Jeong et al., 2019 - Google Patents

Development of an apparatus for chloride induced stress corrosion cracking test using immersion method with constant displacement condition

Jeong et al., 2019

Document ID
9336466384820036306
Author
Jeong J
Lee M
Kim Y
Sindelar R
Duncan A
Publication year
Publication venue
Pressure Vessels and Piping Conference

External Links

Snippet

This paper presents a new test method for assessing chloride induced stress corrosion cracking occurred in metal canisters used for storing spent nuclear fuels. The material applied to experiment is austenitic stainless steel, SS304 similarly used on manufacturing …
Continue reading at asmedigitalcollection.asme.org (other versions)

Classifications

    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/0058—Kind of property studied
    • G01N2203/006—Crack, flaws, fracture or rupture
    • G01N2203/0062—Crack or flaws
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/02—Details not specific for a particular testing method
    • G01N2203/0202—Control of the test
    • G01N2203/0212—Theories, calculations
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/0014—Type of force applied
    • G01N2203/0016—Tensile or compressive
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N17/00—Investigating resistance of materials to the weather, to corrosion, or to light
    • G01N17/04—Corrosion probes
    • G01N17/043—Coupons
    • G01N17/046—Means for supporting or introducing coupons
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N33/00—Investigating or analysing materials by specific methods not covered by the preceding groups
    • G01N33/26—Investigating or analysing materials by specific methods not covered by the preceding groups oils; viscous liquids; paints; inks
    • G01N33/28—Oils, i.e. hydrocarbon liquids
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/02—Details not specific for a particular testing method
    • G01N2203/026—Specifications of the specimen
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/02—Details not specific for a particular testing method
    • G01N2203/022—Environment of the test
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N2203/02—Details not specific for a particular testing method
    • G01N2203/025—Geometry of the test
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N17/00—Investigating resistance of materials to the weather, to corrosion, or to light
    • G01N17/006—Investigating resistance of materials to the weather, to corrosion, or to light of metals
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N3/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N3/08—Investigating strength properties of solid materials by application of mechanical stress by applying steady tensile or compressive forces
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N17/00—Investigating resistance of materials to the weather, to corrosion, or to light
    • G01N17/02—Electrochemical measuring systems for weathering, corrosion or corrosion-protection measurement
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N3/00—Investigating strength properties of solid materials by application of mechanical stress
    • G01N3/40—Investigating hardness or rebound hardness
    • G01N3/42—Investigating hardness or rebound hardness by performing impressions under a steady load by indentors, e.g. sphere, pyramid
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N33/00—Investigating or analysing materials by specific methods not covered by the preceding groups
    • G01N33/38—Investigating or analysing materials by specific methods not covered by the preceding groups concrete; ceramics; glass; bricks
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N33/00—Investigating or analysing materials by specific methods not covered by the preceding groups
    • G01N33/20—Investigating or analysing materials by specific methods not covered by the preceding groups metals
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N27/00—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means
    • G01N27/72—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means by investigating magnetic variables
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N2291/00—Indexing codes associated with group G01N29/00
    • G01N2291/02—Indexing codes associated with the analysed material
    • G01N2291/028—Material parameters
    • G—PHYSICS
    • G01—MEASURING; TESTING
    • G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
    • G01N29/00—Investigating or analysing materials by the use of ultrasonic, sonic or infrasonic waves; Visualisation of the interior of objects by transmitting ultrasonic or sonic waves through the object
    • G01N29/04—Analysing solids
    • G01N29/041—Analysing solids on the surface of the material, e.g. using Lamb, Rayleigh or shear waves

Similar Documents

Publication Publication Date Title
Gajdoš et al. Evaluating the integrity of pressure pipelines by fracture mechanics
Jeong et al. Development of an apparatus for chloride induced stress corrosion cracking test using immersion method with constant displacement condition
Khor Crack tip opening displacement (CTOD) in single edge notched bend (SEN (B))
Jie et al. Corrosion fatigue mechanisms and evaluation methods of high‐strength steel wires: A state‐of‐the‐art review
Clarke et al. Measurement of fluid flow rates through cracks
Duncan et al. Crack Growth Rate Testing of Bolt-Load Compact Tension Specimens Under Chloride-Induced Stress Corrosion Cracking Conditions in Spent Nuclear Fuel Canisters
Jeong et al. Chloride-induced stress corrosion cracking tester for austenitic stainless steel
Nuhi et al. Reliability analysis for degradation effects of pitting corrosion in carbon steel pipes
Polyanskiy et al. Hydrogen embrittlement as a surface phenomenon in deformed metals
Lam et al. Crack growth rate testing and large plate demonstration under chloride-induced stress corrosion cracking conditions in stainless steel canisters for storage of spent nuclear fuel
Duncan et al. Crack Growth Rate Testing With Instrumented Bolt-Load Compact Tension Specimens Under Chloride-Induced Stress Corrosion Cracking Conditions in Spent Nuclear Fuel Canisters
Díaz-Cruz et al. Study of the Effect of Isothermal Aging on API 5L Grade B Steel Through Charpy Energy Testing and Electrochemical Evaluation
Pettersson et al. Corrosion testing of welds, a review of methods
Jeong et al. An Experimental Method for Assessing Chloride Induced Stress Corrosion Cracking in Stainless Steel Canisters
Acosta et al. Microstructure-based Lifetime Assessment of Austenitic Steel AISI 347 Exposed to Corrosion and Fatigue
Yahi et al. Experimental approach to monitoring the degradation status of pipelines transporting hydrocarbons
Cicero et al. Development of a Theory of Critical Distances Based Methodology for Environmentally Assisted Cracking Analyses
Coules et al. Direct observation of elastic and plastic strain fields during ductile tearing of a ferritic steel
Pan et al. Effects of environmental factors and potential on stress corrosion cracking of Fe-Ni-Cr-Mo Alloys in chloride solutions
Dmytrakh et al. Effect of Hydrogen Concentration in Metal on Residual Durability of Defected Pipelines
Holtam et al. The behavior of shallow cracks in a pipeline steel operating in a sour environment
Brossia et al. Stress Corrosion Cracking of Carbon Steel in Nitrate and Carbonate Wastes at Hanford
Nabhani et al. Electrochemical Behaviour of Low Carbon Steel in Aqueous Solutions.
Jain et al. An experimental study into the degradation of elastic, plastic and fracture properties of a pre-corroded ductile material at elevated temperatures
Gorynin et al. Aging of materials of the equipment of nuclear power plants after designed service life