KR101529910B1 - Tips for cutting stone and its manufacturing method - Google Patents
Tips for cutting stone and its manufacturing method Download PDFInfo
- Publication number
- KR101529910B1 KR101529910B1 KR1020130135177A KR20130135177A KR101529910B1 KR 101529910 B1 KR101529910 B1 KR 101529910B1 KR 1020130135177 A KR1020130135177 A KR 1020130135177A KR 20130135177 A KR20130135177 A KR 20130135177A KR 101529910 B1 KR101529910 B1 KR 101529910B1
- Authority
- KR
- South Korea
- Prior art keywords
- cutting
- stone
- layer
- mixture
- tip
- Prior art date
Abstract
본 발명은 석재 절삭용 팁 및 그 제조방법에 관한 것으로, 그 목적은 절삭휠(Shank)의 외주면을 따라 일단이 용접으로 고정되는 절삭용 팁을 인조 다이아몬드 입자가 혼합된 혼합층과 금속분말층을 교번되게 구성하여 형성함으로써, 고가의 인조 다이아몬드를 절약할 수 있고, 절삭휠의 절삭성능을 향상시킬 수 있도록 함과 아울러 인조 다이아몬드 입자가 혼합된 혼합층으로만 석재를 절삭하게 되므로 구동모터의 부하를 줄일 수 있도록 하는 것에 있으며, 이러한 목적은 절삭휠의 회전시 석재를 타격시키는 것에 의해 석재를 탈락시켜 절단가능하도록 구비되는 금속분말층과, 상기 금속분말층 양면에 위치되어 상기 절삭휠이 구동모터에 의해 회전시 석재를 절삭가능하도록 인조 다이아몬드 입자가 혼합되어 구비되는 절삭층을 포함하여 이루어진 것을 특징으로 석재 절삭용 팁 및 그 제조방법에 의해 달성된다.The present invention relates to a tip for cutting a stone and a method for manufacturing the same, and an object of the present invention is to provide a tip for cutting a stone and a method for manufacturing the same, which is characterized in that a cutting tip, one end of which is fixed by welding along an outer peripheral surface of a cutting wheel, Thus, it is possible to save expensive artificial diamonds, improve the cutting performance of the cutting wheel, cut the stone only with the mixed layer of artificial diamond particles, and thus reduce the load on the driving motor The metal powder layer is provided on both sides of the metal powder layer so that the cutting wheel can be rotated by the driving motor. And an cutting layer in which artificial diamond particles are mixed so as to be able to cut the seam stone Characterized in that it is achieved by a tip for cutting a stone and a method of manufacturing the same.
Description
본 발명은 석재 절삭용 팁 및 그 제조방법에 관한 것으로서, 보다 상세하게는 절삭휠(Shank)의 외주면을 따라 일단이 용접으로 고정되는 절삭용 팁을 인조 다이아몬드 입자가 혼합된 혼합층과 금속분말층을 교번되게 구성하여 형성함으로써, 고가의 인조 다이아몬드를 절약할 수 있고, 절삭휠의 절삭성능을 향상시킬 수 있도록 함과 아울러 인조 다이아몬드 입자가 혼합된 혼합층으로만 석재를 절삭하게 되므로 구동모터의 부하를 줄일 수 있도록 한 석재 절삭용 팁 및 그 제조방법에 관한 것이다.
More particularly, the present invention relates to a tip for cutting a stone and a method for manufacturing the same, and more particularly, to a tip for cutting a stone and a method for manufacturing the same, It is possible to save expensive artificial diamonds and to improve the cutting performance of the cutting wheel and to cut the stone only with the mixed layer in which the artificial diamond particles are mixed, And a method for manufacturing the same.
일반적으로 다이아몬드는 경도와 열전도율이 높으므로 절삭공구나 내마모도 공구로서 우수한 성능을 발휘하여 드릴의 팁이나 절삭휠의 절삭용 팁에 주로 사용되고 있다.Generally, diamond has high hardness and high thermal conductivity, and therefore is used as a cutting tool or an abrasion resistance tool, and is mainly used as a tip of a drill or a cutting tip of a cutting wheel.
