Niranatlumpong et al., 2010 - Google Patents

The effect of Mo content in plasma-sprayed Mo-NiCrBSi coating on the tribological behavior

Niranatlumpong et al., 2010

Document ID
6412604928925166323
Author
Niranatlumpong P
Koiprasert H
Publication year
Publication venue
Surface and Coatings Technology

External Links

Snippet

NiCrBSi is a material popularly used as a hard thermal sprayed coating. The coating performs well as a wear resistant coating under low stress. At higher stress in metal-to-metal sliding wear condition, however, the NiCrBSi starts to experience surface deformation, which …
Continue reading at www.sciencedirect.com (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
    • C23C4/04—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the coating material
    • C23C4/10—Oxides, borides, carbides, nitrides or silicides; Mixtures thereof
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
    • C23C4/04—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge characterised by the coating material
    • C23C4/06—Metallic material
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
    • C23C4/02—Pre-treatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C4/00—Coating by spraying the coating material in the molten state, e.g. by flame, plasma or electric discharge
    • C23C4/18—After-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D

Similar Documents

Publication Publication Date Title
Niranatlumpong et al. The effect of Mo content in plasma-sprayed Mo-NiCrBSi coating on the tribological behavior
Liu et al. Effect of heat treatment on structure and property evolutions of atmospheric plasma sprayed NiCrBSi coatings
Miguel et al. Tribological study of NiCrBSi coating obtained by different processes
Paredes et al. The effect of roughness and pre-heating of the substrate on the morphology of aluminium coatings deposited by thermal spraying
Bolelli et al. Mechanical and tribological properties of electrolytic hard chrome and HVOF-sprayed coatings
Grewal et al. Microstructural and mechanical characterization of thermal sprayed nickel–alumina composite coatings
Bolelli et al. Tribological behavior of HVOF-and HVAF-sprayed composite coatings based on Fe-Alloy+ WC–12% Co
Ahn et al. Tribological behaviour of plasma-sprayed chromium oxide coating
Yan et al. Microstructure and wear resistance of plasma-sprayed molybdenum coating reinforced by MoSi 2 particles
Huang et al. Effects of solid lubricant content on the microstructure and properties of NiCr/Cr3C2–BaF2· CaF2 composite coatings
Li et al. Influence of heat treatments on the microstructure as well as mechanical and tribological properties of NiCrAlY-Mo-Ag coatings
Ding et al. Resistance of cavitation erosion of multimodal WC-12Co coatings sprayed by HVOF
EP1785503A2 (en) Method for applying a low coefficient of friction coating
Ouyang et al. Low-pressure plasma-sprayed ZrO2–CaF2 composite coating for high temperature tribological applications
Pakseresht et al. Micro-structural study and wear resistance of thermal barrier coating reinforced by alumina whisker
Asgari et al. Tribological behavior of nanostructured high velocity oxy-fuel (HVOF) thermal sprayed WC-17NiCr coatings
Ouyang et al. Effects of different additives on microstructure and high-temperature tribological properties of plasma-sprayed Cr2O3 ceramic coatings
Ghadami et al. Abrasive wear behavior of nano-ceria modified NiCoCrAlY coatings deposited by the high-velocity oxy-fuel process
Zhai et al. Characterizations the deposition behavior and mechanical properties of detonation sprayed Fe-based amorphous coatings
Yang et al. Correlation between microstructure, chemical components and tribological properties of plasma-sprayed Cr2O3-based coatings
Tailor et al. High-performance molybdenum coating by wire–HVOF thermal spray process
CA3080622A1 (en) Mechanically alloyed metallic thermal spray coating material and thermal spray coating method utilizing the same
Huang et al. Preparation and characterization of atmospheric plasma-sprayed NiCr/Cr3C2–BaF2· CaF2 composite coating
Ahn et al. Improvement of wear resistance of plasma-sprayed molybdenum blend coatings
Vernhes et al. Nanostructured and conventional Cr 2 O 3, TiO 2, and TiO 2-Cr 2 O 3 thermal-sprayed coatings for metal-seated ball valve applications in hydrometallurgy