenol formaldehyde resin and suitable auxiliary viscosity reducers in common hot-fusible pressure-sensitive adhesive, and this kind of component can make that graft reaction occurs between each composition in system increases the consistency between system composition thus the performance increasing glue.Its weak point is: containing small molecules softening agent in formula system, with the macromolecular sheet material compound tense such as HDPE, there will be the phenomenon be diffused into due to softening agent in macromolecular sheet material, efficiency does not avoid the performance loss of sheet material stretching degradation and glue itself.
Summary of the invention
Goal of the invention of the present invention is the many defects for prior art, solve common hot-fusible pressure-sensitive adhesive and be applied in the new problem run in Macromolecular self-adhesive membrane waterproof roll, there is provided a kind of based on linear SIS polymkeric substance, using maleic anhydride graft Low Density Polyethylene and high-activity polyisobutene (HRPIB) as functional additive, be aided with hydrogenated petroleum resin, middle-molecular-weihydroxyethyl polyisobutene and low-molecular-weight polyisobutylene as tackifier, add a kind of response type that antioxidant system and anti-ultraviolet ageing system be made without softening agent SIS hot-fusible pressure-sensitive adhesive, it.
Realize above-mentioned purpose by the following technical solutions:
A kind of response type is without softening agent SIS hot-fusible pressure-sensitive adhesive, with weight parts, it consists of: thermoplastic elastomer 23-39 part, first functional polymer 4-10 part, second functional polymer 5-30 part, first tackifier 15-34 part, second tackifier 15-30 part, 3rd tackifier 41-80 part, anti-aging agent 0.5-2 part, oxidation inhibitor 0.5-1 part, photostabilizer 0.5-1 part.
As preferably, described thermoplastic elastomer is polystyrene-poly isoprene-polystyrene triblock copolymer, and wherein the content of polystyrene phase is 29%, and its average weight-molecular mass is 100000-300000, and melting means is 9-16g/10min.
As preferably, described first functional polymer is maleic anhydride (MAH) graft modification Low Density Polyethylene (LDPE), and its percentage of grafting is 1.2%.
As preferably, described second functional polymer is the activity polyisobutylene of molecular weight between 500 ~ 1500 (HRPIB), and its viscosity is 100mPas ~ 600mPas, and wherein the content of molecule chain end methyl vinylidene is 79% ~ 85%.
As preferably, described first tackifier are the low-molecular-weight polyisobutylene of a kind of molecular weight between 2000-3000.
As preferably, described second tackifier are the middle-molecular-weihydroxyethyl polyisobutene of a kind of viscosity-average molecular weight between 30000-60000, staudinger index 21.5.
As preferably, described 3rd tackifier are the hydrogenation C5 petroleum resin of No. 0 look, and softening temperature is 110-130 DEG C.
Compared with traditional hot-fusible pressure-sensitive adhesive formula, remarkable advantage of the present invention is: not containing small molecules softening agent in formula system of the present invention, with the macromolecular sheet material compound tenses such as HDPE, there will not be the phenomenon be diffused into due to softening agent in macromolecular sheet material, thus effectively can avoid the performance loss of sheet material stretching degradation and glue itself.
Invention introduces the polar group maleic anhydride grafted polyethylene (MAH-g-PE) and high-activity polyisobutene (HRPIB) with reactive behavior, these two kinds of components are all the materials with reactive behavior, and polymer chemistry reaction can occur.Can by control relative quantity that two kinds of components add number come the viscosity of finished product glue, tack and force of cohesion, accomplish the angle deisgn product performance from raw material composition.
The use of middle-molecular-weihydroxyethyl polyisobutene of the present invention increases the elasticity of glue-line, resistance to air loss and force of cohesion, and the tack of glue-line is relatively little, but can have and concrete strong bond.Polyisobutene content in system is comparatively large, therefore resistance to low temperature is excellent, and surface tension is close with PE sheet material, and can fully to soak sheet material bonding well.The ability of glue tolerance uviolizing is excellent, can to accomplish to tan by the sun in 15 days still can with concrete bonding.
