AU2001291137A1 - Temperature dependent electrically resistive yarn - Google Patents

Temperature dependent electrically resistive yarn

Info

Publication number
AU2001291137A1
AU2001291137A1 AU2001291137A AU9113701A AU2001291137A1 AU 2001291137 A1 AU2001291137 A1 AU 2001291137A1 AU 2001291137 A AU2001291137 A AU 2001291137A AU 9113701 A AU9113701 A AU 9113701A AU 2001291137 A1 AU2001291137 A1 AU 2001291137A1
Authority
AU
Australia
Prior art keywords
yarn
yarn according
core
matrix material
conductive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Abandoned
Application number
AU2001291137A
Inventor
Alfred R. Deangelis
Earle Wolynes
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Milliken and Co
Original Assignee
Milliken and Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Milliken and Co filed Critical Milliken and Co
Publication of AU2001291137A1 publication Critical patent/AU2001291137A1/en
Abandoned legal-status Critical Current

Description

TEMPERATURE DEPENDENT ELECTRICALLY RESISTIVE
YARN
Background
The present invention relates generally to electrically conductive yarns, and in particular, to electrically conductive yarns providing a resistance that is variable with temperature. Electrically conductive elements have been used as heating elements in textiles such as knit or woven fabrics. The electrically conductive elements are incorporated into the textile, and electricity is passed though the electrically conductive elements. Therefore, there is a need for electrically conductive elements, such as yarns for use in items such as textiles.
Brief Description Of The Drawings
FIG. 1 shows an enlarged cross-sectional view of an embodiment of the present invention, illustrated as a temperature variable resistive yarn;
FIG. 2 shows a graph of current as a function of voltage through one inch of one embodiment of the yarn in the present invention; and
FIG. 3 shows a graph illustrating the different temperature dependence of the electrical resistance of one embodiment of a yarn made according to the present invention, and "conventional" conducting materials that might be put into a fabric.
Detailed Description
Referring to FIG. 1 , there is shown a temperature dependent electrically resistive yarn 10 illustrating one embodiment of the present invention. The yarn 10 generally comprises a core yarn 100 and a positive temperature coefficient of resistance (PTCR) sheath 200. The yarn 10 can also include an insulator 300 over the PTCR sheath 200. As illustrated, the temperature variable resistive yarn 10 is a circular cross section; however, it is anticipated that the yarn 10 can have other cross sections which are suitable for formation into textiles, such as oval, flat, or the like.
The core yarn 100 is generally any material providing suitable flexibility and strength for a textile yarn. The core yarn 100 can be formed of synthetic yarns such as polyester, nylon, acrylic, rayon, Kevlar, Nomex, glass, or the like, or can be formed of natural fibers such as cotton, wool, silk, flax, or the like. The core yarn 100 can be formed of monofilaments, multifilaments, or staple fibers. Additionally, the core yarn 100 can be flat, spun, or other type yarns that are used in textiles. In one embodiment, the core yarn 100 is a non-conductive material.
The PTCR sheath 200 is a material that provides increased electrical resistance with increased temperature. In the embodiment of the present invention, illustrated in FIG. 1 , the sheath 200 generally comprises distinct electrical conductors 210 intermixed within a thermal expansive low conductive (TELC) matrix 220. The distinct electrical conductors 210 provide the electrically conductive pathway through the PTCR sheath 200. The distinct electrical conductors 210 are preferably particles such as particles of conductive materials, conductive-coated spheres, conductive flakes, conductive fibers, or the like. The conductive particles, fibers, or flakes can be formed of materials such as carbon, graphite, gold, silver, copper, or any other similar conductive material. The coated spheres can be spheres of materials such as glass, ceramic, copper, which are coated with conductive materials such as carbon, graphite, gold, silver, copper or other similar conductive material. The spheres are microspheres, and in one embodiment, the spheres are between about 10 and about 100 microns in diameter. The TELC matrix 220 has a higher coefficient of expansion than the conductive particles 210. The material of the TELC matrix 220 is selected to expand with temperature, thereby separating various conductive particles 210 within the TELC matrix 220. The separation of the conductive particles 210 increases the electrical resistance of the PTCR sheath 200. The TELC matrix 220 is also flexible to the extent necessary to be incorporated