An investigation on corrosion failure of a shell-and-tube heat exchanger in a natural gas treating plantPanahi et al., 2020
- Document ID
- 6395998573843251374
- Author
- Panahi H
- Eslami A
- Golozar M
- Laleh A
- Publication year
- Publication venue
- Engineering Failure Analysis
External Links
Snippet
This study investigates failure of a shell-and-tube heat exchanger used in a natural gas treating plant. The shell was made of carbon steel grade A516, while its interior wall was cladded by grade 304 stainless steel. Tubes and tube-sheet of the heat exchanger were …
- 238000005260 corrosion 0 title abstract description 56
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Panahi et al. | An investigation on corrosion failure of a shell-and-tube heat exchanger in a natural gas treating plant | |
| Thekkuden et al. | Failures and leak inspection techniques of tube-to-tubesheet joints: A review | |
| Moore et al. | Metal corrosion in a supercritical carbon dioxide-liquid sodium power cycle. | |
| Subramanian et al. | Stress corrosion cracking of U tube heat exchanger used for low pressure steam generation in a hydrogen unit of petroleum refinery | |
| Yang et al. | Failure analysis of a 304 stainless steel heat exchanger in liquid sulfur recovery units | |
| Parnian | Failure analysis of austenitic stainless steel tubes in a gas fired steam heater | |
| Bahadori | Corrosion and materials selection: a guide for the chemical and petroleum industries | |
| Makhlouf et al. | Handbook of materials failure analysis with case studies from the chemicals, concrete and power industries | |
| Ravindranath et al. | Failure of stainless steel 304L air cooler tubes due to stress corrosion cracking caused by organic chlorides | |
| Khalifeh et al. | Stress corrosion cracking of a circulation water heater tubesheet | |
| Liu et al. | Corrosion failure analysis of the heat exchanger in a hot water heating boiler | |
| Ali et al. | Corrosion-related failures in heat exchangers | |
| Mohammadi Zahrani | Premature failure of grade-316Ti stainless steel tubing in a boiler feed-water heat exchanger in a steel complex | |
| Chen et al. | Failure analysis on abnormal leakage of TP321 stainless steel pipe of medium temperature shifting gas in hydrogen production system | |
| Zhao et al. | Analysis of heat exchanger corrosion failure in 800,000 light hydrocarbon plant in Liaohe Oilfield | |
| Morake et al. | Failure analysis of corroded heat exchanger CuNi tubes from a geothermal plant | |
| Kane | Corrosion in petroleum refining and petrochemical operations | |
| Fei et al. | Root causes analysis and countermeasures on unexpected perforation of tee pipe in the steam system of specialty chemical plant | |
| RU2566820C1 (en) | Method and apparatus for processing hydrocarbon streams | |
| Zhai et al. | Failure analysis on 304 stainless steel tube of semi water gas preheater in coal chemical plant | |
| Panahi et al. | Failure analysis of type 304 stainless steel amine exchanger sheets in a gas sweetening plant | |
| Gong et al. | Failure analysis of bursting on the inner pipe of a jacketed pipe in a tubular heat exchanger | |
| Schütze et al. | Corrosion Resistance of Steels, Nickel Alloys, and Zinc in Aqueous Media: Waste Water, Seawater, Drinking Water, High-Purity Water | |
| Saffiudeen et al. | Failure Analysis of Heat Exchanger Tubes | |
| Ranjbar et al. | Primming assisted failure of superheater tubes in a sugarcane industry |