Open AccessArticle

A Sensitive A₃B Porphyrin Nanomaterial for CO₂ Detection

Eugenia Fagadar-Cosma

^1,*

Dana Vlascici

^1,2,

Gheorghe Fagadar-Cosma

³,

Anca Palade

¹,

Anca Lascu

¹,

Ionela Creanga

¹,

Mihaela Birdeanu

^1,4,

Rodica Cristescu

⁵

and

Ileana Cernica

⁶

Department of Organic Chemistry, Institute of Chemistry Timisoara of Romanian Academy, M. Viteazul Ave, No. 24, 300223 Timisoara, Romania

Department of Chemistry, Chemistry-Biology-Geography Faculty, West University of Timisoara, Pestalozzi Street, No. 16, 300115 Timisoara, Romania

CAICAM Department, Faculty of Industial Chemistry and Environmental Engineering, Politehnica University, V. Parvan Bv., No. 6, 300223 Timisoara, Romania

⁴

National Institute for Research and Development in Electrochemistry and Condensed Matter, P. Andronescu Street, No. 1, 300224 Timisoara, Romania

⁵

Lasers Department, National Institute for Lasers, Plasma & Radiation Physics, P.O. Box MG-36, Magurele, 077125 Bucharest, Romania

⁶

National R&D Institute for Microtechnology, Erou Iancu Nicolae Street, No. 126 A, Voluntari, 077190 Bucharest, Romania

Author to whom correspondence should be addressed.

Molecules 2014, 19(12), 21239-21252; https://doi.org/10.3390/molecules191221239

Submission received: 4 November 2014 / Revised: 11 December 2014 / Accepted: 11 December 2014 / Published: 17 December 2014

(This article belongs to the Section Molecular Diversity)

Download

Browse Figures

Figure 1
Structure of 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin. "> Figure 2
The UV-vis spectrum of 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin. "> Figure 3
The superposed UV-vis spectra of 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin, in methanol, pH = 5.5 (blue line), and in methanol-water systems with different amounts of HCl 0.1 N, curves 1 to 4. In detail curve 1. "> Figure 4
Excitation and emission spectra of 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin, in THF, at λem = 603 nm (for excitation) and λex = 420 nm (for emission). "> Figure 5
2D AFM image of 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin (2.2 × 2.2 µm) from THF by drop-casting: (a) single and (b) multiple deposition. "> Figure 6
2D AFM image (2.2 × 2.2 µm) of porphyrin (PyTDMeOPP) ring architectures—single deposition from CHCl3. "> Figure 7
Dependence between increasing concentration of CO2 in water and the intensity of absorption of (PyTDMeOPP). "> Figure 8
2D AFM images of ring aggregates of porphyrin in THF/water, before CO2 introduction. "> Figure 9
2D AFM images of ring aggregates of porphyrin (PyTDMeOPP) in THF/water, after 15 min of CO2 introduction. ">

Versions Notes

Abstract

The present report deals with the tailoring, preparation and characterization of novel nanomaterials sensitive to CO₂ for use in detection of this gas during space habitation missions. A new nanostructured material based on mixed substituted asymmetrical A₃B porphyrin: 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)-porphyrin (PyTDMeOPP) was synthesized and characterized by ¹H-NMR, FT-IR, UV-vis, fluorescence, MS, HPLC and AFM. Introducing one pyridyl substituent in the 5-meso-position of porphyrin macrocycle confers some degree of hydrophilicity, which may cause self-assembly properties and a better response to increased acidity. The influence of pH and nature of the solvent upon H and J aggregates of the porphyrin are discussed. Porphyrin aggregation at the air–THF interface gave a triangular type morphology, randomly distributed but uniformly oriented. When deposition was made by multiple drop-casting operations, a network of triangles of uniform size was created and a porous structure was obtained, being reorganized finally in rings. When the deposition was made from CHCl₃, ring structures ranging in internal diameter from 300 nm to 1 µm, but with the same width of the corona circular of approx. 200 nm were obtained. This porphyrin-based material, capable of generating ring aggregates in both THF and CHCl₃, has been proven to be sensitive to CO₂ detection. The dependence between the intensity of porphyrin UV-vis absorption and the concentration of CO₂ has a good correlation of 98.4%.

Keywords:

asymmetric A₃B porphyrins; UV-vis spectroscopy; sensitivity to CO₂; self-assembling; AFM

1. Introduction

Spectrophotometric and colorimetric microsensors for an easy and friendly detection of the air quality (i.e., detection of CO, NO_x and high level of CO₂ and low level of O₂) have attracted much interest in the last decade. Optical CO₂ sensors based on color changes of the pH indicator dye α-naphthol-phthalein coupled with the fluorescence of tetraphenylporphyrin attached to a polystyrene layer have been intensively studied on different substrates, but especially on ethyl cellulose layers [1,2,3,4,5]. The response times of the sensing film in all investigated cases were less than 5.0 s for switching from nitrogen to CO₂, and for switching from CO₂ to nitrogen. Besides nitrogen, the authors also used argon as neutral gas. The detection of CO₂ in water was also attempted using the same combination [6].

