Velázquez et al., 2022 - Google Patents
Probabilistic and statistical techniques to study the impact of localized corrosion defects in oil and gas pipelines: a reviewVelázquez et al., 2022
View HTML- Document ID
- 10926615757196579529
- Author
- Velázquez J
- Hernández-Sánchez E
- Terán G
- Capula-Colindres S
- Diaz-Cruz M
- Cervantes-Tobón A
- Publication year
- Publication venue
- Metals
External Links
Snippet
Corrosion is a major cause of the loss of hermeticity in oil and gas pipelines. Corrosion defects affect the remaining life of in-service pipelines and can lead to failures, ruptures, hydrocarbon leakage, product loss, interruptions, environmental damage, economic losses …
- 238000005260 corrosion 0 title abstract description 411
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N33/00—Investigating or analysing materials by specific methods not covered by the preceding groups
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N17/00—Investigating resistance of materials to the weather, to corrosion, or to light
- G01N17/04—Corrosion probes
-
- G—PHYSICS
- G06—COMPUTING; CALCULATING; COUNTING
- G06Q—DATA PROCESSING SYSTEMS OR METHODS, SPECIALLY ADAPTED FOR ADMINISTRATIVE, COMMERCIAL, FINANCIAL, MANAGERIAL, SUPERVISORY OR FORECASTING PURPOSES; SYSTEMS OR METHODS SPECIALLY ADAPTED FOR ADMINISTRATIVE, COMMERCIAL, FINANCIAL, MANAGERIAL, SUPERVISORY OR FORECASTING PURPOSES, NOT OTHERWISE PROVIDED FOR
- G06Q10/00—Administration; Management
- G06Q10/06—Resources, workflows, human or project management, e.g. organising, planning, scheduling or allocating time, human or machine resources; Enterprise planning; Organisational models
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Velázquez et al. | Probabilistic and statistical techniques to study the impact of localized corrosion defects in oil and gas pipelines: a review | |
| Ossai | A data-driven machine learning approach for corrosion risk assessment—a comparative study | |
| Arriba-Rodriguez et al. | Methods to evaluate corrosion in buried steel structures: a review | |
| Melchers | A review of trends for corrosion loss and pit depth in longer-term exposures | |
| Cao et al. | A review of corrosion under insulation: a critical issue in the oil and gas industry | |
| Wolodko et al. | Modeling of microbiologically influenced corrosion (MIC) in the oil and gas industry-past, present and future | |
| May et al. | Recent advances in nondestructive method and assessment of corrosion undercoating in carbon–steel pipelines | |
| Quej-Ake et al. | Analysis of the physicochemical, mechanical, and electrochemical parameters and their impact on the internal and external SCC of carbon steel pipelines | |
| Brenna et al. | AC corrosion of carbon steel under cathodic protection condition: assessment, criteria and mechanism. A review | |
| Wu et al. | Electrochemical and stress corrosion mechanism of submarine pipeline in simulated seawater in presence of different alternating current densities | |
| Hussain et al. | Review of prediction of stress corrosion cracking in gas pipelines using machine learning | |
| Amaechi et al. | Review on subsea pipeline integrity management: An operator’s perspective | |
| Xu et al. | Experimental study on rebar corrosion using the galvanic sensor combined with the electronic resistance technique | |
| Atadero et al. | An integrated uncertainty-based bridge inspection decision framework with application to concrete bridge decks | |
| Gao et al. | Prediction of corrosive fatigue life of submarine pipelines of API 5L X56 steel materials | |
| Du et al. | Development of Subsea Pipeline Buckling, Corrosion and Leakage Monitoring | |
| Khakzad et al. | Probabilistic failure assessment of oil pipelines due to internal corrosion | |
| Shin et al. | Evaluation of commercial corrosion sensors for real-time monitoring of pipe wall thickness under various operational conditions | |
| Adumene et al. | Influence-based consequence assessment of subsea pipeline failure under stochastic degradation | |
| Wang et al. | Statistical analysis of spatial distribution of external corrosion defects in buried pipelines using a multivariate Poisson-lognormal model | |
| Ossai | Finite element modelling and retained life estimation of corroded pipelines in consideration of burst pressures—A fractural mechanics approach | |
| Bęben et al. | Monitoring and Preventing Failures of Transmission Pipelines at Oil and Natural Gas Plants | |
| Tan | A critical overview of monitoring infrastructural health using corrosion probes | |
| Cheng et al. | Effects of temperature and applied potential on the stress corrosion cracking of X80 steel in a xinzhou simulated soil solution | |
| Wang | Explicitly assessing the durability of RC structures considering spatial variability and correlation |