CA1050250A - Method for making metallic sandwich structures - Google Patents
Method for making metallic sandwich structuresInfo
- Publication number
- CA1050250A CA1050250A CA305,515A CA305515A CA1050250A CA 1050250 A CA1050250 A CA 1050250A CA 305515 A CA305515 A CA 305515A CA 1050250 A CA1050250 A CA 1050250A
- Authority
- CA
- Canada
- Prior art keywords
- stack
- pressure
- workpieces
- chamber
- inert gas
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Abstract
ABSTRACT
A method for fabrication of metallic sandwich struc-tures in which metal blanks, preferably of a titanium alloy, are joined at selected areas and expanded superplastically to form a desired sandwich structure. Various techniques for joining, preferably diffusion bonding, selected areas of the metal blanks are disclosed. These include treating the metal blanks at selected areas to prevent bonding at those areas and selective application of pressure during bonding. In the pre-ferred embodiment, the metal blanks are positioned in a stack after being treated at selected areas. The stack is positioned relative to shaping members and heated to a temperature suitable for superplastic forming and diffusion bonding. Compressive pressure is applied for the selective diffusion bonding. The stack is expanded into contact with the shaping members by increasing the internal pressure therein, preferably with inert gas, thus forming the desired shaped sandwich structure in one operation.
A method for fabrication of metallic sandwich struc-tures in which metal blanks, preferably of a titanium alloy, are joined at selected areas and expanded superplastically to form a desired sandwich structure. Various techniques for joining, preferably diffusion bonding, selected areas of the metal blanks are disclosed. These include treating the metal blanks at selected areas to prevent bonding at those areas and selective application of pressure during bonding. In the pre-ferred embodiment, the metal blanks are positioned in a stack after being treated at selected areas. The stack is positioned relative to shaping members and heated to a temperature suitable for superplastic forming and diffusion bonding. Compressive pressure is applied for the selective diffusion bonding. The stack is expanded into contact with the shaping members by increasing the internal pressure therein, preferably with inert gas, thus forming the desired shaped sandwich structure in one operation.
Description
:~OS~25~.~
BACKGROUND OF THE INVENTION
For many years it has been known that certain metals, such as titanium and many of its alloys, exhibit superplasticity. Super-plasticity is the capability of a material to develop unusually high tensile elongations with reduced tendency toward necking. This cap-ability is exhibited by only a few metals and alloys and within a limited temperature and strain rate range. Titanium and titanium -alloys have been observed to exhibit superplastic characteristics equal to or greater than those of any other metals. With suitable titanium alloys, overall increase in surface areas up to 300% are possible.
The advantages of superplastic forming are numerous: very complex shapes and deep drawn parts can be readily formed; low de-formation stresses are required to form the metal at the superplastic temperature range, thereby permitting forming of parts under low pressures which minimize tool deformation and wear, allows the use of inexpensive tooling materials, and eliminateQ creep in the tool;
single male or female tools can be used; no spring-back occurs; no Bauschinger effect develops; multiple parts of different geometry can be made during a single operation; very small radii can be formed, and no problem with compre~sion buckles or galling are encountered.
However, when superplastic forming of titanium and similar reactive metals, it is necessary to heat and form in a controlled environment to ensure cleanliness of the titanium which is particularly sensitive to oxygen, nitrogen, and water vapor content in the air at elevated temperatures. unless the titanium is protected, it becomes embrittled and its integrity destroyed.
Diffusion bonding refers to the metallurgical joining of sur-faces of similar or dissimilar metals by applying heat and pressure
BACKGROUND OF THE INVENTION
For many years it has been known that certain metals, such as titanium and many of its alloys, exhibit superplasticity. Super-plasticity is the capability of a material to develop unusually high tensile elongations with reduced tendency toward necking. This cap-ability is exhibited by only a few metals and alloys and within a limited temperature and strain rate range. Titanium and titanium -alloys have been observed to exhibit superplastic characteristics equal to or greater than those of any other metals. With suitable titanium alloys, overall increase in surface areas up to 300% are possible.
The advantages of superplastic forming are numerous: very complex shapes and deep drawn parts can be readily formed; low de-formation stresses are required to form the metal at the superplastic temperature range, thereby permitting forming of parts under low pressures which minimize tool deformation and wear, allows the use of inexpensive tooling materials, and eliminateQ creep in the tool;
single male or female tools can be used; no spring-back occurs; no Bauschinger effect develops; multiple parts of different geometry can be made during a single operation; very small radii can be formed, and no problem with compre~sion buckles or galling are encountered.
However, when superplastic forming of titanium and similar reactive metals, it is necessary to heat and form in a controlled environment to ensure cleanliness of the titanium which is particularly sensitive to oxygen, nitrogen, and water vapor content in the air at elevated temperatures. unless the titanium is protected, it becomes embrittled and its integrity destroyed.
Diffusion bonding refers to the metallurgical joining of sur-faces of similar or dissimilar metals by applying heat and pressure
- 2 lOS(~2~
for a time duration so as to cause co-mingling of atoms at the joint interface. Diffusion bonding is accomplished entirely in the solid-state at or above one-half the base metal melting point (absolute).
Actual times, temperatures, and pressures will vary from metal to metal. The joining surface must be brought within atomic distances by application of pressure. Adequate pressure must also be provided to cause some plastic flow to fill normal void areas. If pressures are too low, small voids will remain at the joint interface and the joint strength will be less than the maximum obtainable. The applica-tion of pressure also breaks up the surface oxides and surfaceasperities so as to present clean surfaces for bonding. The elevated temperatures used ~or diffusion bonding serve the functions of accelerating diffusion of atoms at the joint interfaces and providing a metal softening which aids in surface deformation so as to allow more intimate contact for atom bonding and movement across the joint interface. The elevated temperature and application of pressure also resultg in diffusion of the surface contaminants into the base metal during bonding which allows metal atom-to-atom bonding and thereby strengthens the bond. Sufficient time must be allowed to ensure the strengthening of the bond by diffusion of atoms across the joint interface. A protective atmosphere for bonding i8 required when titanium and other similar reactive metals are to be bonded.
The process of superplastic forming of metals and diffusion bonding having individually been dis~losed in the prior art. U.S.
; patent No. 3,340,101 to Fields, Jr., et al discloses a method of superplastic forming where a metal is conditioned to exhibit its effective strain rate sensitivity and then formed by application of vacuum solely or in combi~ation with a metal dye. Patents relating to qolid-state or diffusion bonding include U.S. patent ~o. 3,145,466;
for a time duration so as to cause co-mingling of atoms at the joint interface. Diffusion bonding is accomplished entirely in the solid-state at or above one-half the base metal melting point (absolute).
Actual times, temperatures, and pressures will vary from metal to metal. The joining surface must be brought within atomic distances by application of pressure. Adequate pressure must also be provided to cause some plastic flow to fill normal void areas. If pressures are too low, small voids will remain at the joint interface and the joint strength will be less than the maximum obtainable. The applica-tion of pressure also breaks up the surface oxides and surfaceasperities so as to present clean surfaces for bonding. The elevated temperatures used ~or diffusion bonding serve the functions of accelerating diffusion of atoms at the joint interfaces and providing a metal softening which aids in surface deformation so as to allow more intimate contact for atom bonding and movement across the joint interface. The elevated temperature and application of pressure also resultg in diffusion of the surface contaminants into the base metal during bonding which allows metal atom-to-atom bonding and thereby strengthens the bond. Sufficient time must be allowed to ensure the strengthening of the bond by diffusion of atoms across the joint interface. A protective atmosphere for bonding i8 required when titanium and other similar reactive metals are to be bonded.
The process of superplastic forming of metals and diffusion bonding having individually been dis~losed in the prior art. U.S.
; patent No. 3,340,101 to Fields, Jr., et al discloses a method of superplastic forming where a metal is conditioned to exhibit its effective strain rate sensitivity and then formed by application of vacuum solely or in combi~ation with a metal dye. Patents relating to qolid-state or diffusion bonding include U.S. patent ~o. 3,145,466;
3--~s~s~
3,180,02~; 3,044,160; 2,850,798; and 3,170,234. However, the prior art does not disclose combining these two processes.
In my co-pending Canadian application No. 233,354 there is disclosed a method for superplastic forming of metals with concurrent diffusion bonding. The crux of that invention is the superplastic forming of a metal blank against a shaping member and another metal workpiece so that the m~stal blank is formed and diffusion bonded to the other metal workpiece in one operation. Though a hollow metal structure bonded at peripheral edges can be formed as disclosed in 10 that application, the process is not designed for the forming of sandwich structures. The forming of ~andwich structures according to the present invention requires separate superplastic forming and joining stages and a technique for joining only ~elective areas of the metal blanks employed.
The present invention obviates the prior art problems of forming sandwich structures. A sandwich structure normally comprises a core between face sheets. Previous to applicant's invention, fabrication of sandwich structures typically took the approach of first rolling metal foil or ribbon, forming and joining the foil 20 sheet into the desired cellular core, and then attaching the core to face sheet~ by bracing or spot welding. Problems with the prior art method include the cost of the core due to excess material usage and the great difficulty, excess time consumption, and cost of fabrica-tion of the sandwich shape. Additionally, a separate operation is xequired to join a close out or attachment to the sandwich structure.