Another reported porphyrin derivative used in combination with α-naphtholphthalein as colorimetric pH indicator in order to detect CO₂ is a platinum porphyrin dye (Pt-tetrakispentafluorophenylporphyrin) incorporated in a plastic matrix together with a phase transfer agent tetraoctyl- or cetyltrimethyl-ammonium hydroxide [7]. CO₂ sensors which use an inner filter quenching effect were also described. One such system consisted of a phosphorescent platinum octaetylporphyrin and a pH-sensitive dye in poly(vinylidene chloride-co-vinyl chloride-ethyl cellulose) thin films or microparticles with low permeability to oxygen [8]. A portable instrument to measure CO₂ in the gas phase [9] based on a solid-state sensor film, where the platinum octaethylporphyrin complex is quenched by the deprotonated form of naphtholphthalein [10] was also reported.

Sensing of other toxic gases such as NO₂, NH₃, CO and H₂S has been performed using Langmuir-Blodgett thin films of several Co, Fe, Cu, Ni metalloporphyrins, showing that the complexed inner metal is important for the selectivity of the sensor.

New sensors based on Mn(III)-porphyrins and single wall carbon nanotubes (SWCNTs) embedded in barium stearate multilayers realized by the Langmuir-Blodgett (LB) technique have been tested for sensitivity to NO₂ gas. A sensitive effect of the sensor for NO₂ gas was demonstrated. The coverage of the sensor with a metalloporphyrin (Mn) leads to strong enhancement of the sensitive effect to NO₂, at a few ppm, but the proposed material was not sensitive to the other toxic investigated gases, such as CO and CH₄ besides, the selectivity was preserved both around room temperature and at higher operating temperatures (up to 200 °C) [11].

The importance of the morphology and topography of the thin film was put into evidence in another experiment, based on the same Mn(III)-porphyrin, but realized by the MAPLE technique. In this case the thin film was sensitive to neurotransmitters [12].

A dimer derivative of Ni(II)-octaethylporphyrin also deposited by the LB technique was selectively sensitive to NO gas in the presence of other interfering gases such as NH₃ and CO. A few of these sensors are resistive ones [13].

Polypyrrole was chemically functionalized with 5,10,15,20-tetraphenyl-21H,23H-porphyrin iron(III) chloride (FeTPPCl) with special interest in detecting noxious carbon monoxide (CO) gas at ppm levels. The response of the material on the resistive sensor towards CO was quite fast and reversible [14,15].

The sodium salt of [5,10,15,20-tetra(4-sulphonatophenyl)-porphyrinato]zinc deposited on ZnO rods is sensitive to ppm concentrations of amines and alcohols [16]. The electron transport characteristics of Fe-porphyrin (FeP) and O₂ adsorbed Fe-porphyrin (FeP-O₂) have been investigated by the nonequilibrium Green’s function approach in combination with density functional theory. Recently, chlorophyll fluorescence was used for monitoring CO₂ uptake by earth vegetation [17].

2. Results and Discussion

This work is focused on the preparation and further applications of 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin (PyTDMeOPP) for the easy detection of CO₂ gas in space habitable areas. The structure of (PyTDMeOPP) is presented in Figure 1.

Figure 1. Structure of 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin.

2.1. IR Spectrum of the A₃B Porphyrin

The main features of the IR spectrum of the A₃B porphyrin are the weak band located at 3311 cm⁻¹ assigned to the ν N-H vibration, probably due to the fact that NH groups are involved in intramolecular H-bonding, and the sharp and intense band at 1232 cm⁻¹ corresponding to C-O-CH₃ vibrations.

2.2. ¹H-NMR Spectrum of the Porphyrin (PyTDMeOPP)

The ¹H-NMR spectrum of the porphyrin (PyTDMeOPP) presents a signal corresponding to the internal NH pyrrolic protons that appears as broad singlet at −2.78 ppm and the signals for β-pyrrolic protons, which are located at 8.91 and 8.81 ppm. The signals for the 3,5-pyridyl protons are to be seen as a singlet at 8.20 ppm and those for 5-phenyl as a multiplet at 7.78–7.80. As expected, two singlet signals located at 4.18 and 3.99 ppm are attributed to the 4-methoxy- and 3-methoxyphenyl groups, respectively.

