Carpinteri et al., 2009 - Google Patents
Sickle‐shaped surface crack in a notched round bar under cyclic tension and bendingCarpinteri et al., 2009
View PDF- Document ID
- 5452039117523053438
- Author
- Carpinteri A
- Vantadori S
- Publication year
- Publication venue
- Fatigue & Fracture of Engineering Materials & Structures
External Links
Snippet
ABSTRACT A sickle‐shaped surface crack, also called crescent‐moon (or crescent) crack, is assumed to exist at the root of a circular‐arc circumferential notch in a round bar under tension and bending. For different notch sizes (ie different values of the stress concentration …
- 238000005452 bending 0 title abstract description 34
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/0202—Control of the test
- G01N2203/0212—Theories, calculations
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Berto et al. | Fatigue strength of severely notched specimens made of Ti–6Al–4V under multiaxial loading | |
| Carpinteri et al. | Sickle‐shaped surface crack in a notched round bar under cyclic tension and bending | |
| Chen et al. | A critical plane‐strain energy density criterion for multiaxial low‐cycle fatigue life under non‐proportional loading | |
| Shamsaei et al. | Effect of hardness on multiaxial fatigue behaviour and some simple approximations for steels | |
| Zhu et al. | Mean stress and ratcheting corrections in fatigue life prediction of metals | |
| Berto et al. | Multiaxial fatigue of V‐notched steel specimens: a non‐conventional application of the local energy method | |
| Lazzarin et al. | A notch stress intensity approach to assess the multiaxial fatigue strength of welded tube‐to‐flange joints subjected to combined loadings | |
| Brighenti et al. | Surface cracks in fatigued structural components: a review | |
| Correia et al. | Crack closure effects on fatigue crack propagation rates: application of a proposed theoretical model | |
| Carpinteri et al. | Stress intensity factors and fatigue growth of surface cracks in notched shells and round bars: two decades of research work | |
| Zhao et al. | The evolution of the stress–strain fields near a fatigue crack tip and plasticity‐induced crack closure revisited | |
| Colin et al. | Variable amplitude cyclic deformation and fatigue behaviour of stainless steel 304L including step, periodic, and random loadings | |
| Chen et al. | Low‐cycle fatigue of 1Cr–18Ni–9Ti stainless steel and related weld metal under axial, torsional and 90 out‐of‐phase loading | |
| Kim et al. | Ductile fracture simulation of 304 stainless steel pipes with two circumferential surface cracks | |
| Letcher et al. | An energy‐based critical fatigue life prediction method for AL6061‐T6 | |
| Bahmani et al. | Mixed mode I/III fracture parameters for edge‐notched diametrically compressed disc specimen | |
| Rushton et al. | Prediction of crack growth in 350WT steel subjected to constant amplitude with over-and under-loads using a modified wheeler approach | |
| Chen et al. | Analytical Solutions for Corrosion‐Induced Cohesive Concrete Cracking | |
| Majidi et al. | On combination of the equivalent material concept and J‐integral criterion for ductile failure prediction of U‐notches subjected to tension | |
| Lu et al. | Influence of inclusion size on S‐N curve characteristics of high‐strength steels in the giga‐cycle fatigue regime | |
| Tao et al. | Life prediction based on weight‐averaged maximum shear strain range plane under multiaxial variable amplitude loading | |
| Jie et al. | Effect of stress ratios on corrosion fatigue life of high‐strength steel wires | |
| Chen et al. | A weight function‐critical plane approach for low‐cycle fatigue under variable amplitude multiaxial loading | |
| Jezernik et al. | Numerical modelling of fatigue crack initiation and growth of martensitic steels | |
| Ma et al. | Constitutive and damage modelling of H11 subjected to low‐cycle fatigue at high temperature |