CN104005135A - Polyester-spandex double corn spun yarn and fabric thereof - Google Patents
Polyester-spandex double corn spun yarn and fabric thereof Download PDFInfo
- Publication number
- CN104005135A CN104005135A CN201410111679.1A CN201410111679A CN104005135A CN 104005135 A CN104005135 A CN 104005135A CN 201410111679 A CN201410111679 A CN 201410111679A CN 104005135 A CN104005135 A CN 104005135A
- Authority
- CN
- China
- Prior art keywords
- yarn
- heart yarn
- spandex
- fiber
- fibers
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a polyester-spandex double corn spun yarn which comprises a core yarn and covering fibers; the core yarn is composed of elastic polyester fibers polymerizedby use of polyterephthalic acid and 1,2-propylene glycol alginate, and spandex; the covering fibers are natural fibers or chemical fibers; the weight percentages of the elastic polyester fibers, the spandex and the covering fibers are 3-9%, 2-8% and 84-94%, respectively. Two thick yarns formed from the covering fibers are fed into a flare opening in parallel; the elastic polyester fibers are introduced into a godet wheel by use of a tension adjusting device and the tension value of the elastic polyester fibers is controlled in the range of 28-30CN; the spandex is placed on a godet, pre-drafted by 2.7-3.2 parts, fed into a front roller jaw after being converged with the elastic polyester fibers at the godet wheel, and further converged with the coring fibers and formed into the corn spun yarn under the twisting action of a spinning frame. The double corn spun yarn is prepared by use of the elastic polyester fibers and the spandex so that excellent elasticity of the spandex and the excellent resilience of the polyester fibers are combined, and the formed fabric is comfortable to wear and capable of preserving the shape for a long time.
Description
Technical field
The present invention relates to a kind of cladded yarn, be specifically related to a kind of ammonia double-contracting heart yarn of washing, also relate to the fabric being made into by this double-contracting heart yarn, this belongs to Textile Engineering technical field.
Background technology
Cladded yarn generally take powerful and elastic force all good synthetic fiber filament be core silk, the staple fibres such as outsourcing cotton, hair, viscose are twisted and the yarn that is spun into together.Cladded yarn has the premium properties of long filament heart yarn and outsourcing staple fibre concurrently.More common cladded yarn has polyester-cotton blend cladded yarn, and it take polyester filament as heart yarn, outsourcing cotton fiber.Also have spandex core-spun yarn, it is to take spandex filament as heart yarn, the yarn that other fibers of outsourcing are made.The knitted fabric of being made by this cladded yarn or cowboy's trousering, capable of expansion and contraction while wearing, comfortable fittingness.
Ptt fiber (being commonly called as elasticity terylene) is to be by Shell Chemical(shell chemical company the earliest) new type polyester fiber made by PTA and PDO polymerization, spinning from petroleum technology route and biology corn process route respectively with du pont company.Ptt fiber and PET(polyethylene terephthalate) fiber, PBT(poly terephthalic acid 1.4 butanediol esters) fiber belongs to polyester fiber together.Ptt fiber has the characteristic of terylene, polyamide fibre, acrylic fibers concurrently, except antifouling property well, be easy in addition dyeing, soft, high resilience, extensibility is equally good with spandex fibre, compares be easier to processing with elastomer spandex, is applicable to very much textile garment fabric; PTT also has the features such as dry and comfortable, well-pressed in addition.Compare with spandex fibre, ptt fiber has excellent elongation restorative (extend 20% and still can recover its original length).
Spandex is a kind of elastomer, spandex has deep drawing quality (500%～700%), (200% extends low elastic modulus, 0.04～0.12 gram/dawn) and (200% elongation of high elasticity response rate, 95%～99%), general spandex is not used separately, by making spandex core-spun yarn at other short fibers of spandex filament outsourcing or long filament, the fabric elasticity that spandex core-spun yarn is spun into is good, comfortable and easy to wear, but its elasticity residual rate of fabric and washing shrinkage that elasticity is better also can increase, and the weatherability of spandex fibre and heat resistance poor, fabric is worn for a long time even long storage time and all can be followed the string, produce the phenomenon of lax distortion.
Given this, need to provide the stretch yarn of a kind of elasticity and good stability of the dimension, the long-time spandex core-spun yarn that is difficult for lax deformation of placing, therefore, can consider to utilize the elongation of ptt fiber excellence restorative, improves the easily defect of lax distortion of spandex core-spun yarn.