통상 다이아몬드를 채용한 공구는 다이아몬드 입자를 포함하는 절삭용 팁이 절삭휠(샹크-shank)의 외주면(둘레)을 따라 복수개로 용접에 의해 일단이 접합 고정되어 있고, 절삭휠의 회전에 따라 외주면에 접합 고정된 절삭용 팁이 석재를 절단하도록 구성된다. In a tool employing diamond in general, a cutting tip including diamond particles is joined and fixed by welding a plurality of times along an outer peripheral surface (circumference) of a cutting wheel (shank-shank) A joint fixed cutting tip is configured to cut the stone.
상기한 절삭휠은 4인치에서 120인치까지 다양한 크기로 제작되고 있으며, 절삭용 팁은 절삭휠의 크기에 따라 직선 또는 곡선형상을 구비할 수 있다.The cutting wheel is manufactured in various sizes ranging from 4 to 120 inches, and the cutting tip may have a straight or curved shape depending on the size of the cutting wheel.
그러나, 이와 같이 구성된 절삭휠의 절삭용 팁은 석재를 절삭할 경우 절삭용 팁이 받는 전단응력이 하나의 연장선상 즉, 절삭휠과 절삭용 팁의 접합선에 집중되어 절삭휠의 연마방향과 역방향, 그리고 측면으로부터 받는 순간적인 기계적, 물리적 충격에 대응하지 못하고 팁이 탈락되는 문제점이 있다.However, in the cutting tip of the cutting wheel having the above-described structure, when the stone is cut, the shearing stress received by the cutting tip is concentrated on one extension line, that is, the joining line of the cutting wheel and the cutting tip, And there is a problem in that the tip can not be taken out due to the momentary mechanical or physical impact received from the side.
또한, 석재 절삭시에 연마가 어느 정도 진행되면 절삭휠이 석재 내부로 삽입되어 측면이 석재와 맞닿게 되는데, 이 경우 절삭휠의 경도가 약하여 마모되는 문제점이 발생한다.In addition, when the polishing is progressed to some extent during the stone cutting, the cutting wheel is inserted into the stone and the side faces the stone. In this case, the hardness of the cutting wheel is weak, which causes wear.
이러한 점을 감안하여 특허출원번호 10-2006-0025060호에 가공용 팁 및 이를 장착한 가공용 공구가 출원된바 있다.In consideration of this point, a processing tool and a processing tool equipped with the processing tip have been filed in the patent application No. 10-2006-0025060.
살펴보면, 가공용 팁은 금속재에 경도를 강화시키기 위한 연마재가 혼합되어 소결된 팁몸체 및 금속재와 연마재를 포함하며, 상기 팁몸체와 일체로 소결되고, 상기 샹크가 접합되는 방향으로 돌출되는 적어도 하나의 치합돌기를 포함하며, 상기 팁몸체에는 상기 팁의 연마방향과 다른 방향으로 상기 팁몸체의 일부를 절개하여, 팁몸체의 일부를 구획하는 적어도 하나 이상의 절개홈이 형성되고, 상기 절개홈에는 상기 팁몸체보다 경도가 낮은 재질의 충진재를 포함하여 구성되어 있다.The machining tip includes a tip body and a metal material and an abrasive material mixed with an abrasive for reinforcing the hardness of the metal material. The tip is sintered integrally with the tip body, and the at least one interlocking Wherein at least one cutting groove is formed in the tip body to cut a part of the tip body in a direction different from a direction of polishing the tip so as to define a part of the tip body, And a filling material of a material having a lower hardness.
또한, 상기 팁몸체 및 치합돌기에 포함되는 연마재는 다이아몬드, 실리콘카바이드(SiC), 알루미나(Al2O3) 및 CBN(Cubic boron nitride)로 구성되는 군에서 선택되는 하나 또는 하나 이상의 혼합물로 구성되어 있다.The abrasive included in the tip body and the coupling protrusion is composed of one or a mixture of one or more selected from the group consisting of diamond, silicon carbide (SiC), alumina (Al2O3), and CBN (Cubic boron nitride).
