Luc et al., 2024 - Google Patents

Thermal and thermochemical treatments against fretting failure applied to power transmissions

Luc et al., 2024

View PDF
Document ID
13299904308618597372
Author
Luc A
Yanming C
PASQUIER M
Publication year
Publication venue
Procedia Structural Integrity

External Links

Snippet

Some power transmission components are subject to the fretting corrosion failure mode, which results in rapid wear of mating surfaces or premature fatigue crack initiation. Fretting corrosion is generated by micro-movements of surfaces in contact. In mechanical …
Continue reading at www.sciencedirect.com (PDF) (other versions)

Classifications

    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING ENGINES OR PUMPS
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C33/00—Parts of bearings; Special methods for making bearings or parts thereof
    • F16C33/02—Parts of sliding-contact bearings
    • F16C33/04—Brasses; Bushes; linings
    • F16C33/06—Sliding surface mainly made of metal
    • F16C33/12—Structural composition; Use of special materials or surface treatments, e.g. for rust-proofing
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING ENGINES OR PUMPS
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C33/00—Parts of bearings; Special methods for making bearings or parts thereof
    • F16C33/30—Parts of ball or roller bearings
    • F16C33/58—Raceways; Race rings
    • F16C33/64—Special methods of manufacture
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING ENGINES OR PUMPS
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16C—SHAFTS; FLEXIBLE SHAFTS; ELEMENTS OR CRANKSHAFT MECHANISMS; ROTARY BODIES OTHER THAN GEARING ELEMENTS; BEARINGS
    • F16C9/00—Bearings for crankshafts or connecting-rods; Attachment of connecting-rods
    • F16C9/04—Connecting-rod bearings; Attachments thereof

Similar Documents

Publication Publication Date Title
Kapoor et al. Surface roughness and plastic flow in rail wheel contact
Concli Austempered Ductile Iron (ADI) for gears: Contact and bending fatigue behavior
Li et al. Experimental investigation on the effect of shot peening on contact fatigue strength for carburized and quenched gears
Gorla et al. Contact and bending fatigue behaviour of austempered ductile iron gears
Oila et al. Martensite decay in micropitted gears
Gorla et al. Bending and contact fatigue strength of innovative steels for large gears
Glaeser et al. Contact fatigue
Mahmoudi et al. Effects of black oxide and a WC/aC: H coating on the micropitting of SAE 52100 bearing steel
Alfredsson et al. Standing contact fatigue
Ohue et al. Sliding–rolling contact fatigue and wear of maraging steel roller with ion-nitriding and fine particle shot-peening
Ghalme et al. Effect of lubricant viscosity and surface roughness on coefficient of friction in rolling contact
Terrin et al. A comparison of rolling contact fatigue behaviour of 17NiCrMo6‐4 case‐hardened disc specimens and gears
Chen et al. Experimental Study on High-Speed Aviation Gear Scuffing Based on Tooth Profile and Surface Treatment Improvements
Kong et al. Engineering research of DLC coating in piston pins and bucket tappets
Dommarco et al. The influence of material build up around artificial defects on rolling contact fatigue life and failure mechanism
Lösche New aspects in the realistic prediction of the fatigue life of rolling bearings
Luc et al. Thermal and thermochemical treatments against fretting failure applied to power transmissions
Jbily et al. The influence of shot peening on gear teeth micropitting and contact fatigue failure
Dalcin et al. Correlation between roughness, film thickness, and friction coefficient with pitting wear resistance of spur gears
US9273386B2 (en) Pair of guiding elements of which one is made of specific steel leading to improved anti-seizing performances
Jain et al. Effect of tribological parameters on sliding wear and friction coefficient which relates to preload loss in tapered roller bearing
Wagner et al. Failure mode mapping for rolling/sliding contacts under low lambda conditions
Gao Influence of deep-nitriding and shot peening on rolling contact fatigue performance of 32Cr3MoVA steel
Sagalovych et al. Tribological characteristics of samples made from titanium alloy VT5 nitrided in plasma glow discharge
Gabelli et al. Improved fatigue life analysis of pre-dented raceways used in bearing material testing