WO2014192390A1 - 液晶組成物および液晶表示素子 - Google Patents

液晶組成物および液晶表示素子 Download PDF

Info

Publication number
WO2014192390A1
WO2014192390A1 PCT/JP2014/058256 JP2014058256W WO2014192390A1 WO 2014192390 A1 WO2014192390 A1 WO 2014192390A1 JP 2014058256 W JP2014058256 W JP 2014058256W WO 2014192390 A1 WO2014192390 A1 WO 2014192390A1
Authority
WO
WIPO (PCT)
Prior art keywords
liquid crystal
carbons
component
compound
composition
Prior art date
Application number
PCT/JP2014/058256
Other languages
English (en)
French (fr)
Inventor
将之 齋藤
好優 古里
Original Assignee
Jnc株式会社
Jnc石油化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jnc株式会社, Jnc石油化学株式会社 filed Critical Jnc株式会社
Priority to EP14804176.7A priority Critical patent/EP3006541B1/en
Priority to JP2014530993A priority patent/JP5621952B1/ja
Priority to KR1020157033997A priority patent/KR20160013882A/ko
Priority to US14/889,439 priority patent/US20160090532A1/en
Priority to CN201480025332.3A priority patent/CN105189701B/zh
Publication of WO2014192390A1 publication Critical patent/WO2014192390A1/ja

Abstract

　ネマチック相の高い上限温度、ネマチック相の低い下限温度、小さな粘度、適切な光学異方性、大きな誘電率異方性、大きな比抵抗、紫外線に対する高い安定性、熱に対する高い安定性などの特性において、少なくとも１つの特性を充足する、または少なくとも２つの特性に関して適切なバランスを有する液晶組成物を提供する。短い応答時間、大きな電圧保持率、大きなコントラスト比、長い寿命などを有するＡＭ素子を提供する。　第一成分として大きな誘電率異方性を有する特定の化合物、および第二成分として小さな粘度を有する特定の化合物を含有し、第三成分として高い上限温度または小さな粘度を有する特定の化合物、および第四成分として大きな誘電率異方性を有する特定の化合物を含有してもよく、そしてネマチック相を有する液晶組成物、およびこの組成物を含有する液晶表示素子である。

Description

液晶組成物および液晶表示素子
　本発明は、液晶組成物、この組成物を含有する液晶表示素子などに関する。特に、誘電率異方性が正の液晶組成物、およびこの組成物を含有し、ＴＮ、ＯＣＢ、ＩＰＳ、ＦＦＳ、またはＦＰＡのモードを有するＡＭ（active matrix）素子に関する。
　液晶表示素子において、液晶分子の動作モードに基づいた分類は、ＰＣ（phase change）、ＴＮ（twisted nematic）、ＳＴＮ（super twisted nematic）、ＥＣＢ（electrically controlled birefringence）、ＯＣＢ（optically compensated bend）、ＩＰＳ（in-plane switching）、ＶＡ（vertical alignment）、ＦＦＳ（Fringe Field Switching）、ＦＰＡ（field-induced photo-reactive alignment）などのモードである。素子の駆動方式に基づいた分類は、ＰＭ（passive matrix）とＡＭ（active matrix）である。ＰＭはスタティック（static）とマルチプレックス（multiplex）などに分類され、ＡＭはＴＦＴ（thin film transistor）、ＭＩＭ（metal insulator metal）などに分類される。ＴＦＴの分類は非晶質シリコン（amorphous silicon）および多結晶シリコン（polycrystal silicon）である。後者は製造工程によって高温型と低温型とに分類される。光源に基づいた分類は、自然光を利用する反射型、バックライトを利用する透過型、そして自然光とバックライトの両方を利用する半透過型である。
　液晶表示素子はネマチック相を有する液晶組成物を含有する。この組成物は適切な特性を有する。この組成物の特性を向上させることによって、良好な特性を有するＡＭ素子を得ることができる。２つの特性における関連を下記の表１にまとめる。組成物の特性を市販されているＡＭ素子に基づいてさらに説明する。ネマチック相の温度範囲は、素子の使用できる温度範囲に関連する。ネマチック相の好ましい上限温度は約７０℃以上であり、そしてネマチック相の好ましい下限温度は約－１０℃以下である。組成物の粘度は素子の応答時間に関連する。素子で動画を表示するためには短い応答時間が好ましい。１ミリ秒でもより短い応答時間が望ましい。したがって、組成物における小さな粘度が好ましい。低い温度における小さな粘度はより好ましい。組成物の弾性定数は素子のコントラストに関連する。素子においてコントラストを上げるためには、組成物における大きな弾性定数がより好ましい。
Figure JPOXMLDOC01-appb-I000010
　組成物の光学異方性は、素子のコントラスト比に関連する。素子のモードに応じて、大きな光学異方性または小さな光学異方性、すなわち適切な光学異方性が必要である。組成物の光学異方性（Δｎ）と素子のセルギャップ（ｄ）との積（Δｎ×ｄ）は、コントラスト比を最大にするように設計される。適切な積の値は動作モードの種類に依存する。ＴＮのようなモードの素子では、適切な値は約０．４５μｍである。この場合、小さなセルギャップの素子には大きな光学異方性を有する組成物が好ましい。組成物における大きな誘電率異方性は、素子における低いしきい値電圧、小さな消費電力と大きなコントラスト比に寄与する。したがって、大きな誘電率異方性が好ましい。組成物における大きな比抵抗は、素子における大きな電圧保持率と大きなコントラスト比に寄与する。したがって、初期段階において室温だけでなくネマチック相の上限温度に近い温度でも大きな比抵抗を有する組成物が好ましい。長時間使用したあと、室温だけでなくネマチック相の上限温度に近い温度でも大きな比抵抗を有する組成物が好ましい。紫外線および熱に対する組成物の安定性は、液晶表示素子の寿命に関連する。これらの安定性が高いとき、この素子の寿命は長い。このような特性は、液晶プロジェクター、液晶テレビなどに用いるＡＭ素子に好ましい。
　ＴＮモードを有するＡＭ素子においては正の誘電率異方性を有する組成物が用いられる。ＶＡモードを有するＡＭ素子においては負の誘電率異方性を有する組成物が用いられる。ＩＰＳモードまたはＦＦＳモードを有するＡＭ素子においては正または負の誘電率異方性を有する組成物が用いられる。高分子支持配向（ＰＳＡ；polymer sustained alignment）型のＡＭ素子においては正または負の誘電率異方性を有する組成物が用いられる。正の誘電率異方性を有する液晶組成物の例は次の特許文献１から特許文献２などに開示されている。
国際公開第１９９６／１１８９７号 特開２００１－１３９５１１号公報
　本発明の１つの目的は、ネマチック相の高い上限温度、ネマチック相の低い下限温度、小さな粘度、適切な光学異方性、大きな誘電率異方性、大きな比抵抗、紫外線に対する高い安定性、熱に対する高い安定性、大きな弾性定数などの特性において、少なくとも１つの特性を充足する液晶組成物である。他の目的は、少なくとも２つの特性のあいだで適切なバランスを有する液晶組成物である。別の目的は、このような組成物を含有する液晶表示素子である。別の目的は、短い応答時間、大きな電圧保持率、低いしきい値電圧、大きなコントラスト比、長い寿命などの特性を有するＡＭ素子である。
　本発明は、第一成分として式（１）で表される化合物の群から選択された少なくとも１つの化合物、および第二成分として式（２）で表される化合物の群から選択された少なくとも１つの化合物を含有し、そしてネマチック相を有する液晶組成物、およびこの組成物を含有する液晶表示素子である。
Figure JPOXMLDOC01-appb-I000011

式（１）および式（２）において、Ｒ１およびＲ２は独立して、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、または炭素数２から１２のアルケニルであり；Ｒ３は、炭素数２から１２のアルケニル、または少なくとも１つの水素がフッ素で置き換えられた炭素数２から１２のアルケニルであり；環Ａおよび環Ｂは独立して、１，４－シクロへキシレン、１，４－フェニレン、２－フルオロ－１，４－フェニレン、２，３－ジフルオロ－１，４－フェニレン、２，６－ジフルオロ－１，４－フェニレン、ピリミジン－２，５－ジイル、１，３－ジオキサン－２，５－ジイル、またはテトラヒドロピラン－２，５－ジイルであり；Ｚ１およびＺ２は独立して、単結合、エチレン、ビニレン、メチレンオキシ、カルボニルオキシ、またはジフルオロメチレンオキシであり；Ｌ１およびＬ２は独立して、フッ素または塩素であり；Ｘ１およびＸ２は独立して、水素またはフッ素であり；Ｙ１は、フッ素、塩素、少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルキル、または少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルコキシであり；ｍおよびｊは独立して、０、１、２、または３であり、そしてｍとｊの和は３以下である。
　本発明の長所は、ネマチック相の高い上限温度、ネマチック相の低い下限温度、小さな粘度、適切な光学異方性、大きな誘電率異方性、大きな比抵抗、紫外線に対する高い安定性、熱に対する高い安定性、大きな弾性定数などの特性において、少なくとも１つの特性を充足する液晶組成物である。別の長所は、少なくとも２つの特性のあいだで適切なバランスを有する液晶組成物である。別の長所は、このような組成物を含有する液晶表示素子である。別の長所は、短い応答時間、大きな電圧保持率、低いしきい値電圧、大きなコントラスト比、長い寿命などの特性を有するＡＭ素子である。
　この明細書における用語の使い方は次のとおりである。「液晶組成物」および「液晶表示素子」の用語をそれぞれ「組成物」および「素子」と略すことがある。「液晶表示素子」は液晶表示パネルおよび液晶表示モジュールの総称である。「液晶性化合物」は、ネマチック相、スメクチック相などの液晶相を有する化合物、および液晶相を有しないがネマチック相の温度範囲、粘度、誘電率異方性のような特性を調節する目的で組成物に混合される化合物の総称である。この化合物は、１，４－シクロヘキシレンや１，４－フェニレンのような六員環を有し、その分子構造は棒状（rod like）である。「重合性化合物」は、組成物中に重合体を生成させる目的で添加される化合物である。
　液晶組成物は、複数の液晶性化合物を混合することによって調製される。液晶性化合物の割合（含有量）は、この液晶組成物の重量に基づいた重量百分率（重量％）で表される。この液晶組成物に、光学活性化合物、酸化防止剤、紫外線吸収剤、色素、消泡剤、重合性化合物、重合開始剤、重合禁止剤のような添加物が必要に応じて添加される。添加物の割合（添加量）は、液晶性化合物の割合と同様に、液晶組成物の重量に基づいた重量百分率（重量％）で表される。重量百万分率（ｐｐｍ）が用いられることもある。重合開始剤および重合禁止剤の割合は、例外的に重合性化合物の重量に基づいて表される。
　「ネマチック相の上限温度」を「上限温度」と略すことがある。「ネマチック相の下限温度」を「下限温度」と略すことがある。「比抵抗が大きい」は、組成物が初期段階において室温だけでなくネマチック相の上限温度に近い温度でも大きな比抵抗を有し、そして長時間使用したあと室温だけでなくネマチック相の上限温度に近い温度でも大きな比抵抗を有することを意味する。「電圧保持率が大きい」は、素子が初期段階において室温だけでなくネマチック相の上限温度に近い温度でも大きな電圧保持率を有し、そして長時間使用したあと室温だけでなくネマチック相の上限温度に近い温度でも大きな電圧保持率を有することを意味する。
　「少なくとも１つの‘Ａ’は、‘Ｂ’で置き換えられてもよい」の表現は、‘Ａ’の数は任意であることを意味する。‘Ａ’の数が１つのとき、‘Ａ’の位置は任意であり、‘Ａ’の数が２つ以上のときも、それらの位置は制限なく選択できる。このルールは、「少なくとも１つの‘Ａ’が、‘Ｂ’で置き換えられた」の表現にも適用される。
　成分化合物の化学式において、末端基Ｒ１の記号を複数の化合物に用いた。これらの化合物において、任意の２つのＲ１が表わす２つの基は同一であってもよく、または異なってもよい。例えば、化合物（１）のＲ１がエチルであり、化合物（１－１）のＲ１がエチルであるケースがある。化合物（１）のＲ１がエチルであり、化合物（１－１）のＲ１がプロピルであるケースもある。このルールは、Ｒ４、Ｘ１、Ｙ１などの記号にも適用される。式（１）において、ｍが２のとき、２つの環Ａが存在する。この化合物において、２つの環Ａが表わす２つの環は、同一であってもよく、または異なってもよい。このルールは、ｎが２より大きいとき、任意の２つの環Ａにも適用される。このルールは、Ｚ１、環Ｂなどにも適用される。
　２－フルオロ－１，４－フェニレンは、下記の２つの二価基を意味する。化学式において、フッ素は左向き（Ｌ）であってもよいし、右向き（Ｒ）であってもよい。このルールは、テトラヒドロピラン－２，５－ジイルのような、非対称な環の二価基にも適用される。
Figure JPOXMLDOC01-appb-I000012
　本発明は、下記の項などである。
項１．　第一成分として式（１）で表される化合物の群から選択された少なくとも１つの化合物、および第二成分として式（２）で表される化合物の群から選択された少なくとも１つの化合物を含有し、そしてネマチック相を有する液晶組成物。
Figure JPOXMLDOC01-appb-I000013

