Dehghani et al., 2019 - Google Patents

Fatigue performance and design of concrete-filled steel tubular joints: A critical review

Dehghani et al., 2019

Document ID
9475697298363840054
Author
Dehghani A
Aslani F
Publication year
Publication venue
Journal of Constructional Steel Research

External Links

Snippet

Over recent years, concrete-filled steel tubular (CFST) sections have been considered as a popular approach for the construction of new infrastructures as well as strengthening and repairing critical structural components such as joints. In contrast to the ultimate capacity of …
Continue reading at www.sciencedirect.com (other versions)

Classifications

    • GPHYSICS
    • G01MEASURING; TESTING
    • G01NINVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/0058Kind of property studied
    • G01N2203/006Crack, flaws, fracture or rupture
    • G01N2203/0062Crack or flaws
    • GPHYSICS
    • G01MEASURING; TESTING
    • G01NINVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/02Details not specific for a particular testing method
    • G01N2203/0202Control of the test
    • G01N2203/0212Theories, calculations

Similar Documents

Publication Publication Date Title
Božić et al. The effect of residual stresses on fatigue crack propagation in welded stiffened panels
Mehmanparast et al. Fatigue crack growth rates for offshore wind monopile weldments in air and seawater: SLIC inter-laboratory test results
Dehghani et al. Fatigue performance and design of concrete-filled steel tubular joints: A critical review
Qian et al. Fatigue and residual strength of concrete-filled tubular X-joints with full capacity welds
Wang et al. Fatigue behavior of welded T-joints with a CHS brace and CFCHS chord under axial loading in the brace
Wang et al. Residual stress effects on fatigue behaviour of welded T-joint: a finite fracture mechanics approach
Milosevic et al. Evaluation of true stress–strain diagrams for welded joints by application of Digital Image Correlation
Yan et al. Validate crack assessment models with in-service and hydrotest failures
Manai et al. A probabilistic study of welding residual stresses distribution and their contribution to the fatigue life
Jin et al. Effect of welding residual stress on the performance of CFST tubular joints
Musa et al. Stress concentration factor in concrete-filled steel tubular K-joints under balanced axial load
Hertelé et al. Structural integrity of corroded girth welds in vintage steel pipelines
Bertini et al. Effects of plate stiffness on the fatigue resistance and failure location of pipe-to-plate welded joints under bending
Zong et al. Experimental and numerical study on fatigue damage evolution of Q690D welding details
Feng et al. Review and discussion of strength mismatch of girth welds in high strength pipelines
Song et al. Fatigue fracture assessment of 10CrNi3MoV welded load‐carrying cruciform joints considering mismatch effect
Frendo Analysis of the catastrophic failure of a dockside crane jib
Yang et al. Modeling of fatigue failure mode in U‐rib to deck joints in orthotropic bridge structures
Cosham et al. Crack-like defects in pipelines: the relevance of pipeline-specific methods and standards
Terán-Guillén et al. Structural integrity assessment of the cast Steel upper anchorage elements used in a cable stayed bridge
Carlucci et al. Crack initiation and growth in bimetallic girth welds
Fazzini et al. Experimental validation of the influence of lamination defects in electrical resistance seam welded pipelines
Radu et al. Butt welded joints assessment after fire exposure
Zhu Assessment methods and technical challenges of remaining strength for corrosion defects in pipelines
Hosseini Assessment of crack in corrosion defects in natural gas transmission pipelines