그러나 이와 같이 이루어진 종래의 일반적인 가공용 팁은 연마재가 다이아몬드를 포함하는 혼합물로 구성되어 있어서, 상기 연마재로 가공용 팁을 제조할 경우, 팁몸체와 치합돌기 전체에 다이아몬드가 혼합되어 제조되므로 고가의 다이아몬드가 다량으로 사용될 수 밖에 없어 결국 가공용 팁의 제조단가가 상승되는 단점이 있다.However, in the conventional general working tip thus formed, the abrasive is composed of a mixture containing diamond. Therefore, when the working tip is made of the abrasive, the diamond is mixed with the tip body and the entire engagement protrusion, So that the manufacturing cost of the processing tip is increased.
또한, 상기한 종래의 일반적인 가공용 팁은 피삭재를 절삭할 때 샹크에 일단이 접합된 가공용 팁의 반대면 전체가 피삭재를 절삭하게 되므로, 샹크를 회전시키기 위해 구비되는 모터의 부하가 많이 걸릴 수 밖에 없을 뿐만 아니라 절삭성능이 떨어지는 단점이 있다.
In addition, since the above-described conventional general working tip cuts the workpiece entirely opposite to the machining tip having one end joined to the shank at the time of cutting the workpiece, the load of the motor provided for rotating the shank is very large In addition, there is a drawback that the cutting performance is poor.
이에, 본 발명은 상술한 문제점을 해소하기 위해 안출된 것으로서, 절삭휠(Shank)의 외주면을 따라 일단이 용접으로 고정되는 절삭용 팁을 인조 다이아몬드 입자가 혼합된 혼합층과 금속분말층을 교번되게 구성하여 형성함으로써, 고가의 인조 다이아몬드를 절약할 수 있고, 절삭휠의 절삭성능을 향상시킬 수 있도록 함과 아울러 인조 다이아몬드 입자가 혼합된 혼합층으로만 석재를 절삭하게 되므로 구동모터의 부하를 줄일 수 있도록 한 석재 절삭용 팁 및 그 제조방법을 제공함에 그 목적이 있다.SUMMARY OF THE INVENTION Accordingly, the present invention has been made in order to solve the above-mentioned problems, and it is an object of the present invention to provide a cutting tip whose one end is fixed by welding along an outer circumferential surface of a cutting wheel by alternately arranging a mixed layer in which artificial diamond particles are mixed and a metal powder layer The artificial diamond can be saved and the cutting performance of the cutting wheel can be improved. In addition, since the stone is cut only by the mixed layer in which the artificial diamond particles are mixed, the load of the driving motor can be reduced It is an object of the present invention to provide a tip for cutting a stone and a method of manufacturing the same.
본 발명의 다른 목적들은 기술이 진행되면서 명확해질 것이다.
Other objects of the present invention will become apparent as the description proceeds.
상술한 목적을 달성하기 위한 본 발명은, 절삭휠의 외주면을 따라 복수개로 일면이 용접에 의해 접합 고정되어 구동모터의 구동에 의해 절삭휠이 회전됨에 따른 석재를 절삭가능하도록 한 본 발명에 따른 석재 절삭용 팁에 있어서, 상기 절삭휠의 회전시 석재를 타격시키는 것에 의해 석재를 탈락시켜 절단가능하도록 구비되는 금속분말층과, 상기 금속분말층 양면에 위치되어 상기 절삭휠이 구동모터에 의해 회전시 석재를 절삭가능하도록 인조 다이아몬드 입자가 혼합되어 구비되는 절삭층을 포함하여 이루어진 것을 특징으로 한다.According to an aspect of the present invention, there is provided a method of cutting a stone according to the present invention in which a plurality of pieces are welded and fixed by welding along an outer peripheral surface of a cutting wheel, A cutting tip comprising: a metal powder layer provided on a surface of the metal powder layer so as to be able to cut off stones by striking the stone during rotation of the cutting wheel; And an cutting layer formed by mixing artificial diamond particles so that the stone can be cut.