式（１）および式（２）において、Ｒ１およびＲ２は独立して、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、または炭素数２から１２のアルケニルであり；Ｒ３は、炭素数２から１２のアルケニル、または少なくとも１つの水素がフッ素で置き換えられた炭素数２から１２のアルケニルであり；環Ａおよび環Ｂは独立して、１，４－シクロへキシレン、１，４－フェニレン、２－フルオロ－１，４－フェニレン、２，３－ジフルオロ－１，４－フェニレン、２，６－ジフルオロ－１，４－フェニレン、ピリミジン－２，５－ジイル、１，３－ジオキサン－２，５－ジイル、またはテトラヒドロピラン－２，５－ジイルであり；Ｚ１およびＺ２は独立して、単結合、エチレン、ビニレン、メチレンオキシ、カルボニルオキシ、またはジフルオロメチレンオキシであり；Ｌ１およびＬ２は独立して、フッ素または塩素であり；Ｘ１およびＸ２は独立して、水素またはフッ素であり；Ｙ１は、フッ素、塩素、少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルキル、または少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルコキシであり；ｍおよびｊは独立して、０、１、２、または３であり、そしてｍとｊの和は３以下である。
項２．　第一成分として式（１－１）から式（１－１４）で表される化合物の群から選択された少なくとも１つの化合物を含有する、項１に記載の液晶組成物。
Figure JPOXMLDOC01-appb-I000014

Figure JPOXMLDOC01-appb-I000015

式（１－１）から式（１－１４）において、Ｒ１は、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、または炭素数２から１２のアルケニルであり；Ｌ１およびＬ２は独立して、フッ素または塩素であり；Ｘ１、Ｘ２、Ｘ３、Ｘ４、Ｘ５、Ｘ６、Ｘ７、およびＸ８は独立して、水素またはフッ素であり；Ｙ１は、フッ素、塩素、少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルキル、または少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルコキシである。
項３．　液晶組成物の重量に基づいて、第一成分の割合が５重量％から４０重量％の範囲であり、第二成分の割合が１５重量％から６０重量％の範囲である、項１または２に記載の液晶組成物。
項４．　第三成分として式（３）で表される化合物の群から選択された少なくとも１つの化合物をさらに含有する、項１から３のいずれか１項に記載の液晶組成物。
Figure JPOXMLDOC01-appb-I000016

式（３）において、Ｒ４およびＲ５は独立して、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、炭素数２から１２のアルケニル、または少なくとも１つの水素がフッ素で置き換えられた炭素数２から１２のアルケニルであり；環Ｃおよび環Ｄは独立して、１，４－シクロへキシレン、１，４－フェニレン、２－フルオロ－１，４－フェニレン、または２，５－ジフルオロ－１，４－フェニレンであり；Ｚ３は、単結合、エチレンまたはカルボニルオキシであり；ｎは、１、２、または３であり；ただしｎが１のとき、環Ｃは１，４－フェニレンである。
項５．　第三成分として式（３－１）から式（３－１２）で表される化合物の群から選択された少なくとも１つの化合物を含有する、項１から４のいずれか１項に記載の液晶組成物。
Figure JPOXMLDOC01-appb-I000017

式（３－１）から式（３－１２）において、Ｒ４およびＲ５は独立して、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、炭素数２から１２のアルケニル、または少なくとも１つの水素がフッ素で置き換えられた炭素数２から１２のアルケニルである。
項６．　液晶組成物の重量に基づいて、第三成分の割合が５重量％から３５重量％の範囲である、項４または５に記載の液晶組成物。
項７．　第四成分として式（４）で表される化合物の群から選択された少なくとも１つの化合物をさらに含有する、項１から６のいずれか１項に記載の液晶組成物。
Figure JPOXMLDOC01-appb-I000018

式（４）において、Ｒ６は炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、または炭素数２から１２のアルケニルであり；環Ｅは、１，４－シクロへキシレン、１，４－フェニレン、２－フルオロ－１，４－フェニレン、２，６－ジフルオロ－１，４－フェニレン、ピリミジン－２，５－ジイル、１，３－ジオキサン－２，５－ジイル、またはテトラヒドロピラン－２，５－ジイルであり；Ｚ４は、単結合、エチレン、カルボニルオキシ、またはジフルオロメチレンオキシであり；Ｘ９およびＸ１０は独立して、水素またはフッ素であり；Ｙ２は、フッ素、塩素、少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルキル、または少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルコキシであり；ｐは、１、２、３、または４である。
項８．　第四成分として式（４－１）から式（４－２７）で表される化合物の群から選択された少なくとも１つの化合物を含有する、項１から７のいずれか１項に記載の液晶組成物。
Figure JPOXMLDOC01-appb-I000019

