Emission Properties, Solubility, Thermodynamic Analysis and NMR Studies of Rare-Earth Complexes with Two Different Phosphine Oxides
Next Article in Special Issue
Coating of Carbon Fiber with Polyhedral Oligomeric Silsesquioxane (POSS) to Enhance Mechanical Properties and Durability of Carbon/Vinyl Ester Composites
Previous Article in Journal
Synthesis and Characterization of Multifunctional Chitosan- MnFe2O4 Nanoparticles for Magnetic Hyperthermia and Drug Delivery
Previous Article in Special Issue
Nanocomposites Derived from Polymers and Inorganic Nanoparticles
You seem to have javascript disabled. Please note that many of the page functionalities won't work as expected without javascript enabled.
 
 
Search for Articles:
Title / Keyword
Author / Affiliation / Email
Journal
Article Type
 
 
Advanced Search
 
Section
Special Issue
Volume
Issue
Number
Page
 
Journals
Materials
Volume 3
Issue 7
10.3390/ma3074066
materials-logo
Submit to this Journal Review for this Journal Propose a Special Issue
► Article Menu

Article Menu

share Share announcement Help format_quote Cite question_answer Discuss in SciProfiles
first_page
settings
Order Article Reprints
Font Type:
Arial Georgia Verdana
Font Size:
Aa Aa Aa
Line Spacing:
Column Width:
Background:
Review

Synthesis of Polymer—Mesoporous Silica Nanocomposites

by
Liangming Wei
,
Nantao Hu
and
Yafei Zhang
*
National Key Laboratory of Nano/Micro Fabrication Technology, Key Laboratory for Thin Film and Microfabrication of Ministry of Education, Institute of Micro and Nano Science and Technology, Shanghai Jiao Tong University, Dongchuan Road, Shanghai, China
*
Author to whom correspondence should be addressed.
Materials 2010, 3(7), 4066-4079; https://doi.org/10.3390/ma3074066
Submission received: 13 June 2010 / Accepted: 6 July 2010 / Published: 13 July 2010
(This article belongs to the Special Issue Nanocomposites of Polymers and Inorganic Particles)
Browse Figures
Graphical abstract
"> Figure 1
<p>(a) Postsynthetic functionalization and (b) co-condensation methods for organic modification of mesoporous silica.</p> "> Figure 2
<p>ATRP method for grafting polymer onto the mesoporous silica.</p> "> Figure 3
<p>RAFT method for grafting polymer onto the mesoporous silica.</p> "> Figure 4
<p>(a) The schematic illustration for emulsion polymerization of ethylene from MSN, (b) The TEM of the resulting PE/mesoporous silica composites. Reproduced with permission from [<a href="#B74-materials-03-04066" class="html-bibr">74</a>]. Copyright 2009 John Wiley &amp; Sons, Inc.</p> ">
Versions Notes

Abstract

:
Polymer nanocomposites show unique properties combining the advantages of the inorganic nanofillers and the organic polymers. The mesoporous silica nanofillers have received much attention due to their ordered structure, high surface area and ease for functionalization of the nanopores. To accommodate macromolecules, the nanopores lead to unusually intimate interactions between the polymer and the inorganic phase, and some unusual properties can be observed, when compared with nonporous fillers. Whereas many review articles have been devoted to polymer/nonporous nanofiller nanocomposites, few review articles focus on polymer/mesoporous silica nanocomposites. This review summarizes the recent development in the methods for synthesizing polymer/mesoporous silica nanocomposites based on the papers published from 1998 to 2009, and some unique properties of these composites are also described.

Graphical Abstract">
Graphical Abstract

1. Introduction

Polymer nanocomposites are a class of hybrid materials composed of an organic polymer matrix with dispersed inorganic nanofillers. Polymer nanocomposite shows unique properties, combining the advantages of the inorganic nanofillers (e.g., rigidity, thermal stability) and the organic polymers (e.g., flexibility, dielectric, ductility, and processability) [1]. The inorganic nanofillers have large surface area, leading to a dramatic increase in interfacial area [1,2,3]. These nanofillers, even at very low concentrations, can strongly change the macroscopic properties of the polymer [4]. Inorganic nanofillers include nanotubes, metal oxides (e.g., SiO2, TiO2, Al2O3, Fe3O4), layered silicates (e.g., montmorillonite, saponite), metalic nanoparticles (e.g., Au, Cu), semiconductors (e.g., PbS, CdS) [1], and mesoporous silicas, etc. Whereas many review articles have been devoted to polymer/ nonporous nanofiller nanocomposites [1,2,3], few review articles focus on polymer/mesoporous silica nanocomposites. The mesoporous silica nanofillers have received much attention due to their ordered structure, high surface area and easiness for functionalization of the nanopores. The nanopores are sufficiently porous to accommodate macromolecules which will lead to unusually intimate interactions between the polymer and the inorganic phase [2], and some unusual properties will be observed awhen compared to those nonporous fillers. This review summarizes the recent developments in the methods for synthesis of polymer/mesoporous silica nanocomposites based on the papers published from 1998 to 2009. This review will show a general route for the preparation of the nanocomposites, and then give a brief discussion of the properties of the composites.

