Abdullin et al., 1994 - Google Patents

Corrosion-fatigue durability of pipe steel in carbonate-bicarbonate medium

Abdullin et al., 1994

Document ID
9544294946198646751
Author
Abdullin I
Gareev A
Publication year
Publication venue
Materials Science

External Links

Snippet

Analysis of the operating conditions of gas mains shows that, along with the static stress, a pipe is subjected to cyclically varying stress with a wide frequency spectrum. These stresses consisting of low and high frequency oscillations may result in small cycle corrosion fatigue …
Continue reading at www.osti.gov (other versions)

Classifications

    • G—PHYSICS
    • G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
    • G21C—NUCLEAR REACTORS
    • G21C3/00—Reactor fuel elements and their assemblies; Selection of substances for use as reactor fuel elements
    • G21C3/02—Fuel elements
    • G21C3/04—Constructional details
    • G21C3/06—Casings; Jackets
    • G21C3/07—Casings; Jackets characterised by their material, e.g. alloys

Similar Documents

Publication Publication Date Title
Coffin Jr LOW CYCLE FATIGUE--A REVIEW
Almarnaess Fatigue handbook: offshore steel structures
Abdullin et al. Corrosion-fatigue durability of pipe steel in carbonate-bicarbonate medium
Parkins et al. Stress corrosion cracking of C-Mn steels in environments containing carbon dioxide
Economy et al. Influence of hydrogen partial pressure on the IGSCC behavior of Alloy 600 tubing in 360/sup 0/C water or 400/sup 0/C steam
Tsubota et al. The effect of cold work on the SCC susceptibility of austenitic stainless steels
Beavers et al. Effects of surface condition on the stress corrosion cracking of line pipe steel
Knight Corrosion fatigue related to welded steel structures: a literature survey.[0. 25% carbon 1. 4% Mn steel embrittlement; 12 Ni--5Cr--3Mo steel]
May et al. Effective utilization of high-yield strength steels in fatigue
Leis et al. A mechanics based analysis of stress corrosion cracking of line-pipe steel in a carbonate-bicarbonate environment: Topical report
Magnani Stress corrosion cracking of uranium alloys
Shipilov et al. Rig for low-cycle corrosion-fatigue testing of construction materials
Czajkowski Investigation of shell cracking on the steam generators at Indian Point Unit No. 3
Goldberg et al. Evaluation of cracking in feedwater piping adjacent to the steam generators in Nine Pressurized Water Reactor Plants
Fessler Present understanding of the causes of stress-corrosion cracking in buried pipelines
Tanaka et al. Thermal aging of cast duplex stainless steels
Kiss et al. FATIGUE CRACK GROWTH IN PROTOTYPE PIPING AND COMPONENTS.
Ogiso et al. The study on the fatigue damage estimation method for the buckled reactor vessel under earthquake loading
Voronin et al. Interrelationship of mechanical and corrosion-mechanical characteristics of type 12KhN4MF steel
Ljungberg et al. Hydrogen water chemistry to mitigate intergranular stress corrosion cracking: In-reactor tests
Fontana et al. FUNDAMENTAL CORROSION RESEARCH. Final Report for the period November 1, 1960-January 31, 1961. Report No. 20
Kaap et al. The low-cycle fatigue and creep-fatigue behavior of alloy 800 in the presence of saturated and superheated steam
Gao et al. Quantitative assessment of the role of microstructure in corrosion fatigue in a metastable austenitic steel.[Fe18Cr12Ni]
Zuev et al. Laser mass-spectrometer method of examining hydrogen distribution in chromium-plated steel
Haenninen et al. Determination of the threshold values for corrosion fatigue crack growth rate of pressure vessel steels in PWR primary water