Du et al., 2000 - Google Patents
Inhibition of pure iron in sulphuric acid by N, N-dipropynoxymethylamine acetate and its synergism with chlorideDu et al., 2000
- Document ID
- 1267180737747009427
- Author
- Du T
- Chen J
- Cao D
- Publication year
- Publication venue
- British Corrosion Journal
External Links
Snippet
The inhibition mechanism of N, N-dipropynoxymethylamine acetate on pure iron in H2 SO4 solution and its synergism with chloride was studied by potentiodynamic polarisation and electrochemical impedance techniques. Results showed that the inhibition mechanism was …
- 230000002401 inhibitory effect 0 title abstract description 78
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
- C23F11/00—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent
- C23F11/08—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids
- C23F11/10—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in other liquids using organic inhibitors
- C23F11/14—Nitrogen-containing compounds
- C23F11/149—Heterocyclic compounds containing nitrogen as hetero atom
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
- C23F11/00—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent
- C23F11/02—Inhibiting corrosion of metallic material by applying inhibitors to the surface in danger of corrosion or adding them to the corrosive agent in air or gases by adding vapour phase inhibitors
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
- C23F13/00—Inhibiting corrosion of metals by anodic or cathodic protection
- C23F13/02—Inhibiting corrosion of metals by anodic or cathodic protection cathodic; Selection of conditions, parameters or procedures for cathodic protection, e.g. of electrical conditions
- C23F13/06—Constructional parts, or assemblies of cathodic-protection apparatus
- C23F13/08—Electrodes specially adapted for inhibiting corrosion by cathodic protection; Manufacture thereof; Conducting electric current thereto
- C23F13/12—Electrodes characterised by the material
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23F—NON-MECHANICAL REMOVAL OF METALLIC MATERIAL FROM SURFACE; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL; MULTI-STEP PROCESSES FOR SURFACE TREATMENT OF METALLIC MATERIAL INVOLVING AT LEAST ONE PROCESS PROVIDED FOR IN CLASS C23 AND AT LEAST ONE PROCESS COVERED BY SUBCLASS C21D OR C22F OR CLASS C25
- C23F13/00—Inhibiting corrosion of metals by anodic or cathodic protection
- C23F13/02—Inhibiting corrosion of metals by anodic or cathodic protection cathodic; Selection of conditions, parameters or procedures for cathodic protection, e.g. of electrical conditions
- C23F13/04—Controlling or regulating desired parameters
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Zhang et al. | Corrosion inhibition of aluminum in hydrochloric acid solution by alkylimidazolium ionic liquids | |
| Zhang et al. | Corrosion inhibition of mild steel by alkylimidazolium ionic liquids in hydrochloric acid | |
| Abdel-Aal et al. | Inhibiting effects of some quinolines and organic phosphonium compounds on corrosion of mild steel in 3M HCl solution and their adsorption characteristics | |
| Bentiss et al. | Inhibitor effects of triazole derivatives on corrosion of mild steel in acidic media | |
| Bentiss et al. | 2, 5-bis (n-pyridyl)-1, 3, 4-oxadiazoles as corrosion inhibitors for mild steel in acidic media | |
| Li et al. | Adsorption and inhibition effect of vanillin on cold rolled steel in 3.0 M H3PO4 | |
| Li et al. | Synergistic inhibition effect of rare earth cerium (IV) ion and sodium oleate on the corrosion of cold rolled steel in phosphoric acid solution | |
| Muralidharan et al. | Polyamino‐benzoquinone polymers: a new class of corrosion inhibitors for mild steel | |
| Hackerman et al. | Effects of anions on corrosion inhibition by organic compounds | |
| Hermas et al. | Effect of PgTPhPBr on the electrochemical and corrosion behaviour of 304 stainless steel in H 2 SO 4 solution | |
| Quraishi et al. | Dithiobiurets: a novel class of acid corrosion inhibitors for mild steel | |
| Bentiss et al. | Effect of iodide ions on corrosion inhibition of mild steel by 3, 5-bis (4-methylthiophenyl)-4H-1, 2, 4-triazole in sulfuric acid solution | |
| Mistry et al. | Experimental and quantum chemical studies on corrosion inhibition performance of quinoline derivatives for MS in 1N HCl | |
| Wang et al. | Corrosion inhibition of zinc in phosphoric acid solution by 2-mercaptobenzimidazole | |
| Quraishi et al. | Inhibition of mild steel corrosion in the presence of fatty acid triazoles | |
| Shukla et al. | Triazines: Efficient corrosion inhibitors for mild steel in hydrochloric acid solution | |
| Schweinsberg et al. | An electrochemical and SERS study of the action of polyvinylpyrrolidone and polyethylenimine as inhibitors for copper in aerated H2SO4 | |
| Gašparac et al. | Corrosion protection on copper by imidazole and its derivatives | |
| Du et al. | N, N-Dipropynoxy methyl amine trimethyl phosphonate as corrosion inhibitor for iron in sulfuric acid | |
| Ameer et al. | Adsorption studies of the effect of thiosemicarbazides on the corrosion of steel in phosphoric acid | |
| Wang | Inhibiting effect of 2-mercaptopyrimidine on the corrosion of a low carbon steel in phosphoric acid | |
| Kanojia et al. | An interesting and efficient organic corrosion inhibitor for mild steel in acidic medium | |
| Du et al. | Inhibition of pure iron in sulphuric acid by N, N-dipropynoxymethylamine acetate and its synergism with chloride | |
| Karimi et al. | Electrochemical investigations on the inhibition behavior and adsorption isotherm of synthesized di-(Resacetophenone)-1, 2-cyclohexandiimine Schiff base on the corrosion of steel in 1 M HCl | |
| Fouda et al. | Role of some benzohydrazide derivatives as corrosion inhibitors for carbon steel in HCl solution |