2. Mesoporous Silica and Surface Functionalization

The first mesoporous silica, known as the M41S phase, was developed by the Mobil Oil Company in 1992. Unlike the zeolite, the M41S materials have pore diameters from approximately 2 to 10 nm [5]. This class of material has very large surface areas, ordered pore systems, and well-defined pore radius distributions [5]. The most well-known types of this class of materials include the silica solids MCM-41 (with a hexagonal arrangement of the mesopores, space group p6mm), MCM-48 (with a cubic arrangement of the mesopores, space group Ia3 d), and MCM-50 (with a laminar structure, space group p2) [5]. The use of amphiphilic triblock copolymers as a structure-directing agents has resulted in the preparation of well-ordered hexagonal mesoporous silica structures (SBA-15, SBA: Santa Barbara University) with uniform pore sizes up to approximately 30 nm [5,6]. According to the definition of IUPAC, mesoporous materials are described as materials whose pore diameters lie in the range between 2 and 50 nm [5].The composites based on the microporous silica with the pore size small than 2 nm and the macroporous silica with the pore size above 50 nm are excluded from this review.
Mesoporous silica is synthesized via polycondensation of silica species, which originate from different sources of silica (like sodium silicate, tetraethyl- (TEOS) or tetramethylorthosilica (TMOS)) in the presence of surfactants as structure-directing agents [5,6]. Many types of ionic (e.g., hexadecyltrimethylammonium bromide (CTAB)) and non-ionic surfactants (e.g., amphiphilic triblock copolymers) have been used for obtaining mesoporous silica with different pore structure and morphological characteristics [6]. To full outline the preparation of mesoporous silica, readers are referred to excellent reviews published in these years [5,6].
Both the dispersion of nanofillers in the polymer matrix and the interaction between nanofillers with the polymers is closely related to the properties of composites [4]. In order to get a well-dispersed composite with enhanced interfacial adhesion, surface modification of the nanoparticles is always necessary. Some typical silane coupling agents used for surface functionalization of mesoporous silica are shown in Table 1. Two main pathways (postsynthetic functionalization and co-condensation method) are available for the modification of the surface of mesoporous, whose mechanisms are shown in Figure 1. The readers are encouraged to read the review by Hoffmann et al. [5].
Table
Table 1. Typical silane coupling agents used for surface functionalization of mesoporous silica.
Table 1. Typical silane coupling agents used for surface functionalization of mesoporous silica.
NameStructure
3-aminopropyltriethoxysilaneH2N(CH2)3Si(OC2H5)3
3-aminopropyltrimethoxysilaneH2N(CH2)3Si(OCH3)3
VinyltriethoxysilaneCH2=CHSi(OC2H5)3
VinyltrimethoxysilaneCH2=CHSi(OCH3)3
3-isocyanatopropyltriethoxysilaneOCN(CH2)3Si(OC2H5)3
methacryloxymethyltriethoxysilaneCH2=C(CH3)COO(CH2)3Si(OC2H5)3
3-methacryloxypropyltrimethoxysilaneCH2=C(CH3)COO(CH2)3Si(OCH3)3
mercaptopropyl triethoxysilaneSH(CH2)3Si(OC2H5)3
methyltriethoxysilaneCH3Si(OC2H5)3
phenyltrimethoxysilanePhSi(OCH3)3
bis(triethoxysilylpropyl)tetrasulfane(C2H5O)3Si(CH2)3S4(CH2)3Si(OC2H5)3
3-glycidoxypropyltrimethoxysilaneCH2(O)CHCH2O(CH2)3Si(OCH3)3
Dimethyldichlorosilane(CH3)2SiCl2
Materials 03 04066 g001 1024
Figure 1. (a) Postsynthetic functionalization and (b) co-condensation methods for organic modification of mesoporous silica.
Figure 1. (a) Postsynthetic functionalization and (b) co-condensation methods for organic modification of mesoporous silica.
Materials 03 04066 g001

3. Preparation of Polymer/Mesoporous Silica Nanocomposites

3.1. Blending

Direct mixing of the mesoporous silica into the polymer is the simplest method for preparing polymer/mesoporous silica composites. The mixing can be done by melt blending and solution blending [1]. However, to fully disperse nanoparticles in the polymer matrix is a big challenge due to the strong tendency of nanoparticles to agglomerate. Surface modification of the nanofillers is a general route to enhance the dispersion of the nanofillers and to build up a strong interfacial interaction between the polymer and inorganic nanofillers [1].
Melt blending is done by mixing the mesoporous silica with the polymer above the melting point or above the glass-transition temperature (Tg) of polymers. This method is efficient and operable [1].
Pérez et al. reported styrene-butadiene rubber (SBR)/mesoporous silica nanocomposites synthesized by mixture of SBR and mesoporous silica [7,8,9]. The addition of mesoporous silica into SBR led to an increase in swelling degree, elastic modulus and Tg of the samples. It was observed that the vulcanization rate was higher for the rubber filled with mesoporous silica, which can be explained by chemical interaction between the fillers and rubbers and the penetration of the rubber chains into the mesopores [7,8,9].
Wang et al. reported that mixture of polypropylene (PP) with Na-montmorillonite (Na-MMT) and MCM-41, generating a nanocomposite filled with two different kinds of nanoparticles. In this nanocomposite, Na-MMT layers were exfoliated and the hexagonal framework structure of MCM-41was retained. The mechanical tests showed that with simultaneous nanofiller loading, the co-incorporation of Na-MMT and MCM-41 into the PP matrix gave rise to much enhanced effects than incorporating either Na-MMT or MCM-41 particles separately, due to different interfacial structure between the fillers and the matrix in the PP composite [10].
Solution blending is done by mixing mesoporous silica and polymer in a solvent. After removal of the solvent, the composites are obtained. This method brings about a good molecular level of mixing, and can overcome the limitations of melt mixing [1]. Many polymers have a good mixture with mesoporous silica using this method. However, solution blending has some disadvantages. For example, the appropriate solvent is not easy to obtain and it is necessary to remove the solvent after processing.
Most of the PEO/mesoporous silica nanocomposites were obtained using solution blending [11,12,13,14,15,16,17]. Generally, the mesoporous silica was first dispersed in solvent (e.g., acetonitrile, acetone or methanol), and then PEO and Li+ ions were added to the solution. After the mixture was stirred and the solvent removed, nanocomposites filled with mesoporous silica were obtained. Functionalization of the surface by organic groups (such as amino, 3-glycidyloxypropy groups) is usually used to improve dispersion and compatibility between PEO and mesoporous silica or to promote fast ion transfer [11,12,13,14,15,16,17]. The PEO-based nanocomposites can be used for composite polymer electrolytes. Addition of mesoporous silica nanofillers into the PEO matrix led to an increase in the ionic conductivity and lithium ion transference number of the composite electrolytes.
Nafion/mesoporous silica composite films were prepared by blending Nafion resin and mesoporous silica in dimethyl formamide (DMF) [18,19]. It was found that the Nafion composites filled with mesoporous silica have approximately 1.5 times higher proton conductivities than pure Nafion, and can display good temperature performance relative to pure Nafion and the SiO2 particle composite [18].
Encapsulation of conducting polymers in the nanopores can inhibit interchain effects, resulting in unusual propertied for the polymers [20,21,22,23,24,25]. Posudievsky et al. reported guest–host poly[2-methoxy-5-(2′-ethyl-hexyloxy)-1,4-phenylene vinylene] (MEH-PPV)/MCM-41 composites via insertion of macromolecules inside mesoporous silica in toluene or chlorobenzene [22]. The intensity of photoluminescence of the obtained composites was found to be two orders of magnitude greater than that of the neat polymer [22]. The MEH-PPV/ MCM-41 films with highly oriented and ordered 2d rectangular cmm structure were also reported by Molenkamp et al. [25]. Other conducting polymers, such as poly (2,8-dibenzothiophene-5,5-dioxide-vinylene)-alt-(2-methoxy-5-alkoxy-1,4-phenylenevinylene) (DDMA–PPVs) and poly(9,9’-dioctylfluorene) were also reported to be mixed with MCM-41 in solvent to form composites [26,27]. The results showed evidence of the molecular orbital confinement effect in the composites [26], and the resulting nanocomposite film showed dramatically increased photostability and color purity, as well as higher electroluminescence output [27].
Some studies focused on MCM-41 as an additive to enhance the gas permeability characteristics of high-performance polysulfone films. The polysulfone/mesoporous silica composite films were prepared by mixing polysulfone and mesoporous silica in solvent [28,29]. It was found that for all gases tested (N2, O2, CO2, CH4), the permeability increased in proportion to the weight percent of MCM-41 present in the film, without a loss in selectivity [28].
The poly(dimethylsiloxane)/mesoporous silica composite was prepared by Kim et al. [30]. This material can be loaded with the drug ibuprofen, which can be released from the system by ultrasound. The composites were prepared by mixing the ibuprofen-loaded mesoporous silica with poly(dimethylsiloxane) solution. Other siloxane polymer (e.g., poly(di-n-hexylsilane), poly(methylphenylsilane) based composites were also obtained using solution blending [31,32].

