An investigation on fatigue life evaluation and crack initiation of Al-GFRP bonded lap joints under four-point bendingZamani et al., 2019
- Document ID
- 1275123034587358980
- Author
- Zamani P
- Jaamialahmadi A
- Da Silva L
- Farhangdoost K
- Publication year
- Publication venue
- Composite Structures
External Links
Snippet
In this paper, fatigue life and crack initiation of aluminum-GFRP bonded lap joints are investigated under four-point bending loading. For this purpose, a new fixture was designed and constructed. Fatigue loads vs. number of cycles to failure (LN) were obtained so that the …
- 230000000977 initiatory 0 title abstract description 66
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/026—Specifications of the specimen
- G01N2203/0262—Shape of the specimen
- G01N2203/0278—Thin specimens
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0014—Type of force applied
- G01N2203/0016—Tensile or compressive
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/025—Geometry of the test
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0058—Kind of property studied
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N3/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N3/08—Investigating strength properties of solid materials by application of mechanical stress by applying steady tensile or compressive forces
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Zamani et al. | An investigation on fatigue life evaluation and crack initiation of Al-GFRP bonded lap joints under four-point bending | |
| Kim et al. | Failure mode and strength of uni-directional composite single lap bonded joints with different bonding methods | |
| Liu et al. | Interlaminar failure behavior of GLARE laminates under short-beam three-point-bending load | |
| Liu et al. | An investigation of hygrothermal effects on adhesive materials and double lap shear joints of CFRP composite laminates | |
| Anyfantis et al. | Loading and fracture response of CFRP-to-steel adhesively bonded joints with thick adherents–Part I: experiments | |
| Zhao et al. | Single lap joints with rounded adherend corners: experimental results and strength prediction | |
| Banea et al. | The effect of temperature on the mechanical properties of adhesives for the automotive industry | |
| Shahverdi et al. | Experimental investigation of R-ratio effects on fatigue crack growth of adhesively-bonded pultruded GFRP DCB joints under CA loading | |
| Ji et al. | Effects of bondline thickness on Mode-II interfacial laws of bonded laminated composite plate | |
| Imielińska et al. | Effects of manufacturing and face/core bonding on impact damage in glass/polyester–PVC foam core sandwich panels | |
| Daud et al. | Static and fatigue behaviour of the bond interface between concrete and externally bonded CFRP in single shear | |
| Azari et al. | Fatigue threshold behavior of adhesive joints | |
| Ferraris et al. | Comparison of shear strength tests on AV119 epoxy-joined carbon/carbon composites | |
| Hinz et al. | Damage characterisation of fibre metal laminates under interlaminar shear load | |
| Prabhu et al. | Uniaxial tensile failure of multi-core asymmetric sandwich composite structures with bonded repair | |
| Islam et al. | Effects of hygrothermal and ambient humidity conditioning on shear strength of metal–GFRP single lap joints co-cured in and out of water | |
| Li et al. | Experimental studies on strengthening and failure mechanism for the metal/silicone rubber/metal bonding system | |
| Abbasi et al. | Backface strain as an index to detect damage initiation in composite single-lap bonded joints: Effects of adhesive type and joint dimensions | |
| Amaro et al. | Taper’s angle influence on the structural integrity of single-lap bonded joints | |
| Katnam et al. | The static failure of adhesively bonded metal laminate structures: a cohesive zone approach | |
| Takeda | Mode I fracture toughness determination and environmental durability evaluation of adhesive bonds by wedge test | |
| Casareto et al. | Bond behavior of FRP laminates adhered to masonry | |
| Bardis et al. | Surface preparation effects on mode I testing of adhesively bonded composite joints | |
| Sepe et al. | Fatigue behavior of hybrid and bonded single lap joints made of composite material | |
| Bang et al. | Performance improvement by glass fiber of adhesively bonded metal joints at the cryogenic temperature |