Embodiment
Below in conjunction with specific embodiment, summary of the invention is further elaborated:
The invention discloses a kind of response type without softening agent SIS hot-fusible pressure-sensitive adhesive, be made up of thermoplastic elastomer, functional polymer, tackifier, anti-aging agent, oxidation inhibitor, photostabilizer, wherein functional polymer is divided into the first functional polymer, the second functional polymer; Tackifier are divided into the first tackifier, the second tackifier, the 3rd tackifier.In mass fraction, it consists of: thermoplastic elastomer 23-39 part, first functional polymer 4-10 part, second functional polymer 5-30 part, first tackifier 15-34 part, second tackifier 15-30 part, the 3rd tackifier 41-80 part, anti-aging agent 0.5-2 part, oxidation inhibitor 0.5-1 part, photostabilizer 0.5-1 part.
Thermoplastic elastomer of the present invention is linear polystyrene-polyisoprene-polystrene triblock copolymer, is called for short SIS.Wherein the mass content of polystyrene phase is 29%, and its average weight-molecular mass is 150000-300000, and melting means number is 9-16g/10min.
First functional polymer is maleic anhydride (MAH) graft modification Low Density Polyethylene (LDPE), and its percentage of grafting is 1.2%.The present invention utilizes and is grafted to a small amount of maleic anhydride functional groups on polyethylene long-chain as reflection active site, by the Control of chemical reaction system viscosity between another active ingredient HRPIB and between this two kinds of materials and other unsaturated components and force of cohesion.
Second functional polymer is the activity polyisobutylene of molecular weight between 500 ~ 1500 (HRPIB), and its viscosity is 100mPas ~ 600mPas, and wherein the content of molecule chain end methyl vinylidene is 79% ~ 85%.
First tackifier are the low-molecular-weight polyisobutylene of a kind of molecular weight between 2000-3000.
Second tackifier are the middle-molecular-weihydroxyethyl polyisobutene of a kind of viscosity-average molecular weight between 30000-60000, staudinger index 21.5.
3rd tackifier are the hydrogenation C5 petroleum resin of No. 0 look, and softening temperature is 110-140 DEG C.
Concrete preparation embodiment:
Embodiment 1:
First reactor is preheated to 130 DEG C, tackifier are added in reactor, first the hydrogenation C5 petroleum resin of 500kg the 3rd tackifier No. 0 look, 10kg anti-aging agent, 5kg oxidation inhibitor, the second tackifier 80kg polyisobutene, the first tackifier 360kg polyisobutene and 260kg second functional polymer high-activity polyisobutene is added, keep temperature, start stirring.150 DEG C are warming up to after 40 minutes, add 260kg SIS linear polystyrene-polyisoprene-polystrene triblock copolymer, stir that after SIS melts completely, within 30 minutes, add 40kg first functional polymer be maleic anhydride (MAH) graft modification Low Density Polyethylene (LDPE) and 5kg photostabilizer, keep temperature, after 1h, component can detect after melting completely.Test formulations in table 1, detected result in table 2.
Embodiment 2:
First reactor is preheated to 130 DEG C, 540kg the 3rd tackifier hydrogenating carbon 5 petroleum resin, 10kg anti-aging agent, 5kg oxidation inhibitor, 80kg second tackifier polyisobutene and 360kg first tackifier polyisobutene and 260kg second functional polymer high-activity polyisobutene is added in reactor, keep temperature, start stirring.150 DEG C are warming up to after 40 minutes, add 300kgSIS, stir that after SIS melts completely, within 30 minutes, add 40kg first functional polymer be maleic anhydride (MAH) graft modification Low Density Polyethylene (LDPE) maleic anhydride grafted polyethylene and 5kg photostabilizer, keep temperature, after 1h, component can detect after melting completely.Test formulations in table 1, detected result in table 2.