3.2. In Situ Polymerization

3.2.1. General Polymerization

The in situ polymerization method has many advantages, such as ease of handling and better performance of the final products [1]. Generally, this method involves the dispersion of nanofillers in monomer(s), and then bulk or solution polymerization. The nanofillers are always modified by functional groups to increase the interaction between the polymers and the nanofillers, or to get a good dispersion in the polymer matrix. For example, as-synthesized MCM-48 was modified via silylation with Cl-Si(CH3)3 to generate hydrophobic surface [33].
In 1998, Moller et al. reported poly(methyl methacrylate)(PMMA)/mesoporous silica composites synthesized by adsorption of MMA into the pores and then polymerization initiated with benzoyl peroxide. It was found that the polymers confined in the 6-35 Å diameter channels of the hosts did not show characteristic bulk behavior with respect to their glass transition temperature [34]. Recently, Zhang et al. synthesized PMMA-mesocellular foam silica nanocomposites via batch emulsion polymerization [35]. Ji et al. synthesized a propyl methacrylate functionalized mesoporous silica by condensation of TEOS and (3-trimethoxysilyl)propyl methacrylate [36] in the presence of surfactants. In situ polymerization of (3-trimethoxysilyl)propyl methacrylate among the mesoporous silica particles resulted in nanocomposites with improved mechanical and thermal properties. DSC and SEM results indicated chemical bonding and strong interactions between the polymers and fillers.
The conducting polymer/mesoporous silica composites were synthesized by in situ polymerization of the corresponding monomers, such as phenylene butadiynylene [37], pyrrole [38,39,40,41], aniline [42,43] and diphenylamine [44] in the presence of mesoporous silica. Covalent graft of polyaniline onto the pores walls of SBA-15 was done by Sasidharan et al. [45]. They first synthesized monolayer N-propylaniline functionalized mesoporous silica SBA-15 by co-condensation of N-[3-(trimethoxysilyl)propyl]aniline and TEOS in the present of templates, and then the functionalized SBA-15 was contacted with aniline gas and polymerization occurred in the presence of ammonium peroxodisulfate as oxidant. The grafted polyaniline showed an increased electrical conductivity, compared to non-grafted composites.
Preparation of the conjugated polymer PPV inside the channels of the mesoporous silica MCM-41 was described by Pattantyus-Abraham et al. [46] .In this method, MCM-41 was first converted to a basic form by deprotonating its surface hydroxy groups with a nonaqueous base (tetrabutylammonium hydroxide). The in situ polymerization was performed by the transfer of the basic solid into the solution of xylylene bis(tetrahydrothiophenium chloride).
A poly(lactic acid)-coated mesoporous silica nanosphere (PLA-MSN) was prepared by Radu et al. [47]. In this method, a mercaptopropyl-functionalized mesoporous silica (thiol-MSN) was first synthesized, and then the exterior surface of thiol-MSN was grafted by 1,5,6-epoxyhexyltriethoxysilane. After the grafted epoxyhexyl groups were converted to 5,6-hydroxyhexyl groups by acid, L-Lactide together with a catalyst (tin(II) 2-ethylhexanoate) was added, and polymerization occurred, generating PLA-MSN. PLA-MSN can serve as a fluorescence probe for selective detection of amino-containing neurotransmitters under physiological conditions and can regulate the penetration of molecules in and out of the nanoscale pores by utilizing the PLA layer as a gatekeeper [47].
Dental composites composed of mesoporous silica and resin was prepared by Praveen et al. [48]. The composites were prepared by mixing bisphenyl A glycidyl dimethacrylateand, triethylene glycol dimethacrylate and mesoporous fillers. Camphorquinone and 2-(dimethylamino) ethyl methacrylate were used as photoinitiator and accelerator, respectively. The mesoporous fillers can improve the mechanical and aging properties of experimental dental composites. A rubbery epoxy polymer/mesoporous silica composite was synthesized by Jiao et al. [49,50]. The composites were synthesized by mixture of mesoporous silica with epoxy resin and curing agents (α,ω-polyoxypropylene diamine), and then reacted under 50 or 125 °C. It was demonstrated that an ordered porous network with animopropyl functional groups was essential for polymer reinforcement, and that larger framework pores were superior to those provided by smaller pore derivatives, most likely because of more efficient polymer impregnation of the particle mesopores [49,50].
Lin et al. reported polyimide (PI)/mesoporous silica composite films prepared by condensation polymerization of dianhydride and diamine with silylated mesoporous silica particles, followed with thermal imidization [51]. Min et al. synthesized PI/SBA-15 composites [52]. In this method, different SBA-15 powders modification by octyl or amino were used. The composite films containing SBA-15 modified with amino showed an increased in the tensile strength and elongation compared with those with octyl and pristine SBA-15. The dielectric constant was significantly reduced with increasing SBA-15 modified with amino groups [52]. The same composites were also prepared by Lin et al. [53], and the low dielectric constant was also observed for the PI filled with SBA-15.
A hybrid structure based on vinyl-functionalized MCM-48 and PS was prepared through in situ polymerization of styrene monomer [54]. The results indicated that the inorganic/organic nanocomposites coupled at the nanometer level when the monomers were polymerized with the intrapore grafted vinyl groups. A considerable improvement in Young's modulus and tensile strength were observed in the composites. The PS/MCM-41 [55] and Polyethylene/MCM-41 [56,57] composites were also prepared using in situ polymerization.
Many studies have focused on synthesis of ordered mesoporous silica/poly(N-isopropylacrylamide) (PNIPAAm) copolymer composites [58,59]. The composites were formed by co-condensation of TEOS and PNIPAAm-co-poly(3-methacryloxypropyltrimethoxysilane) in the presence of surfactants [58]. Magnetic mesoporous silica/PNIPAAm composites were also prepared recently [60,61]. These composites could be applied in targeting by magnetic field and controlled release of drugs by temperature change.
A pH-responsive core-shell mesoporous silica/ [poly(methacrylic acid-co-vinyl triethoxylsilane] sphere was synthesized by Gao et al. [62]. The poly(methacrylic acid-co-vinyl triethoxylsilane) was first synthesized via a copolymerization of methacrylic acid and vinyl triethoxylsilane monomer. This polymer was grafted onto the mesoporous silica via reaction of vinyl triethoxylsilane with Si-OH groups on the mesoporous silicas.
Chu et al. reported a bifunctional ordered mesoporous TiO2-SiO2-polymer nanocomposite synthesized by the direct triblockcopolymer-templating route using TEOS as a silica source, tetraisopropyl titanate as a titanium source, phenol and formaldehyde as polymer sources and Pluronic F127 as a template [63]. In this material, the pore walls are composed of polymer, silica and Ti species, and the organic polymers and inorganic solids are homogeneously dispersed inside the pore wall.