2.3. UV-Vis Spectrum of Compound (PyTDMeOPP)

The UV-vis spectrum of compound (PyTDMeOPP) displays the typical very intense Soret band accompanied by four Q-bands in the visible region (Figure 2). The Soret band, located at 423 nm, is attributed to the transition from a_1u (π) → e_g* (π) and the other four absorption maxima around 516, 553, 593 and 650 nm are assigned to the Q bands corresponding to a_2u (π) → e_g* (π) transitions. The UV-vis spectrum shows etio type shape, in which the intensity of the Q bands are decreasing in the order QIV > QIII > QII > QI.

Figure 2. The UV-vis spectrum of 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin.

2.4. The Influence of the Acid Environment on UV-Vis Spectra

In order to be further used for CO₂ sensing, 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)-porphyrin was subjected to some tests regarding its behavior in acidic environments. It is already known that most of the porphyrin bases manifest pronounced aggregation in acidic aqueous solutions, accompanied by changes regarding the position, the shape and the intensity of the main absorption bands [18].

When the acidity is increased to pH = 3 and lower, more additional protons are bonded both to the nitrogen atoms in the center of porphyrin ring, but also on the external pyridyl group. A high ionic strength causes a decrease of the monomer absorption Soret band situated around 420 nm, eventually reducing it to a pronounced shoulder. These changes in spectral shape (Figure 3) are associated with significant increase of the intensity of the QI band, but also with generation of a new band located around 970 nm. The QI band is hyperchromic and also bathochromically shifted from 650 nm (pH = 5) to 690 nm. Besides, the introduction of electron donating groups at the meso-positions raises the energy of the a_2u orbital by increasing its electron density and leads to the red shift of the Q (0,0) band [19], as confirmed in the UV-vis experiments.

With the increased ionic strength of the solution, a clear tendency to form J-aggregates is noticed. The band centered at 420 nm can be unequivocally assigned to the monomer and J-aggregates are characterized by a broadened red-shifted absorption band [20,21,22].

Figure 3. The superposed UV-vis spectra of 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin, in methanol, pH = 5.5 (blue line), and in methanol-water systems with different amounts of HCl 0.1 N, curves 1 to 4. In detail curve 1.

2.5. Excitation and Emission Spectra

From the excitation spectra (Figure 4), recorded at a higher concentration of porphyrin (10⁻⁴ mol/L), it is to be noted that the main peak is split into two peaks displaying a red-shift (433 nm) or a blue-shift (409 nm). This is a well-known behavior of porphyrins that initiate molecular association processes (J and H type aggregation) by increasing the concentration of the solution over 10⁻⁶ mol/L. The shape of the excitation spectra is in agreement with the exciton theory, which predicts that the excited-state energy level of a monomeric porphyrin splits in the course of aggregation. The hypsochromic shifted band located at 409 nm puts into evidence the generation of sandwich-type aggregates (H-aggregates) while the bathochromic shifted branch located at 433 nm is attributed to a side-by-side association process, due to generation of J-aggregates.

The emission spectra of bare porphyrin 2 in THF exhibited two maxima, a strong and broad Q_x (0,0) fluorescence band shifting from 656 nm and a weaker emission band situated at 725 nm, assigned to Q_x (0,1) transition.

Figure 4. Excitation and emission spectra of 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin, in THF, at λ_em = 603 nm (for excitation) and λ_ex = 420 nm (for emission).

2.6. Atomic Force Microscopy Studies

It is unanimously accepted that the porphyrin macrocycle represents a favorite candidate for self-assembly and this can be realized by hydrogen bonding, π-π stacking interactions or hydrophobic effects and also by weak Van der Waals forces [21,23]. Besides, as a function of their tailored amphiphilic structure, A₃B porphyrins can influence the size and shape of the nanoparticles [24,25] generating highly organized nanostructures [26,27,28].

Regarding 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin, the initially formed triangular sandwich structures serve as building blocks for further aggregation into ring architectures (Figure 5 and Figure 6). The samples were formed by THF (or CHCl₃) evaporation from a solution containing the porphyrin on silica plates. The orientation and aggregation of porphyrin (PyTDMeOPP) at the air–THF and air–CHCl₃ interfaces was studied.

Aggregation of porphyrin (PyTDMeOPP) at the air–THF interface gave triangular type morphology (2D AFM images, Figure 5a,b) with size in the range from 400 to 500 nm. These homogeneous triangles are randomly distributed, but uniformly oriented and very stable. If the deposition was made by multiple drop-casting operations, followed by evaporation of the solvent, a network of triangles of uniform size have been created by means of J type aggregation and a porous structure was obtained. Finally, this porous network is reorganized in more densely distributed ring type structures, similar with that presented in Section 2.8 (Figure 8), remaining stable even in its dry state on silica pure plates.

Figure 5. 2D AFM image of 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin (2.2 × 2.2 µm) from THF by drop-casting: (a) single and (b) multiple deposition.

Figure 6. 2D AFM image (2.2 × 2.2 µm) of porphyrin (PyTDMeOPP) ring architectures—single deposition from CHCl₃.

