Mixed mode fracture parameters and fracture characteristics of diorite using cracked straight through Brazilian disc specimenZhu et al., 2023
- Document ID
- 1765984964456637459
- Author
- Zhu Q
- Li D
- Li X
- Han Z
- Ma J
- Publication year
- Publication venue
- Theoretical and Applied Fracture Mechanics
External Links
Snippet
In this study, the cracked straight through Brazilian disc (CSTBD) specimen was applied to study the I/II mixed mode static fracture of diorite. The fracture load and fracture toughness for different prefabricated crack angles β were determined. The fracture and morphological …
- 238000011068 load 0 abstract description 89
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Zhu et al. | Mixed mode fracture parameters and fracture characteristics of diorite using cracked straight through Brazilian disc specimen | |
| Lv et al. | Environmental impact, durability performance, and interfacial transition zone of iron ore tailings utilized as dam concrete aggregates | |
| Zhu et al. | Fatigue life and mechanistic modeling of interior micro-defect induced cracking in high cycle and very high cycle regimes | |
| Fakhri et al. | Crack behavior analysis of roller compacted concrete mixtures containing reclaimed asphalt pavement and crumb rubber | |
| Hu et al. | Insight into the evolution of the elastic properties of calcium-silicate-hydrate (CSH) gel | |
| Němeček et al. | Tensile strength of hydrated cement paste phases assessed by micro-bending tests and nanoindentation | |
| Wu et al. | Residual stress and subsurface damage in machined alumina and alumina/silicon carbide nanocomposite ceramics | |
| Xu et al. | Mechanical properties of 3D fiber reinforced C/SiC composites | |
| Ding et al. | Orientation distribution of polyvinyl alcohol fibers and its influence on bridging capacity and mechanical performances for high ductility cementitious composites | |
| Zhu et al. | Mixed mode I/II fracture behavior and surface morphology of hard rock under dynamic loading | |
| Sadowski et al. | Micromechanical properties within the interphase between heterogeneous layers made of cementitious composites | |
| Xie et al. | The influence of shot peening on the surface properties of (TiB+ TiC)/Ti–6Al–4V | |
| Cao et al. | Relationship of rheology, fiber dispersion, and strengths of polyvinyl alcohol fiber-reinforced cementitious composites | |
| Le et al. | Comparisons of flexural, split tensile, double punch, and direct tension tests on high-performance concrete reinforced with different fiber types | |
| Xie et al. | The variations of microstructures and hardness of titanium matrix composite (TiB+ TiC)/Ti–6Al–4V after shot peening | |
| Ning et al. | A mass abrasion model with the melting and cutting mechanisms during high-speed projectile penetration into concrete slabs | |
| Hemalatha et al. | Micromechanical analysis of self compacting concrete | |
| Wen et al. | Nanoindentation size effect of tungsten single crystal | |
| Lee et al. | Effects of blades inside a nozzle on the fiber orientation and distribution in fiber-reinforced cement-based materials | |
| Yasnii et al. | Correlation of the microdislocation parameters with the hardness of plastically deformed heat-resistant steels | |
| Zhang et al. | Low temperature impact toughness and fracture analysis of EN-GJS-400-18-LT ductile iron under instrumented impact load | |
| Kaynak et al. | Initiation and early growth of short fatigue cracks at inclusions | |
| Ahmad et al. | Proposed equation of elastic modulus of hybrid fibers reinforced concrete cylinders | |
| Shlyakhova et al. | Structure of carbon steel under plastic deformation | |
| Andrushia et al. | SEM image-based porosity analysis of fire damaged high strength concrete |