CN104418505A - Preparation process of colored-drawn colored glaze - Google Patents
Preparation process of colored-drawn colored glaze Download PDFInfo
- Publication number
- CN104418505A CN104418505A CN201310375519.3A CN201310375519A CN104418505A CN 104418505 A CN104418505 A CN 104418505A CN 201310375519 A CN201310375519 A CN 201310375519A CN 104418505 A CN104418505 A CN 104418505A
- Authority
- CN
- China
- Prior art keywords
- coloured glaze
- colored
- colored drawing
- kiln
- glaze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation process of colored-drawn colored glaze, which comprises that: a coloured glaze ware is manufactured according to a design draft, then the outer surface of the coloured glaze ware is subjected to colored drawing of patterns with pigments, and the ware is fired in a kiln. The firing process comprises: (1) adding the colored-drawn coloured glaze into a kiln, heating from normal temperature to 650 DEG C-700 DEG C; (2) cooling for 72 hours to reach a natural temperature. The product of the invention has the characteristics of integration of coloured glaze with colored drawing pigments, bright and firm color, no liability to fade, beauty, practicality, and easy cleaning.
Description
Technical field
The present invention relates to colored drawing coloured glaze field, specifically a kind of preparation technology of colored drawing coloured glaze.
Background technology
Carry out colored drawing on coloured glaze type surface, coloured drawing pigment is generally the common normal temperature pigment such as Chinese painting color, oil colour, and color retentivity is poor, easy to change, is easily scratched, and meets the water capacity and is easily cleaned.How to adopt high temperature process to be combined with pigment by coloured glaze is a difficult problem always, because coloured glaze softening temperature is lower, and the fusing point of beramic color is very high.With beramic color painted decoration coloured glaze type surface, when carrying out high-temperature firing, coloured glaze type has arrived the temperature of softening transform, but beramic color can't melt, and adhere to less than coloured glaze surface, thus color is gloomy.
According to this problem, we adopt various coloured glaze colorant to test, and repeatedly test in sintering technology, have grasped and have fired optimum temps scheme.With the colored drawing coloured glaze type that special coloured glaze pigment high-temperature firing technique is produced, color and luster is graceful, firmly bright and new, shows U.S. of colored drawing art, improves class and the artistic grade of coloured glaze works.
Summary of the invention
The object of this invention is to provide a kind of coloured glaze and coloured drawing pigment combines together, be in bright colors, firmly, colour-fast, both artistic and practical, the preparation technology of easy cleaned colored drawing coloured glaze.
Concrete technical scheme is a kind of preparation technology of colored drawing coloured glaze, first producing coloured glaze type according to design original text, then firing placing kiln after pattern on coloured glaze type outside surface pigment colored drawing.
The preparation technology of above-mentioned colored drawing coloured glaze, wherein, described sintering procedure is that (1) is put into the coloured glaze that colored drawing is good in kiln, and kiln is warming up to 650 DEG C-700 DEG C from normal temperature; (2) temperature 72 is moved back little of natural temperature.
The preparation technology of above-mentioned colored drawing coloured glaze, wherein, described coloured glaze type outside surface is shiny surface.
The preparation technology of above-mentioned colored drawing coloured glaze, wherein, described coloured glaze type outside surface is concave surface decorative pattern.
The preparation technology of above-mentioned colored drawing coloured glaze, wherein, described coloured glaze type outside surface is relief-type decorative pattern.
The present invention has following beneficial effect: coloured glaze and coloured drawing pigment combine together, is in bright colors, firmly, colour-fast, both artistic and practical, is easy to cleaning.
Embodiment
Below in conjunction with embodiment, the present invention is described in further detail.
First embodiment: adopted by coloured glaze type outside surface the instruments such as icking tool, cutter, hammer to carry out seal cutting, then texture good for seal cutting is coated with according to the design of creator and paints upper required pigment, after abundant drying, put into kiln, kiln is stopped heating when normal temperature is warming up to 650 DEG C; Then move back temperature 72 little of natural temperature, coloured glaze and pigment are merged, stablize and be admittedly attached to coloured glaze surface.
Second embodiment: coloured glaze type outside surface is coated with according to the layout of creator and paints upper required pigment, put into kiln after abundant drying, kiln is stopped heating when normal temperature is warming up to 680 DEG C; Then move back temperature 72 little of natural temperature, coloured glaze and pigment are merged, stablize and be admittedly attached to coloured glaze surface.
3rd embodiment: coloured glaze type outside surface is delineated relief-type decorative pattern according to the layout of creator, is then coated with and paints required pigment, after abundant drying, put into kiln on relief-type decorative pattern, and kiln is stopped heating when normal temperature is warming up to 690 DEG C; Then move back temperature 72 little of natural temperature, coloured glaze and pigment are merged, stablize and be admittedly attached to coloured glaze surface.
Because special pigment is applicable to the softening temperature that coloured glaze type allows, so pigment is melted in together completely with coloured glaze, bright, firm, will never fade and coloured glaze type does not also change, thus obtain perfect artistic effect.
Certainly; the present invention also can have other various embodiments; when not deviating from the present invention's spirit and essence thereof; those of ordinary skill in the art are when making various corresponding change and distortion according to the present invention, but these change accordingly and are out of shape the protection domain that all should belong to the claim appended by the present invention.
Claims (5)
1. a preparation technology for colored drawing coloured glaze, is characterized in that, first producing coloured glaze type according to design original text, then firing placing kiln after pattern on coloured glaze type outside surface pigment colored drawing.
2. the preparation technology of colored drawing coloured glaze as claimed in claim 1, it is characterized in that, described sintering procedure is:
(1) coloured glaze that colored drawing is good is put in kiln, kiln is warming up to 650 DEG C-700 DEG C from normal temperature;
(2) temperature 72 is moved back little of natural temperature.
3. the preparation technology of colored drawing coloured glaze as claimed in claim 1, it is characterized in that, described coloured glaze type outside surface is shiny surface.
4. the preparation technology of colored drawing coloured glaze as claimed in claim 1, it is characterized in that, described coloured glaze type outside surface is concave surface decorative pattern.
5. the preparation technology of colored drawing coloured glaze as claimed in claim 1, it is characterized in that, described coloured glaze type outside surface is relief-type decorative pattern.