Sobolev et al., 1976 - Google Patents
Reaction of refractory materials with melts of borosilicate glassesSobolev et al., 1976
- Document ID
- 7678847091611879492
- Author
- Sobolev Y
- Mel'nikova I
- Pavlovskii V
- Publication year
- Publication venue
- Steklo i Keramika
External Links
- 239000011819 refractory material 0 title abstract description 5
Classifications
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES, OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
- C03C3/102—Glass compositions containing silica with 40% to 90% silica, by weight containing lead
- C03C3/108—Glass compositions containing silica with 40% to 90% silica, by weight containing lead containing boron
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES, OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/076—Glass compositions containing silica with 40% to 90% silica, by weight
- C03C3/089—Glass compositions containing silica with 40% to 90% silica, by weight containing boron
- C03C3/091—Glass compositions containing silica with 40% to 90% silica, by weight containing boron containing aluminium
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
- C03B5/00—Melting in furnaces; Furnaces so far as specially adapted for glass manufacture
- C03B5/16—Special features of the melting process; Auxiliary means specially adapted for glass-melting furnaces
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03C—CHEMICAL COMPOSITION OF GLASSES, GLAZES, OR VITREOUS ENAMELS; SURFACE TREATMENT OF GLASS; SURFACE TREATMENT OF FIBRES OR FILAMENTS FROM GLASS, MINERALS OR SLAGS; JOINING GLASS TO GLASS OR OTHER MATERIALS
- C03C3/00—Glass compositions
- C03C3/04—Glass compositions containing silica
- C03C3/062—Glass compositions containing silica with less than 40% silica by weight
-
- C—CHEMISTRY; METALLURGY
- C03—GLASS; MINERAL OR SLAG WOOL
- C03B—MANUFACTURE, SHAPING, OR SUPPLEMENTARY PROCESSES
- C03B19/00—Other methods of shaping glass
- C03B19/10—Forming beads
- C03B19/1005—Forming solid beads
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Sobolev et al. | Reaction of refractory materials with melts of borosilicate glasses | |
| UA5712A1 (en) | Process for the preparation of solder borolead glass | |
| Goel et al. | Mathematical Description of the Thermochemical Properties of Iron--Silicate Slags Containing Lime | |
| Popov | Interaction of refractory materials with silicate glassmelts | |
| Gonzalez-Oliver et al. | INFLUENCE OF PLATINUM AND SILVER ADDITIONS ON CRYSTAL NUCLEATION IN GLASSES NEAR THE NA 2 O. 2 CAO. 3 SIO 2 COMPOSITION AND IN OTHER SODA-LIME-SILICA GLASSES | |
| Dipchikov | Cast glass-ceramics containing bulgarite | |
| Borovkova et al. | Corrosion resistance of quartz glass-based refractories | |
| Dimitrova et al. | Vitreous substances with unstable Cu-containing nucleation centers | |
| Popov et al. | Production tests of Cr-Al-Zr refractory in a container glass tank furnace | |
| Mazurin et al. | Relation between the glass point and liquidus temperature for some eutectic compositions of an Na borate-silicate system | |
| Galakhov | Liquation phenomenon in glasses of the system Nd sub 2 O sub 3- SiO sub 2 with small amounts of Nd sub 2 O sub 3 | |
| Hilger et al. | Corrosion process of electromelted alumina refractories by lead glass | |
| Chernov et al. | Phase Interaction in the NiAs--TiAs System and Evaluation of the Vitrifying Capacity of NiTiAs sub 2 | |
| Balayan | Synthesis and properties of glasses obtained from a charge based on GeO sub 2, SiO sub 2, B sub 2 O sub 3, Al sub 2 O sub 3, Na sub 2 O, and Li sub 2 O | |
| Gaisinskii | Slag glasses for manufacturing colored glassware | |
| Rezenko | Silicate and glass formation in low-alkali slag charges | |
| Ermolenko et al. | Synthesis and study of glasses in the system SiO sub 2-B sub 2 O sub 3-ZnO- Na sub 2 O | |
| Locsei | Cast tank blocks containing ZrO sub 2 concentrate | |
| Galakhov | Liquation in the system Ga sub 2 O sub 3- B sub 2 O sub 3- SiO sub 2 | |
| Min'ko et al. | Vitrification and properties of glasses in the system Na sub 2 O-FeO-SiO sub 2 and Na sub 2 O-Fe sub 2 O sub 3-SiO sub 2 | |
| Gusev | Kinetics of the dissolution of Sn sub 2 O-based refractories in some silicate melts | |
| Elmer | Glass for Tungsten-Halogen Lamps | |
| Zhunina | Influence of temperature-time conditions of synthesis on properties of glasses produced from slag | |
| Shakhmatkin | Thermodynamic functions of vitreous melts of the system Na sub 2 O-B sub 2 O sub 3 at 700-1000 Degrees C | |
| Turkin | Reactions of oxides and compounds of the system ZrO sub/ 2/-Al sub/ 2/ O sub/ 3/-SiO sub/ 2/ with glassmelts |