Koleňák et al., 2011 - Google Patents

Shear strength and wettability of active Sn3. 5Ag4Ti (Ce, Ga) solder on Al2O3 ceramics

Koleňák et al., 2011

View PDF
Document ID
13024113281297818017
Author
Koleňák R
Šebo P
Provazník M
Koleňáková M
Ulrich K
Publication year
Publication venue
Materials & Design

External Links

Snippet

The work deals with the study of wettability of Sn3. 5Ag4Ti (Ce, Ga) solder on ceramic material of Al 2 O 3. The Sn3. 5Ag4Ti (Ce, Ga) solder is used for ultrasonic soldering of metallic and ceramic materials. The microstructure of Sn3. 5Ag4Ti (Ce, Ga) solder consists …
Continue reading at sciencedirect.magic.scholar.google.com (PDF) (other versions)

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/22—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by the composition or nature of the material
    • B23K35/24—Selection of soldering or welding materials proper
    • B23K35/30—Selection of soldering or welding materials proper with the principal constituent melting at less than 1550 degrees C
    • B23K35/3013—Au as the principal constituent
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K35/00—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting
    • B23K35/02—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape
    • B23K35/0222—Rods, electrodes, materials, or media, for use in soldering, welding, or cutting characterised by mechanical features, e.g. shape for use in soldering, brazing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B23—MACHINE TOOLS; METAL-WORKING NOT OTHERWISE PROVIDED FOR
    • B23K—SOLDERING OR UNSOLDERING; WELDING; CLADDING OR PLATING BY SOLDERING OR WELDING; CUTTING BY APPLYING HEAT LOCALLY, e.g. FLAME CUTTING; WORKING BY LASER BEAM
    • B23K1/00—Soldering, e.g. brazing, or unsoldering
    • B23K1/0008—Soldering, e.g. brazing, or unsoldering specially adapted for particular articles or work
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C14/00—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material
    • C23C14/22—Coating by vacuum evaporation, by sputtering or by ion implantation of the coating forming material characterised by the process of coating
    • C23C14/34—Sputtering

Similar Documents

Publication Publication Date Title
Koleňák et al. Shear strength and wettability of active Sn3. 5Ag4Ti (Ce, Ga) solder on Al2O3 ceramics
Kozlova et al. Brazing copper to alumina using reactive CuAgTi alloys
Shiue et al. The interfacial reactions of infrared brazing Cu and Ti with two silver-based braze alloys
Shiue et al. Infrared brazing of TiAl intermetallic using pure silver
US20080063889A1 (en) Reactive Multilayer Joining WIth Improved Metallization Techniques
CN106271214B (en) A kind of preparation method being brazed stainless steel Ag-Cu/W nano-multilayer film solder
Xin et al. Microstructural evolution during the brazing of Al2O3 ceramic to kovar alloy by sputtering Ti/Mo films on the ceramic surface
CN103100800B (en) Paste solder for hard soldering of SiCp/Al composite material and preparation method and use method thereof
Fu et al. Interactions, joining and microstructure of Sn-Ti/ZrO2 system
Appendino et al. Joining of C/C composites to copper
Mu et al. Low-temperature wetting of sapphire using Sn–Ti active solder alloys
Koleňák et al. Wettability and shear strength of active Sn2Ti solder on Al2O3 ceramics
Sun et al. Brazing of TiAl and Ti2AlNb alloys using high-entropy braze fillers
Wang et al. Microstructural characterization and mechanical property of active soldering anodized 6061 Al alloy using Sn–3.5 Ag–xTi active solders
Zhang et al. Wettability in reactive Sn-base alloy/Ni-base metallic glass systems
Song et al. Interfacial microstructure and joining properties of TiAl/Si3N4 brazed joints
Dai et al. Microstructure and properties of 6061 aluminum alloy brazing joint with Al–Si–Zn filler metal
Shang et al. Brazing W and Fe–Ni–Co alloy using Ag–28Cu and Ag–27Cu–3.5 Ti fillers
Xiong et al. Joining of Si3N4 to Si3N4 using a AuPd (Co, Ni)–V filler alloy and the interfacial reactions
Chang et al. Active soldering of ZnS–SiO2 sputtering targets to copper backing plates using an Sn3. 5Ag4Ti (Ce, Ga) filler metal
Koleňák et al. Study of direct bonding ceramics with metal using Sn2La solder
Tsao Microstructural characterization and mechanical properties of microplasma oxidized TiO 2/Ti joints soldered using Sn3. 5Ag4Ti (Ce) active filler
Kolenak et al. Direct bonding of silicon with solders type Sn-Ag-Ti
CN102699573B (en) High temperature brazing filler metal for brazing non-oxide ceramic and composite material as well as preparation method of high temperature brazing filler metal
Liu et al. Effect of Ti content on microstructure and strength of Si3N4/Si3N4 joints brazed with Cu–Pd–Ti filler metals