CN104293187A - Anti-aging and anti-static green paint for cabin and preparation method of paint - Google Patents
Anti-aging and anti-static green paint for cabin and preparation method of paint Download PDFInfo
- Publication number
- CN104293187A CN104293187A CN201410469145.6A CN201410469145A CN104293187A CN 104293187 A CN104293187 A CN 104293187A CN 201410469145 A CN201410469145 A CN 201410469145A CN 104293187 A CN104293187 A CN 104293187A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- aging
- sand
- paint
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-aging and anti-static green paint for a cabin. The anti-aging and anti-static green paint is characterized by being prepared from the following raw materials in parts by weight: 16-18 parts of vinyl MQ organosilicon resin, 5-8 parts of melamine formaldehyde resin, 3-5 parts of asymmetric phenylenediamine, 1-2 parts of titanium oxide, 1-2 parts of N-butyl titanate, 3-5 parts of wood wax oil, 2-4 parts of nanometer aluminum oxide, 2-4 parts of asbestos, 3-4 parts of quartz powder, 3-4 parts of bamboo fiber, 1-2 parts of polydimethylsiloxane, 0.7-1.4 parts of JWK-15 anti-static agent, 1-2 parts of trimethylolpropane, 2-3 parts of epoxy linseed oil, 1-2 parts of ammonium bromide, 24-32 parts of modified asphalt, 6-8 parts of modified waste resin sand, 13-15 parts of xylene, 5-7 parts of acetone and 4-6 parts of turpentine. The melamine formaldehyde resin added to the anti-aging and anti-static green paint for the cabin has good wear resistance, high hardness, good waterproofness and ultrahigh thermal stability and insulation property, and the vinyl MQ organosilicon resin added to the paint has excellent heat resistance and low temperature resistance, good film-forming property, appropriate flexibility, and good anti-aging and anti-ultraviolet properties; besides, the waste resin sand is modified; as a result, the anti-fouling, dust-proof, anti-aging and fireproof effects of the paint are improved, and the environment is also protected, and the pollution on soil and water is avoided.
Description
Technical field
The present invention relates to a kind of paint and preparation method thereof, particularly a kind of anti-aging anti-electrostatic cabin green painting and preparation method thereof.
Background technology
The corrosive environment of ocean is complicated, can be divided into marine atmosphere zone (throughout the year not contacting the part of seawater), Sea Water Splashing Zone (position that the splashing of seawater can be sprayed onto), Tidal zone, ocean (during high tide can by the position of seawater immersion), submerged zone, ocean (throughout the year by the region of sea water immersion) and earth district, seabed (part below water immersion district); Form of corrosion is divided into again uniform corrosion, spot corrosion, crevice corrosion, turbulent flow corrosion, cavitation corrosion, galvanic corrosion and corrosion fatigue etc.Boats and ships; be in for a long time among ocean environment; there is salt fog ocean and band slight alkalinity, wherein seawater is more much harder than land to corrosion of metal, in ocean, also have diversified marine attaching organism; they can above alow adhere to; affect the ship speed of a ship or plane, increase fuel consumption, also have strong ultraviolet etc. simultaneously; if do not take sfgd., the work-ing life of boats and ships is very short.The inner paint requirements sticking power of boats and ships is good, and have higher water tolerance, oil-proofness, chemical-resistant and wear resistance, toxicity is lower, and bituminous varnish has excellent erosion resistance, has excellent weather resistance, but poor heat resistance.
Resin sand is formed by mixed preparing such as silica sand, resin and stiffening agents.The various organic resin contained inside the waste resin sand of bulk deposition or organic-inorganic compound, decomposition rate is slow, serious harm is brought to soil, and can acidified soil soil property, some compounds can along with the inflow rivers that drench with rain, polluted source, people, once drink, bring serious infringement can to the health of people.For this situation, waste resin sand is carried out modification by the present invention, not only solves environmental pollution, and adds in paint the effects such as the dirt-resisting dustproof that improve paint, ageing-resistant and fire prevention to.