상술한 목적을 달성하기 위한 또 다른 본 발명은 석재 절삭용 팁의 제조방법에 있어서, 절삭휠의 외주면을 따라 복수개로 일면이 용접에 의해 접합 고정되어 절삭휠이 회전됨에 따른 석재를 절삭할 수 있도록 절삭층용 혼합물을 제조하는 단계와, 절삭휠의 회전시 석재를 타격시키는 것에 의해 석재를 탈락시켜 절단가능하도록 금속분말층용 혼합물을 제조하는 단계와, 상기 단계에 의해 각각 제조된 절삭층용 혼합물과 금속분말층용 혼합물을 성형틀에 교번되게 적층시키는 단계와, 상기 단계에 의해 성형틀내에서 교번으로 적층된 절삭층용 혼합물과 금속분말층용 혼합물을 가압장치를 통하여 가압하는 단계와, 상기 단계에 의해 가압된 절삭층용 혼합물과 금속분말층용 혼합물을 가열장치를 통하여 가열시키는 단계를 포함하여 이루어진 것을 특징으로 한다.
According to another aspect of the present invention, there is provided a method for manufacturing a stone cutting tip, comprising the steps of: welding a plurality of surfaces of a cutting wheel along an outer circumferential surface of the cutting wheel by welding to cut a stone according to rotation of the cutting wheel; Preparing a mixture for the metal powder layer so as to be able to cut off the stone by striking the stone when the cutting wheel rotates; and a step of mixing the mixture for cutting layer and the metal powder Layer mixture in a forming die; pressing the mixture for the cutting layer and the metal powder layer, which are alternately stacked in the molding die, through a pressurizing device; And heating the mixture and the mixture for the metal powder layer through a heating device It shall be.
상기한 바와 같이 본 발명에 따른 석재 절삭용 팁 및 그 제조방법에 따르면, 절삭휠(Shank)의 외주면을 따라 일단이 용접으로 고정되는 절삭용 팁을 인조 다이아몬드 입자가 혼합된 혼합층과 금속분말층을 교번되게 구성하여 형성함으로써, 고가의 인조 다이아몬드를 절약할 수 있고, 절삭휠의 절삭성능을 향상시킬 수 있도록 함과 아울러 인조 다이아몬드 입자가 혼합된 혼합층으로만 석재를 절삭하게 되므로 구동모터의 부하를 줄일 수 있는 효과가 있다.
As described above, according to the stone cutting tip of the present invention and the method of manufacturing the same, a cutting tip whose one end is fixed by welding along the outer circumferential surface of the cutting wheel is formed of a mixture layer in which artificial diamond particles are mixed and a metal powder layer It is possible to save expensive artificial diamonds and to improve the cutting performance of the cutting wheel and to cut the stone only with the mixed layer in which the artificial diamond particles are mixed, There is an effect that can be.
도 1은 본 발명에 따른 석재 절삭용 팁이 절삭휠에 접합 고정된 상태를 도시한 도면이다.
도 2는 도 1의 A-A'선에 따른 단면도이다.
도 3은 또 다른 본 발명에 따른 석재 절삭용 팁의 제조방법을 설명하기 위한 흐름도이다.1 is a view showing a state in which a stone cutting tip according to the present invention is fixed to a cutting wheel.
2 is a cross-sectional view taken along line A-A 'in Fig.
3 is a flowchart illustrating a method of manufacturing a stone cutting tip according to another embodiment of the present invention.
이하에서는, 본 발명에 따른 석재 절삭용 팁 및 그 제조방법의 일실시예를 들어 상세하게 설명한다.Hereinafter, a tip for cutting a stone according to the present invention and a method of manufacturing the same will be described in detail.
