Li et al., 2015 - Google Patents

Influence of acid slurries on surface quality of LBO crystal in fixed abrasive CMP

Li et al., 2015

View PDF
Document ID
11984258679976709572
Author
Li J
Wang W
Wang H
Song L
Hu Z
Zhu Y
Zuo D
Publication year
Publication venue
The International Journal of Advanced Manufacturing Technology

External Links

Snippet

The chemical action, which is generally determined by acid or alkaline regulator in the slurry, plays an important role in fixed abrasive chemical mechanical polishing (CMP). Experiments were conducted to explore the influence of acid slurries on surface quality and …
Continue reading at www.spm.com.cn (PDF) (other versions)

Classifications

    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/04—Manufacture or treatment of semiconductor devices or of parts thereof the devices having at least one potential-jump barrier or surface barrier, e.g. PN junction, depletion layer, carrier concentration layer
    • H01L21/18—Manufacture or treatment of semiconductor devices or of parts thereof the devices having at least one potential-jump barrier or surface barrier, e.g. PN junction, depletion layer, carrier concentration layer the devices having semiconductor bodies comprising elements of Group IV of the Periodic System or AIIIBV compounds with or without impurities, e.g. doping materials
    • H01L21/30—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26
    • H01L21/302—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26 to change their surface-physical characteristics or shape, e.g. etching, polishing, cutting
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/04—Manufacture or treatment of semiconductor devices or of parts thereof the devices having at least one potential-jump barrier or surface barrier, e.g. PN junction, depletion layer, carrier concentration layer
    • H01L21/18—Manufacture or treatment of semiconductor devices or of parts thereof the devices having at least one potential-jump barrier or surface barrier, e.g. PN junction, depletion layer, carrier concentration layer the devices having semiconductor bodies comprising elements of Group IV of the Periodic System or AIIIBV compounds with or without impurities, e.g. doping materials
    • H01L21/30—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26
    • H01L21/31—Treatment of semiconductor bodies using processes or apparatus not provided for in groups H01L21/20 - H01L21/26 to form insulating layers thereon, e.g. for masking or by using photolithographic techniques; After treatment of these layers
    • H01L21/3205—Deposition of non-insulating-, e.g. conductive- or resistive-, layers on insulating layers; After-treatment of these layers
    • H—ELECTRICITY
    • H01—BASIC ELECTRIC ELEMENTS
    • H01L—SEMICONDUCTOR DEVICES; ELECTRIC SOLID STATE DEVICES NOT OTHERWISE PROVIDED FOR
    • H01L21/00—Processes or apparatus adapted for the manufacture or treatment of semiconductor or solid state devices or of parts thereof
    • H01L21/02—Manufacture or treatment of semiconductor devices or of parts thereof
    • H01L21/02002—Preparing wafers
    • H01L21/02005—Preparing bulk and homogeneous wafers
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; MISCELLANEOUS COMPOSITIONS; MISCELLANEOUS APPLICATIONS OF MATERIALS
    • C09G—POLISHING COMPOSITIONS OTHER THAN FRENCH POLISH; SKI WAXES
    • C09G1/00—Polishing compositions
    • C09G1/02—Polishing compositions containing abrasives or grinding agents
    • C—CHEMISTRY; METALLURGY
    • C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; MISCELLANEOUS COMPOSITIONS; MISCELLANEOUS APPLICATIONS OF MATERIALS
    • C09K—MATERIALS FOR MISCELLANEOUS APPLICATIONS, NOT PROVIDED FOR ELSEWHERE
    • C09K3/00—Materials not provided for elsewhere
    • C09K3/14—Anti-slip materials; Abrasives
    • C09K3/1454—Abrasive powders, suspensions and pastes for polishing
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24B—MACHINES, DEVICES, OR PROCESSES FOR GRINDING OR POLISHING; DRESSING OR CONDITIONING OF ABRADING SURFACES; FEEDING OF GRINDING, POLISHING, OR LAPPING AGENTS
    • B24B37/00—Lapping machines or devices; Accessories
    • B24B37/11—Lapping tools
    • B24B37/20—Lapping pads for working plane surfaces
    • B24B37/24—Lapping pads for working plane surfaces characterised by the composition or properties of the pad materials
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B24—GRINDING; POLISHING
    • B24B—MACHINES, DEVICES, OR PROCESSES FOR GRINDING OR POLISHING; DRESSING OR CONDITIONING OF ABRADING SURFACES; FEEDING OF GRINDING, POLISHING, OR LAPPING AGENTS
    • B24B37/00—Lapping machines or devices; Accessories
    • B24B37/04—Lapping machines or devices; Accessories designed for working plane surfaces

Similar Documents

Publication Publication Date Title
Xu et al. Study on high efficient sapphire wafer processing by coupling SG-mechanical polishing and GLA-CMP
Kim et al. Comparison between sapphire lapping processes using 2-body and 3-body modes as a function of diamond abrasive size
Li et al. Influence of acid slurries on surface quality of LBO crystal in fixed abrasive CMP
JP7298915B2 (en) Method for manufacturing single-crystal silicon carbide substrate
Zhang et al. Highly efficient and damage-free polishing of GaN (0 0 0 1) by electrochemical etching-enhanced CMP process
CN109545680B (en) Rapid preparation method of high-flatness and low-damage monocrystalline silicon carbide substrate
US20060118760A1 (en) Slurry composition and methods for chemical mechanical polishing
Hu et al. Planarization machining of sapphire wafers with boron carbide and colloidal silica as abrasives
CN1230486C (en) Cerium oxide slurry, and method of mfg. substrate
Wang et al. The polishing effect of SiC substrates in femtosecond laser irradiation assisted chemical mechanical polishing (CMP)
CN1337983A (en) Working liquids and methods for modifying structured wafers for semiconductor fabrication
CN101791779A (en) Semiconductor silicon wafer manufacture process
CN110744364B (en) Double-side polishing method for large-size ultrathin lithium niobate substrate
CN103252708A (en) Sapphire substrate ultraprecision machining method based on fixed abrasive pad
US20100260977A1 (en) Chemical mechanical fabrication (cmf) for forming tilted surface features
CN109676437B (en) Silicon carbide wafer and method for producing same
CN109623581A (en) A kind of surface polishing method of hard material
Yang et al. Slurryless electrochemical mechanical polishing of 4-inch 4H–SiC (0001) and (000–1) surfaces
Kirino et al. Ultra-flat and ultra-smooth Cu surfaces produced by abrasive-free chemical–mechanical planarization/polishing using vacuum ultraviolet light
Wang et al. Effect of hydrogen peroxide concentration on surface micro-roughness of silicon wafer after final polishing
Yan et al. Controllable electrochemical-magnetorheological finishing of single-crystal gallium nitride wafers
CN109913133B (en) Efficient high-quality chemical mechanical polishing solution for yttrium aluminum garnet crystals
Lee et al. Self-dressing effect using a fixed abrasive platen for single-sided lapping of sapphire substrate
Li et al. Effect of FAP characteristics on fixed abrasive polishing of CaF2 crystal
Bian et al. Electrolyte composition and removal mechanism of Cu electrochemical mechanical polishing