Sonomura et al., 2022 - Google Patents

Laser butt joining of Al2O3 ceramic plates metallized by friction stir welding

Sonomura et al., 2022

Document ID
4844272360882708700
Author
Sonomura H
Katagiri K
Yamaguchi T
Tanaka K
Ozaki T
Hasegawa Y
Tanaka T
Kakitsuji A
Publication year
Publication venue
Ceramics International

External Links

Snippet

Laser butt joining of Al 2 O 3 ceramic plates was successfully achieved after metallization of the plate end surfaces with Mo by friction stir welding. This pretreatment technique conveniently afforded metallized Al 2 O 3 ceramic plates with a high adhesive strength …
Continue reading at www.sciencedirect.com (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B35/00—Shaped ceramic products characterised by their composition; Ceramics compositions; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/622—Forming processes; Processing powders of inorganic compounds preparatory to the manufacturing of ceramic products
    • C04B35/64—Burning or sintering processes
    • C04B35/645—Pressure sintering
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/30—Composition of layers of ceramic laminates or of ceramic or metallic articles to be joined by heating, e.g. Si substrates
    • C04B2237/32—Ceramic
    • C04B2237/34—Oxidic
    • C04B2237/343—Alumina or aluminates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/65—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes
    • C04B2235/656—Aspects relating to heat treatments of ceramic bodies such as green ceramics or pre-sintered ceramics, e.g. burning, sintering or melting processes characterised by specific heating conditions during heat treatment
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/50—Processing aspects relating to ceramic laminates or to the joining of ceramic articles with other articles by heating
    • C04B2237/70—Forming laminates or joined articles comprising layers of a specific, unusual thickness
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B37/00—Joining burned ceramic articles with other burned ceramic articles or other articles by heating
    • C04B37/003—Joining burned ceramic articles with other burned ceramic articles or other articles by heating by means of an interlayer consisting of a combination of materials selected from glass, or ceramic material with metals, metal oxides or metal salts
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/02—Aspects relating to interlayers, e.g. used to join ceramic articles with other articles by heating
    • C04B2237/12—Metallic interlayers
    • C04B2237/126—Metallic interlayers wherein the active component for bonding is not the largest fraction of the interlayer
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2237/00—Aspects relating to ceramic laminates or to joining of ceramic articles with other articles by heating
    • C04B2237/02—Aspects relating to interlayers, e.g. used to join ceramic articles with other articles by heating
    • C04B2237/04—Ceramic interlayers
    • C04B2237/06—Oxidic interlayers
    • C04B2237/064—Oxidic interlayers based on alumina or aluminates
    • C—CHEMISTRY; METALLURGY
    • C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
    • C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
    • C04B2235/00—Aspects relating to ceramic starting mixtures or sintered ceramic products
    • C04B2235/02—Composition of constituents of the starting material or of secondary phases of the final product

Similar Documents

Publication Publication Date Title
Penilla et al. Ultrafast laser welding of ceramics
Mao et al. Effects of process parameters on interfacial characterization and mechanical properties of 316L/CuCrZr functionally graded material by selective laser melting
Srinath et al. A new approach to joining of bulk copper using microwave energy
Naidich et al. Liquid metal wettability and advanced ceramic brazing
Zhang et al. Vacuum brazing of alumina to stainless steel using femtosecond laser patterned periodic surface structure
Rohde et al. Joining of alumina and steel by a laser supported brazing process
Khirwadkar et al. Fabrication and characterization of tungsten and graphite based PFC for divertor target elements of ITER like tokamak application
Weyrich et al. Low temperature TLP bonding of Al 2 O 3–ceramics using eutectic Au–(Ge, Si) alloys
Sonomura et al. Laser butt joining of Al2O3 ceramic plates metallized by friction stir welding
Yin et al. Microstructure and mechanical strength of diffusion-bonded Ti3SiC2/Ni joints
Sonomura et al. Metallization of Al2O3 ceramic with Mg by friction stir spot welding
Okuni et al. Joining of AlN and graphite disks using interlayer tapes by spark plasma sintering
Shi et al. Reliable brazing of SiBCN ceramic and TC4 alloy using AgCuTi filler with the assist of laser melting deposited FGM layers
Bogomol et al. Hard polycrystalline eutectic composite prepared by spark plasma sintering
Li et al. Brazing YAG ceramic to Kovar alloy with Ag–Cu–Ti filler alloy: Wettability, microstructure and mechanical properties
Zhan et al. Joining of SiC ceramics by combining NITE-SiC interlayer and its thickness control
Nagatsuka et al. Characteristics of dissimilar laser-brazed joints of isotropic graphite to WC–Co alloy
Stoll et al. A novel approach of copper-ceramic-joints manufactured by selective laser melting
Luo et al. Joining of sintered silicon carbide ceramics using sodium borosilicate glass as the solder
Kidane et al. Dynamic constitutive behavior of Ti/TiB FGM under thermo-mechanical loading
Guo et al. Investigation on brazing of zirconia ceramic with Bi2O3-B2O3-Al2O3 glass
KR101039361B1 (en) Low temperature joining method between Ti/Ti-based alloys having a bonding strength higher than those of base metals
Lemus-Ruiz et al. Interface behavior of Al2O3/Ti joints produced by liquid state bonding
Lo et al. High strength alumina joints via transient liquid phase bonding
Tsakiris et al. Joining of C/SiC materials by spark plasma sintering