The nature of the solvent influences the architecture (Figure 6); when the deposition was made from CHCl_3, ring structures ranging in their internal diameter from 300 nm to 1 µm, but with the same width of the corona circular of approx. 200 nm were obtained.

2.7. Preliminary Tests of Porphyrin (PyTDMeOPP) for CO₂ Detection

Recently, optical CO₂ sensors based on the absorbance of pH indicator dye have been developed [4]. In our particular case, an optical CO₂ sensor with the combination of colorimetric change of pH indicator dye will be developed. In order to decide if 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin is appropriate for the formulation of CO₂ sensors, some preliminary tests have been done to see its absorption intensity response to CO₂ exposure and to establish the basis of an UV-vis sensor based on porphyrin for CO₂ in water. A 1/1 THF/water solution of 3 × 10⁻⁵ mol/L of porphyrin (PyTDMeOPP), in a 50 mL vessel was prepared. A CO₂ gas stream was produced by controlling the flow rates of CO₂ and nitrogen gases. All the experiments are carried out at room temperature.

By introducing CO₂ gas, the intensity of absorption of Soret band is increased and this effect is accompanied by the broadening of the Soret band. A linear dependence between absorption intensity measured at 423 nm and the increasing concentration of CO₂ in water is observed (Figure 7).

Figure 7. Dependence between increasing concentration of CO₂ in water and the intensity of absorption of (PyTDMeOPP).

A very good correlation coefficient of 98.4% was obtained for the linear dependence. Further work will focus on single wall carbon nanotube (SWCNT)—porphyrin composites as absorbing materials to improve the performance of the CO₂ sensors [29].

2.8. Comparatively AFM Studies of the Porphyrin Morphology before and after CO₂ Absorption

The study of the porphyrin aggregates deposited on silica from the initial solution of THF/water shows the formation of the ring architectures (Figure 8), this phenomenon being discussed in detail in Section 2.6.

Figure 8. 2D AFM images of ring aggregates of porphyrin in THF/water, before CO₂ introduction.

After CO₂ was introduced into the porphyrin (PyTDMeOPP) solution, the aggregate architecture changes significantly into amorphous deposits and all the inner parts of the porphyrin rings looked as if filled (Figure 9).

Figure 9. 2D AFM images of ring aggregates of porphyrin (PyTDMeOPP) in THF/water, after 15 min of CO₂ introduction.

In order to highlight this statement, AFM measurements reveal that the surface roughness (Sa) is decreased from 81 nm, measured before CO₂ interference (Figure 8 for 1.1 × 1.1 µm), to 5.5 nm, measured after 15 min of CO₂ introduction (Figure 9 for the same size 1.1 × 1.1 µm).

3. Experimental Section

3.1. Apparatus and Reagents

FT-IR spectra were recorded on a JASCO 430 FT-IR apparatus (Easton, PA, USA), in the 4000–400 cm⁻¹ range. Samples were prepared as KBr pellets. UV-visible spectra were recorded on a LAMBDA 12 UV/VIS spectrometer (Perkin Elmer, Boston, MA, USA) and on a JASCO model V-650 UV-visible spectrometer (Tokyo, Japan). Fluorescence spectra were obtained on a Perkin Elmer Model LS 55 apparatus (Boston, MA, USA). ¹H-NMR spectra were registered on a 400 MHz Bruker spectrometer (Delft, Netherland), in CDCl₃. The chemical shifts are expressed in δ (ppm). Proton chemical shifts were internally referenced to the residual proton resonance in CDCl₃ (δ 7.26). The HPLC analyses were performed on a JASCO apparatus (Cremella, Italy) equipped with a KROMASIL 100 SI 5 µm polar column, 240 × 4 mm with a MD 1510 detector, at ambient temperature, using UV detection at 420 nm. The samples were subjected to analysis (20 μL) at a flow rate of 1 mL/min with acetone/toluene of ratio 1/1 as eluent. A Bruker Esquire HCT series mass spectrometer (Daltonics, Bremen, Germany) with Atmospheric Pressure Interface-Electro Spray Ionization was used for recording MS.

3.1.1. Spectroscopic Studies

Absorption, excitation and emission spectra were registered at room temperature using 1 cm path length cells. The fluorescence spectra were recorded using slit widths, 4 for excitation and 3 for emission with 515 nm cut-off filters. Acidic conditions in THF solvent were changed by using 0.1 M HCl stock aqueous solutions. The pH values were measured with a digital Radelkis pH-meter (Budapest, Hungary).

3.1.2. Surface Imaging

Atomic force microscopy (AFM) investigations were carried out with Nanosurf^® EasyScan 2 Advanced Research AFM (Neuchatel, Switzerland). Samples were prepared onto a silica plate [30] from THF or CHCl₃ solutions. All AFM measurements were done in contact mode or tapping mode, in environmental conditions (temperature: 20 ± 2 °C; relative humidity: 50%–70%).