3.3. Surface-Initiated Polymerization

The grafting strategies to construct the polymer/mesoporous silica composite are of great interesting. Generally, two routes are used to graft polymer chains on the surface of the mesoporous silica, e.g., “grafting-to” and “grafting-from” technique [1,2]. The “grafting to” method refers to the grafting of polymers onto inorganic particles. This method usually generates nongrafted chains. Additionally, the grafted polymer chains prevent attachment of the next ones and then limit the graft density [1]. The “grafting-from” technique refers to polymer chains growth from the surface of the inorganic supports. This method is feasible to design polymer/mesoporous silica composite with covalent interaction between polymer and inorganic fillers.
A stimuli-responsive mesoporous material was synthesized via surface-initiated polymerization (“grafting from” technique) [64,65]. The mesoporous silica was first covalently grafted to initiator, 1-(trichlorosilyl)-2-(m/p-(chloromethyl)phenyl)ethane. After addition of monomer NiPAAm, CuCl and bipydine, an atom transfer radical polymerization (ATRP) were performed on the surface of the mesoporous silica (Figure 2). The ATRP has also been applied to synthesize PS [66], polyacrylonitrile [66], poly(2-(dimethylamino)ethyl methacrylate) [66], PMMA [67,68] and peptide [69]/mesoporous silica composites.
The polymer/mesoporous silica composites were also synthesized via a surface-initiated living radical polymerization with a reversible addition–fragmentation chain transfer (RAFT) reaction (Figure 3). A series of PNIPAAm-coated mesoporous silica nanoparticles [70,71,72] and PS shell/mesoporous silica nanoparticle cores [73] nanospheres were synthesized.
Materials 03 04066 g002 1024
Figure 2. ATRP method for grafting polymer onto the mesoporous silica.
Figure 2. ATRP method for grafting polymer onto the mesoporous silica.
Materials 03 04066 g002
Materials 03 04066 g003 1024
Figure 3. RAFT method for grafting polymer onto the mesoporous silica.
Figure 3. RAFT method for grafting polymer onto the mesoporous silica.
Materials 03 04066 g003
We recently reported on emulsion polymerization of ethylene from vinyl functionalized mesoporous silica nanoparticles (V-MSNs) [74]. V-MSNs, with the relative surface coverage of the vinyl monolayers 74%, were synthesized via deposition of vinyl monolayers on the pore walls (Figure 4). These V-MSNs with high surface coverage are desirable for anchoring metal catalysts (A fluorinated P-O-chelated nickel catalyst in this case) onto the nanopores for ethylene aqueous polymerization due to their advantages: high surface coverage with organic groups obviating the destructive interaction of reactive catalysts with silanol groups (Si-OH) lining the framework pore walls; high density of vinyl groups making catalysts easy coordinate to the vinyl groups; hydrophobic surface contributed by vinyl groups preventing catalysts from poison by water. PE chains grew from the pores of V-MSNs, formation of stable nanocomposite lattices with solid content up to 17.3%. Our method resulted in V-MSNs well-dispersed in the PE matrix. Especially, because of a strong interaction between PE and nanoparticles, a stable V-MSNs core/PE shell structure was formed upon thermal treatment above melting temperature of the PE (Figure 4b).
Materials 03 04066 g004 1024
Figure 4. (a) The schematic illustration for emulsion polymerization of ethylene from MSN, (b) The TEM of the resulting PE/mesoporous silica composites. Reproduced with permission from [74]. Copyright 2009 John Wiley & Sons, Inc.
Figure 4. (a) The schematic illustration for emulsion polymerization of ethylene from MSN, (b) The TEM of the resulting PE/mesoporous silica composites. Reproduced with permission from [74]. Copyright 2009 John Wiley & Sons, Inc.
Materials 03 04066 g004

4. Other Methods

Some polymer/mesoporous silica composites can be synthesized by sol-gel method. Fujiwara et al. reported polymer sulfonate/mesoporous silica composites via so-gel method [75]. In this method, the polymer sulfonate (Nation and poly(sodium-styrenesulfonate)), TEOS and surfactants were simply mixed in alkaline aqueous solution to generated a composite. In this composite, organic polymers are incorporated in the framework of mesoporous silica. Madhugiri et al. electrospinned MEH-PPV/SBA-15 composite nanofibers using a dual syringe method [76]. During this electrospinning process, two syringes one containing MEH-PPV solution and the other containing SBA-15 gel were subjected to a voltage of 20 kV. An interesting result is that fluorescence of MEH-PPV was blue shifted in the composites.

