McIlree et al., 1975 - Google Patents
Effects of Variations of Carbon, Sulfur and Phosphorus on the Corrosion Behavior of Alloy 600McIlree et al., 1975
View PDF- Document ID
- 7912963441626794287
- Author
- McIlree A
- Michels H
- Morris P
- Publication year
- Publication venue
- Corrosion
External Links
Snippet
Corrosion tests were conducted on a series of Ni-Cr-Fe heats with C, S, and P varied within the composition range of alloy 600. The materials were in several conditions of heat treatment. Stress corrosion cracking (SCC) tests were conducted in undeaerated and …
- 238000005260 corrosion 0 title abstract description 87
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/051—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/10—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of nickel or cobalt or alloys based thereon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C14/00—Alloys based on titanium
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Hänninen | Influence of metallurgical variables on environment-sensitive cracking of austenitic alloys | |
| Holzworth | Hydrogen embrittlement of type 304L stainless steel | |
| Pan et al. | Effect of electrochemical hydrogen charging on the mechanical property and corrosion behavior of Ti-3Mo alloy | |
| Tjong | Stress corrosion cracking behaviour of the duplex Fe-10Al-29Mn-0.4 C alloy in 20% NaCl solution at 100 C | |
| Parvathavarthini et al. | Sensitization behaviour of modified 316N and 316L stainless steel weld metals after complex annealing and stress relieving cycles | |
| McIlree et al. | Effects of Variations of Carbon, Sulfur and Phosphorus on the Corrosion Behavior of Alloy 600 | |
| Tjong | Aqueous corrosion properties of austenitic Fe-8.7 Al-29.7 Mn-1.04 C alloy | |
| Spurrier et al. | Fractographic aspects of the stress corrosion cracking of titanium in a methanol/HCl mixture | |
| An et al. | Inconel 718 treated with two-stage solution and aging processes: microstructure evolution and enhanced properties | |
| Chiang et al. | Effect of simulated groundwater chemistry on stress corrosion cracking of alloy 22 | |
| Jones | Potential and chloride effects in the stress corrosion cracking of type 304 stainless steel in 290 C water | |
| US5976275A (en) | High-nickel austenitic stainless steel resistant to degradation by neutron irradiation | |
| Louthan Jr | Initial Stages Of Stress Corrosion Cracking In Austenitic Stainless Steels | |
| Bandy et al. | Effect of thermal stabilization on the low temperature stress corrosion cracking of Inconel 600 | |
| Mozhi et al. | The effect of nitrogen and carbon on the stress corrosion cracking performance of sensitized AISI 304 stainless steel in chloride and sulfate solutions at 250 C | |
| Beraldo et al. | Effect of aging heat treatment H950 and H1000 on mechanical and pitting corrosion properties of UNS S46500 stainless steel | |
| KR20010047593A (en) | Alloy steel having corrosion resistance in molten salt containing alkali oxide | |
| Shen et al. | Intergranular stress corrosion cracking of alloy 600 and x-750 in high-temperature deaerated water/steam | |
| Chiang et al. | The combined effect of bicarbonate and chloride ions on the stress corrosion cracking susceptibility of alloy 22 | |
| Jacobs | Grain-Boundary Segregation and IGSCC in Cold-Worked Type 304 SS | |
| Landkof et al. | Stress corrosion cracking of Al-Zn-Mg alloy AA-7039 | |
| Qi et al. | Effects of cathodic polarization on SCC behavior of AA7003 under various aging treatments | |
| Thomas et al. | The failure of stressed zircaloy in aqueous chloride solutions | |
| De et al. | Electrochemical corrosion behavior of alloy 400: intergranular corrosion in acidic Na2SO4 solutions | |
| Lennon et al. | The experimental determination of potential-pH diagrams for the Ni-H2O and low alloy steel-H2O systems |