Figure JPOXMLDOC01-appb-I000020

Figure JPOXMLDOC01-appb-I000021

式（４－１）から式（４－２７）において、Ｒ６は、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、または炭素数２から１２のアルケニルである。
項９．　液晶組成物の重量に基づいて、第四成分の割合が１０重量％から６０重量％の範囲である、項７または８に記載の液晶組成物。
項１０．　ネマチック相の上限温度が７０℃以上であり、波長５８９ｎｍにおける光学異方性（２５℃で測定）が０．０７以上であり、そして周波数１ｋＨｚにおける誘電率異方性（２５℃で測定）が２以上である、項１から９のいずれか１項に記載の液晶組成物。
項１１．　項１から１０のいずれか１項に記載の液晶組成物を含有する液晶表示素子。
項１２．　液晶表示素子の動作モードが、ＴＮモード、ＥＣＢモード、ＯＣＢモード、ＩＰＳモード、ＦＦＳモード、またはＦＰＡモードであり、液晶表示素子の駆動方式がアクティブマトリックス方式である、項１１に記載の液晶表示素子。
項１３．　項１から１０のいずれか１項に記載の液晶組成物の液晶表示素子における使用。
　本発明は、次の項も含む。（ａ）光学活性化合物、酸化防止剤、紫外線吸収剤、色素、消泡剤、重合性化合物、重合開始剤、重合禁止剤などの添加物の少なくとも１つをさらに含有する上記の組成物。（ｂ）上記の組成物を含有するＡＭ素子。（ｃ）重合性化合物をさらに含有する上記の組成物、およびこの組成物を含有する高分子支持配向（ＰＳＡ）型のＡＭ素子。（ｄ）上記の組成物を含有し、この組成物中の重合性化合物が重合されている、高分子支持配向（ＰＳＡ）型のＡＭ素子。（ｅ）上記の組成物を含有し、そしてＰＣ、ＴＮ、ＳＴＮ、ＥＣＢ、ＯＣＢ、ＩＰＳ、ＶＡ、ＦＦＳ、またはＦＰＡのモードを有する素子。（ｆ）上記の組成物を含有する透過型の素子。（ｇ）上記の組成物を、ネマチック相を有する組成物としての使用。（ｈ）上記の組成物に光学活性化合物を添加することによって光学活性な組成物としての使用。
　本発明の組成物を次の順で説明する。第一に、組成物における成分化合物の構成を説明する。第二に、成分化合物の主要な特性、およびこの化合物が組成物に及ぼす主要な効果を説明する。第三に、組成物における成分の組み合わせ、成分の好ましい割合およびその根拠を説明する。第四に、成分化合物の好ましい形態を説明する。第五に、好ましい成分化合物を示す。第六に、組成物に添加してもよい添加物を説明する。第七に、成分化合物の合成法を説明する。最後に、組成物の用途を説明する。
　第一に、組成物における成分化合物の構成を説明する。本発明の組成物は組成物Ａと組成物Ｂに分類される。組成物Ａは、化合物（１）、化合物（２）、化合物（３）、および化合物（４）から選択された液晶性化合物の他に、その他の液晶性化合物、添加物などをさらに含有してもよい。「その他の液晶性化合物」は、化合物（１）、化合物（２）、化合物（３）、および化合物（４）とは異なる液晶性化合物である。このような化合物は、特性をさらに調整する目的で組成物に混合される。添加物は、光学活性化合物、酸化防止剤、紫外線吸収剤、色素、消泡剤、重合性化合物、重合開始剤、重合禁止剤などである。
　組成物Ｂは、実質的に、化合物（１）、化合物（２）、化合物（３）、および化合物（４）から選択された液晶性化合物のみからなる。「実質的に」は、組成物が添加物を含有してもよいが、その他の液晶性化合物を含有しないことを意味する。組成物Ｂは組成物Ａに比較して成分の数が少ない。コストを下げるという観点から、組成物Ｂは組成物Ａよりも好ましい。その他の液晶性化合物を混合することによって特性をさらに調整できるという観点から、組成物Ａは組成物Ｂよりも好ましい。
　第二に、成分化合物の主要な特性、およびこの化合物が組成物の特性に及ぼす主要な効果を説明する。成分化合物の主要な特性を本発明の効果に基づいて表２にまとめる。表２の記号において、Ｌは大きいまたは高い、Ｍは中程度の、Ｓは小さいまたは低い、を意味する。記号Ｌ、Ｍ、Ｓは、成分化合物のあいだの定性的な比較に基づいた分類であり、０（ゼロ）は、値がほぼゼロであることを意味する。
Figure JPOXMLDOC01-appb-I000022
　成分化合物を組成物に混合したとき、成分化合物が組成物の特性に及ぼす主要な効果は次のとおりである。化合物（１）は誘電率異方性を上げる。化合物（２）は粘度を下げる。化合物（３）は上限温度を上げる、または下限温度を下げる。化合物（４）は下限温度を下げ、そして誘電率異方性を上げる。
　第三に、組成物における成分の組み合わせ、成分化合物の好ましい割合およびその根拠を説明する。組成物における成分の組み合わせは、第一成分＋第二成分、第一成分＋第二成分＋第三成分、第一成分＋第二成分＋第四成分、または第一成分＋第二成分＋第三成分＋第四成分である。好ましい組成物における成分の組み合わせは、第一成分＋第二成分＋第三成分または第一成分＋第二成分＋第三成分＋第四成分である。
　第一成分の好ましい割合は、誘電率異方性を上げるために約５重量％以上であり、下限温度を下げるために、または粘度を下げるために、約４０重量％以下である。さらに好ましい割合は約１０重量％から約３５重量％の範囲である。特に好ましい割合は約１５重量％から約３０重量％の範囲である。
　第二成分の好ましい割合は、粘度を下げるために約１５重量％以上であり、誘電率異方性を上げるために約６０重量％以下である。さらに好ましい割合は約２０重量％から約５５重量％の範囲である。特に好ましい割合は約２５重量％から約５０重量％の範囲である。
　第三成分の好ましい割合は、上限温度を上げるために、または粘度を下げるために、約５重量％以上であり、誘電率異方性を上げるために約３５重量％以下である。さらに好ましい割合は約５重量％から約３０重量％の範囲である。特に好ましい割合は約５重量％から約２５重量％の範囲である。
　第四成分の好ましい割合は、誘電率異方性を上げるために約１０重量％以上であり、下限温度を下げるために約６０重量％以下である。さらに好ましい割合は約１５重量％から約５０重量％の範囲である。特に好ましい割合は約２０重量％から約４５重量％の範囲である。
　第四に、成分化合物の好ましい形態を説明する。Ｒ１、Ｒ２およびＲ６は独立して、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、または炭素数２から１２のアルケニルである。好ましいＲ１、Ｒ２またはＲ６は、紫外線または熱に対する安定性を上げるために、炭素数１から１２のアルキルである。Ｒ３は炭素数２から１２のアルケニル、または少なくとも１つの水素がフッ素で置き換えられた炭素数２から１２のアルケニルである。Ｒ４およびＲ５は独立して、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、炭素数２から１２のアルケニル、または少なくとも１つの水素がフッ素で置き換えられた炭素数２から１２のアルケニルである。好ましいＲ４またはＲ５は、紫外線または熱に対する安定性などを上げるために炭素数１から１２のアルキルであり、下限温度を下げるために、または粘度を下げるために炭素数２から１２のアルケニルである。
　好ましいアルキルは、メチル、エチル、プロピル、ブチル、ペンチル、ヘキシル、ヘプチル、またはオクチルである。さらに好ましいアルキルは、粘度を下げるために、エチル、プロピル、ブチル、ペンチル、またはヘプチルである。
　好ましいアルコキシは、メトキシ、エトキシ、プロポキシ、ブトキシ、ペンチルオキシ、ヘキシルオキシ、またはヘプチルオキシである。さらに好ましいアルコキシは、粘度を下げるために、メトキシまたはエトキシである。
　好ましいアルケニルは、ビニル、１－プロペニル、２－プロペニル、１－ブテニル、２－ブテニル、３－ブテニル、１－ペンテニル、２－ペンテニル、３－ペンテニル、４－ペンテニル、１－ヘキセニル、２－ヘキセニル、３－ヘキセニル、４－ヘキセニル、または５－ヘキセニルである。さらに好ましいアルケニルは、粘度を下げるために、ビニル、１－プロペニル、３－ブテニル、または３－ペンテニルである。これらのアルケニルにおける－ＣＨ＝ＣＨ－の好ましい立体配置は、二重結合の位置に依存する。粘度を下げるためなどから、１－プロペニル、１－ブテニル、１－ペンテニル、１－ヘキセニル、３－ペンテニル、３－ヘキセニルのようなアルケニルにおいてはトランスが好ましい。２－ブテニル、２－ペンテニル、２－ヘキセニルのようなアルケニルにおいては、シスが好ましい。これらのアルケニルにおいては、分岐よりも直鎖のアルケニルが好ましい。
　少なくとも１つの水素がフッ素で置き換えられたアルケニルの好ましい例は、２，２－ジフルオロビニル、３，３－ジフルオロ－２－プロペニル、４，４－ジフルオロ－３－ブテニル、５，５－ジフルオロ－４－ペンテニル、または６，６－ジフルオロ－５－ヘキセニルである。さらに好ましい例は、粘度を下げるために、２，２－ジフルオロビニルまたは４，４－ジフルオロ－３－ブテニルである。
　ｍおよびｊは独立して、０、１、２、または３であり、そしてｍとｊの和は３以下である。好ましいｍは、上限温度を上げるために１または２である。好ましいｊは、下限温度を下げるために０である。ｎは、１、２、または３である。好ましいｎは、下限温度を下げるために２である。ｐは、１、２、３、または４である。好ましいｐは、誘電率異方性を上げるために２または３である。
　Ｚ１およびＺ２は独立して、単結合、エチレン、ビニレン、メチレンオキシ、カルボニルオキシ、またはジフルオロメチレンオキシである。好ましいＺ１またはＺ２は、粘度を下げるために単結合である。Ｚ３は、単結合、エチレンまたはカルボニルオキシである。好ましいＺ３は、粘度を下げるために単結合である。Ｚ４は、単結合、エチレン、カルボニルオキシ、またはジフルオロメチレンオキシである。好ましいＺ４は、誘電率異方性を上げるためにジフルオロメチレンオキシである。
　環Ａおよび環Ｂは独立して、１，４－シクロへキシレン、１，４－フェニレン、２－フルオロ－１，４－フェニレン、２，３－ジフルオロ－１，４－フェニレン、２，６－ジフルオロ－１，４－フェニレン、ピリミジン－２，５－ジイル、１，３－ジオキサン－２，５－ジイル、またはテトラヒドロピラン－２，５－ジイルである。好ましい環Ａまたは環Ｂは、光学異方性を上げるために、１，４－フェニレンまたは２－フルオロ－１，４－フェニレンである。環Ｃおよび環Ｄは独立して、１，４－シクロへキシレン、１，４－フェニレン、２－フルオロ－１，４－フェニレン、または２，５－ジフルオロ－１，４－フェニレンであり、ｎが１のとき、環Ｃは１，４－フェニレンである。好ましい環Ｃまたは環Ｄは、粘度を下げるために１，４－シクロへキシレンであり、光学異方性を上げるために１，４－フェニレンである。環Ｅは、１，４－シクロへキシレン、１，４－フェニレン、２－フルオロ－１，４－フェニレン、２，６－ジフルオロ－１，４－フェニレン、ピリミジン－２，５－ジイル、１，３－ジオキサン－２，５－ジイル、またはテトラヒドロピラン－２，５－ジイルである。好ましい環Ｅは光学異方性を上げるために、１，４－フェニレンまたは２－フルオロ－１，４－フェニレンである。１，４－シクロヘキシレンに関する立体配置は、上限温度を上げるためにシスよりもトランスが好ましい。テトラヒドロピラン－２，５－ジイルは、
Figure JPOXMLDOC01-appb-I000023
　Ｘ１、Ｘ２、Ｘ３、Ｘ４、Ｘ５、Ｘ６、Ｘ７、Ｘ８、Ｘ９、およびＸ１０は独立して、水素またはフッ素である。好ましいＸ１、Ｘ２、Ｘ３、Ｘ４、Ｘ５、Ｘ６、Ｘ７、Ｘ８、Ｘ９、またはＸ１０は、誘電率異方性を上げるためにフッ素である。
　Ｙ１およびＹ２は独立して、フッ素、塩素、少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルキル、または少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルコキシである。好ましいＹ１またはＹ２は、下限温度を下げるためにフッ素である。
　第五に、好ましい成分化合物を示す。好ましい化合物（１）は、上記の化合物（１－１）から化合物（１－１４）である。これらの化合物において、第一成分の少なくとも１つが、化合物（１－３）、化合物（１－４）、化合物（１－７）、化合物（１－８）、化合物（１－９）、化合物（１－１０）、化合物（１－１２）、または化合物（１－１３）であることが好ましい。第一成分の少なくとも２つが、化合物（１－３）および化合物（１－９）、化合物（１－４）および化合物（１－７）、化合物（１－４）および化合物（１－１０）、または化合物（１－１０）および化合物（１－１３）の組み合わせであることが好ましい。
　好ましい化合物（３）は、上記の化合物（３－１）から化合物（３－１２）である。これらの化合物において、第三成分の少なくとも１つが、化合物（３－２）、化合物（３－４）、化合物（３－５）、化合物（３－６）、化合物（３－９）、または化合物（３－１２）であることが好ましい。第三成分の少なくとも２つが、化合物（３－２）および化合物（３－４）、化合物（３－２）および化合物（３－５）、または化合物（３－２）および化合物（３－６）の組み合わせであることが好ましい。
　好ましい化合物（４）は、上記の化合物（４－１）から化合物（４－２７）である。これらの化合物において、第四成分の少なくとも１つが、化合物（４－５）、化合物（４－１１）、化合物（４－１２）、化合物（４－１３）、化合物（４－１５）、化合物（４－１６）、化合物（４－２０）、化合物（４－２３）、または化合物（４－２５）であることが好ましい。第四成分の少なくとも２つが、化合物（４-１２）および化合物（４－２３）、化合物（４-１３）および化合物（４－１６）、化合物（４-１５）および化合物（４－１６）、化合物（４－１６）および化合物（４－２５）、化合物（４－２０）および化合物（４－２５）、または化合物（４－２３）および化合物（４－２５）の組み合わせであることが好ましい。
　第六に、組成物に添加してもよい添加物を説明する。このような添加物は、光学活性化合物、酸化防止剤、紫外線吸収剤、色素、消泡剤、重合性化合物、重合開始剤、重合禁止剤などである。
　液晶のらせん構造を誘起してねじれ角を与える目的で光学活性化合物が組成物に添加される。このような化合物の例は、化合物（５－１）から化合物（５－５）である。光学活性化合物の好ましい割合は約５重量％以下である。さらに好ましい割合は約０．０１重量％から約２重量％の範囲である。
Figure JPOXMLDOC01-appb-I000024
　大気中での加熱による比抵抗の低下を防止するために、または素子を長時間使用したあと、室温だけではなく上限温度に近い温度でも大きな電圧保持率を維持するために、酸化防止剤が組成物に添加される。酸化防止剤の好ましい例は、ｔが１から９の整数である化合物（６）などである。
Figure JPOXMLDOC01-appb-I000025
　化合物（６）において、好ましいｔは、１、３、５、７、または９である。さらに好ましいｔは１または７である。ｔが１である化合物（６）は、揮発性が大きいので、大気中での加熱による比抵抗の低下を防止するときに有効である。ｔが７である化合物（６）は、揮発性が小さいので、素子を長時間使用したあと、室温だけではなく上限温度に近い温度でも大きな電圧保持率を維持するのに有効である。酸化防止剤の好ましい割合は、その効果を得るために約５０ｐｐｍ以上であり、上限温度を下げないように、または下限温度を上げないように約６００ｐｐｍ以下である。さらに好ましい割合は、約１００ｐｐｍから約３００ｐｐｍの範囲である。
　紫外線吸収剤の好ましい例は、ベンゾフェノン誘導体、ベンゾエート誘導体、トリアゾール誘導体などである。立体障害のあるアミンのような光安定剤もまた好ましい。これらの吸収剤や安定剤における好ましい割合は、その効果を得るために約５０ｐｐｍ以上であり、上限温度を下げないように、または下限温度を上げないために約１００００ｐｐｍ以下である。さらに好ましい割合は約１００ｐｐｍから約１００００ｐｐｍの範囲である。
　ＧＨ（guest host）モードの素子に適合させるために、アゾ系色素、アントラキノン系色素などのような二色性色素（dichroic dye）が組成物に添加される。色素の好ましい割合は、約０．０１重量％から約１０重量％の範囲である。泡立ちを防ぐために、ジメチルシリコーンオイル、メチルフェニルシリコーンオイルなどの消泡剤が組成物に添加される。消泡剤の好ましい割合は、その効果を得るために約１ｐｐｍ以上であり、表示不良を防ぐために約１０００ｐｐｍ以下である。さらに好ましい割合は、約１ｐｐｍから約５００ｐｐｍの範囲である。