5. Summary and Outline

This review summarized the recent developments in the methods to synthesize polymer/mesoporous silica nanocomposites. Most of the composites were synthesized via blending and in situ polymerization methods. Although these methods have been studied extensively, to further development new method for fabrication of mesoporous silica-based nanocomposites is still a hot topic.
The mesoporous silica-based nanocomposites are relatively new materials, which have only received attention in recent years, and many properties of these materials have not been disclosed. The study of the unique properties of these materials has received much attention and an increasing amount of papers has been published in recent year. Especially, the colloidal polymer/mesoporous silica nanospheres can load drugs and easy transfer cross the living cells [77]. The grafted polymer can be designed to control the loaded drug release in the cells. These features make colloidal polymer/mesoporous silica nanospheres an excellent candidate for next-generation drug carriers.

Acknowledgements

We thank for the financial support from the National Natural Science Foundation of China No. 20504021, 50730008, Natural Science Foundation of shanghai No.10ZR1416300, the Foundation for SMC Excellent Young Teacher in Shanghai Jiao Tong University and National Basic Research Program of China No. 2006CB300406.

References and Notes

  1. Zou, H.; Wu, S.S.; Shen, J. Polymer/silica nanocomposites: preparation, characterization, properties, and applications. Chem. Rev. 2008, 108, 3893–3957. [Google Scholar] [CrossRef] [PubMed]
  2. Mark, J.E. Some novel polymeric nanocomposites. Accounts Chem. Res. 2006, 12, 881–888. [Google Scholar] [CrossRef]
  3. Winey, K.I.; Moniruzzaman, M. Polymer nanocomposites containing carbon nanotubes. Macromolecules 2006, 39, 5194–5205. [Google Scholar] [CrossRef]
  4. Wei, L.M.; Tang, T.; Huang, B.T. Synthesis and characterization of polyethylene/clay–silica nanocomposites: a montmorillonite/silica- hybrid- supported catalyst and in situ polymerization. J. Polym. Sci. Pol. Chem. 2004, 42, 941–949. [Google Scholar] [CrossRef]
  5. Hoffmann, F.; Cornelius, M.; Morell, J.; Fröba, M. Silica-based mesoporous organic-inorganic hybrid materials. Angew. Chem. Int. Edit. 2006, 45, 3216–3251. [Google Scholar] [CrossRef]
  6. Giraldo, L.F.; López, B.L.; Pérez, L.; Urrego, S.; Sierra, L.; Mesa, M. Mesoporous silica applications. Macromol. Symp. 2007, 258, 129–141. [Google Scholar] [CrossRef]
  7. Pérez, L.D.; Giraldo, L.F.; López, B.L.; Hess, M.; de Souza Gomes, A. Reinforcing of elastomers with mesoporous silica. In Proceedings of World Polymer Congress-MACRO, Rio de Janeiro, Brazil, 16-21 July 2006; pp. 628–640.
  8. Pérez, L.D.; Giraldo, L.F.; López, B.L.; Hess, M. Reinforcing of elastomers with mesoporous silica. Macromol. Symp. 2006, 245, 628–640. [Google Scholar]
  9. López, B.L.; Pérez, L.D.; Mesa, M.; Sierra, L.; Devaux, E.; Camargo, M.; Campagne, C.; Giraud, S. Use of mesoporous silica as a reinforcing agent in rubber compounds. E-Polymer 2005, 018, 1–13. [Google Scholar]
  10. Wang, N.; Zhao, C.; Shia, Z.; Shao, Y.; Li, H.; Gao, N. Co-incorporation of MMT and MCM-41 nanomaterials used as fillers. Mater. Sci. Eng. B 2009, 157, 44–47. [Google Scholar] [CrossRef]
  11. Wang, X.L.; Mei, A.; Li, M.; Lin, Y.H.; Nan, C.W. Effect of silane-functionalized mesoporous silica SBA-15 on performance of PEO-based composite polymer electrolytes. Solid State Ionics 2006, 177, 1287–1291. [Google Scholar] [CrossRef]
  12. Xi, J.Y.; Qiu, X.P.; Zhu, W.T.; Tang, X.Z. Enhanced electrochemical properties of poly (ethylene oxide)-based composite polymer electrolyte with ordered mesoporous materials for lithium polymer battery. Micropor. Mesopor. Mat. 2006, 88, 1–7. [Google Scholar] [CrossRef]
  13. Tominaga, Y.; Igawa, S.; Asai, S.; Sumita, M. Ion-conductive properties of mesoporous silica-filled composite polymer electrolytes. Electrochim. Acta 2005, 50, 3949–3954. [Google Scholar] [CrossRef]
  14. Kim, S.; Hwang, E.J.; Park, S.J. An experimental study on the effect of mesoporous silica addition on ion conductivity of poly (ethylene oxide) electrolytes. Curr. Appl. Phys. 2008, 8, 729–731. [Google Scholar] [CrossRef]
  15. Kao, H.M.; Tsai, Y.Y.; Chao, S.W. Functionalized mesoporous silica MCM-41 in poly(ethylene oxide)-based polymer electrolytes: NMR and conductivity study. Solid State Ionics 2005, 176, 1261–1270. [Google Scholar] [CrossRef]
  16. Xia, J.Y.; Qiua, X.P.; Ma, X.M.; Cui, M.Z.; Yang, J.; Tang, X.Z.; Zhu, W.T; Chen, L.Q. Composite polymer electrolyte doped with mesoporous silica SBA-15 for lithium polymer battery. Solid State Ionics 2005, 176, 1249–1260. [Google Scholar] [CrossRef]
