Lee et al., 2022 - Google Patents

Development of hydro-axial tension method for whole pipe butt-fusion joint tensile test

Lee et al., 2022

View HTML
Document ID
5889466732457327722
Author
Lee P
Kim S
Stakenborghs B
Suh Y
Choi S
Publication year
Publication venue
Polymer Testing

External Links

Snippet

Assessing the integrity of the thermo-fusion joint in plastic pipes is important as they can appear as a weak link in the piping system. In this work, a hydro-axial tension (HAT) test was developed as a whole pipe axial tensile test and applied to evaluate the polyethylene (PE) …
Continue reading at www.sciencedirect.com (HTML) (other versions)

Classifications

    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING ENGINES OR PUMPS
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16L—PIPES; JOINTS OR FITTINGS FOR PIPES; SUPPORTS FOR PIPES, CABLES OR PROTECTIVE TUBING; MEANS FOR THERMAL INSULATION IN GENERAL
    • F16L55/00—Devices or appurtenances for use in, or in connection with, pipes or pipe systems
    • F16L55/16—Devices for covering leaks in pipes or hoses, e.g. hose-menders
    • F16L55/162—Devices for covering leaks in pipes or hoses, e.g. hose-menders from inside the pipe
    • F—MECHANICAL ENGINEERING; LIGHTING; HEATING; WEAPONS; BLASTING ENGINES OR PUMPS
    • F16—ENGINEERING ELEMENTS AND UNITS; GENERAL MEASURES FOR PRODUCING AND MAINTAINING EFFECTIVE FUNCTIONING OF MACHINES OR INSTALLATIONS; THERMAL INSULATION IN GENERAL
    • F16L—PIPES; JOINTS OR FITTINGS FOR PIPES; SUPPORTS FOR PIPES, CABLES OR PROTECTIVE TUBING; MEANS FOR THERMAL INSULATION IN GENERAL
    • F16L9/00—Rigid pipes

Similar Documents

Publication Publication Date Title
Lee et al. Development of hydro-axial tension method for whole pipe butt-fusion joint tensile test
Cosham et al. The pipeline defect assessment manual
Al-Owaisi et al. An experimental investigation of the effect of defect shape and orientation on the burst pressure of pressurised pipes
Macdonald et al. Best practice for the assessment of defects in pipelines–gouges and dents
Cosham et al. The effect of dents in pipelines—guidance in the pipeline defect assessment manual
Wham et al. PVCO pipeline performance under large ground deformation
Dake et al. Fracture capacity of girth welded pipelines with 3D surface cracks subjected to biaxial loading conditions
Wilkowski et al. Progress in development of acceptance criteria for local thinned areas in pipe and piping components
Nykyforchyn et al. Analysis and mechanical properties characterization of operated gas main elbow with hydrogen assisted large-scale delamination
Otegui et al. Weld failures in sleeve reinforcements of pipelines
Shen et al. Fracture toughness evaluation of high strength steel pipe
Li et al. External surface cracked offshore steel pipes reinforced with composite repair system subjected to cyclic bending: An experimental investigation
Zhao et al. Elastic-plastic fracture analyses for misaligned clad pipeline containing a canoe shape surface crack subjected to large plastic deformation
Kim et al. Investigation on the thermal butt fusion performance of the buried high density polyethylene piping in nuclear power plant
Zhu et al. Application of constraint corrected J-R curves to fracture analysis of pipelines
Achour et al. Analysis of repaired cracks with bonded composite wrap in pipes under bending
Lai et al. Effects of defects on failure of butt fusion welded polyethylene pipe
Kharchenko et al. Diagnostics of hydrogen macrodelamination in the wall of a bent pipe in the system of gas mains
Farzadi Gas pipeline failure caused by in-service welding
Yayla et al. Squeeze-off of polyethylene pressure pipes: Experimental analysis
Kibey et al. Effect of misalignment on the tensile strain capacity of welded pipelines
Kibey et al. Development of a physics-based approach for the prediction of strain capacity of welded pipelines
Cosham et al. Crack-like defects in pipelines: the relevance of pipeline-specific methods and standards
Bastola et al. Full-and small-scale tests on strain capacity of X80 seamless pipes
Hosseini et al. Experimental testing and evaluation of crack defects in line pipe