into a yarn. In one embodiment, the TELC matrix 220 is an ethylene ethylacrylate (EEA) or a combination of EEA with polyethylene. Other materials that might meet the requirements for a material used as the TELC matrix 220 include, but are not limited to, polyethylene, polyolefins, halo-derivitaves of polyethylene, thermoplastic, or thermoset materials. The PTCR sheath 200 can be applied to the core 100 by extruding, coating, or any other method of applying a layer of material to the core yarn 100. Selection of the particular type of distinct electrical conductors 210 (e.g. flakes, fibers, spheres, etc.) can impart different resistance-to-temperature properties, as well as influence the mechanical properties of the PTCR sheath 200. The TELC matrix 220 can be formed to resist or prevent softening or melting at the operating temperatures. It has been determined that useful resistance values for the yarn 10 could vary anywhere within the range of from about 0.1 Ohms/Inch to about 2500 Ohms/Inch, depending on the desired application.
A description of attributes of a material that could be suitable as the PTCR sheath 200 can also be found in U.S. Patent No. 3,243,753, issued on March 29, 1966 to Fred Kohler, which is hereby incorporated herein in its entirety by specific reference thereto. A description of attributes of another material that could be suitable as the PTCR sheath 200 can also be found in U.S. Patent No. 4,818,439, issued on April 4, 1984 to Blackledge et al., which is also hereby incorporated herein in its entirety by specific reference thereto.
One embodiment of the present invention, the TELC matrix 220 can be set by cross-linking the material, for example through radiation, after application to the core yarn 100. In another embodiment, the TELC matrix 220 can be set by using a thermosetting polymer as the TELC matrix 220. In another embodiment, TELC matrix 220 can be left to soften at a specific temperature to provide a built-in "fuse" that will cut off the conductivity of the TELC matrix 220 at the location of the selected temperature. The insulator 300 is a non-conductive material which is appropriate for the flexibility of a yarn. In one embodiment, the coefficient of expansion is close to the TELC matrix 220. The insulator 300 can be a thermoplastic, thermoset plastic, or a thermoplastic that will change to thermoset upon treatment, such as polyethylene. Materials suitable for the insulator 300 include polyethylene, polyvinylchloride, or the like. The insulator 300 can be applied to the PTCR sheath 200 by extrusion, coating, wrapping, or wrapping and heating the material of the insulator 300.
A voltage applied across the yarn 10 causes a current to flow through the PTCR sheath 200. As the temperature of the yarn 10 increases, the resistance of the PTCR sheath 200 increases. The increase in the resistance of the yarn 10 is obtained by the expansion of the TELC matrix 220 separating conductive particles 210 within the TELC matrix 220, thereby removing the micropaths along the length of the yarn 10 and increasing the total resistance of the PTCR sheath 200. The particular conductivity-to-temperature relationship is tailored to the particular application. For example, the conductivity may increase slowly to a given point, the rise quickly at a cutoff temperature.
The present invention can be further understood by reference to the following examples: Example 1
A temperature dependent electrically resistance yarn was formed from a core yarn of 500 denier multi-filament polyester with a PTCR sheath of fifty percent (50%) carbon conducting particles and fifty percent (50%) EEA. The average yarn size was about 40 mils, with a denier of 8100. Prior to extruding the PTCR sheath onto the core yarn, the material for the PTCR sheath was predried at 165F for at least twenty four (24) hours. The yarn was formed by extrusion coating the TELC material onto the core yarn at a temperature of about 430F through an orifice of about 47 mils, at a pressure of about 6600 psi. The coated core yarn was quenched in water at a temperature of about 85F. The resistance of the yarn was about 350 Ohms/Inch at about 72F. The final yarn had a tenacity of about 9.3 lbs and an elongation at breaking of about 12%, giving a stiffness of 4.3 grams/denier %
Example 2
The yarn of Example 1 was coated with an insulation layer of polyethylene.
The polyethylene was Tenite 812A from Eastman Chemicals. The polyethylene was extruded onto the yarn at a temperature of about 230F at a pressure of about 800 psi, and was water quenched at a temperature of about 75F. The final diameter of the insulated yarn was about 53 mils, and had a denier of about 13,250. The resistance of the insulated yarn was about 400 Ohms/Inch at about 75F.