  17. Xi, J.Y.; Tang, X.J. Enhanced lithium ion transference number and ionic conductivity of composite polymer electrolyte doped with organic–inorganic hybrid P123@SBA-15. Chem. Phys. Lett. 2004, 400, 68–73. [Google Scholar] [CrossRef]
  18. Tominaga, Y.; Hong, I.C.; Asai, S.; Sumita, M. Proton conduction in Nafion composite membranes filled with mesoporous silica. J. Power Sources 2007, 171, 530–534. [Google Scholar] [CrossRef]
  19. Jin, Y.G.; Qiao, S.Z.; Zhang, L.; Xua, Z.P.; Smarta, S; da Costa, J.C.D.; Lu, G.Q. Novel Nafion composite membranes with mesoporous silica nanospheres as inorganic fillers. J. Power Sources 2008, 185, 664–669. [Google Scholar] [CrossRef]
  20. Cardin, D.J. Encapsulated conducting polymer. Adv. Mater. 2002, 14, 553. [Google Scholar] [CrossRef]
  21. Xi, H.A.; Wang, B.H.; Zhang, Y.B.; Qian, X.F.; Yin, J.; Zhu, Z.K. Spectroscopic studies on conjugated polymers in mesoporous channels: influence of polymer side-chain length. J. Phys. Chem. Solids 2003, 64, 2451–2455. [Google Scholar] [CrossRef]
  22. Posudievsky, Y.O.; Telbiza, G.M.; Rossokhaty, V.K. Effect of solvent nature on liquid-phase self-assembly of MEH-PPV/ MCM-41 guest–host composites. J. Mater. Chem. 2006, 16, 2485–2489. [Google Scholar] [CrossRef]
  23. Cadby, A.J.; Tolbert, S.H. Controlling optical properties and interchain interactions in semiconducting polymers by encapsulation in periodic nanoporous silicas with different Pore Sizes. J. Phys. Chem. B. 2005, 109, 17879–17886. [Google Scholar] [CrossRef] [PubMed]
  24. Wu, J.J.; Gross, A.F.; Tolbert, S.H. Host-guest chemistry using an oriented mesoporous host: alignment and Iisolation of a semiconducting polymer in the nanopores of an ordered silica matrix. J. Phys. Chem. B. 1999, 103, 2374–2384. [Google Scholar] [CrossRef]
  25. Molenkamp, W.C.; Watanabe, M.; Miyata, H.; Tolbert, S.H. Highly polarized luminescence from optical quality films of a semiconducting polymer aligned within oriented mesoporous silica. J. Am. Chem. Soc. 2004, 126, 4476–4477. [Google Scholar] [CrossRef] [PubMed]
  26. Wang, B.H.; Xi, H.A.; Yin, J.; Qian, X.F.; Zhu, Z.K. Molecular orbital confinement effect of mesoporous silica of MCM-41 on conjugated polymer. Synt. Met. 2003, 139, 187–190. [Google Scholar] [CrossRef]
  27. Park, J.H.; Kim, S.; Kim, Y.C.; Park, O.O. Polymer/nanoporous silica nanocomposite blue-light-emitting diodes. Nanotechnology 2005, 16, 1793–1797. [Google Scholar] [CrossRef]
  28. Reid, B.D.; Alberto Ruiz-Trevino, F.; Musselman, I.H.; Balkus, K.J.; Ferraris, J.P. Gas permeability properties of polysulfone membranes containing the mesoporous molecular sieve MCM-41. Chem. Mater. 2001, 13, 2366. [Google Scholar] [CrossRef]
  29. Zornoza, B.; Irusta, S.; Tellez, C.; Coronas, J. Mesoporous silica sphere-polysulfone mixed matrix membranes for gas separation. Langmuir 2009, 25, 5903–5909. [Google Scholar] [CrossRef] [PubMed]
  30. Kim, H.J.; Matsuda, H.; Zhou, H.; Honma, I. Ultrasound-triggered smart drug release from a poly(dimethylsiloxane)–mesoporous silica composite. Adv. Mater. 2006, 18, 3083–3088. [Google Scholar] [CrossRef]
  31. Bose, A.; Gilpin, R.K.; Jaroniec, M. Adsorption and thermogravimetric studies of mesoporous silica coated with siloxane polymer. J. Colloid Interf. Sci. 2001, 240, 224–228. [Google Scholar] [CrossRef]
  32. Ostapenko, N.; Kotova, N.; Telbiz, G.; Suto, S. Size effect in the fluorescence spectra of polysilanes embedded in mesoporous materials. Low. Temp. Phys. 2004, 30, 494. [Google Scholar] [CrossRef]
  33. He, J.; Shen, Y.B.; Yang, J.; Evans, D.G.; Duan, X. Nanocomposite structure based on silylated MCM-48 and poly(vinyl acetate). Chem. Mater. 2003, 15, 3894–3902. [Google Scholar]
  34. Moller, K.; Bein, T.; Fischer, R.X. Entrapment of PMMA polymer strands in micro- and mesoporous materials. Chem. Mater. 1998, 10, 1841–1852. [Google Scholar] [CrossRef]
  35. Zhang, F.A.; Lee, D.K.; Pinnavaia, T.J. PMMA-mesocellular foam silica nanocomposites prepared through batch emulsion polymerization and compression molding. Polymer 2009, 50, 4768–4774. [Google Scholar] [CrossRef]
  36. Ji, X.L.; Hampsey, J.E.; Hu, Q.Y.; He, J.B.; Yang, Z.Z.; Lu, Y.F. Mesoporous silica-reinforced polymer nanocomposites. Chem. Mater. 2003, 15, 3656–3662. [Google Scholar] [CrossRef]
  37. Lin, V.S.Y.; Radu, D.R.; Han, M.K.; Deng, W.; Kuroki, S.; Shanks, B.H.; Pruski, M. Oxidative polymerization of 1, 4-diethynylbenzene into highly conjugated poly (phenylene butadiynylene) within the channels of surface-functionalized mesoporous silica and alumina materials. J. Am. Chem. Soc. 2002, 124, 9040–9041. [Google Scholar] [CrossRef] [PubMed]
  38. Nakayama, M.; Yano, J.; Nakaoka, K.; Ogura, K. Electrodeposition of composite films consisting of polypyrrole and mesoporous silica. Synthetic. Met. 2002, 128, 57–62. [Google Scholar] [CrossRef]