　高分子支持配向（ＰＳＡ）型の素子に適合させるために重合性化合物が組成物に添加される。重合性化合物の好ましい例はアクリレート、メタクリレート、ビニル化合物、ビニルオキシ化合物、プロペニルエーテル、エポキシ化合物（オキシラン、オキセタン）、ビニルケトンなどの重合可能な基を有する化合物である。さらに好ましい例は、アクリレートまたはメタクリレートの誘導体である。重合性化合物の好ましい割合は、その効果を得るために、約０．０５重量％以上であり、表示不良を防ぐために約１０重量％以下である。さらに好ましい割合は、約０．１重量％から約２重量％の範囲である。重合性化合物は紫外線照射により重合する。光重合開始剤などの開始剤の存在下で重合させてもよい。重合のための適切な条件、開始剤の適切なタイプ、および適切な量は、当業者には既知であり、文献に記載されている。例えば光開始剤であるＩｒｇａｃｕｒｅ６５１（登録商標；ＢＡＳＦ）、Ｉｒｇａｃｕｒｅ１８４（登録商標；ＢＡＳＦ）、またはＤａｒｏｃｕｒｅ１１７３（登録商標；ＢＡＳＦ）がラジカル重合に対して適切である。光重合開始剤の好ましい割合は、重合性化合物の重量に基づいて約０．１重量％から約５重量％の範囲である。さらに好ましい割合は、約１重量％から約３重量％の範囲である。
　重合性化合物を保管するとき、重合を防止するために重合禁止剤を添加してもよい。重合性化合物は、通常は重合禁止剤を除去しないまま組成物に添加される。重合禁止剤の例は、ヒドロキノン、メチルヒドロキノンのようなヒドロキノン誘導体、４-tert-ブチルカテコール、４-メトキシフェノ－ル、フェノチアジンなどである。
　第七に、成分化合物の合成法を説明する。これらの化合物は既知の方法によって合成できる。合成法を例示する。化合物（２）は、特開昭５９－１７６２２１号公報に記載された方法で合成する。化合物（３－１２）は、特開平２－２３７９４９号公報に記載された方法で合成する。化合物（４－３）および化合物（４－８）は、特開平２－２３３６２６号公報に記載された方法で合成する。酸化防止剤は市販されている。式（６）のｔが１である化合物は、アルドリッチ（Sigma-Aldrich Corporation）から入手できる。ｔが７である化合物（６）などは、米国特許３６６０５０５号明細書に記載された方法によって合成する。化合物（１－４）として、例えば化合物（１－４－１）は、下記記載の方法により合成する。
Figure JPOXMLDOC01-appb-I000026
第１工程
　窒素雰囲気下、化合物（Ｔ－１）（９．２５ｇ）、トルエン（２０．０ｍｌ）、および２，２，４－トリメチルペンタン（２０．０ｍｌ）を反応器に入れて、６０℃に加熱した。そこへプロパンジチオール（４．３１ｍｌ）を加え１時間撹拌したのち、トリフルオロメタンスルホン酸（７．６３ｍｌ）をゆっくりと加え１時間撹拌した。続いて留出してくる水を除去しつつ、さらに２時間加熱還流を行った。反応混合物を室温まで冷却したのち、減圧下で濃縮し、残渣をｔ－ブチルメチルエーテルからの再結晶により精製して、化合物（Ｔ－２）（１３．９ｇ；７８％）を得た。
第２工程
　窒素雰囲気下、化合物（Ｔ－３）（５．３８ｇ）、トリエチルアミン（５．４８ｍｌ）、およびジクロロメタン（５０．０ｍｌ）を反応器に入れて、－７０℃に冷却した。そこへ化合物（Ｔ－２）（１３．９ｇ）のジクロロメタン（２００ｍｌ）溶液をゆっくりと加え１時間撹拌した。次にフッ化水素トリエチルアミン錯体（１４．８ｍｌ）をゆっくりと加え３０分間撹拌した。続いて臭素（７．８０ｍｌ）をゆっくりと加えさらに１時間撹拌した。反応混合物を氷水に注ぎ込み、炭酸水素ナトリウムを用いて中和したのち、水層をジクロロメタンで抽出した。一緒にした有機層を水で洗浄し、無水硫酸マグネシウムで乾燥した。この溶液を減圧下で濃縮し、残渣をシリカゲルクロマトグラフィー（ヘプタン）で精製して、化合物（Ｔ－４）（１１．０ｇ；９３％）を得た。
第３工程
　窒素雰囲気下、化合物（Ｔ－４）（４．００ｇ）、化合物（Ｔ－５）（１．８６ｇ）、テトラキス（トリフェニルホスフィン）パラジウム（０．１１９ｇ）、炭酸カリウム（２．８４ｇ）、テトラブチルアンモニウムブロミド（ＴＢＡＢ）（０．６６３ｇ）、トルエン（４０．０ｍｌ）、ソルミックス（日本アルコール販売株式会社；登録商標）Ａ－１１（４０．０ｍｌ）、および水（４０．０ｍｌ）を反応器に入れて、５時間加熱還流を行った。反応混合物を水に注ぎ込み、水層をトルエンで抽出した。一緒にした有機層を水で洗浄し、無水硫酸マグネシウムで乾燥した。この溶液を減圧下で濃縮し、残渣をシリカゲルクロマトグラフィー（ヘプタン）で精製した。さらにソルミックス（日本アルコール販売株式会社；登録商標）Ａ－１１からの再結晶により精製して、化合物（Ｎｏ．１－４－１）（３．７３ｇ；８５％）を得た。
　化学シフトδ（ｐｐｍ；ＣＤＣｌ3）：７．５１－７．４４（ｍ，３Ｈ）、７．３３－７．２６（ｍ，３Ｈ）、７．０３－６．９６（ｍ，２Ｈ）、２．６６（ｔ，Ｊ＝７．９Ｈｚ，２Ｈ）、１．７５－１．６４（ｍ，２Ｈ）、０．９８（ｔ，Ｊ＝７．４Ｈｚ，３Ｈ）．
　合成法を記載しなかった化合物は、オーガニック・シンセシス（Organic Syntheses, John Wiley & Sons, Inc）、オーガニック・リアクションズ（Organic Reactions, John Wiley & Sons, Inc）、コンプリヘンシブ・オーガニック・シンセシス（Comprehensive Organic Synthesis, Pergamon Press）、新実験化学講座（丸善）などの成書に記載された方法によって合成できる。組成物は、このようにして得た化合物から公知の方法によって調製される。例えば、成分化合物を混合し、そして加熱によって互いに溶解させる。
　最後に、組成物の用途を説明する。本発明の組成物は主として、約－１０℃以下の下限温度、約７０℃以上の上限温度、そして約０．０７から約０．２０の範囲の光学異方性を有する。この組成物を含有する素子は大きな電圧保持率を有する。この組成物はＡＭ素子に適する。この組成物は透過型のＡＭ素子に特に適する。成分化合物の割合を制御することによって、またはその他の液晶性化合物を混合することによって、約０．０８から約０．２５の範囲の光学異方性を有する組成物、さらには約０．１０から約０．３０の範囲の光学異方性を有する組成物を調製してもよい。この組成物は、ネマチック相を有する組成物としての使用、光学活性化合物を添加することによって光学活性な組成物としての使用が可能である。
　この組成物はＡＭ素子への使用が可能である。さらにＰＭ素子への使用も可能である。この組成物は、ＰＣ、ＴＮ、ＳＴＮ、ＥＣＢ、ＯＣＢ、ＩＰＳ、ＦＦＳ、ＶＡ、ＦＰＡなどのモードを有するＡＭ素子およびＰＭ素子への使用が可能である。ＴＮ、ＯＣＢ、ＩＰＳモードまたはＦＦＳモードを有するＡＭ素子への使用は特に好ましい。ＩＰＳモードまたはＦＦＳモードを有するＡＭ素子において、電圧が無印加のとき、液晶分子の配列がガラス基板に対して並行であってもよく、または垂直であってもよい。これらの素子が反射型、透過型または半透過型であってもよい。透過型の素子への使用は好ましい。非結晶シリコン－ＴＦＴ素子または多結晶シリコン－ＴＦＴ素子への使用も可能である。この組成物をマイクロカプセル化して作製したＮＣＡＰ（nematic curvilinear aligned phase）型の素子や、組成物中に三次元の網目状高分子を形成させたＰＤ（polymer dispersed）型の素子にも使用できる。
　実施例により本発明をさらに詳しく説明する。本発明はこれらの実施例によっては制限されない。本発明は、実施例１の組成物と実施例２の組成物との混合物を含む。本発明は、実施例の組成物の少なくとも２つを混合した混合物をも含む。合成した化合物は、ＮＭＲ分析などの方法により同定した。化合物および組成物の特性は、下記に記載した方法により測定した。
　ＮＭＲ分析：測定には、ブルカーバイオスピン社製のＤＲＸ－５００を用いた。１Ｈ－ＮＭＲの測定では、試料をＣＤＣｌ３などの重水素化溶媒に溶解させ、測定は、室温で、５００ＭＨｚ、積算回数１６回の条件で行った。テトラメチルシランを内部標準として用いた。１９Ｆ－ＮＭＲの測定では、ＣＦＣｌ３を内部標準として用い、積算回数２４回で行った。核磁気共鳴スペクトルの説明において、ｓはシングレット、ｄはダブレット、ｔはトリプレット、ｑはカルテット、ｑｕｉｎはクインテット、ｓｅｘはセクステット、ｍはマルチプレット、ｂｒはブロードであることを意味する。
　ガスクロマト分析：測定には島津製作所製のＧＣ－１４Ｂ型ガスクロマトグラフを用いた。キャリアーガスはヘリウム（２ｍＬ／分）である。試料気化室を２８０℃に、検出器（ＦＩＤ）を３００℃に設定した。成分化合物の分離には、Agilent Technologies Inc.製のキャピラリカラムＤＢ－１（長さ３０ｍ、内径０．３２ｍｍ、膜厚０．２５μｍ；固定液相はジメチルポリシロキサン；無極性）を用いた。このカラムは、２００℃で２分間保持したあと、５℃／分の割合で２８０℃まで昇温した。試料はアセトン溶液（０．１重量％）に調製したあと、その１μＬを試料気化室に注入した。記録計は島津製作所製のＣ－Ｒ５Ａ型Chromatopac、またはその同等品である。得られたガスクロマトグラムは、成分化合物に対応するピークの保持時間およびピークの面積を示した。
　試料を希釈するための溶媒は、クロロホルム、ヘキサンなどを用いてもよい。成分化合物を分離するために、次のキャピラリカラムを用いてもよい。Agilent Technologies Inc.製のＨＰ－１（長さ３０ｍ、内径０．３２ｍｍ、膜厚０．２５μｍ）、Restek Corporation製のＲｔｘ－１（長さ３０ｍ、内径０．３２ｍｍ、膜厚０．２５μｍ）、SGE International Pty. Ltd製のＢＰ－１（長さ３０ｍ、内径０．３２ｍｍ、膜厚０．２５μｍ）。化合物ピークの重なりを防ぐ目的で島津製作所製のキャピラリカラムＣＢＰ１－Ｍ５０－０２５（長さ５０ｍ、内径０．２５ｍｍ、膜厚０．２５μｍ）を用いてもよい。
　組成物に含有される液晶性化合物の割合は、次のような方法で算出してよい。液晶性化合物の混合物をガスクロマトグラフ（ＦＩＤ）で検出する。ガスクロマトグラムにおけるピークの面積比は液晶性化合物の割合（重量比）に相当する。上に記載したキャピラリカラムを用いたときは、各々の液晶性化合物の補正係数を１とみなしてよい。したがって、液晶性化合物の割合（重量％）は、ピークの面積比から算出することができる。
　測定試料：組成物の特性を測定するときは、組成物をそのまま試料として用いた。化合物の特性を測定するときは、この化合物（１５重量％）を母液晶（８５重量％）に混合することによって測定用の試料を調製した。測定によって得られた値から外挿法によって化合物の特性値を算出した。（外挿値）＝｛（試料の測定値）－０．８５×（母液晶の測定値）｝／０．１５。この割合でスメクチック相（または結晶）が２５℃で析出するときは、化合物と母液晶の割合を１０重量％：９０重量％、５重量％：９５重量％、１重量％：９９重量％の順に変更した。この外挿法によって化合物に関する上限温度、光学異方性、粘度、および誘電率異方性の値を求めた。
　下記の母液晶を用いた。成分化合物の割合は重量％で示した。
Figure JPOXMLDOC01-appb-I000027
　測定方法：特性の測定は下記の方法で行った。これらの多くは、社団法人電子情報技術産業協会（Japan Electronics and Information Technology Industries Association；以下ＪＥＩＴＡという）で審議制定されるＪＥＩＴＡ規格（ＪＥＩＴＡ・ＥＤ－２５２１Ｂ）に記載された方法、またはこれを修飾した方法であった。測定に用いたＴＮ素子には、薄膜トランジスター（ＴＦＴ）を取り付けなかった。
（１）ネマチック相の上限温度（ＮＩ；℃）：偏光顕微鏡を備えた融点測定装置のホットプレートに試料を置き、１℃／分の速度で加熱した。試料の一部がネマチック相から等方性液体に変化したときの温度を測定した。ネマチック相の上限温度を「上限温度」と略すことがある。
（２）ネマチック相の下限温度（ＴＣ；℃）：ネマチック相を有する試料をガラス瓶に入れ、０℃、－１０℃、－２０℃、－３０℃、および－４０℃のフリーザー中に１０日間保管したあと、液晶相を観察した。例えば、試料が－２０℃ではネマチック相のままであり、－３０℃では結晶またはスメクチック相に変化したとき、ＴＣを＜－２０℃と記載した。ネマチック相の下限温度を「下限温度」と略すことがある。
（３）粘度（バルク粘度；η；２０℃で測定；ｍＰａ・ｓ）：測定には東京計器株式会社製のＥ型回転粘度計を用いた。
（４）粘度（回転粘度；γ１；２５℃で測定；ｍＰａ・ｓ）：測定は、M. Imai et al., Molecular Crystals and Liquid Crystals, Vol. 259, 37 (1995)に記載された方法に従った。ツイスト角が０°であり、そして２枚のガラス基板の間隔（セルギャップ）が５μｍであるＴＮ素子に試料を入れた。この素子に１６Ｖから１９．５Ｖの範囲で０．５Ｖ毎に段階的に印加した。０．２秒の無印加のあと、ただ１つの矩形波（矩形パルス；０．２秒）と無印加（２秒）の条件で印加を繰り返した。この印加によって発生した過渡電流（transient current）のピーク電流（peak current）とピーク時間（peak time）を測定した。これらの測定値とM. Imaiらの論文中の４０頁記載の計算式（８）とから回転粘度の値を得た。この計算で必要な誘電率異方性の値は、この回転粘度を測定した素子を用い、下に記載した方法で求めた。
（５）光学異方性（屈折率異方性；Δｎ；２５℃で測定）：測定は、波長５８９ｎｍの光を用い、接眼鏡に偏光板を取り付けたアッベ屈折計により行なった。主プリズムの表面を一方向にラビングしたあと、試料を主プリズムに滴下した。屈折率ｎ∥は偏光の方向がラビングの方向と平行であるときに測定した。屈折率ｎ⊥は偏光の方向がラビングの方向と垂直であるときに測定した。光学異方性の値は、Δｎ＝ｎ∥－ｎ⊥、の式から計算した。
（６）誘電率異方性（Δε；２５℃で測定）：２枚のガラス基板の間隔（セルギャップ）が９μｍであり、そしてツイスト角が８０度であるＴＮ素子に試料を入れた。この素子にサイン波（１０Ｖ、１ｋＨｚ）を印加し、２秒後に液晶分子の長軸方向における誘電率（ε∥）を測定した。この素子にサイン波（０．５Ｖ、１ｋＨｚ）を印加し、２秒後に液晶分子の短軸方向における誘電率（ε⊥）を測定した。誘電率異方性の値は、Δε＝ε∥－ε⊥、の式から計算した。
（７）しきい値電圧（Ｖｔｈ；２５℃で測定；Ｖ）：測定には大塚電子株式会社製のＬＣＤ５１００型輝度計を用いた。光源はハロゲンランプであった。２枚のガラス基板の間隔（セルギャップ）が０．４５／Δｎ（μｍ）であり、ツイスト角が８０度であるノーマリーホワイトモード（normally white mode）のＴＮ素子に試料を入れた。この素子に印加する電圧（３２Ｈｚ、矩形波）は０Ｖから１０Ｖまで０．０２Ｖずつ段階的に増加させた。この際に、素子に垂直方向から光を照射し、素子を透過した光量を測定した。この光量が最大になったときが透過率１００％であり、この光量が最小であったときが透過率０％である電圧－透過率曲線を作成した。しきい値電圧は透過率が９０％になったときの電圧で表した。
（８）電圧保持率（ＶＨＲ－１；２５℃で測定；％）：測定に用いたＴＮ素子はポリイミド配向膜を有し、そして２枚のガラス基板の間隔（セルギャップ）は５μｍであった。この素子は試料を入れたあと紫外線で硬化する接着剤で密閉した。このＴＮ素子にパルス電圧（５Ｖで６０マイクロ秒）を印加して充電した。減衰する電圧を高速電圧計で１６．７ミリ秒のあいだ測定し、単位周期における電圧曲線と横軸との間の面積Ａを求めた。面積Ｂは減衰しなかったときの面積であった。電圧保持率は面積Ｂに対する面積Ａの百分率で表した。
（９）電圧保持率（ＶＨＲ－２；８０℃で測定；％）：２５℃の代わりに、８０℃で測定した以外は、上記と同じ手順で電圧保持率を測定した。得られた値をＶＨＲ－２で表した。
