Olsen et al., 1999 - Google Patents

Nickel ferrite as inert anodes in aluminium electrolysis: Part I Material fabrication and preliminary testing

Olsen et al., 1999

Document ID
4974413472555160292
Author
Olsen E
Thonstad J
Publication year
Publication venue
Journal of Applied Electrochemistry

External Links

Snippet

Dense, sintered samples of nickel ferrite/nickel oxide–copper cermets were produced and characterized. Three compositions were chosen, each with different NiO content. A new method of powder preparation involving no use of water as dispersant resulted in a well …
Continue reading at link.springer.com (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25C—PROCESSES FOR THE ELECTROLYTIC PRODUCTION, RECOVERY OR REFINING OF METALS; APPARATUS THEREFOR
    • C25C3/00—Electrolytic production, recovery or refining of metals by electrolysis of melts
    • C25C3/06—Electrolytic production, recovery or refining of metals by electrolysis of melts of aluminium
    • C25C3/08—Cell construction, e.g. bottoms, walls, cathodes
    • C—CHEMISTRY; METALLURGY
    • C25—ELECTROLYTIC OR ELECTROPHORETIC PROCESSES; APPARATUS THEREFOR
    • C25C—PROCESSES FOR THE ELECTROLYTIC PRODUCTION, RECOVERY OR REFINING OF METALS; APPARATUS THEREFOR
    • C25C3/00—Electrolytic production, recovery or refining of metals by electrolysis of melts
    • C25C3/06—Electrolytic production, recovery or refining of metals by electrolysis of melts of aluminium
    • C25C3/14—Devices for feeding or crust breaking
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/64—Burning or sintering processes
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/01—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products based on oxide ceramics
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C32/00—Non-ferrous alloys containing at least 5% by weight but less than 50% by weight of oxides, carbides, borides, nitrides, silicides or other metal compounds, e.g. oxynitrides, sulfides whether added as such or formed in situ
    • C22C32/0084—Non-ferrous alloys containing at least 5% by weight but less than 50% by weight of oxides, carbides, borides, nitrides, silicides or other metal compounds, e.g. oxynitrides, sulfides whether added as such or formed in situ carbon or graphite as the main non-metallic constituent
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C29/00—Alloys based on carbides, oxides, nitrides, borides, or silicides, e.g. cermets, or other metal compounds, e.g. oxynitrides, sulfides
    • C22C29/12—Alloys based on carbides, oxides, nitrides, borides, or silicides, e.g. cermets, or other metal compounds, e.g. oxynitrides, sulfides based on oxides
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/80—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone of only ceramics
    • C04B41/81—Coating or impregnation
    • C04B41/85—Coating or impregnation with inorganic materials
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B41/00—After-treatment of mortars, concrete, artificial stone or ceramics; Treatment of natural stone
    • C04B41/45—Coating or impregnating, e.g. injection in masonry, partial coating of green or fired ceramics, organic coating compositions for adhering together two concrete elements
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C1/00—Making alloys

Similar Documents

Publication Publication Date Title
Olsen et al. Nickel ferrite as inert anodes in aluminium electrolysis: Part I Material fabrication and preliminary testing
Pawlek Inert anodes: an update
US6372119B1 (en) Inert anode containing oxides of nickel iron and cobalt useful for the electrolytic production of metals
GB2069529A (en) Cermet anode for electrowinning metals from fused salts
CA2768992A1 (en) Composition for making wettable cathode in aluminum smelting
Feng et al. Exploring Cu2O/Cu cermet as a partially inert anode to produce aluminum in a sustainable way
AU2791789A (en) Cermet anode compositions with high content alloy phase
CA2388908C (en) Inert anode containing oxides of nickel, iron and zinc useful for the electrolytic production of metal
Tian et al. Effect of sintering atmosphere on corrosion resistance of Ni/(NiFe2O4–10NiO) cermet inert anode for aluminum electrolysis
US4472258A (en) Anode for molten salt electrolysis
Yan et al. Aluminate spinels as sidewall linings for aluminum smelters
CA2850856C (en) Inert anodes for aluminum electrolysis and method of production thereof
Xianxi Inert Anodes for Aluminum Electrolysis
Tao et al. Oxidation and corrosion behavior of (Cu-10Cu2O)-(NiFe2O4-10NiO) cermet inert anode with interpenetrating structure
Liu et al. Microstructure and electrolysis behavior of self-healing Cu–Ni–Fe composite inert anodes for aluminum electrowinning
Li et al. Corrosion resistance of the ZnCr2O4 spinel in NaF-KF-AlF3 bath
US4495049A (en) Anode for molten salt electrolysis
XI et al. Effect of additive on corrosion resistance of NiFe2O4 ceramics as inert anodes
LAI et al. Results from 100 h electrolysis testing of NiFe2O4 based cermet as inert anode in aluminum reduction
TIAN et al. Effect of Ni content on corrosion behavior of Ni/(10NiO-90NiFe2O4) cermet inert anode
Zhu et al. Fe-30Ni-5NiO alloy as inert anode for low-temperature aluminum electrolysis
Tian et al. Effect of sintering atmosphere on corrosion resistance of NiFe2O4 ceramic in Na3AlF6–Al2O3 melt
Ma et al. Inert anode composed of Ni–Cr alloy substrate, intermediate oxide film and α-Al2O3/Au (Au–Pt, Au–Pd, Au–Rh) surface composite coating for aluminium electrolysis
SE425804B (en) PROCEDURE FOR ELECTROLYST OF A LIQUID ELECTROLYT BETWEEN AN ANOD AND A CATHOD
ZHANG et al. Effect of metallic phase content on mechanical properties of (85Cu-15Ni)/(10NiO-NiFe2O4) cermet inert anode for aluminum electrolysis