Abstract
In this work, Ag and Au nanoparticles (AgNPs and AuNPs) stable colloid solution were prepared by laser ablation of chemically pure silver rod and gold film in liquid monomer isodecyl acrylate (IDA). Sizes of obtained nanoparticles were determined by scanning electron microscope and vary from 30 to 130 nm. Nanocomposites films were prepared from obtained stable colloid solution by photocuring. To prepare solid film based on aliphatic polymer IDA long molecules cross-linking, 1,6-Hexandiol diacrylate was used. Obtained films were transparent, homogenous and colored in brown for AgNPs and purple for AuNPs-filled nanocomposites. Prepared nanomaterials exhibit strong third-order nonlinear optical responses under CW laser irradiation at 532 nm, which was estimated by using z-scan technique performed with open and close aperture. The real and imaginary parts of third-order nonlinear optical coefficients of the studied nanocomposites were found to be up to Reχ (3) = 1.31 × 10−5 (esu) and Imχ (3) = 7.64 × 10−5 (esu), for samples negative nonlinear refractive index was obtained, which corresponds to self-defocusing effect.
Similar content being viewed by others
References
I.-Y. Jeon, Y.-B. Baek, Materials 3, 3654 (2010)
O.V. Sakhno, L.M. Goldenberg, J. Stumpe, T.N. Smirnova, J. Opt. A: Pure Appl. Opt. 11, 024013 (2009)
R.A. Ganeev, M. Baba, A.I. Ryasnyansky, M. Suzuki, H. Kuroda, Opt. Commun. 240, 437–448 (2004)
S. Kassavetis, S. Kaziannis, N. Pliatsikas, A. Avgeropoulos, A.E. Karantzalis, C. Kosmidis, E. Lidorikis, P. Patsalas, Appl. Surf. Sci. 336, 262–266 (2005)
Y. Tamaki, T. Asahi, H. Masuhara, J. Phys. Chem. 106, 241–243 (2002)
S. Barcikowski, M. Hustedt, B. Chichkov, Polimery 53(9), 657–662 (2008)
R.A. Ganeev, A.S. Zakirov, G.S. Boltaev, R.I. Tugushev, T. Usmanov et al. Opt. Mater. 33, 419–423 (2011)
H.O. Jeschke, M.E. Garsia, K.H. Bennemann, Phys. Rev. Lett. 87, 015003 (2001)
D. Perez, L.J. Lewis, Phys. Rev. B 67, 184102 (2003)
J. Burunkova, S. Kokenyesi, I. Csarnovics, A. Bonyár, M. Veres, A. Csike Eur. Polym. J. 64, 189–195 (2015)
J. Burunkova, I. Csarnovics, I. Denisyuk, L. Daróczi, S. Kökényesi, J. Non-Cryst. Solids 402, 200–203 (2014)
M. Sheik-Bahae, A. Said, T.-H. Wei, D.J. Hagan, E.W. Van Stryland, J. Quant. Electron. 26, 760–769 (1990)
K. Lance Kelly, E. Coronado, L.L. Zhao, G.C. Schatz, J. Phys. Chem. B 107, 668–677 (2003)
D.L. Pavia, G.M. Lampman, G.S. Kriz, Introduction to spectroscopy, 3rd edn. (Cole Publ. Co., Brooks, 2000), p. 784
V. Subhashini, S. Ponnusamy, C. Muthamizhchelvan, B. Dhanalakshmi, Opt. Mater. 35, 1327–1334 (2013)
S. Qu, Y. Gao, X. Jiang, K. Hirao, Opt. Commun. 224, 321–327 (2003)
M.D. Zidan, A.W. Allaf, A. Allahham, A. AL-Zier, Opt. Laser Technol. 80, 72–76 (2016)
Acknowledgements
The authors thank RFBR according to the research project No. 16-32-00448, Federal program # 3.432.2014/K 2014–2016.
Author information
Authors and Affiliations
Corresponding author
Rights and permissions
About this article
Cite this article
Zulina, N.A., Pavlovetc, I.M., Baranov, M.A. et al. Synthesis and optical properties study of nanocomposites based on AuNPs and AgNPs obtained by laser ablation in liquid monomer. Appl. Phys. A 123, 39 (2017). https://doi.org/10.1007/s00339-016-0630-6
Received:
Accepted:
Published:
DOI: https://doi.org/10.1007/s00339-016-0630-6