Pongphot et al., 2016 - Google Patents

The effect of alumina (Al2O3) on the characteristics of sintered mullite-cordierite Ceramics Synthesized with Kaolin from Naratiwas of Thailand

Pongphot et al., 2016

Document ID
17332676922278550777
Author
Pongphot S
Thiansem S
Publication year
Publication venue
Key Engineering Materials

External Links

Snippet

Mullite-cordierite ceramics was prepared by the three composition of talc, kaolin (kaolin from Naratiwas in Thailand)(NT) and alumina. The different amounts of alumina (5, 10, 15 and 20 wt%) were added to produce various mullite-cordierite alumina mixtures which are denoted …
Continue reading at www.scientific.net (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3205—Alkaline earth oxides or oxide forming salts thereof, e.g. beryllium oxide
    • C04B2235/3206—Magnesium oxides or oxide-forming salts thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/32—Metal oxides, mixed metal oxides, or oxide-forming salts thereof, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3217—Aluminum oxide or oxide forming salts thereof, e.g. bauxite, alpha-alumina
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C04B35/16—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on silicates other than clay
    • C04B35/18—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics based on silicates other than clay rich in aluminium oxide
    • C04B35/195—Alkaline earth aluminosilicates, e.g. cordierite or anorthite
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3427—Silicates other than clay, e.g. water glass
    • C04B2235/3436—Alkaline earth metal silicates, e.g. barium silicate
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/30—Constituents and secondary phases not being of a fibrous nature
    • C04B2235/34—Non-metal oxides, non-metal mixed oxides, or salts thereof that form the non-metal oxides upon heating, e.g. carbonates, nitrates, (oxy)hydroxides, chlorides
    • C04B2235/3427—Silicates other than clay, e.g. water glass
    • C04B2235/3463—Alumino-silicates other than clay, e.g. mullite
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/52—Constituents or additives characterised by their shapes
    • C04B2235/528—Spheres
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
    • C04B2235/5427—Particle size related information expressed by the size of the particles or aggregates thereof millimeter or submillimeter sized, i.e. larger than 0,1 mm
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product
    • C04B2235/50—Constituents or additives of the starting mixture chosen for their shape or used because of their shape or their physical appearance
    • C04B2235/54—Particle size related information
    • C04B2235/5418—Particle size related information expressed by the size of the particles or aggregates thereof
    • C04B2235/5436—Particle size related information expressed by the size of the particles or aggregates thereof micrometer sized, i.e. from 1 to 100 micron
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/656—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes characterised by specific heating conditions during heat treatment
    • C04B2235/6565—Cooling rate
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/70—Aspects relating to sintered or melt-casted ceramic products
    • C04B2235/96—Properties of ceramic products, e.g. mechanical properties such as strength, toughness, wear resistance
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/64—Burning or sintering processes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/626—Preparing or treating the powders individually or as batches ; preparing or treating macroscopic reinforcing agents for ceramic products, e.g. fibres; mechanical aspects section B
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/515—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics
    • C04B35/58—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on non-oxide ceramics based on borides, nitrides, i.e. nitrides, oxynitrides, carbonitrides or oxycarbonitrides or silicides
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2111/00—Mortars, concrete or artificial stone or mixtures to prepare them, characterised by specific function, property or use
    • C04B2111/00474—Uses not provided for elsewhere in C04B2111/00
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B38/00—Porous mortars, concrete, artificial stone or ceramic ware; Preparation thereof
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B33/00—Clay-wares
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements

Similar Documents

Publication Publication Date Title
Kamseu et al. Characterisation of porcelain compositions using two china clays from Cameroon
Ma et al. Preparation and properties of porous mullite ceramics with high-closed porosity and high strength from fly ash via reaction synthesis process
Johari et al. Effect of the change of firing temperature on microstructure and physical properties of clay bricks from Beruas (Malaysia)
Kuscer et al. The microstructure, coefficient of thermal expansion and flexural strength of cordierite ceramics prepared from alumina with different particle sizes
Martín-Márquez et al. Effect of microstructure on mechanical properties of porcelain stoneware
ES2638051T3 (en) Processing of fly ash and manufacture of articles that incorporate fly ash compositions
Jiang et al. Novel ceramics prepared from inferior clay rich in CaO and Fe2O3: Properties, crystalline phases evolution and densification process
Tai et al. A new approach to anorthite porcelain bodies using nonplastic raw materials
Ochen et al. Physical and mechanical properties of porcelain tiles made from raw materials in Uganda
Mukhopadhyay et al. Effect of fly ash on the physico-chemical and mechanical properties of a porcelain composition
Boyraz et al. Investigation of wear properties of mullite and aluminium titanate added porcelain ceramics
Deng et al. The effect of different solid phases on the pyroplastic deformation of porcelain
Zawrah et al. Recycling and utilization of some waste clays for production of sintered ceramic bodies
Sittiakkaranon Thermal shock resistance of mullite-cordierite ceramics from kaolin, talc and alumina raw materials
Vodova et al. The effect of CaO addition on mechanical properties of ceramic tiles
Kumar et al. Thermo-mechanical properties of mullite—zirconia composites derived from reaction sintering of zircon and sillimanite beach sand: Effect of CaO
Darweesh et al. Densification and thermomechanical properties of conventional ceramic composites containing two different industrial byproducts
Sadik et al. Effect of andalusite rich schist grain size and the addition of metallic aluminum powder on the properties of silica–alumina refractory
Pongphot et al. The effect of alumina (Al2O3) on the characteristics of sintered mullite-cordierite Ceramics Synthesized with Kaolin from Naratiwas of Thailand
Wahsh et al. The effect of microsilica and aluminum metal powder on the densification parameters, mechanical properties and microstructure of alumina–Mullite ceramic composites
Ariyajinno et al. Characterization and properties of cordierite–mullite refractories from raw materials and Narathiwat clay (in Thailand)
Tabit et al. Low‐temperature synthesis of mullite‐based ceramics from Moroccan naturally occurring andalusite and marble waste
Omerašević et al. Mechanical properties and thermal shock resistance of anorthite ceramics obtained by slip casting
Akkuş et al. Fabrication and characterization of aluminium titanate and mullite added Porcelain ceramics
Naga et al. Mullite/β-spodumene composites: Preparation and characterization