Sheu et al., 2016 - Google Patents

Investigation on the corrosion resistance of trivalent chromium conversion passivate on electroplated Zn–Ni alloy

Sheu et al., 2016

Document ID
6006375003640904731
Author
Sheu H
Lee H
Jian S
Hsu C
Lee C
Publication year
Publication venue
Surface and Coatings Technology

External Links

Snippet

The corrosion resistance of electroplated Zn–Ni alloy using trivalent chromium conversion treatment in alkaline electrolyte was investigated. Among the Zn–Ni coatings electroplated on steel substrate with raising current densities, the Ni content and corrosion resistance …
Continue reading at www.sciencedirect.com (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of work-pieces
    • C25D5/10—Electroplating with more than one layer of the same or of different metals
    • C25D5/12—Electroplating with more than one layer of the same or of different metals at least one layer being of nickel or chromium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/32—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer
    • C23C28/321—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one pure metallic layer with at least one metal alloy layer
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/02—Electroplating: Baths therefor from solutions
    • C25D3/56—Electroplating: Baths therefor from solutions of alloys
    • C25D3/565—Electroplating: Baths therefor from solutions of alloys containing more than 50% by weight of zinc
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D3/00—Electroplating: Baths therefor
    • C25D3/02—Electroplating: Baths therefor from solutions
    • C25D3/12—Electroplating: Baths therefor from solutions of nickel or cobalt
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of work-pieces
    • C25D5/48—After-treatment of electroplated surfaces
    • C25D5/50—After-treatment of electroplated surfaces by heat-treatment
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/30—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer
    • C23C28/34—Coatings combining at least one metallic layer and at least one inorganic non-metallic layer including at least one inorganic non-metallic material layer, e.g. metal carbide, nitride, boride, silicide layer and their mixtures, enamels, phosphates and sulphates
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C28/00—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D
    • C23C28/02—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material
    • C23C28/023—Coating for obtaining at least two superposed coatings either by methods not provided for in a single one of groups C23C2/00 - C23C26/00 or by combinations of methods provided for in subclasses C23C and C25C or C25D only coatings only including layers of metallic material only coatings of metal elements only
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D5/00—Electroplating characterised by the process; Pretreatment or after-treatment of work-pieces
    • C25D5/34—Pretreatment of metallic surfaces to be electroplated
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25D—PROCESSES FOR THE ELECTROLYTIC OR ELECTROPHORETIC PRODUCTION OF COATINGS; ELECTROFORMING; APPARATUS THEREFOR
    • C25D7/00—Electroplating characterised by the article coated
    • C25D7/06—Wires; Strips; Foils
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
    • C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
    • C23C18/31—Coating with metals
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C30/00—Coating with metallic material characterised only by the composition of the metallic material, i.e. not characterised by the coating process
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material

Similar Documents

Publication Publication Date Title
Sheu et al. Investigation on the corrosion resistance of trivalent chromium conversion passivate on electroplated Zn–Ni alloy
Ranganatha et al. Development of electroless Ni–Zn–P/nano-TiO2 composite coatings and their properties
Bekish et al. Electrodeposited Ni–B alloy coatings: structure, corrosion resistance and mechanical properties
Eliaz et al. Electroplating and characterization of Zn–Ni, Zn–Co and Zn–Ni–Co alloys
Rashmi et al. Multilayered Zn-Ni alloy coatings for better corrosion protection of mild steel
Ghaziof et al. Characterization of as-deposited and annealed Cr–C alloy coatings produced from a trivalent chromium bath
Lee et al. Mechanical properties of electrodeposited Ni-W thinfilms with alternate W-rich and W-poor multilayers
Nia et al. Influence of metallurgical parameters on the electrochemical behavior of electrodeposited Ni and Ni–W nanocrystalline alloys
Pavithra et al. Magnetic property and corrosion resistance of electrodeposited nanocrystalline iron–nickel alloys
Alfantazi et al. Pulse plating of Zn-Ni alloy coatings
Wu et al. Influence of boric acid on the electrodepositing process and structures of Ni–W alloy coating
Fei et al. Electrodeposition of zinc–nickel compositionally modulated multilayer coatings and their corrosion behaviours
Nayana et al. Influence of additive on nanocrystalline, bright Zn–Fe alloy electrodeposition and its properties
de Lima-Neto et al. A comparative study of the physicochemical and electrochemical properties of Cr and Ni–W–P amorphous electrocoatings
Zarebidaki et al. Microstructure and corrosion behavior of electrodeposited nano-crystalline nickel coating on AZ91 Mg alloy
Srivastava et al. Effect of pH on anomalous co-deposition and current efficiency during electrodeposition of Ni-Zn-P alloys
Panagopoulos et al. Adhesion and corrosion behaviour of Zn–Co electrodeposits on mild steel
Feng et al. Corrosion mechanism of nanocrystalline Zn–Ni alloys obtained from a new DMH-based bath as a replacement for Zn and Cd coatings
Mousavi et al. Improvement of corrosion resistance of NiMo alloy coatings: Effect of heat treatment
Nayana et al. Effect of ethyl vanillin on ZnNi alloy electrodeposition and its properties
Haerifar et al. Effect of current density and electrolyte pH on microstructure of Mn–Cu electroplated coatings
Muralidhara et al. Electrochemical deposition of nanocrystalline zinc on steel substrate from acid zincate bath
Feng et al. Effect of additives on the corrosion mechanism of nanocrystalline zinc–nickel alloys in an alkaline bath
Bahadormanesh et al. Ni-P/Zn-Ni compositionally modulated multilayer coatings–Part 2: Corrosion and protection mechanisms
Winiarski et al. The effect of pH of plating bath on electrodeposition and properties of protective ternary Zn–Fe–Mo alloy coatings