（１０）電圧保持率（ＶＨＲ－３；２５℃で測定；％）：紫外線を照射したあと、電圧保持率を測定し、紫外線に対する安定性を評価した。測定に用いたＴＮ素子はポリイミド配向膜を有し、そしてセルギャップは５μｍであった。この素子に試料を注入し、光を２０分間照射した。光源は超高圧水銀ランプＵＳＨ－５００Ｄ（ウシオ電機製）であり、素子と光源の間隔は２０ｃｍであった。ＶＨＲ－３の測定では、１６．７ミリ秒のあいだ減衰する電圧を測定した。大きなＶＨＲ－３を有する組成物は紫外線に対して大きな安定性を有する。ＶＨＲ－３は９０％以上が好ましく、９５％以上がより好ましい。
（１１）電圧保持率（ＶＨＲ－４；２５℃で測定；％）：試料を注入したＴＮ素子を８０℃の恒温槽内で５００時間加熱したあと、電圧保持率を測定し、熱に対する安定性を評価した。ＶＨＲ－４の測定では、１６．７ミリ秒のあいだ減衰する電圧を測定した。大きなＶＨＲ－４を有する組成物は熱に対して大きな安定性を有する。
（１２）応答時間（τ；２５℃で測定；ｍｓ）：測定には大塚電子株式会社製のＬＣＤ５１００型輝度計を用いた。光源はハロゲンランプであった。ローパス・フィルター（Low-pass filter）は５ｋＨｚに設定した。２枚のガラス基板の間隔（セルギャップ）が５．０μｍであり、ツイスト角が８０度であるノーマリーホワイトモード（normally white mode）のＴＮ素子に試料を入れた。この素子に矩形波（６０Ｈｚ、５Ｖ、０．５秒）を印加した。この際に、素子に垂直方向から光を照射し、素子を透過した光量を測定した。この光量が最大になったときが透過率１００％であり、この光量が最小であったときが透過率０％であるとみなした。立ち上がり時間（τｒ：rise time；ミリ秒）は、透過率が９０％から１０％に変化するのに要した時間である。立ち下がり時間（τｆ：fall time；ミリ秒）は透過率１０％から９０％に変化するのに要した時間である。応答時間は、このようにして求めた立ち上がり時間と立ち下がり時間との和で表した。
（１３）弾性定数（Ｋ；２５℃で測定；ｐＮ）：測定には横河・ヒューレットパッカード株式会社製のＨＰ４２８４Ａ型ＬＣＲメータを用いた。２枚のガラス基板の間隔（セルギャップ）が２０μｍである水平配向素子に試料を入れた。この素子に０ボルトから２０ボルト電荷を印加し、静電容量および印加電圧を測定した。測定した静電容量（Ｃ）と印加電圧（Ｖ）の値を「液晶デバイスハンドブック」（日刊工業新聞社）、７５頁にある式（２．９８）、式（２．１０１）を用いてフィッティングし、式（２．９９）からＫ１１およびＫ３３の値を得た。次に同１７１頁にある式（３．１８）に、先ほど求めたＫ１１およびＫ３３の値を用いてＫ２２を算出した。弾性定数は、このようにして求めたＫ１１、Ｋ２２、およびＫ３３の平均値で表した。
（１４）比抵抗（ρ；２５℃で測定；Ωｃｍ）：電極を備えた容器に試料１．０ｍＬを注入した。この容器に直流電圧（１０Ｖ）を印加し、１０秒後の直流電流を測定した。比抵抗は次の式から算出した。（比抵抗）＝｛（電圧）×（容器の電気容量）｝／｛（直流電流）×（真空の誘電率）｝。
（１５）らせんピッチ（Ｐ；室温で測定；μｍ）：らせんピッチはくさび法にて測定した。「液晶便覧」、１９６頁（２０００年発行、丸善）を参照。試料をくさび形セルに注入し、室温で２時間静置した後、ディスクリネーションラインの間隔（ｄ２－ｄ１）を偏光顕微鏡（ニコン（株）、商品名ＭＭ４０／６０シリーズ）によって観察した。らせんピッチ（Ｐ）は、くさびセルの角度をθと表した次の式から算出した。Ｐ＝２×（ｄ２－ｄ１）×ｔａｎθ。
（１６）短軸方向における誘電率（ε⊥；２５℃で測定）：２枚のガラス基板の間隔（セルギャップ）が９μｍであり、そしてツイスト角が８０度であるＴＮ素子に試料を入れた。この素子にサイン波（０．５Ｖ、１ｋＨｚ）を印加し、２秒後に液晶分子の短軸方向における誘電率（ε⊥）を測定した。
　実施例における化合物は、下記の表３の定義に基づいて記号により表した。表３において、１，４－シクロヘキシレンに関する立体配置はトランスである。記号の後にあるかっこ内の番号は化合物の番号に対応する。（－）の記号はその他の液晶性化合物を意味する。液晶性化合物の割合（百分率）は、液晶組成物の重量に基づいた重量百分率（重量％）である。最後に、組成物の特性値をまとめた。
Figure JPOXMLDOC01-appb-I000028
［比較例１］
　国際公開第１９９６／１１８９７号パンフレットに開示された組成物の中から実施例３９を選んだ。根拠は、この組成物が化合物（４）を含有し、そしてηが最も小さいからである。この組成物の成分および特性は下記のとおりであった。
３－ＨＢＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４）　　　　　　３％
５－ＨＢＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４）　　　　　　８％
３－ＨＢＸＢ－ＯＣＦ３　　　　　　　　　　　（４）　　　　　　５％
２－ＨＢＢ（Ｆ）－Ｆ　　　　　　　　　　　　（４）　　　　　　８％
３－ＨＢＢ（Ｆ）－Ｆ　　　　　　　　　　　　（４）　　　　　　８％
５－ＨＢＢ（Ｆ）－Ｆ　　　　　　　　　　　　（４）　　　　　１６％
５－ＨＢ－Ｆ　　　　　　　　　　　　　　　　（４）　　　　　　６％
７－ＨＢ－Ｆ　　　　　　　　　　　　　　　　（４）　　　　　　６％
５－ＨＨＢ－ＯＣＦ３　　　　　　　　　　　　（４）　　　　　　８％
３－Ｈ２ＨＢ－ＯＣＦ３　　　　　　　　　　　（４）　　　　　　８％
５－Ｈ２ＨＢ－ＯＣＦ３　　　　　　　　　　　（４）　　　　　　８％
３－ＨＨ２Ｂ－ＯＣＦ３　　　　　　　　　　　（４）　　　　　　８％
５－ＨＨ２Ｂ－ＯＣＦ３　　　　　　　　　　　（４）　　　　　　８％
　ＮＩ＝８４．９℃；Δｎ＝０．１０１；Δε＝５．５；Ｖｔｈ＝２．１２Ｖ；η＝１６．６ｍＰａ・ｓ．
［比較例２］
　特開２００１－１３９５１１号公報に開示された組成物の中から使用例１８を選んだ。根拠は、この組成物が化合物（３－１）、化合物（３－４）、および化合物（４）を含有し、そしてηが最も小さいからである。この組成物の成分および特性は下記のとおりであった。
３－ＨＢｘＢ（２Ｆ，３Ｆ）－Ｏ２　　　　　　（－）　　　　　　５％
５－ＨＢｘＢ（２Ｆ，３Ｆ）－Ｏ２　　　　　　（－）　　　　　　５％
７－ＨＢ（Ｆ）－Ｆ　　　　　　　　　　　　　（４）　　　　　　５％
５－Ｈ２Ｂ（Ｆ）－Ｆ　　　　　　　　　　　　（４）　　　　　　５％
３－ＨＢ－Ｏ２　　　　　　　　　　　　　　　（３－１）　　　１０％
３－ＨＨ－４　　　　　　　　　　　　　　　　（－）　　　　　　５％
２－ＨＨＢ（Ｆ）－Ｆ　　　　　　　　　　　　（４）　　　　　１０％
３－ＨＨＢ（Ｆ）－Ｆ　　　　　　　　　　　　（４）　　　　　１０％
３－Ｈ２ＨＢ（Ｆ）－Ｆ　　　　　　　　　　　（４）　　　　　　５％
２－ＨＢＢ（Ｆ）－Ｆ　　　　　　　　　　　　（４）　　　　　　３％
３－ＨＢＢ（Ｆ）－Ｆ　　　　　　　　　　　　（４）　　　　　　３％
５－ＨＢＢ（Ｆ）－Ｆ　　　　　　　　　　　　（４）　　　　　　６％
２－Ｈ２ＢＢ（Ｆ）－Ｆ　　　　　　　　　　　（４）　　　　　　５％
３－Ｈ２ＢＢ（Ｆ）－Ｆ　　　　　　　　　　　（４）　　　　　　６％
３－ＨＨＢ－１　　　　　　　　　　　　　　　（３－４）　　　　８％
３－ＨＨＢ－Ｏ１　　　　　　　　　　　　　　（３－４）　　　　５％
３－ＨＨＢ－３　　　　　　　　　　　　　　　（３－４）　　　　４％
　ＮＩ＝８９．２℃；Δｎ＝０．０９９；Δε＝２．２；Ｖｔｈ＝３．０５Ｖ；η＝２０．２ｍＰａ・ｓ．
［実施例１］
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　１９％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　３２％
３－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　　５％
Ｖ－ＨＨＢ－１　　　　　　　　　　　　　　　（３－４）　　　１３％
１－ＢＢ（Ｆ）Ｂ－２Ｖ　　　　　　　　　　　（３－６）　　　　２％
２－ＨＨＢＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－１７）　　　３％
３－ＨＨＢＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－１７）　　　３％
３－ＨＢＢＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　（４－２０）　　　８％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２５）　　　２％
４－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２５）　　　７％
５－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２５）　　　６％
　ＮＩ＝８６．３℃；Ｔｃ＜－２０℃；Δｎ＝０．１１６；Δε＝７．６；Ｖｔｈ＝１．５６Ｖ；η＝１０．０ｍＰａ・ｓ；γ１＝８０．１ｍＰａ・ｓ；ε⊥／Δε＝０．４７．
［実施例２］
５－ＨＢ（２Ｆ，３Ｆ）Ｂ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ
　　　　　　　　　　　　　　　　　　　　　　（１）　　　　　　６％
３－ＧＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－３）　　　　７％
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　　８％
４－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　２０％
４－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　１２％
７－ＨＢ－１　　　　　　　　　　　　　　　　（３－１）　　　　３％
３－ＨＨＥＨ－３　　　　　　　　　　　　　　（３－３）　　　　３％
３－ＨＨＥＨ－５　　　　　　　　　　　　　　（３－３）　　　　４％
３－ＨＢＢ－２　　　　　　　　　　　　　　　（３－５）　　　　３％
５－Ｂ（Ｆ）ＢＢ－２　　　　　　　　　　　　（３－７）　　　　５％
５－Ｂ（Ｆ）ＢＢ－３　　　　　　　　　　　　（３－７）　　　　３％
３－ＨＨＸＢ（Ｆ，Ｆ）－ＣＦ３　　　　　　　（４）　　　　　　６％
３－ＨＢ－ＣＬ　　　　　　　　　　　　　　　（４－１）　　　　３％
３－ＨＢＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－８）　　　　３％
３－ＧＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　　（４－１２）　　　５％
３－ＨＢＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　（４－２１）　　　３％
３－ＢＢ（Ｆ，Ｆ）ＸＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ（４－２６）　　　３％
５－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ
　　　　　　　　　　　　　　　　　　　　　　（４－２７）　　　３％
　ＮＩ＝７１．４℃；Ｔｃ＜－２０℃；Δｎ＝０．１０５；Δε＝７．０；Ｖｔｈ＝１．６５Ｖ；η＝１３．９ｍＰａ・ｓ；γ１＝８３．７ｍＰａ・ｓ；ε⊥／Δε＝０．５１．
［実施例３］
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）－Ｆ　　　　（１－４）　　　　５％
３－ＨＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－７）　　　　５％
３－ｄｈＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（１－８）　　　　５％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　１０％
３－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　　５％
３－ＨＨ－ＶＦＦ　　　　　　　　　　　　　　（２）　　　　　２２％
Ｖ２－ＢＢ－１　　　　　　　　　　　　　　　（３－２）　　　　５％
３－ＨＢ（Ｆ）ＨＨ－２　　　　　　　　　　　（３－８）　　　　４％
５－ＨＢＢ（Ｆ）Ｂ－２　　　　　　　　　　　（３－１２）　　　４％
５－ＨＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－２）　　　　４％
３－ＨＨＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－５）　　　　６％
３－ＢＢＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－１５）　　　３％
３－ＢＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　　（４－１６）　　　３％
３－ｄｈＢＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（４－２２）　　　５％
３－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２３）　　　５％
５－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２３）　　　４％
１Ｏ１－ＨＢＢＨ－５　　　　　　　　　　　　（－）　　　　　　５％
　ＮＩ＝８６．２℃；Ｔｃ＜－２０℃；Δｎ＝０.１１２；Δε＝７．８；Ｖｔｈ＝１．５３Ｖ；η＝１１．１ｍＰａ・ｓ；γ１＝８１．１ｍＰａ・ｓ；ε⊥／Δε＝０．４６．
［実施例４］
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　１０％
３－ＧＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－９）　　　　６％
３－ＧＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）－Ｆ　　　（１－９）　　　　５％
１Ｖ２－ＨＨ－１　　　　　　　　　　　　　　（２）　　　　　１０％
１Ｖ２－ＨＨ－３　　　　　　　　　　　　　　（２）　　　　　１２％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　１９％
３－ＢＢ（２Ｆ，５Ｆ）Ｂ－３　　　　　　　　（３）　　　　　　３％
３－ＨＨＥＢＨ－３　　　　　　　　　　　　　（３－９）　　　　５％
３－ＨＨＥＢＨ－５　　　　　　　　　　　　　（３－９）　　　　５％
３－ＨＨＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－３）　　　　６％
３－ＨＧＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－６）　　　　３％
Ｖ－ＨＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　　（４－９）　　　　５％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　　（４－１３）　　　３％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）－Ｆ　　（４－２４）　　　３％
４－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）－Ｆ　　（４－２４）　　　５％
　ＮＩ＝９３．９℃；Ｔｃ＜－２０℃；Δｎ＝０．１１０；Δε＝５．７；Ｖｔｈ＝１．８１Ｖ；η＝１３．４ｍＰａ・ｓ；γ１＝８３．０ｍＰａ・ｓ；ε⊥／Δε＝０．４９．
［実施例５］
３－ＧＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－３）　　　　６％