Fabrication of an unusual shape for the sandwich structure such as a taper, is nearly impossible.
_ y ~so~
SUMMARY OF THE I~VENTIO~
It is, therefore, an objec~ of the present invention to com-bine the processe~ of metal joining and superplastic forming to form metal sandwich structures.
It i9 another object of the present invention to form metal sandwich structure~ in one operation, thereby significantly lowering the cost, difficulty, and time involved.
It i~ yet another object of the pre~ent invention to form a sandwich structure and join an attachment or close-out in the same operation.
It is still another objsct of the present invention to heat, ~uperplastically form, and join the sandwich in the same apparatus, thereby s2ving fabrication time and equipment costs.
Briefly, in accordance with the invention, there is provided a method for making a metallic sandwich structure from a plurality of metal blank workpieces initially positioned in a 4tacked position.
~he blanks are joined at selected area~. At least one of the blanks i~ superplastically formed against a shaping member to form the desired ~andwich structure. The core configuration is determined by the location, size, and shape of the joined areas.
Other objectq and advantages of the invention will become apparent upon reading the following detailed description -and upon reference to the drawings.
B~I~F D~SCRIPTION OF THE DRAWINGS
Figure 1 i9 an exploded view of a three-piece metal sheet a~sembly treated for 3elective diffusion bonding prior to insertion in ~he forming apparatus:
Figure 2 is a cros~-sectional elevational view of a preferred embodiment of a forming apparatus used for fabrication of metal ~ oso~s~
sandwich structures with the three piece metal sheet assembly of Figure 1 inserted therein;
Figure 3 illustrates the fully expanded three-piece metal sheet assembly within the forming apparatus of Figure 2 with broken lines added to delineate the final position of the component metal sheets of the expanded joined assembly:
Figure 4 is a detail view of an inflation tube connection to the three-sheet assembly:
Figures 5 and 6 are cross-sectional elevational views of a modified forming apparatus with a three-piece metal sheet assembly inserted therein in its initial position in Figure 5 and in its final expanded po~ition in Figure 6 Figures 7 and 8 are cross-sectional elevational views of a modified forming apparatus with a two-piece metal sheet assembly inserted therein in its initial position in Figure 7 and in its final expanded position in Figure 8;
Figure 9 is a cross-sectional elevational view of a modified forming apparatus illustrating a tapered three-piece metal sheet assembly in final formed position with an attachment joined to the sandwich structure at the broken lines;
Figure 10 i8 a perspective view with the ends cut off of the formed sandwich structuxe of Figure 9:
Figure 11 is a fragmentary cro~s-sectional elevational view of a modified forming apparatus illustrating the positioning of an inflation t~be relative to a four-piece metal sheet assembly:
Fîgure 12 is a cross-sectional elevational view of a sandwich structure formed from a four-piece metal sheet assembly: and Figure 13 is a fragmentary perspective view of the sandwich structure shown in Figure 12.
~o~o While the invention will be described in connection with the preferred procedures, it will be understood that it is not intended to limit the invention to those procedures. On the contrary, it is intended to cover all alternatives, modifications, and equivalents that may be included within the ~pirit and scope of the invention as defined by the appended claim~
D13TAILED Dl~SCRIPTION OF THE INV~TION
In order for superplastic forming to be successful, it is necessary to u~e a material that is suitable. The extent to which the material selected will exhibit superplastic properties is pre-dictable in general terms from a determination of the strain rate sensitivity and a design determination of the permissible variation in wall thickness. Strain rate sensitivity can be defined as m where m egual~ dl~ and ~ i~ stre~s in pounds per square inch and e is strain rate in re~procal minutes. Strain rate sensitivity may be determined by a ~imple and now well recognized torsion test described in the article, "Determi.nation of Strain Hardening Characteristics by Torsion Testing" by D.S. Fields, Jr., and W.A. Backofen, published in the Proceedinga of the A.S.T.M., 1957, Volume 57, page~ 1259-1272.
A strain rate sensitivity of about 0.5 or greater can be expected to produce satisfactory results. The larger the value (to a maximum of one3 the greater the superplastic properties. Maximum ~train rate ~ensitivity in metals is seen to occur, if at all, as metals are de-- formed near the phase transformation temperature. Accordingly, the temperature immediately below the phase transformation temperature can be expected to produce the greatest ~train rate sensitivi~y. For titanium alloys, the temperature range in which superplasticity can be observed is about 1450 F. to about 1850 F. depending on the ~pecific alloy u~ed.
1050~5~
Other variables have been found to effect strain rate sen-sitivity and therefore should be considered in selecting a suitable metal material. Decreasing grain size results in correspondingly higher values for strain rate sensitivity. Additionally strain rate and material texture effect the strain rate ~ensitivity. It has been found that for titanium the m value reaches a peak at an intermediate value of strain rate (approximately 10 in./in./sec.). For maximum ~table deformation, superplastic forming should be done at or near this ~train rate. Too great a variance from the optimum strain rate may re~ult in loss of superpla-~tic properties.
Diffu~ion bonding, where separate elements form a single uni-; tary ma~s therefrom, may be practiced in a wide variety of metals and alloy~. However, the quality of the bond and the parameter~ employed will neces~arily vaxy for each particular choice of workpiece material~
Among the metals or alloys which may be joined by solid state dif- ~`
fus~on bonding are aluminium, stainles~ steel, titanium, nickel, ` tantalum, molybdenum, zirconium, columbium, and beryllium.
The present invention i~ particularly directed to the reactive metals whose surfaces would be contaminated at the elevated tempera-tures required for superplastic forming and diffu~ion bonding.
Titanium and its alloys are examples of ~uch metals which have also been found to be particularly well suited for a proces~ of the present invention in that the~alloys exhibit very high superplastic pro-perties in a temperature range suitable for diffuqion bonding, i.e.
1450F. to about 1850P. depending on the ~pecific alloy used.
Turning first to Figure 1, there is shown an exploded view of a three-piece metal sheet assembly to be formed into a ~andwich structure according to the present invention. ~he assembly is made up of metal blanks 10, 12 and 14, all preferably in the form of sheets ~ c~so~o having upper and lower opposed principal surfaces 15 and 16, 17 and 18, and 19 and 20, respectively (see also Figure 4). The number of sheets used will vary depending on load condi~ions and design require-ments However, a minimum of two sheets must be utilized and normally no moxe than four sheets would be used. The metal sheets must have the ability to be joined by such methods as bracing, welding, or diffusion bonding. Depending on the number of sheets to be expanded, at least one of the sheets muqt exhibit superplastic properties. Any metal tha~ exhibits suitable superplastic properties within a work-10 able temperature range can be used for such sheet, but the present --invention is particularly concerned with metals that exhibit super-plastic properties ~ithin the temperature range required for diffusion bonding and that are subject to contamination at forming temperatures, as titanium or an alloy thereo such as Ti-6Al-4V. When using Ti-6Al-4V, the forming temperature is preferably approximately 1700F.
Initial thickness of metal blankq 10, 12 and 14 are determined by the dimenqions of the part to be formed.
In order to join only selected areas of the metal qheets, a - preferred step is to apply a suitable stop-off material to thoqe areas within the stack where no attachment or joining between the sheets is desired. Thus, areas 30, 32, and 34 are covered with a stopooff material to pre~ent bonding in those areas. Other areas on surfaces 15, 18 and 20 could also be so covered for prevention of joining. Alternatively, the metal sheet structure could be spot welded or brazed at those areas where joining i8 desired. Addition-ally, as hereinafter explained, the metal sheet structure or stack 40 could be diffusion bonded at selected areas by selective applica-tion of pressureO
Figure 2 illustrates a preferred forming apparatus generally _ g _ ~C~S02S0 indicated at 42 for carrying out the invention. Upper tooling frame 44 has preferably integral side walls 45 in the form of a ring which can be of any desired shape. Lower tooling frame 46 which prefer-ably has the same outer area dimensions as upper frame 42 can be flat and act as a base as illustrated for supporting the stack of metal blanks 40. For purposes of the claims, both upper tooling frame 44 and lower tooling frame 46 are to be considered shaping members as both combine to form the desired shaped structure. The inner surface of upper tooling frame 44 defines an inner chamber 48 and a female die surface. One or more male die members (not shown) can be provided in chamber 48 to vary the shape of the part to be formed. The stack of metal blanks 40, which is supported on lower tooling frame 46, covers chamber 48. The metal blanks of t~e stack must all be of a material suitable ~or joining such aq by welding, brazing, or diffusion bonding. At least one of the outer metal blanks, and most likely the inner blanks, must have an effective strain rate sensitivity for exhibiting superplastic properties at a desired forming temperature and preferably within a temperature range required for diffusion bonding of the stack. This is shown in Figure 3 by the expanded stack 40 where both sheet~ 12 and 14 have been superplastically expanded, while sheet 10 of the formed stack has been sub~tantially unchanged. Initial thicknesses of the sheets of stack 40 are deter-mined by the dimension~ of the parts to be formed. The joining method to be used, namely welding, brazing, or diffusion bonding, depend~ on the material selected for the metal blanks, the temperature required for superplastic forming, and the desired strength. However, especially for titanium, diffu~ion bonding is preferred as this results in the strongest joining and the bonding temperature is generally suitable for superplastic forming.