All reagents were p.a. grade and were provided by Fluka (Basel, Switzerland), Aldrich (Taufkirchen, Germany) and Merck (Darmstadt, Germany) and used as received, excepting pyrrole, which was distilled prior to use. The solvents, such as chloroform were stored over 4 Å molecular sieves and CH₂Cl₂ was distilled from CaH₂ under nitrogen.

3.2. Method for Synthesis of 5-(4-Pyridyl)-10,15,20-tris-(3,4-dimethoxyphenyl)-porphyrin

Porphyrin (PyTDMeOPP) was synthesized by the multicomponent method [31,32,33,34,35,36] from a mixture of 3,4-dimethoxybenzaldehyde (3.375 g, 22.5 mmol) and isonicotinaldehyde (0.803 g, 7.5 mmol) dissolved in propionic acid (220 mL) and propionic anhydride (3.85 mL, 30 mmol), stirred at 100 °C. Then, pyrrole (2.13 mL, 30 mmol) mixed with propionic acid (5 mL) was slowly added. The resulting mixture was allowed to reflux for 90 min at 141 °C, further it was cooled to room temperature and then it was poured into ethyl ether (200 mL). No oxidant was added to the reaction mixture and the six mixed porphyrins were directly obtained in their oxidized form by using atmospheric O₂. The precipitated material (dark-violet mass) was collected by vacuum filtration.

3.3. Separation Procedure

The solid product, which is a mixture of six porphyrins (two symmetrical, two unsymmetrical A₃B and AB₃ and the cis and trans isomers of A₂B₂ structure) was washed repeatedly with hot water, in 100 mL portions, until the rinse solution was no longer dark. The precipitate was dried under vacuum at 120 °C for 6 hours to remove propionic acid.

The purple product, isolated from polypyrrolic side-reaction compounds, was subjected to HPLC on preparative polar Kromasil column using as eluent acetone/toluene 1/1 and porphyrin (PyTDMeOPP) gave its signal at 4.680 min (assigned after NMR and MS).

3.4. The Main Characteristics of 5-(4-Pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)porphyrin

Dark violet crystalline solid; yield: 10.1% mp > 320 °C: FT-IR (KBr, ν, cm⁻¹): 754 and 796 (γ C-H_Pirol), 1017, 1232 and 1250 (aromatic C-O-CH₃), 1507 (C-O-CH₃ and/or ν C=N), 1587(ν C=C_Ph), 2830 and 2927 (ν C-H), 3311 (ν N-H); ¹H-NMR (400 MHz, CDCl₃): 8.91 (6H, s, β pyrrole ), 8.81 (2H, s, β pyrrole), 8.20 (2H, s, 3,5-pyridyl), 7.78–7.80 (3H, m, 5-phenyl), 7.27–7.25 [8H, m, (6H, 2,6-phenyl and 2H, 2,6-pyridyl)], 4.18 (9H, bs, 4-methoxy), 3.99 (9H, bs, 3-methoxy), −2.78 (2H, bs, internal pyrrole); UV-vis, THF (λ_max (log ε)): 423.2 (5.58); 516.5 (4.38); 553.2 (4.14); 593.3 (3.90); 650.3 (3.77); HPLC (KROMASIL column, acetone/toluene = 1/1), R_T, min: 4.680; MS (ESI⁺): m/z = 796.2 [M]⁺ (C₄₉H₄₁N₅O₆)⁺ molecular ion, calcd for [M]⁺795.87.

4. Conclusions

A new nanostructured material based on a mixed substituted asymmetrical A₃B porphyrin, namely: 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)-porphyrin (PyTDMeOPP) was synthesized by multicomponent reaction and characterized by ¹H-NMR, FT-IR, UV-vis, fluorescence, MS, HPLC and AFM techniques. Introducing one pyridyl substituent in the 5-meso-position of porphyrin macrocycle confers some degree of hydrophilicity and may cause amazing self-assembly properties and a better response to increased acidity. The influence of pH and nature of the used solvent upon H and J aggregates of the porphyrin were discussed. Aggregation of porphyrin (PyTDMeOPP) at the air–THF interface gave a triangular type morphology, randomly distributed but uniformly oriented. If the deposition was made by multiple drop-casting operations, followed by evaporation of the solvent, a network of triangles of uniform size has been created and a porous structure was obtained, finally being reorganized into rings. When the deposition was made from CHCl_3, ring structures ranging in internal diameter from 300 nm to 1 µm, but with the same width of the corona circle of approx. 200 nm were obtained. This porphyrin-based material, capable of generating ring type architectures in both THF and CHCl₃, has been proven to be sensitive to CO₂. The linear dependence between the intensity of the porphyrin UV-vis absorption at a wavelength of 423 nm and the concentration of CO₂ has a good correlation of 98.4%. In order to develop a sensor for CO₂ detection, further work will be done to study the use of SWCNs and (PyTDMeOPP), and all the steps for validation of the sensor will be performed.