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）－Ｆ　　　　（１－４）　　　　８％
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　　７％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　２５％
３－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　　６％
１Ｖ２－ＢＢ－１　　　　　　　　　　　　　　（３－２）　　　　４％
５－ＨＢＢＨ－３　　　　　　　　　　　　　　（３－１０）　　　６％
５－ＨＥＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４）　　　　　　３％
３－ＨＨＢ－ＣＬ　　　　　　　　　　　　　　（４）　　　　　　５％
５－ＨＨＢ－ＣＬ　　　　　　　　　　　　　　（４）　　　　　　４％
３－ＨＨＥＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－４）　　　　４％
５－ＨＨＥＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－４）　　　　４％
３－ＨＢＥＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－１０）　　　３％
５－ＨＢＥＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－１０）　　　３％
４－ＨＨＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　（４－１８）　　　７％
４－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ、Ｆ）－Ｆ（４－２５）　　　５％
　ＮＩ＝８３．９℃；Ｔｃ＜－２０℃；Δｎ＝０．１０５；Δε＝６．４；Ｖｔｈ＝１．６９Ｖ；η＝１２．２ｍＰａ・ｓ；γ１＝８２．２ｍＰａ・ｓ；ε⊥／Δε＝０．５０．
［実施例６］
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　１０％
３－ＨＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－７）　　　　５％
３－ｄｈＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（１－８）　　　　５％
４－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　１２％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　２０％
３－ＨＨＢ－１　　　　　　　　　　　　　　　（３－４）　　　　６％
３－ＨＨＢ－３　　　　　　　　　　　　　　　（３－４）　　　　７％
５－ＨＢ（Ｆ）ＢＨ－３　　　　　　　　　　　（３－１１）　　　２％
３－Ｈ２ＧＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４）　　　　　　４％
３－ＧＨＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－７）　　　　３％
５－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　　（４－１１）　　　３％
３－ＢＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　　（４－１６）　　　６％
３－ＧＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　（４－１９）　　　３％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）－Ｆ　　（４－２４）　　　５％
１Ｏ１－ＨＢＢＨ－３　　　　　　　　　　　　（－）　　　　　　３％
１Ｏ１－ＨＢＢＨ－４　　　　　　　　　　　　（－）　　　　　　３％
１Ｏ１－ＨＢＢＨ－５　　　　　　　　　　　　（－）　　　　　　３％
　ＮＩ＝９４．９℃；Ｔｃ＜－２０℃；Δｎ＝０.１１０；Δε＝６．１；Ｖｔｈ＝１．７４Ｖ；η＝１４．６ｍＰａ・ｓ；γ１＝８４．０ｍＰａ・ｓ；ε⊥／Δε＝０．４８．
［実施例７］
５－ＨＢ（２Ｆ，３Ｆ）Ｂ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ
　　　　　　　　　　　　　　　　　　　　　　（１）　　　　　　４％
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　　９％
３－ＧＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－９）　　　　５％
３－ＧＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）－Ｆ　　　（１－９）　　　　５％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　２０％
３－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　　４％
３－ＨＨ－ＶＦＦ　　　　　　　　　　　　　　（２）　　　　　　３％
３－ＨＨＥＨ－３　　　　　　　　　　　　　　（３－３）　　　　４％
３－ＨＨＥＨ－５　　　　　　　　　　　　　　（３－３）　　　　３％
４－ＨＨＥＨ－３　　　　　　　　　　　　　　（３－３）　　　　４％
Ｖ２－ＢＢ（Ｆ）Ｂ－１　　　　　　　　　　　（３－６）　　　　２％
３－ＨＨＢ－Ｆ　　　　　　　　　　　　　　　（４）　　　　　　４％
５－ＨＢ－ＣＬ　　　　　　　　　　　　　　　（４－１）　　　　５％
１－ＨＨＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－５）　　　　５％
３－ＨＨＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－５）　　　　５％
３－ＧＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　　（４－１２）　　　８％
３－ＨＨＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　（４－１８）　　　４％
３－ＨＨ－５　　　　　　　　　　　　　　　　（－）　　　　　　６％
　ＮＩ＝７９．９℃；Ｔｃ＜－２０℃；Δｎ＝０.０９２；Δε＝６．３；Ｖｔｈ＝１．７０Ｖ；η＝１２．１ｍＰａ・ｓ；γ１＝８２．０ｍＰａ・ｓ；ε⊥／Δε＝０．５１．
［実施例８］
３－ＧＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－３）　　　１０％
３－ＨＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－７）　　　　５％
３－ｄｈＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（１－８）　　　　６％
５－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　　６％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　３１％
３－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　　８％
５－Ｂ（Ｆ）ＢＢ－２　　　　　　　　　　　　（３－７）　　　　３％
５－Ｂ（Ｆ）ＢＢ－３　　　　　　　　　　　　（３－７）　　　　２％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）－ＣＦ３　　　　　（４－１４）　　　４％
５－ＨＢＢＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　（４－２０）　　　８％
３－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２３）　　　２％
４－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２３）　　　５％
５－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２３）　　　７％
３－ＨＨ－Ｏ１　　　　　　　　　　　　　　　（－）　　　　　　３％
　ＮＩ＝７８．７℃；Ｔｃ＜－２０℃；Δｎ＝０．１０５；Δε＝９．１；Ｖｔｈ＝１．３５Ｖ；η＝１３．０ｍＰａ・ｓ；γ１＝８２．７ｍＰａ・ｓ；ε⊥／Δε＝０．４７．
［実施例９］
５－ＨＢ（２Ｆ，３Ｆ）Ｂ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ
　　　　　　　　　　　　　　　　　　　　　　（１）　　　　　　４％
３－ＧＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－３）　　　　８％
３－ＧＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－９）　　　　５％
３－ＧＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）－Ｆ　　　（１－９）　　　　５％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　１８％
４－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　１０％
５－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　１０％
５－ＨＢ－Ｏ２　　　　　　　　　　　　　　　（３－１）　　　　４％
Ｖ－ＨＨＢ－１　　　　　　　　　　　　　　　（３－４）　　　　８％
３－ＨＨ２ＢＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　（４）　　　　　　３％
４－ＨＨ２ＢＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　（４）　　　　　　３％
３－ＨＨＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－３）　　　　４％
５－ＨＨＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－３）　　　　３％
３－ＨＢＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－８）　　　　５％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２５）　　　２％
５－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２５）　　　６％
５－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ
　　　　　　　　　　　　　　　　　　　　　　（４－２７）　　　２％
　ＮＩ＝８５．６℃；Ｔｃ＜－２０℃；Δｎ＝０．１０３；Δε＝６．７；Ｖｔｈ＝１．６６Ｖ；η＝１４．２ｍＰａ・ｓ；γ１＝８３．９ｍＰａ・ｓ；ε⊥／Δε＝０．５１．
［実施例１０］
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）－Ｆ　　　　（１－４）　　　　６％
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　　６％
３－ＨＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－７）　　　　５％
３－ｄｈＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（１－８）　　　　５％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　２６％
３－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　　５％
３－ＨＨ－ＶＦＦ　　　　　　　　　　　　　　（２）　　　　　　４％
１Ｖ－ＨＢＢ－２　　　　　　　　　　　　　　（３－５）　　　　５％
３－ＨＨＥＢＨ－４　　　　　　　　　　　　　（３－９）　　　　３％
３－ＨＨＥＢＨ－５　　　　　　　　　　　　　（３－９）　　　　４％
５－ＨＢ（Ｆ）ＢＨ－３　　　　　　　　　　　（３－１１）　　　５％
５－ＨＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－２）　　　　６％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　　（４－１３）　　　３％
３－ＨＢＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　（４－２１）　　　３％
２－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）－Ｆ　　（４－２４）　　　３％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）－Ｆ　　（４－２４）　　　３％
４－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）－Ｆ　　（４－２４）　　　４％
３－ＨＨ－４　　　　　　　　　　　　　　　　（－）　　　　　　４％
　ＮＩ＝９３．２℃；Ｔｃ＜－２０℃；Δｎ＝０.１１２；Δε＝５．４；Ｖｔｈ＝１．８５Ｖ；η＝９．４ｍＰａ・ｓ；γ１＝７８．４ｍＰａ・ｓ；ε⊥／Δε＝０．５１．
［実施例１１］
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－ＣＦ３（１－４）　　　１９％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　３２％
３－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　　５％
Ｖ－ＨＨＢ－１　　　　　　　　　　　　　　　（３－４）　　　１３％
１－ＢＢ（Ｆ）Ｂ－２Ｖ　　　　　　　　　　　（３－６）　　　　２％
２－ＨＨＢＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－１７）　　　３％
３－ＨＨＢＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－１７）　　　３％
３－ＨＢＢＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　（４－２０）　　　８％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２５）　　　２％
４－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２５）　　　７％
５－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２５）　　　６％
　ＮＩ＝８５．９℃；Ｔｃ＜－２０℃；Δｎ＝０．１１７；Δε＝９．４；Ｖｔｈ＝１．４９Ｖ；η＝１１．６ｍＰａ・ｓ；γ１＝８１．９ｍＰａ・ｓ；ε⊥／Δε＝０．４８．
［実施例１２］
３－ＨＨ１ＯＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ
　　　　　　　　　　　　　　　　　　　　　　（１）　　　　　　６％
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　　８％