Embodiment 3:
First reactor is preheated to 130 DEG C, 580kg the 3rd tackifier hydrogenating carbon 5 petroleum resin, 10kg anti-aging agent, 5kg oxidation inhibitor, 80kg second tackifier polyisobutene and 360kg first tackifier polyisobutene and 230kg second functional polymer high-activity polyisobutene is added in reactor, keep temperature, start stirring.150 DEG C are warming up to after 40 minutes, add 350kg SIS, stir that after SIS melts completely, within 30 minutes, add 40kg first functional polymer be maleic anhydride (MAH) graft modification Low Density Polyethylene (LDPE) maleic anhydride grafted polyethylene and 5kg photostabilizer, keep temperature, after 1h, component can detect after melting completely.Test formulations in table 1, detected result in table 2.
Embodiment 4:
First reactor is preheated to 130 DEG C, add 540kg the 3rd tackifier hydrogenating carbon 5 petroleum resin, 10kg anti-aging agent, 5kg oxidation inhibitor, 80kg second tackifier polyisobutene and 360kg first tackifier polyisobutene and 170kg second functional polymer high-activity polyisobutene wherein, keep temperature, start stirring.150 DEG C are warming up to after 40 minutes, add 300kgSIS, stir that after SIS melts completely, within 30 minutes, add 40kg first functional polymer be maleic anhydride (MAH) graft modification Low Density Polyethylene (LDPE) maleic anhydride grafted polyethylene and 5kg photostabilizer, keep temperature, after 1h, component can detect after melting completely.Test formulations in table 1, detected result in table 2.
As can be seen from the test number in table 2, utilizing the over-all properties of the hot-fusible pressure-sensitive adhesive prepared by the present invention higher than national standard requirement, is the product of excellent performance.
Although above the present invention is described in detail with a general description of the specific embodiments, on basis of the present invention, can make some modifications or improvements it, this will be apparent to those skilled in the art.Therefore, these modifications or improvements without departing from theon the basis of the spirit of the present invention, all belong to the scope of protection of present invention.
Claims (7)
1. a response type is without softening agent SIS hot-fusible pressure-sensitive adhesive, it is characterized in that, with weight parts, it consists of: thermoplastic elastomer 23-39 part, first functional polymer 4-10 part, second functional polymer 5-30 part, first tackifier 15-34 part, second tackifier 15-30 part, the 3rd tackifier 41-80 part, anti-aging agent 0.5-2 part, oxidation inhibitor 0.5-1 part, photostabilizer 0.5-1 part.
2. a kind of response type according to claim 1 is without softening agent SIS hot-fusible pressure-sensitive adhesive, it is characterized in that, described thermoplastic elastomer is polystyrene-poly isoprene-polystyrene triblock copolymer, wherein the content of polystyrene phase is 29%, its average weight-molecular mass is 100000-300000, and melting means is 9-16g/10min.
3. a kind of response type according to claim 1 is without softening agent SIS hot-fusible pressure-sensitive adhesive, it is characterized in that, described first functional polymer is maleic anhydride (MAH) graft modification Low Density Polyethylene (LDPE), and its percentage of grafting is 1.2%.
4. a kind of response type according to claim 1 is without softening agent SIS hot-fusible pressure-sensitive adhesive, it is characterized in that, described second functional polymer is the activity polyisobutylene of molecular weight between 500 ~ 1500 (HRPIB), its viscosity is 100mPas ~ 600mPas, and wherein the content of molecule chain end methyl vinylidene is 79% ~ 85%.
5. a kind of response type according to claim 1 is without softening agent SIS hot-fusible pressure-sensitive adhesive, it is characterized in that, described first tackifier are the low-molecular-weight polyisobutylene of a kind of molecular weight between 2000-3000.
6. a kind of response type according to claim 1 is without softening agent SIS hot-fusible pressure-sensitive adhesive, it is characterized in that, described second tackifier are the middle-molecular-weihydroxyethyl polyisobutene of a kind of viscosity-average molecular weight between 30000-60000, staudinger index 21.5.
7. a kind of response type according to claim 1 is without softening agent SIS hot-fusible pressure-sensitive adhesive, it is characterized in that, described 3rd tackifier are the hydrogenation C5 petroleum resin of No. 0 look, and softening temperature is 110-130 DEG C.