~OS025i0 As previously mentioned, stop-off can be used at areas 30, 32 and 34 to prevent bonding at those areas. The particular stop- -off selected must prevent bonding and be compatible with the métal or metals of the stack (nonreactive with the stack metals and minimal diffusion into the stack metals). For titanium metal blanks, suitable stop-off materials are graphite, boron nitride, and yttria. Typically, when using yttria stop-off, the stop-off pattern on the blanks is sprayed with a solution of yttria and a binder therefor. The binder holds the yttria in position during bonding and eventually vaporizes 10 below forming temperature. ~ -Joining the stack 40 at selected locations, when by brazing or spot welding i8 normally accomplished outside of the forming apparatus 42 before the stack is placed therein. When diffusion bonding, the unjoined stack 40 i~ preferably bonded after placement in the forming apparatus 42, thereby saving fabrication time and equipment costs (although the ~tack could be diffusion bonded as by press bonding or roll bonding before placing it in the forming apparatus 42). The weight of upper tooling frame 44 acts as a clam-ping means for the stack 40. A single continuous edge of the stack 40 i~ effectively constrained between the upper tooling frame 44 and the lower tooling frame 46. This insures that those portions of the blanks of the stack to be formed, will be stretched rather than ; drawn. Should it be desired, additional tightening means such as bolts (not shownl can be employed to more effectively constrain the ~tack 40. Another additional tightening means that could be employed is a preqs (not shown), preferably hydraulic, having platens 50.
Forming apparatu~ 42 i~ positioned between platens 50 and compressed thereby as~uring that stack 40 is effectively constrained and cham-ber 48 qealed fr~m the air. This arrangement is particularly advan-~(~S(:~5~
tageous as the platens 50 can be made of ceramic material and resistance heated wires 52 can be provided therein for heating stack 40 to the forming temperature. Other heating methods could be used with lthe forming apparatus 42 ordinarily surrounded by a heating means if the heating platens are not used.
For contamination prevention and diffusion bonding of the ~tack 40 when unjoined within the forming apparatus 42, an environ-metal control ~ystem is provided. The purpose of the system is to expoae the ~tack 40 only to inert gas or vacuum while heating, forming and bonding, and optionally, to diffusion bond the stack by fluid pressure. The metal blanks of stack 40 will not react with inert gas due to the nature of inert gas, even at the elevated forming and bonding temperatures. In a high vacuum, there are substantially no elements for the stack 40 to react with. Thus, in this environment, contamination of the stack 40 will be prevented.
Line 52 i8 connected to a source of pressurized inert gas at one end (not shown) and to chamber 48 through orifice 54 in upper tooling frame 44. A valve 56 for governing the flow of inert gas through line 52 into chamber 48 and a pre~qure gauge 58 to indicate pressure are provided. The inert gas used is preferably argon in liquia form. Line 52 also functions as an outlet for inert gas in chamber 48 and could also be connected to a source of vacuum, such as a suction pump (not shown) for creating vacuum in chamber 48.
When line 52 ia uqed as an outlet, valve 56 governs flow of inert gas from chamber 48. An additional line 60 is optimally provided on ; the opposite ~ide of tooling frame 44 and functions a~ an outlet for inert gas in chamber 48. Line 60 is connected to chamber 48 through orifice 62 in upper tooling frame 44. Line 60 has a valve 64 pro-vided therein for regulation of inert gaq flow from chamber 48.
-- ~(350~2SQ
Line 60 can simply function as a vent or be connected to a source of vacuum, such as a suction pump (not shown).
AS previously stated, the contamination prevention system can also function as a means for gas pressure diffusion bonding stack 40. Thus, when stack 40 is placed in forming apparatus 42 as illustrated in Figure 2, the stack can be heated in an inert gas atmosphere to a suitable diffusion bonding temperature (approximately 1700F. when the metal blank3 of stack 40 are of Ti-6Al-4V) by heat generated from heating platens 50, and then applying pressure to stack 40 by increasing the pregsure in chamber 48 by adding additional pressurized inert gas through line 52 while maintaining line 60 closed by valve 64. In this manner, the untreated areas of stack 40 will ; be diffusion bonded by the application of such pres~ure, which i8 preferably approximately 500 p3i for Ti-6Al-4V, for a ~uitable forming t~me, which depends on the thickness of stack 40 and may vary from 30 minutes to 12 hours. The edges of the blanks of stack 40 may also be diffusion bonded if desired by virtue of sealing pressure thereon ! in the form of the weight of upper tooling 44 and optionally pressure from a press and/or a clamping means. After diffusion bonding stack . 20 40, excess inert gas would be removed from chamber 48 through lines 52 and 60 to allow for inflation of stack 40.
For expansion of stack 40 to the configuration shown in Figure 3 expan~ion tubes 72 and 74 are provided, the details of which are best illustrated in Figures 1 and 4. Expansion tube 72 (and likewise expansion tube 74 located on the opposite side of stack 40) is positioned between metal blanks 10 and 14 and protrudes into a channel 75 defined by recesses 76 and 78 and that portion of ~urface 20 of metal blank 14 which overlies recess 78. Recesses 77 and 79 are provid0d on the opposite sides of blanks 10 and 12 respectively ~ s~so to provide a channel for inflation tube 74. The positioning of expansion tube 72 in such a channel 75 prevents compression of tube 72 by the tooling frames 44 and 46. Also, by locating tube 72 so that it protrude~ only partially into channel 75, inert gas will flow fairly evenly between the metal blanks of stack 40, in this case on either side of blank 12 as shown by arrows 80 and 82. As shown in :-Figure 2 expansion tubes 72 and 74 have valves 84 and 86 therein respectively for governing flow of inert gas therethrough, and pres-sure gauges 88 and 90 for indicating pressure.
Expansion tubes 72 and 74 can also serve to draw off vaporized binder. To this end, tube 72 could act as an inlet and tube 72 an outlet with inert ga~ flow being transmitted through stack 40 prior ; to expansion of ~tack 40 to draw off the vaporized binder.
A pair of lateral grooves 71 (not shown) and 73 are preferably provided on opposite sides of lower tooling frame 46 with groove 71 in alignment with recess 77 and groove 73 in alignment with recess 76. The grooves 71 and 73 are provided to insure that passage of inert gas from inflation tubes 72 and 74 betwaen the metal blanks of stack 40 is not prevented from reaching treated areas 30 and 34 by pinching of the ~tack due to the pre~sure exerted by upper and lower tooling frames 44 and 46. The width of grooves 71 and 73 are prefer-ably the same as recesses 76 and 77, but grooves 71 and 73 terminate further inward in stack 40 so that pinching does not occur before the inert gas flow reaches treated areas 30 and 34.
As Rhown in Figure 1 when treating as by stop-off selected areas of stack 40 to prevent diffusion bonding thereon, additional areas such aR that shown at 92 and 94 ~hould likewise be treated to prevent bonding thereon so that the gas from inflation tubes 72 and 74 will reach the selected treated areas for expansion of stack 40.
l~S~ iO
Apertures 96 are provided in treated areas 300 32 and 34 for further transmitting the inert gas from inflation tubes 72 and 74 inside stack 40 to the other treated areas and to insure equal pressure inside stack 40 (in this case on either side of metal blank 12).
If pressure is unequal, the resulting core of the sandwich, metal blank 12 in the configuration illustrated in Figure 3, would be dis-torted with a consequent effect on load carrying ability on the final sandwich structure.
In order to make the expanded metallic sandwich structure as shown in Figure 3 according to applicants' inventive method, metal blank workpieces 10, 12 and 14 are provided. Both sheets 12 and 14 must be of a material having an effective strain rate sensitivity for superplastic forming. Optimally one or more of the blanks are treated at specified locations such as 30, 32 and 34 so that when the metal blanks are arranged in a stack 40 and diffusion bonded, only ; selected areas of the stack will be joined thereby. Alternately, the stack 40 could be spot welded or brazed for selective joining.
When joining by diffu~ion bonding, the stack 40 would optimally be placed in the forming apparatus 42 before forming. The pressure in chamber 48 would be increased by flow of pressurized inert gas through line 52 into chamber 48. Once ~hamber 48 had an inert gas atmosphere, the stack 40 would ~e heated by resi~tance wires 52 in heating platens 50 to a temperature which optimally woula be suitable for both di-ffu~ion bonding and superplastic forming, although the temperature ~o~ld later be raised or lowered if a different temperature is re-quired for superplastic forming. The pressure in chamber 48 would be increased b~ addgtional pressurized inert gas through line 52 to a pressure suitable for diffusion bonding of stack 40. That pressure would be maintained for a time duration sufficient for diffusion ~C~50~2S~:?
bonding. When the metal blanks of stack 40 are of Ti-4V-6Al alloy, the temperature used would be approximately 1700F. and the pressure about 500 psi. These values can of course be varied during forming and bonding as long as they are maintained within a suitable range.