Summary of the invention
The object of this invention is to provide a kind of anti-aging anti-electrostatic cabin green painting and preparation method thereof.
In order to realize object of the present invention, the present invention is by following scheme implementation:
A kind of anti-aging anti-electrostatic cabin green painting, be made up of the raw material of following weight part: vinyl MQ silicone resin 16-18, terpolycyantoamino-formaldehyde resin 5-8, inclined phenylenediamine 3-5, titanium oxide 1-2, tetrabutyl titanate 1-2, wood wax oil 3-5, nano aluminium oxide 2-4, asbestos 2-4, silica powder 3-4, bamboo fibers 3-4, polydimethylsiloxane 1-2, JWK-15 static inhibitor 0.7-1.4, TriMethylolPropane(TMP) 1-2, epoxidized linseed oil 2-3, brometo de amonio 1-2, modifying asphalt 24-32, modified abandoned resin sand 6-8, dimethylbenzene 13-15, acetone 5-7, turps 4-6,
Described modifying asphalt is made up of the raw material of following weight part: pitch 78-84, sulphur 0.4-1.0, Poly Propylene Wax 0.4-0.8, nano diatomite 0.5-1.0, diaminodiphenylmethane 0.3-0.7, gac 1-2, vinyl chloride-vinyl acetate resin 8-12, maleic anhydride 4-6, Potassium aluminum sulfate dodecahydrate 0.3-0.6, tetrahydrofuran (THF) 7-9, zirconium iso-octoate 0.2-0.4, dibenzoyl peroxide 0.05-0.12, sodium lignosulfonate 0.4-0.8, nano-glass scale 0.4-0.7; Preparation method is to melting by asphalt heating; maleic anhydride and dibenzoyl peroxide is slowly added under the protection of nitrogen; temperature is controlled at 170-180 ° of C; modifying asphalt is obtained stir 0.5-1 hour under 600-800 rev/min after; vinyl chloride-vinyl acetate resin, tetrahydrofuran (THF), zirconium iso-octoate, diaminodiphenylmethane, Poly Propylene Wax are mixed and heated to 130-150 ° of C; then will mix with modifying asphalt, then add all the other surplus materialss and with 800-1200 rev/min of lower agitation grinding 1-1.5 hour.
One of the present invention anti-aging anti-electrostatic cabin green painting, be made up of following concrete steps:
(1) vinyl MQ silicone resin, terpolycyantoamino-formaldehyde resin, modifying asphalt, bamboo fibers, acetone, turps, dimethylbenzene, partially phenylenediamine are dropped in reactor and is heated to 200-250 ° of C, after being uniformly mixed by mixture, under 600-800 rev/min, stir 2-3 hour;
(2) under identical rotating speed, add modified abandoned resin sand, asbestos, silica powder, nano aluminium oxide, titanium oxide, tetrabutyl titanate stirring 30-50 minute, temperature is reduced to 70-90 ° of C, add all the other remaining compositions again, stir in reactor, disperse, material after dispersion is added to grinding distribution in sand mill even, and stirs 20-30 minute under 1200-1400 rev/min;
(3) finely dispersed material is added in filter filters, after filtration, obtain the material that fineness is 20-40 μm, by the material package after filtering.
Modified abandoned resin sand of the present invention, discarded resin sand is added in shakeout to carry out knockout by preparation method, the metal sundries on removing surface and dirt settling, again by the effect of waste resin sand by oscillator, whizzer, the binding agent on removing surface, again antiquated sand is worn into 400-600 order fine powder by ball mill, add the nano-attapulgite of antiquated sand weight 12%, 5% nano zine oxide, 0.4% Sodium hexametaphosphate 99, the alkylphenol polyoxyethylene of 0.2%, the silicon sol of 8% and 0.5-1% silane coupling agent KH560 mixed grinding evenly.