Example 3 The yarn of Example 1 was coated with an insulation layer of polyethylene, the polyethylene being Dow 955I from Dow Plastics. The polyethylene was extruded onto the yarn at a temperature of about 230F at a pressure of about 800 psi, and was water quenched at a temperature of about 75F. The final diameter of the insulated yarn was about 53 mils, and had a denier of about 13,250. The resistance of the insulated yarn was about 400 Ohms/Inch at about 75F.
Example 4
A temperature dependent electrically resistance yarn was formed from a core yarn of 500 denier multi-filament polyester with a PTCR sheath of fifty percent (50%) carbon conducting particles and fifty percent (50%) EEA. The average yarn size was about 46 mils. Prior to extruding the PTCR sheath onto the core yarn, the material for the PTCR sheath was predried at 165F for at least twenty four (24) hours. The yarn was formed by extrusion coating the TELC material onto the core yarn at a temperature of about 430F through an orifice of about 59 mils, at a pressure of about
5600 psi. The coated core yarn was quenched in water at a temperature of about
70F. The resistance of the yarn was about 250 Ohms/Inch at about 72F.
Example 5
A temperature dependent electrically resistance yarn was formed from a core yarn of 1000 denier multi-filament Kevlar with a PTCR sheath of fifty percent (50%) carbon conducting particles and fifty percent (50%) EEA. The average yarn size was about 44 mils. Prior to extruding the PTCR sheath onto the core yarn, the material for the PTCR sheath was predried at 165F for at least twenty four (24) hours. The yam was formed by extrusion coating the TELC material onto the core yarn at a temperature of about 415F through an orifice of about 47 mils, at a pressure of about 3900 psi. The coated core yarn was quenched in water at a temperature of about 70F. The resistance of the yarn was about 390 Ohms/Inch at about 72F.
Example 6 A temperature dependent electrically resistance yarn was formed from a core yarn of 1000 denier multi-filament Kevlar with a PTCR sheath of fifty percent (50%) carbon conducting particles and fifty percent (50%) EEA. The average yarn size was about 32 mils. Prior to extruding the PTCR sheath onto the core yarn, the material for the PTCR sheath was predried at 165F for at least twenty four (24) hours. The yarn was formed by extrusion coating the TELC material onto the core yarn at a temperature of about 415F through an orifice of about 36 mils, at a pressure of about 3700 psi. The coated core yarn was quenched in water at a temperature of about 70F. The resistance of the yarn was about 1000 Ohms/Inch at about 72F.
Referring now to FIG. 2, there is show a graph of current as a function of voltage through one inch of the yarn from Example 1. A 4-probe resistance setup was used to apply a steadily increasing DC voltage to the yarn in ambient air. The voltage across and current through- a 1-inch length of yarn was monitored and plotted in FIG. 2. FIG. 2 shows that the yarn of this invention can be used to limit the total current draw. The limitation on current draw both controls heat generation and helps prevent thermal stress to the yarn, reducing the possibility of broken heating elements. As shown the current draw for a yarn from Example 1 was limited to about 15 mA per yarn. A larger yarn would pass more current, as would a more conductive yarn. Conversely, a smaller or less conductive yarn would pass less current.
Referring now to FIG. 3, there is show a graph illustrating the different temperature dependence of the electrical resistance of a yarn made according to the present invention, and "conventional" conducting materials that might be put into a fabric. "TDER yarn" is the yarn from Example 1. "Copper wire" is a commercially available 14 gage single-strand wire. "Silver-coated nylon" is a 30 denier nylon yarn coated with silver, available from Instrument Specialties - Sauquoit of Scranton, Pennsylvania. "Stainless steel yarn" is a polyester yarn with 4 filaments of stainless steel twisted around the outside, available from Bekaert Fibre Technologies of Marietta, Georgia. In FIG. 3, the Relative Resistance is the resistance of the material relative to its value at 100F. The three conventional materials all show very small temperature coefficients, whereas the resistance of the TDER yarn changes by more than a factor of 6 at 250 F. As is typically the case for polymer-based PTCR materials, further heating will reduce the resistance. In actual use, products can be designed so they do not reach this temperature range during operation. Table 1 below lists the temperature coefficients for each material in the range of 150F - 200F. From the last column we see that the TDER yarn has 50 or more times the temperature coefficient of other typically available conductive materials suitable for construction of a textile.
Table 1