우선, 도면들 중, 동일한 구성요소 또는 부품들은 가능한 한 동일한 참조부호를 나타내고 있음에 유의하여야 한다. 본 발명을 설명함에 있어, 관련된 공지기능 혹은 구성에 대한 구체적인 설명은 발명의 요지를 모호하지 않게 하기 위하여 생략한다. First, it should be noted that, in the drawings, the same components or parts have the same reference numerals as much as possible. In describing the present invention, a detailed description of known functions and configurations incorporated herein will be omitted so as not to obscure the gist of the invention.
도시된 바와 같이 본 발명에 따른 석재 절삭용 팁 및 그 제조방법은 절삭휠의 외주면을 따라 복수개로 용접에 의해 일단이 접합 고정되어 있고, 절삭휠이 구동모터의 구동에 의해 회전함에 따라 석재를 구동모터의 부가가 걸리지 않도록 신속하게 절단할 수 있도록 구성된다. As shown in the drawings, a tip for cutting a stone and a method of manufacturing the same according to the present invention have a plurality of welded ends fixedly joined along the outer circumferential surface of the cutting wheel. As the cutting wheel rotates by driving the driving motor, So that the motor can be cut quickly so as not to be added.
즉, 절삭휠(10)의 외주면을 따라 복수개로 일면이 용접에 의해 접합 고정되어 구동모터(미도시함)의 구동에 의해 절삭휠(10)이 회전됨에 따른 석재(미도시함)를 절삭가능하도록 한 본 발명에 따른 석재 절삭용 팁(100)은, 상기 절삭휠(10)의 회전시 석재를 타격시키는 것에 의해 석재를 탈락시켜 절단가능하도록 구비되는 금속분말층(110)과, 상기 금속분말층(110) 양면에 위치되어 상기 절삭휠(10)이 구동모터에 의해 회전시 석재를 절삭가능하도록 인조 다이아몬드 입자가 혼합되어 구비되는 절삭층(130)으로 이루어진다.That is, a plurality of faces are welded and fixed along the outer circumferential surface of the
여기서, 상기한 석재 절삭용 팁(100)은 석재 절삭시 구동모터의 부하를 줄이면서 절삭성능을 향상시킬 수 있도록 절삭층(130)과 금속분말층(110)이 교번으로 3~7층으로 구성된다. The
또한, 상기한 석재 절삭용 팁(100)의 양측면을 형성하는 절삭층(130)의 외측면은 석재 절삭시 절삭용 팁의 양측면이 석재와 접촉 면적이 최소화되도록 하여 구동모터의 부하를 줄이면서 절삭 속도를 향상시킬 수 있도록 단차부(130a,130b)가 형성되어 구비된다.
The outer surface of the
한편, 또 다른 본 발명에 따른 석재 절삭용 팁의 제조방법은 절삭휠의 외주면을 따라 복수개로 일면이 용접에 의해 접합 고정되어 절삭휠이 회전됨에 따른 석재를 절삭할 수 있도록 절삭층용 혼합물을 제조하는 단계(S210)와, 절삭휠의 회전시 석재를 타격시키는 것에 의해 석재를 탈락시켜 절단가능하도록 금속분말층용 혼합물을 제조하는 단계(S220)와, 상기 단계(S210, S220)에 의해 각각 제조된 절삭층용 혼합물과 금속분말층용 혼합물을 성형틀에 교번되게 적층시키는 단계(S230)와, 상기 단계(S230)에 의해 성형틀내에서 교번으로 적층된 절삭층용 혼합물과 금속분말층용 혼합물을 가압장치를 통하여 가압하는 단계(S240)와, 상기 단계(S240)에 의해 가압된 절삭층용 혼합물과 금속분말층용 혼합물을 가열장치를 통하여 가열시키는 단계(S250)를 포함하여 이루어진다.In another method of manufacturing a stone cutting tip according to the present invention, a plurality of cutting surfaces are welded and fixed to a plurality of surfaces along a circumference of a cutting wheel to manufacture a cutting layer mixture so that a stone can be cut as the cutting wheel is rotated (S220) of cutting the stone by blowing the stone during rotation of the cutting wheel (S220), and a step S220 of manufacturing the mixture for the metal powder layer so that the stone can be cut off so as to be cutable. (S230) of alternately laminating the mixture for the layer mixture and the metal powder layer to the mold, and a step for pressing the mixture for the cutting layer and the metal powder layer alternately stacked in the mold by the step (S230) (S240), and heating the mixed mixture for the cutting layer and the metal powder layer through the heating device (S250) by the step S240 Loses.
