Correlation between failure and local material property in chopped carbon fiber chip‐reinforced sheet molding compound composites under tensile loadTang et al., 2019
View PDF- Document ID
- 17598302689215436856
- Author
- Tang H
- Chen Z
- Zhou G
- Li Y
- Avery K
- Guo H
- Kang H
- Zeng D
- Su X
- Publication year
- Publication venue
- Polymer Composites
External Links
Snippet
To develop further understanding towards the role of a heterogeneous microstructure on tensile crack initiation and failure behavior in chopped carbon fiber chip‐reinforced composites, uni‐axial tensile tests are performed on coupons cut from compression molded …
- 229920000049 Carbon (fiber) 0 title abstract description 24
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0058—Kind of property studied
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0014—Type of force applied
- G01N2203/0016—Tensile or compressive
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N3/00—Investigating strength properties of solid materials by application of mechanical stress
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Tang et al. | Correlation between failure and local material property in chopped carbon fiber chip‐reinforced sheet molding compound composites under tensile load | |
| Mehdikhani et al. | Multi-scale digital image correlation for detection and quantification of matrix cracks in carbon fiber composite laminates in the absence and presence of voids controlled by the cure cycle | |
| Caminero et al. | Damage assessment of composite structures using digital image correlation | |
| Feraboli et al. | Notched behavior of prepreg-based discontinuous carbon fiber/epoxy systems | |
| Colombo et al. | Influence of delamination on fatigue properties of a fibreglass composite | |
| Sitohang et al. | Effect of in-plane fiber waviness defects on the compressive properties of quasi-isotropic thermoplastic composites | |
| Shahkhosravi et al. | Fatigue life reduction of GFRP composites due to delamination associated with the introduction of functional discontinuities | |
| Mohammadi et al. | The effect of mode II fatigue crack growth rate on the fractographic features of CFRP composite laminates: An acoustic emission and scanning electron microscopy analysis | |
| Lai et al. | Experimental assessment of drilling-induced damage in impacted composite laminates for resin-injection repair: Influence of open/blind hole-hole interaction and orientation | |
| Czabaj et al. | Observation of intralaminar cracking in the edge crack torsion specimen | |
| Liu et al. | A study on the intralaminar damage and interlaminar delamination of carbon fiber composite laminates under three-point bending using acoustic emission | |
| Lyu et al. | Damage and failure analysis of hybrid laminates with different ply-stacking sequences under low-velocity impact and post-impact compression | |
| De Finis et al. | Fatigue damage analysis of composite materials using thermography-based techniques | |
| Ramezani et al. | A study of the fracture mechanisms of hybrid carbon fiber reinforced polymer laminates reinforced by thin‐ply | |
| Cândido et al. | Hygrothermal effects on quasi-isotropic carbon epoxy laminates with machined and molded edges | |
| Sabaghi et al. | Critical strain energy release rate of woven carbon/epoxy composites subjected to thermal cyclic loading | |
| Kim et al. | Mode II fracture toughness of two‐part acrylic‐based adhesive in an adhesively bonded joint: end‐notched flexure tests under static loading | |
| Yoon Park et al. | Review of material test standardization status for the material qualification of laminated thermosetting composite structures | |
| Casapu et al. | Experimental Characterization of Internal Structure and Physical Properties of Unidirectional Ply‐Level Hybrid Carbon Composite Material | |
| Khechai et al. | Strength improvement and stress analysis of E-glass laminated plates with circular notches using digital image correlation | |
| Bossi et al. | Composite structure development decisions using X-ray CT measurements | |
| Sause et al. | Failure of fiber-reinforced composites | |
| Haluza et al. | Comparison of woven and stitched out-of-autoclave E-glass/epoxy composites subjected to quasi-static and cyclic tensile loads | |
| Keršienė et al. | Energo-mechanical evaluation of damage growth and fracture initiation in aviation composite structures | |
| Chen et al. | A comparative study of two astm shear test standards for chopped carbon fiber smc |