Summary of the invention
The technical problem to be solved in the present invention be to provide a kind of brute force high, there is the lasting flexible ammonia double-contracting heart yarn of washing.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of ammonia double-contracting heart yarn of washing, comprise heart yarn and outer wrapping fiber, and its innovative point is: ptt fiber and the spandex thread of described heart yarn for being formed by poly terephthalic acid and 1,3-PD polyisocyanate polyaddition; Described outer wrapping fiber is natural fabric or chemical fibre; The mass percent of described elasticity polyster fibre, spandex thread and outer wrapping fiber is 4～9%:2～8%:84～94%.
Further, described heart yarn adopts the ptt fiber of 40～82dtex and the spandex thread of 38～46dtex, and washing ammonia double-contracting heart yarn is 16～48tex.
Further, described chemical fibre is one or both in bamboo Dai Er fiber, Modal fibre, zein fiber, tencel fiber.
Bamboo Dai Er fiber, Modal fibre, zein fiber and tencel fiber are regenerated fiber, the absorption good permeability of fiber, comfortable feel, the fabric good luster being made into.
The present invention also provides a kind of production method of washing ammonia double-contracting heart yarn, the method is: outer wrapping fiber is through conventional scutching cotton, comb and parallel cotton fibers prior to spinning, drafting, Roving Frames enters drafting mechanism of spinning machine after making rove, at front roller place and heart yarn, converge, its innovative point is: spinning process is by the rove feeding horn mouth of being made by outer wrapping fiber, ptt fiber is introduced godet roller by tension-adjusting gear, controller tension value is 28～30CN, spandex thread is positioned on godet roller, through 2.7～3.2 times of preliminary drafts, after converging, godet roller and ptt fiber feed front roller nip, converge with outer wrapping fiber, under fine spining machine twisting effect, form cladded yarn, in order to obtain high-quality yarn, spun yarn spindle speed is 8000～12000rpm, spun yarn twist factor is 300～420.
Further, described spinning process adopts match network spinning process, and by two parallel feeding horn mouths of the rove of being made by outer wrapping fiber, horn mouth spacing is set to 2.5mm～3.5mm.
The fabric of being made by above-mentioned double-contracting heart yarn, what described warp thread adopted 16～32tex washs ammonia double-contracting heart yarn or non-stretch yarn, and what weft yarn adopted 24～48tex washs ammonia double-contracting heart yarn, weave fabric through close be 368～382/10cm, filling density is 208.5～216/10cm, adopts twill weave.
Beneficial effect of the present invention: the present invention prepares double-contracting heart yarn by ptt fiber and spandex thread, combines the recovery of the good elasticity of spandex thread and ptt fiber excellence; Adopt match network spinning process, further improved yarn strength, filoplume and evenness quality, the fabric of being made by upper cladded yarn of the present invention is comfortable and easy to wear, conformal lastingly, undergarment.
The specific embodiment
Below in conjunction with specific embodiment, technical scheme of the present invention is elaborated.
embodiment 1
(1) yarn specification
Outer wrapping fiber: cotton 229, mic value 4.3
The ptt fiber of heart yarn: 72dtex; The spandex thread of 38dtex
Double-contracting heart yarn specification: cotton/ptt fiber/spandex 3/2/95
Wash ammonia double-contracting heart yarn 27.8tex
(2) production technology
Adopt match network spinning process, by the rove feeding horn mouth of being made by cotton fiber, the ptt fiber of 72dtex is introduced godet roller by tension-adjusting gear, controller tension value is 28CN, 38dtex spandex thread is positioned on godet roller, through 2.7 times of preliminary drafts, after converging, godet roller and ptt fiber feed front roller nip, cotton fiber is through conventional scutching cotton, comb and parallel cotton fibers prior to spinning, drafting, Roving Frames enters drafting mechanism of spinning machine after making rove, at front roller place and heart yarn, converge, under fine spining machine twisting effect, form cladded yarn, spun yarn spindle speed is 8000rpm, spun yarn twist factor is 320.
(3) fabric
What warp thread and weft yarn all adopted 27.8tex washs ammonia double-contracting heart yarn, on ZAX-N air-jet loom, weave adopt and on twill-weave once, fabric width is 160cm, weave fabric through close be 368/10cm, filling density is 208.5/10cm.
The fabric resilience of the present embodiment is good, and yarn strength is high, conformal lastingly, and fabric is all flexible through broadwise, comfortable and easy to wear.
embodiment 2
(1) spinning specification
Outer wrapping fiber: bamboo Dai Er fiber 1.33dtex * 38mm
The ptt fiber of heart yarn: 82dtex; The spandex thread of 46dtex
Double-contracting heart yarn specification: bamboo Dai Er fiber/ptt fiber/spandex 5/4/91
Wash ammonia double-contracting heart yarn 24.3tex
(2) production method:
Spinning process is with embodiment 1
(3) fabric
Warp thread adopts that 24.3tex's in the present embodiment wash ammonia double-contracting heart yarn, weft yarn adopts that 27.8tex's in embodiment 1 wash ammonia double-contracting heart yarn, on ZAX-N air-jet loom, adopt and weave with cassimere twill, fabric width is 160cm, weave fabric through close be 376/10cm, filling density is 212.5/10cm.