The time duration will vary depending upon the alloys used, tempera- ;
ture, pressure, and thickness of stack 40. Duration may vary from 30 minutes to 15 hours, but three hours is a fairly repre~entative expectation. As previously stated, bonding temperature may vary from 1450F. to about 1850F. Bonding pressure may vary from about 100 psi to 2000 psi or more with the preferred range being 150 psi to 600 p3i.
Before expanding stack 40, the pressure in chamber 48 is reduced thxough lines 52 and 60. When stack 40 is joined prior to insertion in forming apparatus 42, the preceding di~fusion bonding step in forming apparatus 42 would be omitted. At superplastic forming temperature, which is approximately 1700F for Ti-6Al-4v alloy (generally 1650-1750F.), stack 40 i~ expanded by flowing pres-surized inert gas through lines 72 and 74 while optimally a vacuum is applied to chamber 48 through lines 52 and 60. The pressurized inert gas, which protects the interior of stack 40 from contamination at the elevated forming temperatures, flows from tubes 72 and 74 into channel~ 75, preferably on opposite sides of stack 40, whereupon the ., iner~ gas flows within stack 40~ Such pressurized inert gas within stack 40 forces the expansion of stack 40 due to the pre~sure dif-ferential between the interior of stack 40 and chamber 48. The pres-~ure differential normally used for superplastic forming of Ti-6Al-4V
i3 normally in a range of from 25 to 250 psi. Metal blank 14 is initially lifted by the pressure differential and pulls with it at the ~elected joined area~ metal blank 12. Such expansion allows the ~3s~
pressurized inert gas to flow through apertures 96 to provide an equal pressure within stack 40 so that the core (workpiece 12) is formed uniformly. The equal pressure also retains metal blank 10 of stack 40 in its initial position, it being forced against the base or lower tooling frame 46.
Figures 5 and 6 illustrate the use of a differently con-figured lower tooling frame 100 having preferably integral sidewalls 102,104 which define a chamber 106. Tube lines 108 and 110 are pro-vided in lower tooling frame 100 for creating an inert gas environ-ment in chamber 106 and to act as vents or vacuum lines when super-pla~tically expanding stack 40. If stack 40 is diffusion bonded in forming apparatus 120, the pressure in both chambers 48 and 106 would have to be increased, preferably equally, so that a suitable pressure is applied to stack 40 for diffusion bonding. For superplastically expanding stack 40, the pressure within stack 40 would be increased by allowing flow of inert pressurized gas into c2tack 40 through lines 72 and 74 so that the pressure within stack 40 is greater than that in chambers 48 and 106. Additionally, the precsure in chambers 48 and 106 ~ould have been reduced and optimally exposed to vacuum through lines 108, 110, 52 and 60. As shown in Figure 6, since all three of the-metal blanks of stack 40 would be superplastically expanded, each of the blanks must be of a material with an effective ætrain rate sensitivity for superplastic forming. As illustrated, metal blank 14 is forced upwards into chamber 48, metal blank 10 is forced d~wnward into chamber 106, and metal bLank 12, by virtue of being selectively joined at specified locations to both metal blank 10 and metal blank 14 i deformed in both directions and forms the core of the sandwich structure as shown.
~C~50~5~ :
Figures 7 and 8 illustrate a modified forming apparatus 130 and the use of a different technique for selective joining. The use of a two sheet stack 132 with metal blanks 134 and 136 is also illustrated. Stack 132 could be ~oined as by diffusion bonding, brazing, or spot welding prior to insertion in forming apparatus 130.
If diffusion bonded, the metal blanks 134 and 136 would first be ~electively treated with a suitable stop-off so that only certain predetermined areas of the stack would be joined. Optimally, how-ever, the stack 132 would be unjoined prior to insertion in the forming apparatus 130. When such is the ca~e, stop-off need not be applied.
Forming apparatus 130 utilizes an upper tooling frame 140 having a lower arcuate surface defined by a plurality of protuberances 142 spaced from each other by intermediate recesses or chambers 144.
Lower tooling frame 150 has a complimentary upper arcuate surface 152 *o that deined by protuberances 142. Inflation tube~ 160 and 162 are positioned between the two metal blanks 134 and 136.
Similar to recesses 76 and 77 in metal blank 10 (Figure 1) blanks 134 and 136 are provided with aligned recesQes (not shown) which define a cylindrical chamber (not shown) in which tubes 160 and 162 are located~ Lines 164 and 166, like lines 52 and 60 of Figure 2, provide an inert gas environment in chambers 144 and act as vents or connection to ~ources of vacuum for drawing out the inert gas from chamber~ 144 for superplastically expanding metal blank 134 within those chambers. ~ach of tube~ 164 and 166 would be provided with a valve (not shown) and pressure gauge (not ~hown) to control addition and removal of inert gas in chambers 144~ Tubes 164 and 166 are connected to bores 170 and 172 respectively which provide access to chambers 144.
~(~50ZS0 Depending on the thickness and desired curvature of stack 132, l:he stack can be preformed to this shape prior to insertion in forming apparatus 130 by conventional sheet metal forming, as roll forming or superplastic forming, or subsequent to insertion in forming apparatus 130 by pressure applied to stack 132 by the pro-tuberances 142 o~ upper tooling frame 140 and surface 152 of lower tooling frame 150. Preforming in the forming apparatus 130 is pre-ferable as the preforming and selective diffusion bonding are accomplished simultaneously when the stack is also unjoined prior to insertion in forming apparatus 130, thereby saving fabrication time and equipment costs.
Using this forming apparatus 130, the unjoined stack can be diffusion bonded by application of pressurs from upper tooling frame 140 and lower tooling frame 15~ at required temperature for a suit-able time duration. By virtue of protuberances 142, the pressure is only applied to selected areas of stack 132 so that only those areas are diffusion bonded, thereby allowing for expansion in the unbonded areas.
After di4fusion bonding (or insertion into forming apparatus 130 if the stack 132 has already been joined) and preforming, stack 132 is inflated by flow of inert gas through lines 160 and 162 so that the unjoined areas of metal blank 134 are expanded into chambers 144. Optimally a vacuum would be applied to chambers 144 thrDugh lines 164 and 166. As the only space provided for expansion is chambers 144, only metal blank 134 is expanded and consequently only that blan~ must be of a material suitable for superplastic forming.
It is seen from the above that diffusion bonding, pre-forming, and superplastic expansion can all be done in the same apparatus in one operation 1 ~ _ 50~
It should be noted that the superplastic expansion could be done prior to diffusion bonding of stack 132 by sealing the sur-rounding area around stack 132 without applying pressure to stack 1327 Thus, upper tooling frame 140 could be applied to stack 132 con-tacting at its protuberances 142 without sufficient pressure for diffucion bonding. With this procedure, stack 132 would be expanded into chambers 144 by superplastic inflation with protuberances 142 preventing expansion at other areas without applicatuon of pressure by virtue of the position of tooling frame 140. After ~uch expansion, sufficient pressure would be applied by tooling frames 140 and 150 at areas corresponding to the lower surface of protuberances 142 to . diffusion bond those corresponding areas of stack 132.
Figure 9 illustrates the forming of a variably shaped : structure, here shown as a tapered sandwich ~tructure with an attach-ment joined thereto. Applicant accompliahes tapering of the sand-wich structure by suitably aesigning the corresponding shaping ~ur-face of the upper tooling frame. In Figure 9, upper tooling frame 170 has an upper shaping surface 172 which angles downwardly from one ~ide to the other (shown ai left to right). Thus, when the upper ~ 20 metal blank 174 of stack 176 is ~uperplastically expanded again~t .~ surface 172, it is shaped into the taper of such surface. The core formed by blank member 178 of stack 176 is also tapered by virtue of its dependence upon the movement of upper blank 174.
~ttachment 180, shown in an arbitrary design, is joined to the stack 176 on the upper member 174 along bond line 182 during the uperplastic expansion of stack 176 in the same forming apparatus, ~ : thereby lowering fabrication time, apparatus cost, and forming dif-~ ficulty. A3 set out in our prior co-pending application, Serial No.
511,900, attachment 180 could be positioned within a suitably shaped 10502S~
groove, here shown at 182, where the attachment may or may not protrude from such groove, or be located in the forming chamber, without the use of a groove so that it forms either a male or female shaping surface itself. For purposes of the claims, when a groove is used, it is considered part of the forming chamber, so that the attachment is positioned within the chamber when in the groove. In the embodiment illustrated, when stack 176 is superplastically expanded i.t contacts attachment 180 along bond line 182. By virtue of the superplastic forming temperature, which attachment 180 is also heated to, and the pressure expand-ing stack 176 which eventually forces upper member 174 to bear against surface 172 and attachment 182, attachment 182 is diffu-sion bonded to stack 176 along bond line 182 when the temperature and pressure are maintained at a required diffusion bonding level -for a suitable time duration. Optimally, the temperature and pressure for superplastic forming of members 174 and 178 would also be suitable for diffusion bonding so that the pressure or temperature would not have to be increased or decreased after forming in order to diffusion bond. The material selected for attachment 182 should be one that is suitable for diffusion bonding to the material of member 174, preferably a like mate-rial. As the superplastic forming gas pressure typically used j is 150 psi, a pressure considerably less than the 2000 psi used ,~ normally in diffusion bonding, the bond which results may not develop full parent metal strength, but would likely be analo-gous to a high quality braze joint. However, once the sandwich ~; structure is fully expanded, as shown in Figure 9, the pressure can be increased within the expanded sandwich through inflation tubes 190 and 192 to a level more suitable for complete diffusion , 30 bonding.