Acknowledgments

This work was supported by the Romanian Academy Institute of Chemistry Timisoara under Grant No. 2, Project No. 2.1/2014; and STAR-ROSA Agency under Grant No. 76/2013 Project SAFEAIR.

Author Contributions

EFC designed the whole research concept and wrote the manuscript, DV and GFC performed the studies regarding the CO₂ influence on the porphyrin. AL, AP and IC (Ionela Creanga) synthesized the porphyrins and performed their spectroscopic and ¹H-NMR characterization. MB performed the AFM studies, RC recorded the excitation and emission spectra, IC (Ileana Cernica) performed the chromatographic separation. All authors read and approved the final manuscript.

Conflicts of Interest

The authors declare no conflict of interest.

References

Amao, Y.; Nakamura, N. Optical CO₂ sensor with the combination of colorimetric change of α-naphtholphthalein and internal reference fluorescent porphyrin dye. Sens. Actuators B 2004, 100, 347–351. [Google Scholar] [CrossRef]
Amao, Y.; Komori, T.; Nishide, H. Rapid responsible optical CO₂ sensor of the combination of colorimetric change of α-naphtholphthalein in poly(trimethylsiliylpropyne) layer and internal reference fluorescent porphyrin in polystyrene layer. React. Funct. Polym. 2005, 63, 35–41. [Google Scholar] [CrossRef]
Amao, Y.; Komori, T. Optical CO₂ sensor of the combination of colorimetric change of α-naphtholphthalein in poly(isobutyl methacrylate) and fluorescent porphyrin in polystyrene. Talanta 2005, 66, 976–981. [Google Scholar] [CrossRef] [PubMed]
Amao, Y.; Nakamura, N. An optical sensor with the combination of colorimetric change of α-naphtholphthalein and internal reference luminescent dye for CO₂ in water. Sens. Actuators B 2005, 107, 861–865. [Google Scholar] [CrossRef]
Borchert, N.B.; Kerry, J.P.; Papkovsky, D.B. A CO₂ sensor based on Pt-porphyrin dye and FRET scheme for food packaging applications. Sens. Actuators B 2013, 176, 157–165. [Google Scholar] [CrossRef]
Perez de Vargas-Sansalvador, I.M.; Carvajal, M.A.; Roldán-Muñoz, O.; Banqueri, J.; Fernández-Ramos, M.; Capitán-Vallvey, L. Phosphorescent sensing of carbon dioxide based on secondary inner-filter quenching. Anal. Chim. Acta 2009, 655, 66–74. [Google Scholar]
Carvajal, M.A.; Pérez de Vargas-Sansalvador, I.M.; Palma, A.J.; Fernández-Ramos, M.D.; Capitán-Vallvey, L.F. Hand-held optical instrument for CO2 in gas phase based on sensing film coating optoelectronic elements. Sens. Actuators B 2010, 144, 232–238. [Google Scholar] [CrossRef]
Bevilaqua, R.C.A.; Zanella, I.; Fagan, S.B. Chlorophyll a and pheophytin a as gas sensors of CO₂ and O₂ molecules. Chem. Phys. Lett. 2010, 496, 310–315. [Google Scholar]
Gu, C.; Sun, L.; Zhang, T.; Li, T. The design and characteristics of a porphyrin LB film ChemFET gas sensor. Thin Solid Films 1996, 284–285, 863–865. [Google Scholar] [CrossRef]
Arnold, D.P.; Manno, D.; Micocci, G.; Serra, A.; Tepore, A.; Valli, L. Gas-sensing properties of porphyrin dimer Langmuir-Blodgett films. Thin Solid Films 1998, 327–329, 341–344. [Google Scholar] [CrossRef]
Popescu, M.; Simandan, I.D.; Sava, F.; Velea, A.; Fagadar-Cosma, E. Sensor of nitrogen dioxide based on single wall carbon nanotubes and manganese-porphyrin. Dig. J. Nanomater. Biostructures 2011, 6, 1253–1256. [Google Scholar]
Cristescu, R.; Popescu, C.; Popescu, A.C.; Grigorescu, S.; Mihailescu, I.N.; Ciucu, A.A.; Iordache, S.; Andronie, A.; Stamatin, I.; Fagadar-Cosma, E.; et al. MAPLE deposition of Mn(III) metalloporphyrin thin films: Structural, topographical and electrochemical investigations. Appl. Surf. Sci. 2011, 257, 5293–5297. [Google Scholar] [CrossRef]
Sivalingam, Y.; Magna, G.; Pomarico, G.; Catini, A.; Martinelli, E.; Paolesse, R.; di Natale, C. The light enhanced gas selectivity of one-pot grown porphyrins coated ZnO nanorods. Sens. Actuators B 2013, 188, 475–481. [Google Scholar] [CrossRef]
Li, Y.W.; Yao, J.H.; Liu, C.J.; Yang, J.W.; Yang, C.L. Theoretical investigation of the O₂ adsorption effect in the electron transport of single Fe-porphyrin molecule. Phys. Lett. A 2009, 373, 3974–3977. [Google Scholar] [CrossRef]
Baschir, L.; Fagadar-Cosma, E.; Creanga, I.; Palade, A.; Lascu, A.; Birdeanu, M.; Savastru, D.; Savu, V.; Antohe, S.; Velea, A.; et al. UV sensing effect in Langmuir-Blodgett complex films containing a novel synthesized Fe(III) porphyrin. Dig. J. Nanomater. Biostructures 2014, 9, 847–857. [Google Scholar]
Tripathi, V.S.; Lakshminarayana, G.; Nogami, M. Optical oxygen sensors based on platinum porphyrin dyes encapsulated in ORMOSILS. Sens. Actuators B 2010, 147, 741–747. [Google Scholar] [CrossRef]