The fabric resilience of the present embodiment is good, and yarn strength is high, conformal lastingly, and sucting wet air permeability is good, and fabric is all flexible through broadwise, comfortable and easy to wear.
embodiment 3
Outer wrapping fiber: model 1.33dtex * 38mm
The ptt fiber of heart yarn: 76dtex; The spandex thread of 42dtex
Double-contracting heart yarn specification: model/ptt fiber/spandex 4/3/93
Wash ammonia double-contracting heart yarn 48tex
(2) production method:
Spinning process is with embodiment 1.
(3) fabric
Warp thread adopt embodiment 1 27.8tex wash ammonia double-contracting heart yarn, what weft yarn adopted 48tex washs ammonia double-contracting heart yarn, on ZAX-N air-jet loom, adopt and on twill weave once, fabric width is 160cm, weave fabric through close be 378/10cm, filling density is 214.5/10cm.
The fabric resilience of the present embodiment is good, and yarn strength is high, conformal lastingly, and sucting wet air permeability is good, and fabric is all flexible through broadwise, comfortable and easy to wear.
embodiment 4
(1) spinning specification
Outer wrapping fiber: model 1.33dtex * 38mm bamboo Dai Er 1.33dtex * 38mm
Model/bamboo Dai Er 45/55
The ptt fiber of heart yarn: 82dtex; The spandex thread of 46dtex
Double-contracting heart yarn specification: the blended yarn/ptt fiber/spandex 3/5/92 of bamboo Dai Er and model
Wash ammonia double-contracting heart yarn 27.6tex
(2) production method:
Adopt match network spinning process, by the parallel feeding horn mouth of two rove of being made with Modal fibre by bamboo Dai Er fiber respectively, horn mouth spacing is set to 2.5cm * 1.5cm, the ptt fiber of 82dtex is introduced godet roller by tension-adjusting gear, controller tension value is 28CN, 46dtex spandex thread is positioned on godet roller, through 3.2 times of preliminary drafts, after converging, godet roller and ptt fiber feed front roller nip, Modal fibre and bamboo Dai Er fiber are through conventional scutching cotton, comb and parallel cotton fibers prior to spinning, drafting, Roving Frames enters drafting mechanism of spinning machine after making rove, at front roller place and heart yarn, converge, under fine spining machine twisting effect, form cladded yarn, spun yarn spindle speed is 10000rpm, spun yarn twist factor is 400.
(3) fabric
What warp thread adopted 24.3tex washs ammonia double-contracting heart yarn, and what weft yarn adopted 27.6tex washs ammonia double-contracting heart yarn, on ZAX-N air-jet loom, adopt and on twill weave once, fabric width is 160cm, weave fabric through close be 382/10cm, filling density is 215.5/10cm.
The fabric resilience of the present embodiment is good, and yarn strength is high, conformal lastingly, and sucting wet air permeability is good, and fabric is all flexible through broadwise, comfortable and easy to wear.
embodiment 5
Outer wrapping fiber: tencel fiber 1.33dtex * 38mm
The ptt fiber of heart yarn: 76dtex; The spandex thread of 42dtex
Double-contracting heart yarn specification: tencel fiber/ptt fiber/spandex 6/6/88
Wash ammonia double-contracting heart yarn 26.7tex
(2) production method:
Spinning process is with embodiment 1.
(3) fabric
Warp thread adopts that 26.7tex's wash ammonia double-contracting heart yarn, weft yarn adopt embodiment 1 27.8tex wash ammonia double-contracting heart yarn, on ZAX-N air-jet loom, adopt and on twill weave once, fabric width is 160cm, weave fabric through close be 378/10cm, filling density is 214.5/10cm.
comparative example 1
Outer wrapping fiber: cotton 229, mic value 4.3
The spandex thread of heart yarn: 38dtex
Double-contracting heart yarn specification: cotton/spandex 5/95
Cladded yarn 27.8tex
Spinning method is with embodiment 1.
comparative example 2
Outer wrapping fiber: bamboo Dai Er fiber 1.33dtex * 38mm
The spandex thread of heart yarn: 46dtex
Double-contracting heart yarn specification: bamboo Dai Er fiber/spandex 8/92
Cladded yarn 24.3tex
Spinning method is with embodiment 2.
