Lu et al., 2013 - Google Patents

Reduction of load-bearing capacity of all-ceramic crowns due to cement aging

Lu et al., 2013

Document ID
1532629078563881092
Author
Lu C
Wang R
Mao S
Arola D
Zhang D
Publication year
Publication venue
journal of the mechanical behavior of biomedical materials

External Links

Snippet

The purpose of this study was to investigate how water aging of the resin cement influences the stress distribution in all-ceramic crowns and if there is an increase in the propensity for crown failure. The failure of all-ceramic crowns attributed to cement degradation was …
Continue reading at www.sciencedirect.com (other versions)

Classifications

    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
    • A61C13/00—Dental prostheses; Making same
    • A61C13/0003—Making bridge-work, inlays, implants or the like
    • A61C13/0022—Blanks or green, unfinished dental restoration parts
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61K—PREPARATIONS FOR MEDICAL, DENTAL, OR TOILET PURPOSES
    • A61K6/00—Preparations for dentistry
    • A61K6/02—Use of preparations for artificial teeth, for filling or for capping teeth
    • A61K6/08—Use of natural or synthetic resins
    • A61K6/083—Compounds obtained by reactions only involving carbon-to-carbon unsaturated bonds
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61K—PREPARATIONS FOR MEDICAL, DENTAL, OR TOILET PURPOSES
    • A61K6/00—Preparations for dentistry
    • A61K6/02—Use of preparations for artificial teeth, for filling or for capping teeth
    • A61K6/0205—Ceramics
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61K—PREPARATIONS FOR MEDICAL, DENTAL, OR TOILET PURPOSES
    • A61K6/00—Preparations for dentistry
    • A61K6/02—Use of preparations for artificial teeth, for filling or for capping teeth
    • A61K6/027—Use of non-metallic elements or compounds thereof, e.g. carbon
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61K—PREPARATIONS FOR MEDICAL, DENTAL, OR TOILET PURPOSES
    • A61K6/00—Preparations for dentistry
    • A61K6/007—Preparations for dentistry characterized by the presence of inorganic additives
    • A61K6/0073—Fillers
    • A61K6/0091—Glass
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
    • A61C13/00—Dental prostheses; Making same
    • A61C13/0003—Making bridge-work, inlays, implants or the like
    • A61C13/0004—Computer-assisted sizing or machining of dental prostheses
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61C—DENTISTRY; APPARATUS OR METHODS FOR ORAL OR DENTAL HYGIENE
    • A61C13/00—Dental prostheses; Making same
    • A61C13/08—Artificial teeth; Making same
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61K—PREPARATIONS FOR MEDICAL, DENTAL, OR TOILET PURPOSES
    • A61K6/00—Preparations for dentistry
    • A61K6/0002—Compositions characterised by physical properties
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61K—PREPARATIONS FOR MEDICAL, DENTAL, OR TOILET PURPOSES
    • A61K6/00—Preparations for dentistry
    • A61K6/0023—Chemical means for temporarily or permanently fixing teeth, palates or the like
    • A—HUMAN NECESSITIES
    • A61—MEDICAL OR VETERINARY SCIENCE; HYGIENE
    • A61K—PREPARATIONS FOR MEDICAL, DENTAL, OR TOILET PURPOSES
    • A61K38/00—Medicinal preparations containing peptides
    • A61K38/16—Peptides having more than 20 amino acids; Gastrins; Somatostatins; Melanotropins; Derivatives thereof
    • A61K38/17—Peptides having more than 20 amino acids; Gastrins; Somatostatins; Melanotropins; Derivatives thereof from animals; from humans

Similar Documents

Publication Publication Date Title
Lu et al. Reduction of load-bearing capacity of all-ceramic crowns due to cement aging
Zahran et al. Fracture strength and fatigue resistance of all‐ceramic molar crowns manufactured with CAD/CAM technology
Campos et al. Adhesive cementation promotes higher fatigue resistance to zirconia crowns
Preis et al. In vitro failure and fracture resistance of veneered and full-contour zirconia restorations
Nordahl et al. Fracture strength of ceramic monolithic crown systems of different thickness
Pereira et al. Lithium disilicate glass-ceramic vs translucent zirconia polycrystals bonded to distinct substrates: Fatigue failure load, number of cycles for failure, survival rates, and stress distribution
Xible et al. Effect of silica coating and silanization on flexural and composite-resin bond strengths of zirconia posts: An in vitro study
Ban Reliability and properties of core materials for all-ceramic dental restorations
Blatz et al. In vitro evaluation of shear bond strengths of resin to densely-sintered high-purity zirconium-oxide ceramic after long-term storage and thermal cycling
Subaşı et al. Influence of surface treatments and resin cement selection on bonding to zirconia
Yang et al. A comparison of the fracture resistance of three machinable ceramics after thermal and mechanical fatigue
Rohr et al. Loading capacity of zirconia implant supported hybrid ceramic crowns
Chai et al. On the interfacial fracture resistance of resin-bonded zirconia and glass-infiltrated graded zirconia
Ferrari et al. Fracture resistance of three porcelain-layered CAD/CAM zirconia frame designs
Alhasanyah et al. Effect of core thickness differences on post‐fatigue indentation fracture resistance of veneered zirconia crowns
Valandro et al. A brief review on fatigue test of ceramic and some related matters in Dentistry
Basso et al. Reliability and failure behavior of CAD-on fixed partial dentures
Nicolaisen et al. Comparison of fatigue resistance and failure modes between metal-ceramic and all-ceramic crowns by cyclic loading in water
Hao et al. Influence of low-temperature degradation on the wear characteristics of zirconia against polymer-infiltrated ceramic-network material
Aldegheishem et al. Wear behavior of zirconia substrates against different antagonist materials.
Burkhardt et al. RETENTION AND MARGINAL INTEGRITY OF CAD/CAM FABRICATED CROWNS ADHESIVELY CEMENTED TO TITANIUM BASE ABUTMENTS--INFLUENCE OF BONDING SYSTEM AND RESTORATIVE MATERIAL.
Rayyan et al. Static and Fatigue Loading of Veneered Implant‐Supported Fixed Dental Prostheses
Dikicier et al. Influence of core thickness and artificial aging on the biaxial flexural strength of different all-ceramic materials: An in-vitro study
Dähne et al. Retention of different temporary cements tested on zirconia crowns and titanium abutments in vitro
Ereifej et al. Edge strength of indirect restorative materials