Frankenberg, C.; O’Dell, C.; Berry, J.; Guanter, L.; Joiner, J.; Köhler, P.; Pollock, R.; Taylor, T.E. Prospects for chlorophyll fluorescence remote sensing from the Orbiting Carbon Observatory-2. Remote Sens. Environ. 2014, 147, 1–12. [Google Scholar] [CrossRef]
Fagadar-Cosma, E.; Enache, C.; Vlascici, D.; Fagadar-Cosma, G.; Vasile, M.; Bazylak, G. Novel nanomaterials based on 5,10,15,20-tetrakis(3,4-dimethoxyphenyl)-21H,23H-porphyrin entrapped in silica matrices. Mater. Res. Bull. 2009, 44, 2186–2193. [Google Scholar] [CrossRef]
Zakavi, S.; Gharab, N.G. Interaction of para-substituted meso-tetraphenylporphyrins and meso-tetra(n-propyl)porphyrin with weak and strong carboxylic acids: A UV-vis spectroscopic study. Polyhedron 2007, 26, 2425–2432. [Google Scholar] [CrossRef]
McRae, E.G.; Kasha, M. The enhancement of phosphorescence ability upon aggregation of dye molecules. J. Chem. Phys. 1958, 28, 721–722. [Google Scholar] [CrossRef]
Di Natale, C.; Monti, D.; Paolesse, R. Chemical sensitivity of porphyrin assemblies. Mater. Today 2010, 13, 46–52. [Google Scholar] [CrossRef]
Mihailescu, G.; Olenic, L.; Garabagiu, S.; Blanita, G.; Fagadar-Cosma, E.; Biris, A. A coupling between plasmonic resonances in nanoparticles and porphyrins molecules. J. Nanosci. Nanotechnol. 2010, 10, 2527–2530. [Google Scholar] [CrossRef] [PubMed]
Mohnani, S.; Bonifazi, D. Supramolecular architectures of porphyrins on surfaces: The structural evolution from 1D to 2D to 3D to devices. Coord. Chem. Rev. 2010, 254, 2342–2362. [Google Scholar] [CrossRef]
Grama, S.; Hurduc, N.; Fagadar-Cosma, E.; Vasile, M.; Tarabukina, E.; Fagadar-Cosma, G. Novel porphyrin-based polysiloxane micromaterial. Dig. J. Nanomater. Biostructures 2010, 5, 959–973. [Google Scholar]
Fagadar-Cosma, E.; Enache, C.; Fagadar-Cosma, G.; Savii, C. Design of hybrid nanomaterials based on silica-porphyrin. AFM characterization. J. Optoelectron. Adv. Mater. 2007, 9, 1878–1883. [Google Scholar]
Cristescu, R.; Popescu, C.; Popescu, A.C.; Mihailescu, I.N.; Ciucu, A.A.; Andronie, A.; Iordache, S.; Stamatin, I.; Fagadar-Cosma, E.; Chrisey, D.B. Functional porphyrin thin films deposited by matrix assisted pulsed laser evaporation. Mater. Sci. Eng. B-Adv. 2010, 169, 106–110. [Google Scholar] [CrossRef]
Teixeira, R.; Andrade, S.M.; Vaz Serra, V.; Paulo, P.M.R; Sánchez-Coronilla, A.; Neves, M.G.P.M.S.; Cavaleiro, J.A.S.; Costa, S.M.B. Reorganization of Self-Assembled Dipeptide Porphyrin J-Aggregates in Water–Ethanol Mixtures. J. Phys. Chem. B 2012, 116, 2396–2404. [Google Scholar] [CrossRef] [PubMed]
Vaz Serra, V.; Andrade, S.M.; Neves, M.G.P.M.S.; Cavaleiro, J.A.S.; Costa, S.M.B. J-aggregate formation in bis-(4-carboxyphenyl)porphyrins in water: pH and counterion dependence. New J. Chem. 2010, 34, 2757–2765. [Google Scholar] [CrossRef]
Lvova, L.; Mastroianni, M.; Pomarico, G.; Santonico, M.; Pennazza, G.; di Natale, C.; Paolesse, R.; D’Amico, A. Carbon nanotubes modified with porphyrin units for gaseous phase chemical sensing. Sens. Actuators B 2012, 170, 163–171. [Google Scholar] [CrossRef]
Fagadar-Cosma, E.; Enache, C.; Dascalu, D.; Fagadar-Cosma, G.; Gavrila, R. FT-IR, fluorescence and electronic spectra for monitoring the aggregation process of tetra-pyridylporphyrine entrapped in silica matrices. Optoelectron. Adv. Mater. 2008, 2, 437–441. [Google Scholar]
Adler, A.D.; Longo, F.R.; Goldmacher, J.; Assour, J.; Korsakoff, L. A simplified synthesis for meso-tetraphenylporphine. J. Org. Chem. 1967, 32, 476. [Google Scholar] [CrossRef]
Lindsey, J.S.; Schreiman, I.C.; Hsu, H.C.; Kearney, P.C.; Marguerettaz, A.M. Rothemund and Adler-Longo reactions revisited: Synthesis of tetraphenylporphyrins under equilibrium conditions. J. Org. Chem. 1987, 52, 827–836. [Google Scholar] [CrossRef]
Fazekas, M.; Pintea, M.; Senge, M.O.; Zawadzka, M. Synthetic strategies and porphyrin building blocks for unsymmetrical multichromophores. Tetrahedron Lett. 2008, 49, 2236–2239. [Google Scholar] [CrossRef]
Marek, D.; Narra, M.; Schneider, A.; Swavey, S. Synthesis, characterization and electrode adsorption studies of porphyrins coordinated to ruthenium(II) polypyridyl complexes. Inorg. Chim. Acta 2006, 359, 789–799. [Google Scholar] [CrossRef]
Lindsey, J.S. Self-assembly in synthetic routes to molecular devices. Biological principles and chemical perspectives: A review. New. J. Chem. 1991, 15, 153–180. [Google Scholar]
Fagadar-Cosma, E.; Cseh, L.; Badea, V.; Fagadar-Cosma, G.; Vlascici, D. Combinatorial synthesis and characterization of new asymmetric porphyrins as potential photosensitizers in photodynamic therapy. Comb. Chem. High Throughput Screen. 2007, 10, 466–472. [Google Scholar] [CrossRef] [PubMed]