  39. Cheng, Q.L.; Pavlinek, V.; Lengalova, A.; Li, C.Z.; Belza, T.; Saha, P. Electrorheological properties of new mesoporous material with conducting polypyrrole in mesoporous silica. Micropor. Mesopor. Mater. 2006, 94, 193–199. [Google Scholar] [CrossRef]
  40. Cheng, Q.L.; Pavlinek, V.; Li, C.Z.; Lengalova, A.; He, Y.; Saha, P. Synthesis and characterization of new mesoporous material with conducting polypyrrole confined in mesoporous silica. Mater. Chem. Phys. 2006, 98, 504–508. [Google Scholar] [CrossRef]
  41. Cheng, Q.L.; Pavlinek, V.; Lengalova, A.; Li, C.; He, Y.; Saha, P. Conducting polypyrrole confined in ordered mesoporous silica SBA-15 channels: preparation and its electrorheology. Micropor. Mesopor. Mater. 2006, 93, 263–269. [Google Scholar] [CrossRef]
  42. Li, N.; Li, X.T.; Geng, W.C.; Zhang, T.; Zuo, Y.; Qiu, S.L. Synthesis and humidity sensitivity of conducting polyaniline in SBA-15. J. Appl. Polym. Sci. 2004, 93, 1597–1601. [Google Scholar] [CrossRef]
  43. Fang, F.F.; Choi, H.J.; Ahn, W.S. Electroactive response of mesoporous silica and its nanocomposites with conducting polymers. Compos. Sci. Technol. 2009, 69, 2088–2092. [Google Scholar] [CrossRef]
  44. Showkata, A.M.; Lee, K.P.; Gopalan, A.I.; Kim, M.S.; Choic, S.H.; Kang, H.D. A novel self-assembly approach to form tubular poly(diphenylamine) inside the mesoporous silica. Polymer 2005, 46, 1804–1812. [Google Scholar] [CrossRef]
  45. Sasidharan, M.; Mal, N.K.; Bhaumik, A. In-situ polymerization of grafted aniline in the channels of mesoporous silica SBA-15. J. Mater. Chem. 2007, 17, 278–283. [Google Scholar] [CrossRef]
  46. Pattantyus-Abraham, A.G.; Wolf, M.O. A PPV/MCM-41 composite material. Chem. Mater. 2004, 16, 2180–2186. [Google Scholar] [CrossRef]
  47. Radu, D.R.; Lai, C.Y.; Wiench, J.W.; Pruski, M.; Lin, V.S.Y. Gatekeeping layer effect: A poly(lactic acid)-coated mesoporous silica nanosphere-based fluorescence probe for detection of amino-containing neurotransmitters. J. Am. Chem. Soc. 2004, 126, 1640–1641. [Google Scholar] [CrossRef] [PubMed]
  48. Praveen, S.; Sun, Z.F.; Xu, J.G.; Patel, A.; Wei, Y.; Ranade, R.; Baran, G. Compression and aging properties of experimental dental composites containing mesoporous silica as fillers. Mol. Cryst. Liq. Crys. 2006, 448, 223–231. [Google Scholar] [CrossRef]
  49. Jiao, J.; Sun, X.; Pinnavaia, T.J. Reinforcement of a rubbery epoxy polymer by mesostructured silica and organosilica with wormhole framework structures. Adv. Funct. Mater. 2008, 18, 1067–1074. [Google Scholar] [CrossRef]
  50. Jiao, J.; Sun, X.; Pinnavaia, T.J. Mesostructured silica for the reinforcement and toughening of rubbery and glassy epoxy polymers. Polymer 2009, 50, 983–989. [Google Scholar] [CrossRef]
  51. Lin, B.P.; Tang, J.; Liu, H.J.; Sun, Y.M.; Yuan, C.W. Structure and infrared emissivity of polyimide/mesoporous silica composite films. J. Solid. State. Chem. 2005, 178, 650. [Google Scholar] [CrossRef]
  52. Min, C.K.; Wu, T.B.; Yang, W.T.; Chen, C.L. Functionalized mesoporous silica/polyimide nanocomposite thin films with improved mechanical properties and low dielectric constant. Compos. Sci. Technol. 2008, 68, 1570–1578. [Google Scholar] [CrossRef]
  53. Lin, J.J; Wang, X.D. Novel low-k polyimide/mesoporous silica composite films: Preparation, microstructure, and properties. Polymer 2007, 48, 318–329. [Google Scholar] [CrossRef]
  54. He, J; Shen, Y.B; Evans, D.G. A nanocomposite structure based on modified MCM-48 and polystyrene. Micropor. Mesopor. Mater. 2008, 109, 73–83. [Google Scholar] [CrossRef]
  55. Pérez, L.D.; López, J.F.; Orozco, V.H.; Kyu, T.; López, B. L. Effect of the chemical characteristics of mesoporous silica MCM-41 on morphological, thermal, and rheological properties of composites based on polystyrene. J. Appl. Polym. Sci. 2008, 111, 2229–2237. [Google Scholar] [CrossRef]
  56. Wang, N.; Shi, Z.X.; Zhang, J.; Wang, L. The influence of modification of mesoporous silica with polyethylene via In situ Ziegler–Natta polymerization on PE/MCM-41 nanocomposite. J. Compos. Mater. 2008, 42, 1151. [Google Scholar] [CrossRef]
  57. Campos, J.M.; Lourenco, J.P.; Perez, E; Cerrada, M.L; Ribeiro, M.R. Self-reinforced hybrid polyethylene/MCM-41 nanocomposites: In-situ polymerisation and effect of MCM-41 content on rigidity. J. Nanosci. Nanotechnol. 2009, 9, 3966–3974. [Google Scholar]
  58. Fu, Q.; Rama Rao, G.V.; Ward, T.L.; Lu, Y.F.; Lopez, G.P. Thermoresponsive Transport through Ordered mesoporous silica/PNIPAAm copolymer membranes and microspheres. Langmuir 2007, 23, 170–174. [Google Scholar] [CrossRef] [PubMed]
  59. Tian, B.S.; Yang, C. Temperature-responsive nanocomposites based on mesoporous SBA-15 silica and PNIPAAm: synthesis and characterization. J. Phys. Chem. C. 2009, 113, 4925–4931. [Google Scholar] [CrossRef]