４－ＢＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－１０）　　　７％
４－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　２０％
４－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　１２％
７－ＨＢ－１　　　　　　　　　　　　　　　　（３－１）　　　　３％
３－ＨＨＥＨ－３　　　　　　　　　　　　　　（３－３）　　　　３％
３－ＨＨＥＨ－５　　　　　　　　　　　　　　（３－３）　　　　４％
３－ＨＢＢ－２　　　　　　　　　　　　　　　（３－５）　　　　３％
５－Ｂ（Ｆ）ＢＢ－２　　　　　　　　　　　　（３－７）　　　　５％
５－Ｂ（Ｆ）ＢＢ－３　　　　　　　　　　　　（３－７）　　　　３％
３－ＨＨＸＢ（Ｆ，Ｆ）－ＣＦ３　　　　　　　（４）　　　　　　６％
３－ＨＢ－ＣＬ　　　　　　　　　　　　　　　（４－１）　　　　３％
３－ＨＢＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－８）　　　　３％
３－ＧＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　　（４－１２）　　　５％
３－ＨＢＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　（４－２１）　　　３％
３－ＢＢ（Ｆ，Ｆ）ＸＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ（４－２６）　　　３％
５－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ
　　　　　　　　　　　　　　　　　　　　　　（４－２７）　　　３％
　ＮＩ＝８０．７℃；Ｔｃ＜－２０℃；Δｎ＝０．１１２；Δε＝５．９；Ｖｔｈ＝１．７０Ｖ；η＝１４．５ｍＰａ・ｓ；γ１＝８４．０ｍＰａ・ｓ；ε⊥／Δε＝０．５０．
［実施例１３］
５－ＨＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ
　　　　　　　　　　　　　　　　　　　　　　（１）　　　　　　５％
３－ＨＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）－ＯＣＦ３（１－７）　　　　５％
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ
　　　　　　　　　　　　　　　　　　　　　　（１－１３）　　　５％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　１０％
３－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　　５％
３－ＨＨ－ＶＦＦ　　　　　　　　　　　　　　（２）　　　　　２２％
Ｖ２－ＢＢ－１　　　　　　　　　　　　　　　（３－２）　　　　５％
３－ＨＢ（Ｆ）ＨＨ－２　　　　　　　　　　　（３－８）　　　　４％
５－ＨＢＢ（Ｆ）Ｂ－２　　　　　　　　　　　（３－１２）　　　４％
５－ＨＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－２）　　　　４％
３－ＨＨＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－５）　　　　６％
３－ＢＢＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－１５）　　　３％
３－ＢＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　　（４－１６）　　　３％
３－ｄｈＢＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（４－２２）　　　５％
３－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２３）　　　５％
５－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２３）　　　４％
１Ｏ１－ＨＢＢＨ－５　　　　　　　　　　　　（－）　　　　　　５％
　ＮＩ＝９２．７℃；Ｔｃ＜－２０℃；Δｎ＝０.１１６；Δε＝８．１；Ｖｔｈ＝１．５０Ｖ；η＝１３．０ｍＰａ・ｓ；γ１＝７６．５ｍＰａ・ｓ；ε⊥／Δε＝０．４７．
［実施例１４］
３－Ｂ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　（１－１）　　　　５％
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　１０％
２Ｏ－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－４）　　　　６％
１Ｖ２－ＨＨ－１　　　　　　　　　　　　　　（２）　　　　　１０％
１Ｖ２－ＨＨ－３　　　　　　　　　　　　　　（２）　　　　　１２％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　１９％
３－ＢＢ（２Ｆ，５Ｆ）Ｂ－３　　　　　　　　（３）　　　　　　３％
３－ＨＨＥＢＨ－３　　　　　　　　　　　　　（３－９）　　　　５％
３－ＨＨＥＢＨ－５　　　　　　　　　　　　　（３－９）　　　　５％
３－ＨＨＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－３）　　　　６％
３－ＨＧＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－６）　　　　３％
Ｖ－ＨＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　　（４－９）　　　　５％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　　（４－１３）　　　３％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）－Ｆ　　（４－２４）　　　３％
４－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）－Ｆ　　（４－２４）　　　５％
　ＮＩ＝７５．６℃；Ｔｃ＜－２０℃；Δｎ＝０．０９９；Δε＝５．５；Ｖｔｈ＝１．８３Ｖ；η＝９．２ｍＰａ・ｓ；γ１＝７３．５ｍＰａ・ｓ；ε⊥／Δε＝０．５０．
［実施例１５］
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　　７％
２Ｏ－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－ＣＦ３
　　　　　　　　　　　　　　　　　　　　　　（１－４）　　　　６％
２Ｏ－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）－ＯＣＦ３（１－４）　　　　８％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　２５％
３－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　　６％
１Ｖ２－ＢＢ－１　　　　　　　　　　　　　　（３－２）　　　　４％
５－ＨＢＢＨ－３　　　　　　　　　　　　　　（３－１０）　　　６％
５－ＨＥＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４）　　　　　　３％
３－ＨＨＢ－ＣＬ　　　　　　　　　　　　　　（４）　　　　　　５％
５－ＨＨＢ－ＣＬ　　　　　　　　　　　　　　（４）　　　　　　４％
３－ＨＨＥＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－４）　　　　４％
５－ＨＨＥＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－４）　　　　４％
３－ＨＢＥＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－１０）　　　３％
５－ＨＢＥＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－１０）　　　３％
４－ＨＨＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　（４－１８）　　　７％
４－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ、Ｆ）－Ｆ（４－２５）　　　５％
　ＮＩ＝８９．３℃；Ｔｃ＜－２０℃；Δｎ＝０．１１２；Δε＝７．３；Ｖｔｈ＝１．６２Ｖ；η＝１３．１ｍＰａ・ｓ；γ１＝８４．１ｍＰａ・ｓ；ε⊥／Δε＝０．４９．
［実施例１６］
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　１０％
１Ｖ２－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（１－４）　　　　５％
１Ｖ２－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－ＣＦ３
　　　　　　　　　　　　　　　　　　　　　　（１－４）　　　　５％
４－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　１２％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　２０％
３－ＨＨＢ－１　　　　　　　　　　　　　　　（３－４）　　　　６％
３－ＨＨＢ－３　　　　　　　　　　　　　　　（３－４）　　　　７％
５－ＨＢ（Ｆ）ＢＨ－３　　　　　　　　　　　（３－１１）　　　２％
３－Ｈ２ＧＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４）　　　　　　４％
３－ＧＨＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　　（４－７）　　　　３％
５－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　　（４－１１）　　　３％
３－ＢＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　　（４－１６）　　　６％
３－ＧＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　（４－１９）　　　３％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ）－Ｆ　　（４－２４）　　　５％
１Ｏ１－ＨＢＢＨ－３　　　　　　　　　　　　（－）　　　　　　３％
１Ｏ１－ＨＢＢＨ－４　　　　　　　　　　　　（－）　　　　　　３％
１Ｏ１－ＨＢＢＨ－５　　　　　　　　　　　　（－）　　　　　　３％
　ＮＩ＝８６．３℃；Ｔｃ＜－２０℃；Δｎ＝０.１０９；Δε＝６．９；Ｖｔｈ＝１．７０Ｖ；η＝１２．２ｍＰａ・ｓ；γ１＝８０．２ｍＰａ・ｓ；ε⊥／Δε＝０．４８．
［実施例１７］
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　（１－４）　　　　９％
２Ｏ－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－４）　　　　５％
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ
　　　　　　　　　　　　　　　　　　　　　　（１－１３）　　　４％
３－ＧＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ）－Ｆ　　　（１－９）　　　　５％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　２０％
３－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　　４％
３－ＨＨ－ＶＦＦ　　　　　　　　　　　　　　（２）　　　　　　３％
３－ＨＨＥＨ－３　　　　　　　　　　　　　　（３－３）　　　　４％
３－ＨＨＥＨ－５　　　　　　　　　　　　　　（３－３）　　　　３％
４－ＨＨＥＨ－３　　　　　　　　　　　　　　（３－３）　　　　４％
Ｖ２－ＢＢ（Ｆ）Ｂ－１　　　　　　　　　　　（３－６）　　　　２％
３－ＨＨＢ－Ｆ　　　　　　　　　　　　　　　（４）　　　　　　４％
５－ＨＢ－ＣＬ　　　　　　　　　　　　　　　（４－１）　　　　５％
１－ＨＨＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－５）　　　　５％
３－ＨＨＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　　（４－５）　　　　５％
３－ＧＢ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　　　　（４－１２）　　　８％
３－ＨＨＢ（Ｆ）Ｂ（Ｆ，Ｆ）－Ｆ　　　　　　（４－１８）　　　４％
３－ＨＨ－５　　　　　　　　　　　　　　　　（－）　　　　　　６％
　ＮＩ＝７５．２℃；Ｔｃ＜－２０℃；Δｎ＝０.０９２；Δε＝６．５；Ｖｔｈ＝１．６８Ｖ；η＝９．５ｍＰａ・ｓ；γ１＝７２．６ｍＰａ・ｓ；ε⊥／Δε＝０．５０．
［実施例１８］
３－ＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－ＣＦ３（１－４）　　　１０％
３－ＨＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－７）　　　　５％
４－ＢＢＢ（２Ｆ，３Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ　（１－１０）　　　６％
５－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　　６％
３－ＨＨ－Ｖ　　　　　　　　　　　　　　　　（２）　　　　　３１％
３－ＨＨ－Ｖ１　　　　　　　　　　　　　　　（２）　　　　　　８％
５－Ｂ（Ｆ）ＢＢ－２　　　　　　　　　　　　（３－７）　　　　３％
５－Ｂ（Ｆ）ＢＢ－３　　　　　　　　　　　　（３－７）　　　　２％
３－ＢＢ（Ｆ）Ｂ（Ｆ，Ｆ）－ＣＦ３　　　　　（４－１４）　　　４％
５－ＨＢＢＸＢ（Ｆ，Ｆ）－Ｆ　　　　　　　　（４－２０）　　　８％
３－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２３）　　　２％
４－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２３）　　　５％
５－ＧＢ（Ｆ）Ｂ（Ｆ，Ｆ）ＸＢ（Ｆ，Ｆ）－Ｆ（４－２３）　　　７％
３－ＨＨ－Ｏ１　　　　　　　　　　　　　　　（－）　　　　　　３％
　ＮＩ＝７８．２℃；Ｔｃ＜－２０℃；Δｎ＝０．１１３；Δε＝９．２；Ｖｔｈ＝１．３４Ｖ；η＝１２．１ｍＰａ・ｓ；γ１＝７７．３ｍＰａ・ｓ；ε⊥／Δε＝０．４８．
　比較例１から比較例２の組成物の粘度（η）は、１６．６から２０．２であった。一方、実施例１から実施例１８の組成物の粘度は、９．２から１４．６であった。このように、実施例の組成物は、比較例の組成物と比べて、小さな粘度を有した。したがって、本発明の液晶組成物は優れた特性を有すると結論される。
　本発明の液晶組成物は、高い上限温度、低い下限温度、小さな粘度、適切な光学異方性、大きな誘電率異方性、大きな比抵抗、大きな弾性定数、紫外線に対する高い安定性、熱に対する高い安定性、大きな弾性定数などの特性において、少なくとも１つの特性を充足する、または少なくとも２つの特性に関して適切なバランスを有する。この組成物を含有する液晶表示素子は、短い応答時間、大きな電圧保持率、大きなコントラスト比、長い寿命などを有するので、液晶プロジェクター、液晶テレビなどに用いることができる。