Sample Availability: Sample of the compound 5-(4-pyridyl)-10,15,20-tris(3,4-dimethoxyphenyl)-porphyrin is available from the authors.

© 2014 by the authors. Licensee MDPI, Basel, Switzerland. This article is an open access article distributed under the terms and conditions of the Creative Commons Attribution license ( http://creativecommons.org/licenses/by/4.0/).

Share and Cite

MDPI and ACS Style

Fagadar-Cosma, E.; Vlascici, D.; Fagadar-Cosma, G.; Palade, A.; Lascu, A.; Creanga, I.; Birdeanu, M.; Cristescu, R.; Cernica, I. A Sensitive A₃B Porphyrin Nanomaterial for CO₂ Detection. Molecules 2014, 19, 21239-21252. https://doi.org/10.3390/molecules191221239

AMA Style

Fagadar-Cosma E, Vlascici D, Fagadar-Cosma G, Palade A, Lascu A, Creanga I, Birdeanu M, Cristescu R, Cernica I. A Sensitive A₃B Porphyrin Nanomaterial for CO₂ Detection. Molecules. 2014; 19(12):21239-21252. https://doi.org/10.3390/molecules191221239

Chicago/Turabian Style

Fagadar-Cosma, Eugenia, Dana Vlascici, Gheorghe Fagadar-Cosma, Anca Palade, Anca Lascu, Ionela Creanga, Mihaela Birdeanu, Rodica Cristescu, and Ileana Cernica. 2014. "A Sensitive A₃B Porphyrin Nanomaterial for CO₂ Detection" Molecules 19, no. 12: 21239-21252. https://doi.org/10.3390/molecules191221239

APA Style

Fagadar-Cosma, E., Vlascici, D., Fagadar-Cosma, G., Palade, A., Lascu, A., Creanga, I., Birdeanu, M., Cristescu, R., & Cernica, I. (2014). A Sensitive A₃B Porphyrin Nanomaterial for CO₂ Detection. Molecules, 19(12), 21239-21252. https://doi.org/10.3390/molecules191221239

Article Menu

A Sensitive A₃B Porphyrin Nanomaterial for CO₂ Detection

Abstract

1. Introduction