Effect of corrosion damage on a pipeline burst pressure and repairing methodsAmara et al., 2019
View PDF- Document ID
- 6103054082379369414
- Author
- Amara M
- Bouledroua O
- Hadj Meliani M
- Azari Z
- Tahar Abbess M
- Pluvinage G
- Bozic Z
- Publication year
- Publication venue
- Archive of Applied Mechanics
External Links
Snippet
On the basis of the calculation of the stress field around the corrosion-damaged areas on the external part of a pipeline used for the transport of hydrocarbons, an analysis of the effect of the level of post-repair burst pressure by composite patches is proposed. This work …
- 238000005260 corrosion 0 title abstract description 46
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Zhu | A comparative study of burst failure models for assessing remaining strength of corroded pipelines | |
| Amara et al. | Effect of corrosion damage on a pipeline burst pressure and repairing methods | |
| Valadi et al. | XFEM fracture analysis of cracked pipeline with and without FRP composite repairs | |
| Barkanov et al. | Non-destructive Testing and repair of pipelines | |
| Shuai et al. | Development of an empirical model to predict the burst pressure of corroded elbows of pipelines by finite element modelling | |
| Li et al. | Numerical analysis on the SIF of internal surface cracks in steel pipes reinforced with CRS subjected to bending | |
| Cui et al. | A new magnetic structural algorithm based on virtual crack closure technique and magnetic flux leakage testing for circumferential symmetric double-crack propagation of X80 oil and gas pipeline weld | |
| Hadj Meliani et al. | The inspections, standards and repairing methods for pipeline with composite: a review and case study | |
| Zhang et al. | Reliability-Based Assessment of Cracked Pipelines Using Monte Carlo Simulation Technique With CorLAS™ | |
| Abdelkader et al. | Structural integrity assessment of corroded pipelines repaired with composite materials–Literature review | |
| Belachew et al. | Strength assessment of a corroded pipeline through the burst test: case study | |
| Cao et al. | Novel Prediction Model of Tensile Strain Capacity for Pipelines with Corrosion Defects | |
| Zangeneh | Fitness-for-service assessment and failure analysis of hydrogen-induced cracking in a pipeline steel | |
| Zhu et al. | Progress of assessment model development for determining remaining strength of corroded pipelines | |
| Salina Farini Bahaman et al. | Integrity of API 5L X56 offshore pipeline subjected to girth weld anomalies and corrosion using probabilistic methods | |
| Zangeneh | Fitness-for-service assessment of local thin area in a line pipe | |
| Alnaser et al. | Multiple-output fracture characteristics optimization of Bi-material interfaces for composite pipe repair using swarm intelligence technique | |
| Savari | Crack assessment in spiral-welded pipelines repaired by composite patch: A SMART and failure assessment diagram approach | |
| Xie et al. | Impact analysis of inline inspection accuracy on pipeline integrity planning | |
| Cosham et al. | PDAM 2. | |
| Boreman et al. | Repair technologies for gas transmission pipelines | |
| Xie et al. | A Method to Analyze the Impact of Inline Inspection Accuracy on Integrity Management Program Planning of Pipelines | |
| Zecheru et al. | Development of an Experimental Programme for Industrial Approbation | |
| Kara Achira et al. | Optimal design of the geometrical parameters of biocomposite wraps using in repairing of corroded pipeline under internal pressure: application for Algerian MEDGAZ | |
| Pahnaneh et al. | Microstructure Analysis and Fitness-for-Service Assessment of Hydrogen-Induced Cracking in an Amine Tower |