  60. Zhu, Y.F.; Kaskel, S.; Ikoma, T.; Hanagata, N. Magnetic SBA-15/poly(N-isopropylacrylamide) composite: Preparation, characterization and temperature-responsive drug release property. Micropor. Mesopor. Mater. 2009, 123, 107–112. [Google Scholar] [CrossRef]
  61. Liu, C.; Guo, J.; Yang, W.; Hu, J.; Wang, C.; Fu, S. Magnetic mesoporous silica microspheres with thermo-sensitive polymer shell for controlled drug release. J. Mater. Chem. 2009, 19, 4764–4770. [Google Scholar] [CrossRef]
  62. Gao, Q.; Xu, Y.; Wu, D.; Sun, Y.; Li, X.A. PH-responsive drug release from polymer-coated mesoporous silica spheres. J. Phys. Chem. C. 2009, 113, 12753–12758. [Google Scholar] [CrossRef]
  63. Chu, H.Q.; Yu, C.; Wan, Y.; Zhao, D.Y. Synthesis of ordered mesoporous bifunctional TiO2-SiO2-polymer nanocomposites. J. Mater. Chem. 2009, 19, 8610–8618. [Google Scholar] [CrossRef]
  64. Fu, Q.; Rama Rao, G.V.; Ista, L.K.; Wu, Y.; Andrzejewski, B.P.; Sklar, L.A.; Ward, T.L; López, G.P. Control of molecular transport through stimuli-responsive ordered mesoporous materials. Adv. Mater. 2003, 15, 1262. [Google Scholar] [CrossRef]
  65. Zhou, Z.Y.; Zhu, S.M.; Zhang, D. Grafting of thermo-responsive polymer inside mesoporous silica with large pore size using ATRP and investigation of its use in drug release. J. Mater. Chem. 2007, 17, 2428–2433. [Google Scholar] [CrossRef]
  66. Kruk, M.; Dufour, B.; Celer, E.B.; Kowalewski, T.; Jaroniec, M.; Matyjaszewski, K. Grafting monodisperse polymer chains from concave surfaces of ordered mesoporous silicas. Macromolecules 2008, 41, 8584–8591. [Google Scholar] [CrossRef]
  67. Audouin, F.; Blas, H.; Pasetto, P.; Beaunier, P.; Boissière, C.; Sanchez, C.; Save, M.; Charleux, B. Structured hybrid nanoparticles via surface-initiated ATRP of methyl methacrylate from ordered mesoporous silica. Macromol. Rapid Comm. 2008, 29, 914–921. [Google Scholar] [CrossRef]
  68. Anwander, R.; Nagl, I.; Zapilko, C.; Widenmeyer, M. Methyl methacrylate polymerization at samarium(II)-grafted MCM-41. Tetrahedron 2003, 59, 10567–10574. [Google Scholar] [CrossRef]
  69. Lunn, J.D.; Shantz, D.F. Peptide brush-ordered mesoporous silica nanocomposite materials. Chem. Mater. 2009, 21, 3638–3648. [Google Scholar] [CrossRef]
  70. Chung, P.W.; Kumar, R.; Pruski, M.; Lin, V.S.Y. Temperature responsive solution partition of organic–inorganic hybrid poly(N-isopropylacrylamide)-coated mesoporous silica nanospheres. Adv. Funct. Mater. 2008, 18, 1390–1398. [Google Scholar] [CrossRef]
  71. Hong, C.Y.; Li, X.; Pan, C.Y. Smart core-shell nanostructure with a mesoporous core and a stimuli-responsive nanoshell synthesized via surface reversible addition-fragmentation chain transfer polymerization. J. Phys. Chem. C. 2008, 112, 15320–15324. [Google Scholar] [CrossRef]
  72. Roohi, F.; Titirici, M.M. Thin thermo-responsive polymer films onto the pore system of chromatographic beads via reversible addition–fragmentation chain transfer polymerization. New J. Chem. 2008, 32, 1409–1414. [Google Scholar] [CrossRef]
  73. Hong, C.Y.; Li, X.; Pan, C.Y. Grafting polymer nanoshell onto the exterior surface of mesoporous silica nanoparticles via surface reversible addition-fragmentation chain transfer polymerization. Euro. Polym. J. 2007, 43, 4114–4122. [Google Scholar] [CrossRef]
  74. Wei, L.M.; Zhang, Y.F. Emulsion polymerization of ethylene from mesoporous silica nanoparticles with vinyl functionalized monolayers. J. Polym. Sci. Part A: Polym. Chem. 2009, 47, 1393–1402. [Google Scholar] [CrossRef]
  75. Fujiwara, M.; Shiokawa, K.; Zhu, Y.C. Preparation of mesoporous silica/polymer sulfonate composite materials. J.Mol. Catal. A: Chem 2007, 264, 153–161. [Google Scholar] [CrossRef]
  76. Madhugiri, S.; Dalton, A.; Gutierrez, J.; Ferraris, J. P.; Balkus, K.J., Jr. Electrospun MEH-PPV/SBA-15 composite nanofibers using a dual syringe method. J. Am. Chem. Soc. 2003, 125, 14531–14538. [Google Scholar] [CrossRef] [PubMed]
  77. Zhang, L. X.; Zhu, M.; Guo, L. M.; Li, L.; Shi, J.L. Bilirubin adsorption property of mesoporous silica and amine-grafted mesoporous silica. Nano-Micro Lett. 2009, 1, 14–18. [Google Scholar]

Share and Cite

MDPI and ACS Style

Wei, L.; Hu, N.; Zhang, Y. Synthesis of Polymer—Mesoporous Silica Nanocomposites. Materials 2010, 3, 4066-4079. https://doi.org/10.3390/ma3074066

AMA Style

Wei L, Hu N, Zhang Y. Synthesis of Polymer—Mesoporous Silica Nanocomposites. Materials. 2010; 3(7):4066-4079. https://doi.org/10.3390/ma3074066

Chicago/Turabian Style

Wei, Liangming, Nantao Hu, and Yafei Zhang. 2010. "Synthesis of Polymer—Mesoporous Silica Nanocomposites" Materials 3, no. 7: 4066-4079. https://doi.org/10.3390/ma3074066

APA Style

Wei, L., Hu, N., & Zhang, Y. (2010). Synthesis of Polymer—Mesoporous Silica Nanocomposites. Materials, 3(7), 4066-4079. https://doi.org/10.3390/ma3074066

Article Metrics

Back to TopTop