Cai et al., 2018 - Google Patents
Residual ultimate strength of damaged seamless metallic pipelines with metal lossCai et al., 2018
- Document ID
- 11418827668262020424
- Author
- Cai J
- Jiang X
- Lodewijks G
- Pei Z
- Wu W
- Publication year
- Publication venue
- Marine Structures
External Links
Snippet
On the basis of an experimental investigation [1], numerical investigation is conducted in this paper on damaged seamless metallic pipelines with metal loss (diameter-to-thickness ratio D/t around 21) through nonlinear finite element method (FEM). Numerical models are …
- 229910052751 metal 0 title abstract description 55
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N3/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N3/08—Investigating strength properties of solid materials by application of mechanical stress by applying steady tensile or compressive forces
- G01N3/10—Investigating strength properties of solid materials by application of mechanical stress by applying steady tensile or compressive forces generated by pneumatic or hydraulic pressure
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/0202—Control of the test
- G01N2203/0212—Theories, calculations
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N17/00—Investigating resistance of materials to the weather, to corrosion, or to light
- G01N17/04—Corrosion probes
- G01N17/043—Coupons
- G01N17/046—Means for supporting or introducing coupons
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0058—Kind of property studied
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N27/00—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means
- G01N27/72—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means by investigating magnetic variables
- G01N27/82—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means by investigating magnetic variables for investigating the presence of flaws
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Keshtegar et al. | Modified response surface method basis harmony search to predict the burst pressure of corroded pipelines | |
| Yeom et al. | Integrity assessment of a corroded API X70 pipe with a single defect by burst pressure analysis | |
| Cai et al. | Residual ultimate strength of damaged seamless metallic pipelines with metal loss | |
| Netto et al. | On the effect of corrosion defects on the collapse pressure of pipelines | |
| Al-Owaisi et al. | Analysis of shape and location effects of closely spaced metal loss defects in pressurised pipes | |
| Cai et al. | Residual ultimate strength of offshore metallic pipelines with structural damage–a literature review | |
| Ghaednia et al. | Safe burst strength of a pipeline with dent–crack defect: effect of crack depth and operating pressure | |
| Teixeira et al. | Reliability analysis of pipelines with local corrosion defects under external pressure | |
| Motta et al. | Comparative studies for failure pressure prediction of corroded pipelines | |
| Chen et al. | The effect of general and localized corrosions on the collapse pressure of subsea pipelines | |
| Cai et al. | Residual ultimate strength of damaged seamless metallic pipelines with combined dent and metal loss | |
| Huang et al. | Effect of Bauschinger effect and yield criterion on residual stress distribution of autofrettaged tube | |
| Zhao et al. | Influence of random pitting corrosion on moment capacity of thin-walled circular tubes subjected to compression force | |
| Medjo et al. | Failure resistance of drilling rig casing pipes with an axial crack | |
| Yuan et al. | Influence of random pit corrosion on axial stiffness of thin-walled circular tubes | |
| Kamaya et al. | Failure pressure of straight pipe with wall thinning under internal pressure | |
| Bhardwaj et al. | Failure assessment of corroded ultra-high strength pipelines under combined axial tensile loads and internal pressure | |
| Chen et al. | Residual bending capacity for pipelines with corrosion defects | |
| Chatzopoulou et al. | Finite element analysis of cyclically-loaded steel pipes during deep water reeling installation | |
| MacKay et al. | Experimental investigation of the strength and stability of submarine pressure hulls with and without artificial corrosion damage | |
| Cai et al. | Residual ultimate strength of seamless metallic pipelines under a bending moment-a numerical investigation | |
| Musraty et al. | Ductile fracture of pipe-ring notched bend specimens–Micromechanical analysis | |
| Cai et al. | Numerical investigation of residual ultimate strength of dented metallic pipes subjected to pure bending | |
| Papadaki et al. | Buckling of internally-pressurized spiral-welded steel pipes under bending | |
| Zhu | Exact solution of burst pressure for thick-walled pipes using the flow theory of plasticity |