The invention has the advantages that: the terpolycyantoamino-formaldehyde resin that paint of the present invention adds has that wear resistance is good, hardness is high, the thermostability of water-tolerant and superelevation and insulating effect; the vinyl MQ silicone resin added has excellent thermotolerance, resistance to low temperature, good film-forming properties, appropriate snappiness and anti-aging ultraviolet-resistent property; discarded resin sand is also carried out modification by the present invention; not only increase the effects such as the dirt-resisting dustproof of paint, ageing-resistant and fire prevention; but also protect environment, avoid the pollution of soil, water quality.
specific embodiments
Below by specific examples, the present invention is described in detail.
A kind of anti-aging anti-electrostatic cabin green painting, is made up of the raw material of following weight part (kilogram): vinyl MQ silicone resin 18, terpolycyantoamino-formaldehyde resin 7, partially phenylenediamine 5, titanium oxide 1, tetrabutyl titanate 1, wood wax oil 4, nano aluminium oxide 2, asbestos 2, silica powder 3, bamboo fibers 3, polydimethylsiloxane 1, JWK-15 static inhibitor 0.8, TriMethylolPropane(TMP) 1, epoxidized linseed oil 2, brometo de amonio 1, modifying asphalt 28, modified abandoned resin sand 6, dimethylbenzene 14, acetone 6, turps 5;
Described modifying asphalt is made up of the raw material of following weight part (kilogram): pitch 82, sulphur 0.6, Poly Propylene Wax 0.5, nano diatomite 0.8, diaminodiphenylmethane 0.4, gac 1, vinyl chloride-vinyl acetate resin 9, maleic anhydride 4, Potassium aluminum sulfate dodecahydrate 0.4, tetrahydrofuran (THF) 8, zirconium iso-octoate 0.2, dibenzoyl peroxide 0.07, sodium lignosulfonate 0.5, nano-glass scale 0.5; Preparation method is to melting by asphalt heating; maleic anhydride and dibenzoyl peroxide is slowly added under the protection of nitrogen; temperature is controlled at 170-180 ° of C; modifying asphalt is obtained stir 0.5-1 hour under 600-800 rev/min after; vinyl chloride-vinyl acetate resin, tetrahydrofuran (THF), zirconium iso-octoate, diaminodiphenylmethane, Poly Propylene Wax are mixed and heated to 130-150 ° of C; then will mix with modifying asphalt, then add all the other surplus materialss and with 800-1200 rev/min of lower agitation grinding 1-1.5 hour.
One of the present invention anti-aging anti-electrostatic cabin green painting, be made up of following concrete steps:
(1) vinyl MQ silicone resin, terpolycyantoamino-formaldehyde resin, modifying asphalt, bamboo fibers, acetone, turps, dimethylbenzene, partially phenylenediamine are dropped in reactor and is heated to 200-250 ° of C, after being uniformly mixed by mixture, under 600-800 rev/min, stir 2-3 hour;
(2) under identical rotating speed, add modified abandoned resin sand, asbestos, silica powder, nano aluminium oxide, titanium oxide, tetrabutyl titanate stirring 30-50 minute, temperature is reduced to 70-90 ° of C, add all the other remaining compositions again, stir in reactor, disperse, material after dispersion is added to grinding distribution in sand mill even, and stirs 20-30 minute under 1200-1400 rev/min;
(3) finely dispersed material is added in filter filters, after filtration, obtain the material that fineness is 20-40 μm, by the material package after filtering.
Modified abandoned resin sand of the present invention, discarded resin sand is added in shakeout to carry out knockout by preparation method, the metal sundries on removing surface and dirt settling, again by the effect of waste resin sand by oscillator, whizzer, the binding agent on removing surface, again antiquated sand is worn into 400-600 order fine powder by ball mill, add the nano-attapulgite of antiquated sand weight 12%, 5% nano zine oxide, 0.4% Sodium hexametaphosphate 99, the alkylphenol polyoxyethylene of 0.2%, the silicon sol of 8% and 0.5-1% silane coupling agent KH560 mixed grinding evenly.