Claims (40)

WHAT IS CLAIMED IS:
1. A temperature dependent electrically resistance yarn comprising: a core yarn; a sheath having a positive temperature coefficient of resistance, said sheath including: a matrix material a plurality of distinct electrical conductors intermixed throughout the matrix.
2. The yarn according to Claim 1 , wherein said yarn further comprises a circular cross-section.
3. The yarn according to Claim 1 , wherein said yarn further comprises a oval cross-section.
4. The yarn according to Claim 1 , wherein said yarn further comprises a flat cross-section.
5. The yarn according to Claim 1 , wherein said core yarn comprises a synthetic yarn.
6. The yarn according to Claim 5, wherein said core yarn includes a material selected from polyester, nylon, acrylic, rayon, or glass.
7. The yarn according to Claim 1 , wherein said core yarn comprises a natural fiber yarn.
8. The yarn according to Claim 7, wherein said core yarn includes a material selected from cotton, wool, silk, or flax.
9. The yarn according to Claim 1 , wherein said core yarn comprises a monofilament yarn.
10. The yarn according to Claim 1 , wherein said core yarn comprises a multifilament yarn.
11. The yarn according to Claim 1 , wherein said core yarn comprises a flat yarn.
12. The yarn according to Claim 1 , wherein said core yarn comprises a spun yarn.
13. The yarn according to Claim 1 , wherein said core yarn comprises a staple fiber yarn.
14. The yarn according to Claim 1 , wherein said core yarn comprises a nonconductive yarn.
15. The yarn according to Claim 1 , wherein the electrical conductors comprises conductive particles.
16. The yarn according to Claim 15, wherein the conductive particles comprise one of the following materials: carbon, graphite, gold, silver, or copper.
17. The yarn according to Claim 1 , wherein the electrical conductors comprise conductive flakes.
18. The yarn according to Claim 17, wherein the conductive flakes comprise one of the following materials: carbon, graphite, gold, silver, or copper.
19. The yarn according to Claim 1 , wherein the electrical conductors comprise conductive fibers.
20. The yarn according to Claim 19, wherein the conductive fibers comprise one of the following materials: carbon, graphite, gold, silver, or copper.
21. The yarn according to Claim 1 , wherein the electrical conductors are conductive coated spheres.
22. The yarn according to Claim 21 , wherein the electrical conductors are spheres coated with a conductive material.
23. The yarn according to Claim 22, wherein the spheres comprise one of the following materials: glass, ceramic or copper.
24. The yarn according to Claim 22, wherein the conductive material comprises one of the following materials: carbon, graphite, gold, silver, or copper.
25. The yarn according to Claim 21 , wherein the spheres are between about 10 microns and about 100 microns.
26. The yarn according to Claim 1 , wherein said matrix material has a higher coefficient of expansion than the electrical conductors.
27. The yarn according to Claim 1 , wherein said matrix material comprises a material that expands with a temperature increase.
28. The yarn according to Claim 1 , wherein said matrix material comprises ethylene ethylacrylate.
29. The yarn according to Claim 28, wherein said matrix material further includes polyethylene.
30. The yarn according to Claim 1 , wherein said matrix material comprises one of the following materials: polyethylene, polyolefins, halo-derivatives of polyethylene.
31. The yarn according to Claim 1 , wherein said matrix material comprises a thermoplastic
32. The yarn according to Claim 1 , wherein said matrix material comprises a thermoset material.
33. The yarn according to Claim 1 , wherein the resistance value of the yarn is from about 01 Ohms/Inch to about 2500 Ohms/Inch.
34. The yarn according to Claim 1 , wherein said matrix material is cross-linked.
35. The yarn according to Claim 1 , further including an insulator covering the sheath.
36. The yarn according to Claim 35, wherein the coefficient of expansion of the insulator is substantially the same as the coefficient of expansion of the matrix material of the sheath.
37. The yarn according to Claim 35, wherein the insulator comprises a thermoplastic.
38. The yam according to Claim 35, wherein the insulator comprises a thermoset plastic.
39. The yarn according to Claim 35, wherein the insulator comprises polyethylene.
40. The yarn according to Claim 35, wherein the insulator comprises polyvinylchloride.
AU2001291137A 2000-09-21 2001-09-19 Temperature dependent electrically resistive yarn Abandoned AU2001291137A1 (en)