Fry et al., 2002 - Google Patents
Oxidation of alloys in steam environments-a review.Fry et al., 2002
View PDF- Document ID
- 5231652037587493875
- Author
- Fry A
- Osgerby S
- Wright M
- Publication year
External Links
Snippet
Traditionally materials designed for use at high temperature have been developed primarily for their mechanical properties but there is now a growing realisation that oxidation may limit lifetime. The purpose of this report is to review existing information regarding oxidation of …
- 238000007254 oxidation reaction 0 title abstract description 133
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/058—Alloys based on nickel or cobalt based on nickel with chromium without Mo and W
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/051—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Fry et al. | Oxidation of alloys in steam environments-a review. | |
| Viswanathan et al. | Boiler materials for ultra-supercritical coal power plants—steamside oxidation | |
| Sequeira | High temperature corrosion: fundamentals and engineering | |
| Wright et al. | A review of the oxidation behaviour of structural alloys in steam | |
| Zhang et al. | Oxidation of ferritic and ferritic–martensitic steels in flowing and static supercritical water | |
| Bruemmer et al. | Microstructural and microchemical mechanisms controlling intergranular stress corrosion cracking in light-water-reactor systems | |
| Cowan et al. | Intergranular corrosion of iron-nickel-chromium alloys | |
| Li et al. | State of the art overview material degradation in high-temperature supercritical CO2 environments | |
| Marriott et al. | High temperature alloys: their exploitable potential | |
| Li et al. | Corrosion of SS310 and Alloy 740 in high temperature supercritical CO2 with impurities H2O and O2 | |
| Yang et al. | Microstructural understanding of the oxidation and inter-diffusion behavior of Cr-coated Alloy 800H in supercritical water | |
| Kumar et al. | Comparative parabolic rate constant and coating properties of nickel, cobalt, iron and metal oxide based coating: a review | |
| Leong et al. | Oxidation behavior of Fe-Cr-2Si alloys in high temperature steam | |
| Rebak et al. | Resistance of Ferritic FeCrAl alloys to stress corrosion cracking for light water reactor fuel cladding applications | |
| Chen et al. | Effect of surface conditions and alloying elements on the early oxidation behaviour of two austenitic alloys in the pure steam environment | |
| Wang et al. | Steam oxidation behavior of T92 steel tube for high temperature reheater after long-term service in ultra-supercritical boilers | |
| Gibbs | Corrosion of various engineering alloys in supercritical carbon dioxide | |
| Liu et al. | Effects of External Stress on High-Temperature Corrosion Behavior of T92 Ferrite Steel with Na 2 SO 4-K 2 SO 4 Molten Salts | |
| Li et al. | Condensed phase corrosion of P91 and DSS 2205 steels at advanced oxygen‐fired pressurized fluidized bed combustion plants | |
| Agüero et al. | Diffusion stable aluminide coatings: Behaviour under steam and oxy-fuel fire-side conditions at 650° C and accelerated diffusion tests at 900° C | |
| Abstoss et al. | Experience with 9Cr3W3CoVNbBN steel in terms of welding, creep and oxidation | |
| Sundaresan et al. | Oxidation behaviour of austenitic stainless steel 304HCu in Advanced Ultra Supercritical (AUSC) steam and the efficacy of shot-peening treatment | |
| Fontana | Perspectives on corrosion of materials | |
| Ennis et al. | Mechanisms of oxidation and the influence of steam oxidation on service life of steam power plant components | |
| Li et al. | Corrosion behavior of superalloys in high temperature gas cooled reactor in impure helium with corrosion time |