Paint paint film appearance flat smooth of the present invention, sticking power tests 6 grades, shock-resistance/cm 50, salt water resistance (NaCl of 3%, 27 ° of C ± 6 ° C, 24h) paint film is non-foaming, does not come off, non-corrosive, water tolerance (27 ° of C ± 6 ° C, 240h) is non-foaming, and do not come off, salt spray resistance (1000h) paint film is non-foaming, do not come off, non-corrosive, artificial accelerated aging performance (1200h) paint film without efflorescence, without variable color, flawless, abrasion-resistant (750g, 500 turns)/mg 13.
Claims (3)
1. an anti-aging anti-electrostatic cabin green painting, it is characterized in that, be made up of the raw material of following weight part: vinyl MQ silicone resin 16-18, terpolycyantoamino-formaldehyde resin 5-8, inclined phenylenediamine 3-5, titanium oxide 1-2, tetrabutyl titanate 1-2, wood wax oil 3-5, nano aluminium oxide 2-4, asbestos 2-4, silica powder 3-4, bamboo fibers 3-4, polydimethylsiloxane 1-2, JWK-15 static inhibitor 0.7-1.4, TriMethylolPropane(TMP) 1-2, epoxidized linseed oil 2-3, brometo de amonio 1-2, modifying asphalt 24-32, modified abandoned resin sand 6-8, dimethylbenzene 13-15, acetone 5-7, turps 4-6,
Described modifying asphalt is made up of the raw material of following weight part: pitch 78-84, sulphur 0.4-1.0, Poly Propylene Wax 0.4-0.8, nano diatomite 0.5-1.0, diaminodiphenylmethane 0.3-0.7, gac 1-2, vinyl chloride-vinyl acetate resin 8-12, maleic anhydride 4-6, Potassium aluminum sulfate dodecahydrate 0.3-0.6, tetrahydrofuran (THF) 7-9, zirconium iso-octoate 0.2-0.4, dibenzoyl peroxide 0.05-0.12, sodium lignosulfonate 0.4-0.8, nano-glass scale 0.4-0.7; Preparation method is to melting by asphalt heating; maleic anhydride and dibenzoyl peroxide is slowly added under the protection of nitrogen; temperature is controlled at 170-180 ° of C; modifying asphalt is obtained stir 0.5-1 hour under 600-800 rev/min after; vinyl chloride-vinyl acetate resin, tetrahydrofuran (THF), zirconium iso-octoate, diaminodiphenylmethane, Poly Propylene Wax are mixed and heated to 130-150 ° of C; then will mix with modifying asphalt, then add all the other surplus materialss and with 800-1200 rev/min of lower agitation grinding 1-1.5 hour.
2. a kind of anti-aging anti-electrostatic cabin green painting according to claim 1, is characterized in that, be made up of following concrete steps:
(1) vinyl MQ silicone resin, terpolycyantoamino-formaldehyde resin, modifying asphalt, bamboo fibers, acetone, turps, dimethylbenzene, partially phenylenediamine are dropped in reactor and is heated to 200-250 ° of C, after being uniformly mixed by mixture, under 600-800 rev/min, stir 2-3 hour;
(2) under identical rotating speed, add modified abandoned resin sand, asbestos, silica powder, nano aluminium oxide, titanium oxide, tetrabutyl titanate stirring 30-50 minute, temperature is reduced to 70-90 ° of C, add all the other remaining compositions again, stir in reactor, disperse, material after dispersion is added to grinding distribution in sand mill even, and stirs 20-30 minute under 1200-1400 rev/min;
(3) finely dispersed material is added in filter filters, after filtration, obtain the material that fineness is 20-40 μm, by the material package after filtering.
3. modified abandoned resin sand according to claim 1, it is characterized in that, discarded resin sand is added in shakeout to carry out knockout by preparation method, the metal sundries on removing surface and dirt settling, again waste resin sand is passed through oscillator, the effect of whizzer, the binding agent on removing surface, again antiquated sand is worn into 400-600 order fine powder by ball mill, add the nano-attapulgite of antiquated sand weight 12%, the nano zine oxide of 5%, the Sodium hexametaphosphate 99 of 0.4%, the alkylphenol polyoxyethylene of 0.2%, the silicon sol of 8% and the silane coupling agent KH560 mixed grinding of 0.5-1% are evenly.