comparative example 3
Outer wrapping fiber: model 1.33dtex * 38mm
The spandex thread of heart yarn: 42dtex
Double-contracting heart yarn specification: model/spandex 7/93
Cladded yarn 48tex
Spinning method is with embodiment 3.
comparative example 4
Outer wrapping fiber: model 1.33dtex * 38mm bamboo Dai Er 1.33dtex * 38mm
Model/bamboo Dai Er 45/55
The spandex thread of heart yarn: 46dtex
Double-contracting heart yarn specification: the blended yarn/spandex 3/5/92 of bamboo Dai Er and model
Cladded yarn 27.6tex
Spinning method is with embodiment 4.
comparative example 5
Outer wrapping fiber: tencel fiber 1.33dtex * 38mm
The spandex thread of heart yarn: 742dtex
Double-contracting heart yarn specification: tencel fiber/spandex 6/6/88
Cladded yarn 26.7tex
Spinning method is with embodiment 5.
Adopt Y391 type elasticity instrument, specimen length is 100mm, adopts constant load method to measure elasticity.First pre-tension stretches sample and fixing sample in accordance with regulations, hangs up heavy load and by " under push rod "; Read immediately sample stretch value S1; After 3min, again read sample stretch value S2, be sample general extension; The difference of S2 and S1 is yarn creep compliance; Take off heavy load, read immediately sample stretch value S3, the difference of S2 and S3 is the anxious elastic recovery deflection of yarn; After Yarn relaxation 2min, under initial load, read sample stretch value S4, the difference of S3 and S4 is slow elastic recovery deflection; Each sample repeats 10 times, averages.Relevant calculating formulas is as follows:
Anxious elastic recovery rate (%)=
Slow elastic recovery rate (%)=
Proof resilience response rate (%)=
Creep elongation rate of change is=
Table 1 is the yarn property test result of embodiment 1～5
Table 2 is the performance test results of the yarn of comparative example 1～5
Good by contrast table 1 and the known fabric resilience of the present invention of table 2, yarn strength is high, conformal lastingly, and sucting wet air permeability is good, and fabric is all flexible through broadwise, comfortable and easy to wear.
Claims (6)
1. wash an ammonia double-contracting heart yarn, comprise heart yarn and outer wrapping fiber, it is characterized in that: elasticity polyster fibre and the spandex thread of described heart yarn for being formed by poly terephthalic acid and 1,3-PD polyisocyanate polyaddition; Described outer wrapping fiber is natural fabric or chemical fibre; The mass percent of described elasticity polyster fibre, spandex thread and outer wrapping fiber is 4～9%:2～8%:84～94%.
2. a kind of ammonia double-contracting heart yarn of washing according to claim 1, is characterized in that: described heart yarn adopts the elasticity polyster fibre of 40～82dtex and the spandex thread of 38～46dtex, and washing ammonia double-contracting heart yarn is 16～48tex.
3. a kind of ammonia double-contracting heart yarn of washing according to claim 1, is characterized in that: described chemical fibre is one or both in bamboo Dai Er fiber, Modal fibre, zein fiber, tencel fiber.
4. a production method of washing ammonia double-contracting heart yarn claimed in claim 1, outer wrapping fiber is through conventional scutching cotton, comb and parallel cotton fibers prior to spinning, drafting, Roving Frames enters drafting mechanism of spinning machine after making rove, at front roller place and heart yarn, converge, it is characterized in that: spinning process is by the rove feeding horn mouth of being made by outer wrapping fiber, elasticity polyster fibre is introduced godet roller by tension-adjusting gear, controller tension value is 28～30CN, spandex thread is positioned on godet roller, through 2.7～3.2 times of preliminary drafts, after converging, godet roller and elasticity polyster fibre feed front roller nip, converge with outer wrapping fiber, under fine spining machine twisting effect, form cladded yarn, spun yarn spindle speed is 8000～12000rpm, spun yarn twist factor is 300～420.
5. a kind of production method of washing ammonia double-contracting heart yarn according to claim 4, it is characterized in that: described spinning process adopts match network spinning process, by two parallel feeding horn mouths of the rove of being made by outer wrapping fiber, horn mouth spacing is set to 2.5mm～3.5mm.
6. claimed in claim 1ly wash the fabric that ammonia double-contracting heart yarn is made into for one kind, it is characterized in that: described warp thread adopts that 16～32tex's wash ammonia double-contracting heart yarn or non-stretch yarn, weft yarn adopts that 24～48tex's wash ammonia double-contracting heart yarn, weave fabric through close be 368～382/10cm, filling density is 208.5～216/10cm, adopts twill weave.