Puttick, 1960 - Google Patents
The shear component of ductile fracturePuttick, 1960
- Document ID
- 6029503508608451818
- Author
- Puttick K
- Publication year
- Publication venue
- Philosophical Magazine
External Links
Snippet
There are two well-defined stages in the fracture of a cylindrical test piece of a ductile metal. The first stage begins on the axis in the centre of the necked region, and the general directions of propagation of the crack lie in a plane normal to the tensile axis; this is usually …
- 238000000034 method 0 abstract description 7
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Puttick | The shear component of ductile fracture | |
| Liu et al. | Twinning, dynamic recrystallization, and crack in AZ31 magnesium alloy during high strain rate plane strain compression across a wide temperature | |
| Petch | XVI. The ductile fracture of polycrystalline α-iron | |
| Beardmore et al. | Deformation and fracture of tungsten single crystals | |
| Marciniak et al. | Limit strains in the processes of stretch-forming sheet metal | |
| Johnson et al. | On the shape and size of the fracture zones on glass fracture surfaces | |
| Chang | Further studies of the maximum stress criterion on the angled crack problem | |
| Hannink et al. | The effect of domain size on the hardness of ordered VC0. 84 | |
| Klesnil et al. | Dislocation structure associated with fracture surface of fatigued copper single crystals | |
| Armstrong | On determining the ductile–brittle transition temperature | |
| Enahoro et al. | An investigation of the transition from a continuous to a discontinuous chip in orthogonal machining | |
| Tanada et al. | The impact of high progesterone levels on the day of HCG administration in assisted human reproduction treatments | |
| Wadsworth et al. | Observations on the fatigue fracture of copper | |
| Wood et al. | Internal stresses in metals | |
| Houston et al. | Edge Effects in a Circular Aperture | |
| Alic et al. | Direct observation of tensile and fatigue cracks | |
| Pim | Electrical breakdown strength of air at ultra high-frequencies | |
| Chang et al. | Compression-Induced High-Strain-Rate Void Collapse | |
| Jackson | Hardening in cadmium resulting from pyramidal glide | |
| Besag et al. | The effect of pressurization on yield by twinning in Armco iron | |
| Weinberg | Grain boundary shear in aluminum | |
| Heald | On the cleavage fracture of zinc | |
| Wilkins et al. | Non-propagating fatigue cracks in an aluminium-1/2% magnesium alloy | |
| SU868445A1 (en) | Method of tensile-compression of testing specimens of tubes | |
| Rosakis et al. | Dynamic crack growth criteria in structural metals |