A close-out such as shown at 194 can also be formed to the..............................................................
' ~:
,. - . . . . . . .
~ 05(~2~ 2 ~ -expanded sandwich structure in the same operation by diffusion bonding the close out 194, which comprises an unexpanded end of stack 176, by heating stack 176 to the diffusion bonding temperature with application of pressure by upper and lower tooling frames 170 --and 171 respectively. The expanded sandwich structure 200 of Figure 9 removed from the forming apparatus is shown at Figure 10 with the side ends cut off.
Figure 11 illustrate~ the positioning of an inflation tube ~
10 relative to a four-piece metal sheet assembly or stack 212 in a --10forming apparatus having upper and lower chambers 214 and 216 -respectively. Inflation tube 210 is positioned bet~een the upper metal blank 217 and lower metal blank 218 with the lower metal blank 218 having a reces~ 220 at its periphery such as rece~s 76 shown in Figure 1. Inner metal blanks 221 and 222 of stack 212 have a recess such as that shown at 78 in Figure 1 which allows for positioning of inflation tube 210 between members 217 and 218. Apertures 230, for transmitting inflating gas, and stop-off 232 at areas for which no bonding i8 desired, are also illustrated. Illu~trative views of the final foxmed sandwich structure 240 of Figure 11 are shown at Figure-Q 12 and 13.
Thus it is apparent that there ha~ been provided, in accordance with the invention, a method for making metallic sandwich structure~ from a plurality of workpieces that fully ~atisfies the objective~, aim~, and ad~antages set forth above. While the inven-tion has been de~cribed in conjunction with specific embodiments thereof, it i~ evident that many alternatives, modifications, and variations, will be apparent to those skilled in the art in light of the foregoing de~cription. Accordingly, it is intended to embrace all such alternatives, modifications, and variations which fall within the spirit and scope of the appended claims.
3,180,02~; 3,044,160; 2,850,798; and 3,170,234. However, the prior art does not disclose combining these two processes.
In my co-pending Canadian application No. 233,354 there is disclosed a method for superplastic forming of metals with concurrent diffusion bonding. The crux of that invention is the superplastic forming of a metal blank against a shaping member and another metal workpiece so that the m~stal blank is formed and diffusion bonded to the other metal workpiece in one operation. Though a hollow metal structure bonded at peripheral edges can be formed as disclosed in 10 that application, the process is not designed for the forming of sandwich structures. The forming of ~andwich structures according to the present invention requires separate superplastic forming and joining stages and a technique for joining only ~elective areas of the metal blanks employed.
The present invention obviates the prior art problems of forming sandwich structures. A sandwich structure normally comprises a core between face sheets. Previous to applicant's invention, fabrication of sandwich structures typically took the approach of first rolling metal foil or ribbon, forming and joining the foil 20 sheet into the desired cellular core, and then attaching the core to face sheet~ by bracing or spot welding. Problems with the prior art method include the cost of the core due to excess material usage and the great difficulty, excess time consumption, and cost of fabrica-tion of the sandwich shape. Additionally, a separate operation is xequired to join a close out or attachment to the sandwich structure.
Fabrication of an unusual shape for the sandwich structure such as a taper, is nearly impossible.
_ y ~so~
SUMMARY OF THE I~VENTIO~
It is, therefore, an objec~ of the present invention to com-bine the processe~ of metal joining and superplastic forming to form metal sandwich structures.
It i9 another object of the present invention to form metal sandwich structure~ in one operation, thereby significantly lowering the cost, difficulty, and time involved.
It i~ yet another object of the pre~ent invention to form a sandwich structure and join an attachment or close-out in the same operation.
It is still another objsct of the present invention to heat, ~uperplastically form, and join the sandwich in the same apparatus, thereby s2ving fabrication time and equipment costs.
Briefly, in accordance with the invention, there is provided a method for making a metallic sandwich structure from a plurality of metal blank workpieces initially positioned in a 4tacked position.
~he blanks are joined at selected area~. At least one of the blanks i~ superplastically formed against a shaping member to form the desired ~andwich structure. The core configuration is determined by the location, size, and shape of the joined areas.
Other objectq and advantages of the invention will become apparent upon reading the following detailed description -and upon reference to the drawings.
B~I~F D~SCRIPTION OF THE DRAWINGS
Figure 1 i9 an exploded view of a three-piece metal sheet a~sembly treated for 3elective diffusion bonding prior to insertion in ~he forming apparatus:
Figure 2 is a cros~-sectional elevational view of a preferred embodiment of a forming apparatus used for fabrication of metal ~ oso~s~
sandwich structures with the three piece metal sheet assembly of Figure 1 inserted therein;
Figure 3 illustrates the fully expanded three-piece metal sheet assembly within the forming apparatus of Figure 2 with broken lines added to delineate the final position of the component metal sheets of the expanded joined assembly:
Figure 4 is a detail view of an inflation tube connection to the three-sheet assembly:
Figures 5 and 6 are cross-sectional elevational views of a modified forming apparatus with a three-piece metal sheet assembly inserted therein in its initial position in Figure 5 and in its final expanded po~ition in Figure 6 Figures 7 and 8 are cross-sectional elevational views of a modified forming apparatus with a two-piece metal sheet assembly inserted therein in its initial position in Figure 7 and in its final expanded position in Figure 8;
Figure 9 is a cross-sectional elevational view of a modified forming apparatus illustrating a tapered three-piece metal sheet assembly in final formed position with an attachment joined to the sandwich structure at the broken lines;
Figure 10 i8 a perspective view with the ends cut off of the formed sandwich structuxe of Figure 9:
Figure 11 is a fragmentary cro~s-sectional elevational view of a modified forming apparatus illustrating the positioning of an inflation t~be relative to a four-piece metal sheet assembly:
Fîgure 12 is a cross-sectional elevational view of a sandwich structure formed from a four-piece metal sheet assembly: and Figure 13 is a fragmentary perspective view of the sandwich structure shown in Figure 12.
~o~o While the invention will be described in connection with the preferred procedures, it will be understood that it is not intended to limit the invention to those procedures. On the contrary, it is intended to cover all alternatives, modifications, and equivalents that may be included within the ~pirit and scope of the invention as defined by the appended claim~
D13TAILED Dl~SCRIPTION OF THE INV~TION
In order for superplastic forming to be successful, it is necessary to u~e a material that is suitable. The extent to which the material selected will exhibit superplastic properties is pre-dictable in general terms from a determination of the strain rate sensitivity and a design determination of the permissible variation in wall thickness. Strain rate sensitivity can be defined as m where m egual~ dl~ and ~ i~ stre~s in pounds per square inch and e is strain rate in re~procal minutes. Strain rate sensitivity may be determined by a ~imple and now well recognized torsion test described in the article, "Determi.nation of Strain Hardening Characteristics by Torsion Testing" by D.S. Fields, Jr., and W.A. Backofen, published in the Proceedinga of the A.S.T.M., 1957, Volume 57, page~ 1259-1272.
A strain rate sensitivity of about 0.5 or greater can be expected to produce satisfactory results. The larger the value (to a maximum of one3 the greater the superplastic properties. Maximum ~train rate ~ensitivity in metals is seen to occur, if at all, as metals are de-- formed near the phase transformation temperature. Accordingly, the temperature immediately below the phase transformation temperature can be expected to produce the greatest ~train rate sensitivi~y. For titanium alloys, the temperature range in which superplasticity can be observed is about 1450 F. to about 1850 F. depending on the ~pecific alloy u~ed.
1050~5~
Other variables have been found to effect strain rate sen-sitivity and therefore should be considered in selecting a suitable metal material. Decreasing grain size results in correspondingly higher values for strain rate sensitivity. Additionally strain rate and material texture effect the strain rate ~ensitivity. It has been found that for titanium the m value reaches a peak at an intermediate value of strain rate (approximately 10 in./in./sec.). For maximum ~table deformation, superplastic forming should be done at or near this ~train rate. Too great a variance from the optimum strain rate may re~ult in loss of superpla-~tic properties.
Diffu~ion bonding, where separate elements form a single uni-; tary ma~s therefrom, may be practiced in a wide variety of metals and alloy~. However, the quality of the bond and the parameter~ employed will neces~arily vaxy for each particular choice of workpiece material~
Among the metals or alloys which may be joined by solid state dif- ~`
fus~on bonding are aluminium, stainles~ steel, titanium, nickel, ` tantalum, molybdenum, zirconium, columbium, and beryllium.
The present invention i~ particularly directed to the reactive metals whose surfaces would be contaminated at the elevated tempera-tures required for superplastic forming and diffu~ion bonding.
Titanium and its alloys are examples of ~uch metals which have also been found to be particularly well suited for a proces~ of the present invention in that the~alloys exhibit very high superplastic pro-perties in a temperature range suitable for diffuqion bonding, i.e.
1450F. to about 1850P. depending on the ~pecific alloy used.