Claims (13)

  1. 　第一成分として式（１）で表される化合物の群から選択された少なくとも１つの化合物、および第二成分として式（２）で表される化合物の群から選択された少なくとも１つの化合物を含有し、そしてネマチック相を有する液晶組成物。
    Figure JPOXMLDOC01-appb-I000001

    式（１）および式（２）において、Ｒ１およびＲ２は独立して、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、または炭素数２から１２のアルケニルであり；Ｒ３は、炭素数２から１２のアルケニル、または少なくとも１つの水素がフッ素で置き換えられた炭素数２から１２のアルケニルであり；環Ａおよび環Ｂは独立して、１，４－シクロへキシレン、１，４－フェニレン、２－フルオロ－１，４－フェニレン、２，３－ジフルオロ－１，４－フェニレン、２，６－ジフルオロ－１，４－フェニレン、ピリミジン－２，５－ジイル、１，３－ジオキサン－２，５－ジイル、またはテトラヒドロピラン－２，５－ジイルであり；Ｚ１およびＺ２は独立して、単結合、エチレン、ビニレン、メチレンオキシ、カルボニルオキシ、またはジフルオロメチレンオキシであり；Ｌ１およびＬ２は独立して、フッ素または塩素であり；Ｘ１およびＸ２は独立して、水素またはフッ素であり；Ｙ１は、フッ素、塩素、少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルキル、または少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルコキシであり；ｍおよびｊは独立して、０、１、２、または３であり、そしてｍとｊの和は３以下である。
  2. 　第一成分として式（１－１）から式（１－１４）で表される化合物の群から選択された少なくとも１つの化合物を含有する、請求項１に記載の液晶組成物。
    Figure JPOXMLDOC01-appb-I000002

    Figure JPOXMLDOC01-appb-I000003

    式（１－１）から式（１－１４）において、Ｒ１は、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、または炭素数２から１２のアルケニルであり；Ｌ１およびＬ２は独立して、フッ素または塩素であり；Ｘ１、Ｘ２、Ｘ３、Ｘ４、Ｘ５、Ｘ６、Ｘ７、およびＸ８は独立して、水素またはフッ素であり；Ｙ１は、フッ素、塩素、少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルキル、または少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルコキシである。
  3. 　液晶組成物の重量に基づいて、第一成分の割合が５重量％から４０重量％の範囲であり、第二成分の割合が１５重量％から６０重量％の範囲である、請求項１または２に記載の液晶組成物。
  4. 　第三成分として式（３）で表される化合物の群から選択された少なくとも１つの化合物をさらに含有する、請求項１から３のいずれか１項に記載の液晶組成物。
    Figure JPOXMLDOC01-appb-I000004

    式（３）において、Ｒ４およびＲ５は独立して、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、炭素数２から１２のアルケニル、または少なくとも１つの水素がフッ素で置き換えられた炭素数２から１２のアルケニルであり；環Ｃおよび環Ｄは独立して、１，４－シクロへキシレン、１，４－フェニレン、２－フルオロ－１，４－フェニレン、または２，５－ジフルオロ－１，４－フェニレンであり；Ｚ３は、単結合、エチレンまたはカルボニルオキシであり；ｎは、１、２、または３であり；ただしｎが１のとき、環Ｃは１，４－フェニレンである。
  5. 　第三成分として式（３－１）から式（３－１２）で表される化合物の群から選択された少なくとも１つの化合物を含有する、請求項１から４のいずれか１項に記載の液晶組成物。
    Figure JPOXMLDOC01-appb-I000005

    式（３－１）から式（３－１２）において、Ｒ４およびＲ５は独立して、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、炭素数２から１２のアルケニル、または少なくとも１つの水素がフッ素で置き換えられた炭素数２から１２のアルケニルである。
  6. 　液晶組成物の重量に基づいて、第三成分の割合が５重量％から３５重量％の範囲である、請求項４または５に記載の液晶組成物。
  7. 　第四成分として式（４）で表される化合物の群から選択された少なくとも１つの化合物をさらに含有する、請求項１から６のいずれか１項に記載の液晶組成物。
    Figure JPOXMLDOC01-appb-I000006

    式（４）において、Ｒ６は炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、または炭素数２から１２のアルケニルであり；環Ｅは、１，４－シクロへキシレン、１，４－フェニレン、２－フルオロ－１，４－フェニレン、２，６－ジフルオロ－１，４－フェニレン、ピリミジン－２，５－ジイル、１，３－ジオキサン－２，５－ジイル、またはテトラヒドロピラン－２，５－ジイルであり；Ｚ４は、単結合、エチレン、カルボニルオキシ、またはジフルオロメチレンオキシであり；Ｘ９およびＸ１０は独立して、水素またはフッ素であり；Ｙ２は、フッ素、塩素、少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルキル、または少なくとも１つの水素がハロゲンで置き換えられた炭素数１から１２のアルコキシであり；ｐは、１、２、３、または４である。
  8. 　第四成分として式（４－１）から式（４－２７）で表される化合物の群から選択された少なくとも１つの化合物を含有する、請求項１から７のいずれか１項に記載の液晶組成物。
    Figure JPOXMLDOC01-appb-I000007

    Figure JPOXMLDOC01-appb-I000008

    Figure JPOXMLDOC01-appb-I000009

    式（４－１）から式（４－２７）において、Ｒ６は、炭素数１から１２のアルキル、炭素数１から１２のアルコキシ、または炭素数２から１２のアルケニルである。
  9. 　液晶組成物の重量に基づいて、第四成分の割合が１０重量％から６０重量％の範囲である、請求項７または８に記載の液晶組成物。
  10. 　ネマチック相の上限温度が７０℃以上であり、波長５８９ｎｍにおける光学異方性（２５℃で測定）が０．０７以上であり、そして周波数１ｋＨｚにおける誘電率異方性（２５℃で測定）が２以上である、請求項１から９のいずれか１項に記載の液晶組成物。
  11. 　請求項１から１０のいずれか１項に記載の液晶組成物を含有する液晶表示素子。
  12. 　液晶表示素子の動作モードが、ＴＮモード、ＥＣＢモード、ＯＣＢモード、ＩＰＳモード、ＦＦＳモード、またはＦＰＡモードであり、液晶表示素子の駆動方式がアクティブマトリックス方式である、請求項１１に記載の液晶表示素子。
  13. 　請求項１から１０のいずれか１項に記載の液晶組成物の液晶表示素子における使用。
PCT/JP2014/058256 2013-05-28 2014-03-25 液晶組成物および液晶表示素子 WO2014192390A1 (ja)