Turning first to Figure 1, there is shown an exploded view of a three-piece metal sheet assembly to be formed into a ~andwich structure according to the present invention. ~he assembly is made up of metal blanks 10, 12 and 14, all preferably in the form of sheets ~ c~so~o having upper and lower opposed principal surfaces 15 and 16, 17 and 18, and 19 and 20, respectively (see also Figure 4). The number of sheets used will vary depending on load condi~ions and design require-ments However, a minimum of two sheets must be utilized and normally no moxe than four sheets would be used. The metal sheets must have the ability to be joined by such methods as bracing, welding, or diffusion bonding. Depending on the number of sheets to be expanded, at least one of the sheets muqt exhibit superplastic properties. Any metal tha~ exhibits suitable superplastic properties within a work-10 able temperature range can be used for such sheet, but the present --invention is particularly concerned with metals that exhibit super-plastic properties ~ithin the temperature range required for diffusion bonding and that are subject to contamination at forming temperatures, as titanium or an alloy thereo such as Ti-6Al-4V. When using Ti-6Al-4V, the forming temperature is preferably approximately 1700F.
Initial thickness of metal blankq 10, 12 and 14 are determined by the dimenqions of the part to be formed.
In order to join only selected areas of the metal qheets, a - preferred step is to apply a suitable stop-off material to thoqe areas within the stack where no attachment or joining between the sheets is desired. Thus, areas 30, 32, and 34 are covered with a stopooff material to pre~ent bonding in those areas. Other areas on surfaces 15, 18 and 20 could also be so covered for prevention of joining. Alternatively, the metal sheet structure could be spot welded or brazed at those areas where joining i8 desired. Addition-ally, as hereinafter explained, the metal sheet structure or stack 40 could be diffusion bonded at selected areas by selective applica-tion of pressureO
Figure 2 illustrates a preferred forming apparatus generally _ g _ ~C~S02S0 indicated at 42 for carrying out the invention. Upper tooling frame 44 has preferably integral side walls 45 in the form of a ring which can be of any desired shape. Lower tooling frame 46 which prefer-ably has the same outer area dimensions as upper frame 42 can be flat and act as a base as illustrated for supporting the stack of metal blanks 40. For purposes of the claims, both upper tooling frame 44 and lower tooling frame 46 are to be considered shaping members as both combine to form the desired shaped structure. The inner surface of upper tooling frame 44 defines an inner chamber 48 and a female die surface. One or more male die members (not shown) can be provided in chamber 48 to vary the shape of the part to be formed. The stack of metal blanks 40, which is supported on lower tooling frame 46, covers chamber 48. The metal blanks of t~e stack must all be of a material suitable ~or joining such aq by welding, brazing, or diffusion bonding. At least one of the outer metal blanks, and most likely the inner blanks, must have an effective strain rate sensitivity for exhibiting superplastic properties at a desired forming temperature and preferably within a temperature range required for diffusion bonding of the stack. This is shown in Figure 3 by the expanded stack 40 where both sheet~ 12 and 14 have been superplastically expanded, while sheet 10 of the formed stack has been sub~tantially unchanged. Initial thicknesses of the sheets of stack 40 are deter-mined by the dimension~ of the parts to be formed. The joining method to be used, namely welding, brazing, or diffusion bonding, depend~ on the material selected for the metal blanks, the temperature required for superplastic forming, and the desired strength. However, especially for titanium, diffu~ion bonding is preferred as this results in the strongest joining and the bonding temperature is generally suitable for superplastic forming.
~OS025i0 As previously mentioned, stop-off can be used at areas 30, 32 and 34 to prevent bonding at those areas. The particular stop- -off selected must prevent bonding and be compatible with the métal or metals of the stack (nonreactive with the stack metals and minimal diffusion into the stack metals). For titanium metal blanks, suitable stop-off materials are graphite, boron nitride, and yttria. Typically, when using yttria stop-off, the stop-off pattern on the blanks is sprayed with a solution of yttria and a binder therefor. The binder holds the yttria in position during bonding and eventually vaporizes 10 below forming temperature. ~ -Joining the stack 40 at selected locations, when by brazing or spot welding i8 normally accomplished outside of the forming apparatus 42 before the stack is placed therein. When diffusion bonding, the unjoined stack 40 i~ preferably bonded after placement in the forming apparatus 42, thereby saving fabrication time and equipment costs (although the ~tack could be diffusion bonded as by press bonding or roll bonding before placing it in the forming apparatus 42). The weight of upper tooling frame 44 acts as a clam-ping means for the stack 40. A single continuous edge of the stack 40 i~ effectively constrained between the upper tooling frame 44 and the lower tooling frame 46. This insures that those portions of the blanks of the stack to be formed, will be stretched rather than ; drawn. Should it be desired, additional tightening means such as bolts (not shownl can be employed to more effectively constrain the ~tack 40. Another additional tightening means that could be employed is a preqs (not shown), preferably hydraulic, having platens 50.
Forming apparatu~ 42 i~ positioned between platens 50 and compressed thereby as~uring that stack 40 is effectively constrained and cham-ber 48 qealed fr~m the air. This arrangement is particularly advan-~(~S(:~5~
tageous as the platens 50 can be made of ceramic material and resistance heated wires 52 can be provided therein for heating stack 40 to the forming temperature. Other heating methods could be used with lthe forming apparatus 42 ordinarily surrounded by a heating means if the heating platens are not used.
For contamination prevention and diffusion bonding of the ~tack 40 when unjoined within the forming apparatus 42, an environ-metal control ~ystem is provided. The purpose of the system is to expoae the ~tack 40 only to inert gas or vacuum while heating, forming and bonding, and optionally, to diffusion bond the stack by fluid pressure. The metal blanks of stack 40 will not react with inert gas due to the nature of inert gas, even at the elevated forming and bonding temperatures. In a high vacuum, there are substantially no elements for the stack 40 to react with. Thus, in this environment, contamination of the stack 40 will be prevented.
Line 52 i8 connected to a source of pressurized inert gas at one end (not shown) and to chamber 48 through orifice 54 in upper tooling frame 44. A valve 56 for governing the flow of inert gas through line 52 into chamber 48 and a pre~qure gauge 58 to indicate pressure are provided. The inert gas used is preferably argon in liquia form. Line 52 also functions as an outlet for inert gas in chamber 48 and could also be connected to a source of vacuum, such as a suction pump (not shown) for creating vacuum in chamber 48.
When line 52 ia uqed as an outlet, valve 56 governs flow of inert gas from chamber 48. An additional line 60 is optimally provided on ; the opposite ~ide of tooling frame 44 and functions a~ an outlet for inert gas in chamber 48. Line 60 is connected to chamber 48 through orifice 62 in upper tooling frame 44. Line 60 has a valve 64 pro-vided therein for regulation of inert gaq flow from chamber 48.
-- ~(350~2SQ
Line 60 can simply function as a vent or be connected to a source of vacuum, such as a suction pump (not shown).
AS previously stated, the contamination prevention system can also function as a means for gas pressure diffusion bonding stack 40. Thus, when stack 40 is placed in forming apparatus 42 as illustrated in Figure 2, the stack can be heated in an inert gas atmosphere to a suitable diffusion bonding temperature (approximately 1700F. when the metal blank3 of stack 40 are of Ti-6Al-4V) by heat generated from heating platens 50, and then applying pressure to stack 40 by increasing the pregsure in chamber 48 by adding additional pressurized inert gas through line 52 while maintaining line 60 closed by valve 64. In this manner, the untreated areas of stack 40 will ; be diffusion bonded by the application of such pres~ure, which i8 preferably approximately 500 p3i for Ti-6Al-4V, for a ~uitable forming t~me, which depends on the thickness of stack 40 and may vary from 30 minutes to 12 hours. The edges of the blanks of stack 40 may also be diffusion bonded if desired by virtue of sealing pressure thereon ! in the form of the weight of upper tooling 44 and optionally pressure from a press and/or a clamping means. After diffusion bonding stack . 20 40, excess inert gas would be removed from chamber 48 through lines 52 and 60 to allow for inflation of stack 40.
For expansion of stack 40 to the configuration shown in Figure 3 expan~ion tubes 72 and 74 are provided, the details of which are best illustrated in Figures 1 and 4. Expansion tube 72 (and likewise expansion tube 74 located on the opposite side of stack 40) is positioned between metal blanks 10 and 14 and protrudes into a channel 75 defined by recesses 76 and 78 and that portion of ~urface 20 of metal blank 14 which overlies recess 78. Recesses 77 and 79 are provid0d on the opposite sides of blanks 10 and 12 respectively ~ s~so to provide a channel for inflation tube 74. The positioning of expansion tube 72 in such a channel 75 prevents compression of tube 72 by the tooling frames 44 and 46. Also, by locating tube 72 so that it protrude~ only partially into channel 75, inert gas will flow fairly evenly between the metal blanks of stack 40, in this case on either side of blank 12 as shown by arrows 80 and 82. As shown in :-Figure 2 expansion tubes 72 and 74 have valves 84 and 86 therein respectively for governing flow of inert gas therethrough, and pres-sure gauges 88 and 90 for indicating pressure.
Expansion tubes 72 and 74 can also serve to draw off vaporized binder. To this end, tube 72 could act as an inlet and tube 72 an outlet with inert ga~ flow being transmitted through stack 40 prior ; to expansion of ~tack 40 to draw off the vaporized binder.
A pair of lateral grooves 71 (not shown) and 73 are preferably provided on opposite sides of lower tooling frame 46 with groove 71 in alignment with recess 77 and groove 73 in alignment with recess 76. The grooves 71 and 73 are provided to insure that passage of inert gas from inflation tubes 72 and 74 betwaen the metal blanks of stack 40 is not prevented from reaching treated areas 30 and 34 by pinching of the ~tack due to the pre~sure exerted by upper and lower tooling frames 44 and 46. The width of grooves 71 and 73 are prefer-ably the same as recesses 76 and 77, but grooves 71 and 73 terminate further inward in stack 40 so that pinching does not occur before the inert gas flow reaches treated areas 30 and 34.
As Rhown in Figure 1 when treating as by stop-off selected areas of stack 40 to prevent diffusion bonding thereon, additional areas such aR that shown at 92 and 94 ~hould likewise be treated to prevent bonding thereon so that the gas from inflation tubes 72 and 74 will reach the selected treated areas for expansion of stack 40.
l~S~ iO
Apertures 96 are provided in treated areas 300 32 and 34 for further transmitting the inert gas from inflation tubes 72 and 74 inside stack 40 to the other treated areas and to insure equal pressure inside stack 40 (in this case on either side of metal blank 12).
If pressure is unequal, the resulting core of the sandwich, metal blank 12 in the configuration illustrated in Figure 3, would be dis-torted with a consequent effect on load carrying ability on the final sandwich structure.
In order to make the expanded metallic sandwich structure as shown in Figure 3 according to applicants' inventive method, metal blank workpieces 10, 12 and 14 are provided. Both sheets 12 and 14 must be of a material having an effective strain rate sensitivity for superplastic forming. Optimally one or more of the blanks are treated at specified locations such as 30, 32 and 34 so that when the metal blanks are arranged in a stack 40 and diffusion bonded, only ; selected areas of the stack will be joined thereby. Alternately, the stack 40 could be spot welded or brazed for selective joining.
When joining by diffu~ion bonding, the stack 40 would optimally be placed in the forming apparatus 42 before forming. The pressure in chamber 48 would be increased by flow of pressurized inert gas through line 52 into chamber 48. Once ~hamber 48 had an inert gas atmosphere, the stack 40 would ~e heated by resi~tance wires 52 in heating platens 50 to a temperature which optimally woula be suitable for both di-ffu~ion bonding and superplastic forming, although the temperature ~o~ld later be raised or lowered if a different temperature is re-quired for superplastic forming. The pressure in chamber 48 would be increased b~ addgtional pressurized inert gas through line 52 to a pressure suitable for diffusion bonding of stack 40. That pressure would be maintained for a time duration sufficient for diffusion ~C~50~2S~:?
bonding. When the metal blanks of stack 40 are of Ti-4V-6Al alloy, the temperature used would be approximately 1700F. and the pressure about 500 psi. These values can of course be varied during forming and bonding as long as they are maintained within a suitable range.
The time duration will vary depending upon the alloys used, tempera- ;
ture, pressure, and thickness of stack 40. Duration may vary from 30 minutes to 15 hours, but three hours is a fairly repre~entative expectation. As previously stated, bonding temperature may vary from 1450F. to about 1850F. Bonding pressure may vary from about 100 psi to 2000 psi or more with the preferred range being 150 psi to 600 p3i.
Before expanding stack 40, the pressure in chamber 48 is reduced thxough lines 52 and 60. When stack 40 is joined prior to insertion in forming apparatus 42, the preceding di~fusion bonding step in forming apparatus 42 would be omitted. At superplastic forming temperature, which is approximately 1700F for Ti-6Al-4v alloy (generally 1650-1750F.), stack 40 i~ expanded by flowing pres-surized inert gas through lines 72 and 74 while optimally a vacuum is applied to chamber 48 through lines 52 and 60. The pressurized inert gas, which protects the interior of stack 40 from contamination at the elevated forming temperatures, flows from tubes 72 and 74 into channel~ 75, preferably on opposite sides of stack 40, whereupon the ., iner~ gas flows within stack 40~ Such pressurized inert gas within stack 40 forces the expansion of stack 40 due to the pre~sure dif-ferential between the interior of stack 40 and chamber 48. The pres-~ure differential normally used for superplastic forming of Ti-6Al-4V
i3 normally in a range of from 25 to 250 psi. Metal blank 14 is initially lifted by the pressure differential and pulls with it at the ~elected joined area~ metal blank 12. Such expansion allows the ~3s~
pressurized inert gas to flow through apertures 96 to provide an equal pressure within stack 40 so that the core (workpiece 12) is formed uniformly. The equal pressure also retains metal blank 10 of stack 40 in its initial position, it being forced against the base or lower tooling frame 46.
Figures 5 and 6 illustrate the use of a differently con-figured lower tooling frame 100 having preferably integral sidewalls 102,104 which define a chamber 106. Tube lines 108 and 110 are pro-vided in lower tooling frame 100 for creating an inert gas environ-ment in chamber 106 and to act as vents or vacuum lines when super-pla~tically expanding stack 40. If stack 40 is diffusion bonded in forming apparatus 120, the pressure in both chambers 48 and 106 would have to be increased, preferably equally, so that a suitable pressure is applied to stack 40 for diffusion bonding. For superplastically expanding stack 40, the pressure within stack 40 would be increased by allowing flow of inert pressurized gas into c2tack 40 through lines 72 and 74 so that the pressure within stack 40 is greater than that in chambers 48 and 106. Additionally, the precsure in chambers 48 and 106 ~ould have been reduced and optimally exposed to vacuum through lines 108, 110, 52 and 60. As shown in Figure 6, since all three of the-metal blanks of stack 40 would be superplastically expanded, each of the blanks must be of a material with an effective ætrain rate sensitivity for superplastic forming. As illustrated, metal blank 14 is forced upwards into chamber 48, metal blank 10 is forced d~wnward into chamber 106, and metal bLank 12, by virtue of being selectively joined at specified locations to both metal blank 10 and metal blank 14 i deformed in both directions and forms the core of the sandwich structure as shown.
~C~50~5~ :
Figures 7 and 8 illustrate a modified forming apparatus 130 and the use of a different technique for selective joining. The use of a two sheet stack 132 with metal blanks 134 and 136 is also illustrated. Stack 132 could be ~oined as by diffusion bonding, brazing, or spot welding prior to insertion in forming apparatus 130.
If diffusion bonded, the metal blanks 134 and 136 would first be ~electively treated with a suitable stop-off so that only certain predetermined areas of the stack would be joined. Optimally, how-ever, the stack 132 would be unjoined prior to insertion in the forming apparatus 130. When such is the ca~e, stop-off need not be applied.
Forming apparatus 130 utilizes an upper tooling frame 140 having a lower arcuate surface defined by a plurality of protuberances 142 spaced from each other by intermediate recesses or chambers 144.
Lower tooling frame 150 has a complimentary upper arcuate surface 152 *o that deined by protuberances 142. Inflation tube~ 160 and 162 are positioned between the two metal blanks 134 and 136.
Similar to recesses 76 and 77 in metal blank 10 (Figure 1) blanks 134 and 136 are provided with aligned recesQes (not shown) which define a cylindrical chamber (not shown) in which tubes 160 and 162 are located~ Lines 164 and 166, like lines 52 and 60 of Figure 2, provide an inert gas environment in chambers 144 and act as vents or connection to ~ources of vacuum for drawing out the inert gas from chamber~ 144 for superplastically expanding metal blank 134 within those chambers. ~ach of tube~ 164 and 166 would be provided with a valve (not shown) and pressure gauge (not ~hown) to control addition and removal of inert gas in chambers 144~ Tubes 164 and 166 are connected to bores 170 and 172 respectively which provide access to chambers 144.
~(~50ZS0 Depending on the thickness and desired curvature of stack 132, l:he stack can be preformed to this shape prior to insertion in forming apparatus 130 by conventional sheet metal forming, as roll forming or superplastic forming, or subsequent to insertion in forming apparatus 130 by pressure applied to stack 132 by the pro-tuberances 142 o~ upper tooling frame 140 and surface 152 of lower tooling frame 150. Preforming in the forming apparatus 130 is pre-ferable as the preforming and selective diffusion bonding are accomplished simultaneously when the stack is also unjoined prior to insertion in forming apparatus 130, thereby saving fabrication time and equipment costs.
Using this forming apparatus 130, the unjoined stack can be diffusion bonded by application of pressurs from upper tooling frame 140 and lower tooling frame 15~ at required temperature for a suit-able time duration. By virtue of protuberances 142, the pressure is only applied to selected areas of stack 132 so that only those areas are diffusion bonded, thereby allowing for expansion in the unbonded areas.
After di4fusion bonding (or insertion into forming apparatus 130 if the stack 132 has already been joined) and preforming, stack 132 is inflated by flow of inert gas through lines 160 and 162 so that the unjoined areas of metal blank 134 are expanded into chambers 144. Optimally a vacuum would be applied to chambers 144 thrDugh lines 164 and 166. As the only space provided for expansion is chambers 144, only metal blank 134 is expanded and consequently only that blan~ must be of a material suitable for superplastic forming.
It is seen from the above that diffusion bonding, pre-forming, and superplastic expansion can all be done in the same apparatus in one operation 1 ~ _ 50~
It should be noted that the superplastic expansion could be done prior to diffusion bonding of stack 132 by sealing the sur-rounding area around stack 132 without applying pressure to stack 1327 Thus, upper tooling frame 140 could be applied to stack 132 con-tacting at its protuberances 142 without sufficient pressure for diffucion bonding. With this procedure, stack 132 would be expanded into chambers 144 by superplastic inflation with protuberances 142 preventing expansion at other areas without applicatuon of pressure by virtue of the position of tooling frame 140. After ~uch expansion, sufficient pressure would be applied by tooling frames 140 and 150 at areas corresponding to the lower surface of protuberances 142 to . diffusion bond those corresponding areas of stack 132.
Figure 9 illustrates the forming of a variably shaped : structure, here shown as a tapered sandwich ~tructure with an attach-ment joined thereto. Applicant accompliahes tapering of the sand-wich structure by suitably aesigning the corresponding shaping ~ur-face of the upper tooling frame. In Figure 9, upper tooling frame 170 has an upper shaping surface 172 which angles downwardly from one ~ide to the other (shown ai left to right). Thus, when the upper ~ 20 metal blank 174 of stack 176 is ~uperplastically expanded again~t .~ surface 172, it is shaped into the taper of such surface. The core formed by blank member 178 of stack 176 is also tapered by virtue of its dependence upon the movement of upper blank 174.
~ttachment 180, shown in an arbitrary design, is joined to the stack 176 on the upper member 174 along bond line 182 during the uperplastic expansion of stack 176 in the same forming apparatus, ~ : thereby lowering fabrication time, apparatus cost, and forming dif-~ ficulty. A3 set out in our prior co-pending application, Serial No.
511,900, attachment 180 could be positioned within a suitably shaped 10502S~
groove, here shown at 182, where the attachment may or may not protrude from such groove, or be located in the forming chamber, without the use of a groove so that it forms either a male or female shaping surface itself. For purposes of the claims, when a groove is used, it is considered part of the forming chamber, so that the attachment is positioned within the chamber when in the groove. In the embodiment illustrated, when stack 176 is superplastically expanded i.t contacts attachment 180 along bond line 182. By virtue of the superplastic forming temperature, which attachment 180 is also heated to, and the pressure expand-ing stack 176 which eventually forces upper member 174 to bear against surface 172 and attachment 182, attachment 182 is diffu-sion bonded to stack 176 along bond line 182 when the temperature and pressure are maintained at a required diffusion bonding level -for a suitable time duration. Optimally, the temperature and pressure for superplastic forming of members 174 and 178 would also be suitable for diffusion bonding so that the pressure or temperature would not have to be increased or decreased after forming in order to diffusion bond. The material selected for attachment 182 should be one that is suitable for diffusion bonding to the material of member 174, preferably a like mate-rial. As the superplastic forming gas pressure typically used j is 150 psi, a pressure considerably less than the 2000 psi used ,~ normally in diffusion bonding, the bond which results may not develop full parent metal strength, but would likely be analo-gous to a high quality braze joint. However, once the sandwich ~; structure is fully expanded, as shown in Figure 9, the pressure can be increased within the expanded sandwich through inflation tubes 190 and 192 to a level more suitable for complete diffusion , 30 bonding.
A close-out such as shown at 194 can also be formed to the..............................................................
' ~:
,. - . . . . . . .
~ 05(~2~ 2 ~ -expanded sandwich structure in the same operation by diffusion bonding the close out 194, which comprises an unexpanded end of stack 176, by heating stack 176 to the diffusion bonding temperature with application of pressure by upper and lower tooling frames 170 --and 171 respectively. The expanded sandwich structure 200 of Figure 9 removed from the forming apparatus is shown at Figure 10 with the side ends cut off.
Figure 11 illustrate~ the positioning of an inflation tube ~
10 relative to a four-piece metal sheet assembly or stack 212 in a --10forming apparatus having upper and lower chambers 214 and 216 -respectively. Inflation tube 210 is positioned bet~een the upper metal blank 217 and lower metal blank 218 with the lower metal blank 218 having a reces~ 220 at its periphery such as rece~s 76 shown in Figure 1. Inner metal blanks 221 and 222 of stack 212 have a recess such as that shown at 78 in Figure 1 which allows for positioning of inflation tube 210 between members 217 and 218. Apertures 230, for transmitting inflating gas, and stop-off 232 at areas for which no bonding i8 desired, are also illustrated. Illu~trative views of the final foxmed sandwich structure 240 of Figure 11 are shown at Figure-Q 12 and 13.
Thus it is apparent that there ha~ been provided, in accordance with the invention, a method for making metallic sandwich structure~ from a plurality of workpieces that fully ~atisfies the objective~, aim~, and ad~antages set forth above. While the inven-tion has been de~cribed in conjunction with specific embodiments thereof, it i~ evident that many alternatives, modifications, and variations, will be apparent to those skilled in the art in light of the foregoing de~cription. Accordingly, it is intended to embrace all such alternatives, modifications, and variations which fall within the spirit and scope of the appended claims.
Claims (12)
PROPERTY OR PRIVILEGE IS CLAIMED ARE DEFINED AS FOLLOWS:
1. A method of making a metallic sandwich structure from a plurality of workpieces comprising:
providing at least two shaping members;
providing a plurality of metal workpieces, each of said workpieces having two opposed principal surfaces, at least one of said workpieces having superplastic characteristics;
positioning said workpieces in a stack contacting at their principal surfaces, at least one of the outer workpieces of said stack having superplastic characteristics;
enclosing at least one chamber by positioning said stack of workpieces relative to said shaping members;
heating said workpieces to within a temperature range sufficient to produce diffusion bonding of said workpieces at preselected areas under coordinated temperature-pressure-time duration conditions;
applying compressive pressure to selected areas of said stack sufficient for diffusion bonding of said preselected areas;
maintaining said pressure and said temperature for a time duration sufficient to produce diffusion bonding of said workpieces at said preselected areas; and inducing tensile stress in said at least one outer workpiece causing at least a portion of said at least one outer workpiece to expand superplastically into said at least one chamber and to form against, and into intimate contact with at least one of said shaping members.
providing at least two shaping members;
providing a plurality of metal workpieces, each of said workpieces having two opposed principal surfaces, at least one of said workpieces having superplastic characteristics;
positioning said workpieces in a stack contacting at their principal surfaces, at least one of the outer workpieces of said stack having superplastic characteristics;
enclosing at least one chamber by positioning said stack of workpieces relative to said shaping members;
heating said workpieces to within a temperature range sufficient to produce diffusion bonding of said workpieces at preselected areas under coordinated temperature-pressure-time duration conditions;
applying compressive pressure to selected areas of said stack sufficient for diffusion bonding of said preselected areas;
maintaining said pressure and said temperature for a time duration sufficient to produce diffusion bonding of said workpieces at said preselected areas; and inducing tensile stress in said at least one outer workpiece causing at least a portion of said at least one outer workpiece to expand superplastically into said at least one chamber and to form against, and into intimate contact with at least one of said shaping members.
2. The method of claim 1 wherein said temperature suffici-ent to produce diffusion bonding is suitable for superplastic forming.
3. The method of claim 1 also including after the step of maintaining said pressure and temperature the step of adjust-ing the temperature to a value suitable for superplastic forming.
4. The method as set out in claim 2 also including after the step of enclosing at least one chamber, the step of providing an inert gas environment in said at least one chamber.
5. The method as set out in claim 4 wherein said tensile stress is induced by applying an inert gas pressure loading across the principal surfaces of said at least one outer work-piece for a substantial period of time inversely related to the induced tensile stress, and said at least one outer workpiece is stretched substantially in excess of its original surface area.
6. The method as set out in claim 5 wherein one of said shaping members has at least one protruding portion and said compressive pressure is applied to selected areas of said stack by said at least one protruding portion.
7. The method as set out in claim 5 wherein said pressure loading is applied by establishing a higher inert gas pressure in the interstices between unjoined areas of said workpieces of said stack than in said chamber.
8. The method as set out in claim 4 wherein said compres-sive pressure performs said stack of workpieces.
9. The method as defined in claim 7 wherein said at least one chamber is vented to allow for efflux of inert gas as said at least one outer workpiece expands and thereby reduces the size of said at least one chamber.
10. The method as defined in claim 7 wherein said pressure loading comprises application of vacuum to said at least one chamber while maintaining a positive pressure of inert gas between the workpiece of said stack.
11. The method as defined in claim 5 wherein said inert gas is argon, said metal workpieces are titanium alloy sheet, said temperature range is about 1650-1750°F.
12. The method as defined in claim 5 also including the step of providing at least one metal attachment to be diffusion bonded to said at least one outer workpiece, and wherein said at least one attachment is located within said at least one chamber, and said at least one outer workpiece also deforms against and diffusion bonds to said at least one attachment.