여기서, 상기한 절삭층용 혼합물 제조단계(S210)는 석재의 절삭능력을 향상시키면서 절삭용 팁을 저가로 제조할 수 있도록 금속합금혼합물을 제조하는 단계(S211)와, 상기 단계(S211)에 의해 제조된 금속합금혼합물에 인조 다이아몬드 입자를 혼합하는 단계(S212)로 이루어진다.The step S210 of manufacturing the mixture for cutting layer may include a step S211 of manufacturing a metal alloy mixture so as to improve the cutting ability of the stone and a cutting tip at a low cost, And mixing synthetic diamond particles with the metal alloy mixture (S212).
또한, 상기한 가압장치를 통하여 교번으로 적층된 절삭층용 혼합물과 금속분말층용 혼합물을 가압하는 단계(S240)에서 절삭층용 혼합물의 양외측면에 석재 절삭시 절삭용 팁의 양측면이 석재와 접촉 면적이 최소화되도록 하여 구동모터의 부하를 줄이면서 절삭 속도를 향상시킬 수 있도록 단차부(130a,130b)가 형성되게 40~60톤(ton)의 가압력을 갖는 가압장치로 가압하게 되고, 가열단계(S250)에서 가열장치의 가열 온도는 700℃~800℃로 3분 내지 7분 동안 가열한다.
In addition, in the step S240 of pressing the mixture for the cutting layer and the metal powder layer alternately stacked through the above-described pressing device, both side surfaces of the cutting tip at the time of cutting the stone are minimized in contact area with the stone So that the
이하에서, 상기한 본 발명에 따른 석재 절삭용 팁을 첨부된 도면을 참조하여 보다 상세하게 설명하면 다음과 같다.Hereinafter, the stone cutting tip according to the present invention will be described in detail with reference to the accompanying drawings.
먼저, 상기한 본 발명에 따른 석재 절삭용 팁(100)의 금속분말층(110)은, 절삭층(130) 사이에 적층되어 고가의 다이아몬드 입자를 배제시키면서 석재를 타격하는 것에 의해 절단시킬 수 있도록 구성된다.First, the
여기서, 상기한 금속분말층(110)은, 75~85중량%의 철(Fe)과 12~17중량%의 구리(Cu) 및 3~7중량%의 주석(Sn)으로 구성된다.Here, the
상기한 절삭층(130)은 금속분말층(110) 양면에 위치되어 상기 절삭휠(10)이 구동모터에 의해 회전시 석재를 절삭가능하도록 인조 다이아몬드 입자가 혼합되어 구비된다.The
즉, 상기한 절삭층(130)은 25~35중량%의 철(Fe)과 15~25중량%의 구리(Cu)와 3~7중량%의 주석(Sn)과, 25~35중량%의 코발트(Co)로 혼합된 금속합금혼합물 92~97중량%에 인조 다이아몬드 입자 3~8중량%가 혼합되어 구성된다.That is, the
여기서, 상기한 인조 다이아몬드 입자를 8중량% 이상으로 혼합하게 되면 석재 절삭용 팁의 제조단가가 상승하게 되고, 3중량% 이하로 혼합하게 되면 절삭능력이 떨아지게 되므로 3~8중량%로 혼합하는 것이 바람직하다.If the artificial diamond particles are mixed in an amount of 8 wt% or more, the manufacturing cost of the stone cutting tip is increased. When the artificial diamond particles are mixed at 3 wt% or less, the cutting ability is reduced. .
한편, 본 발명에 따른 석재 절삭용 팁의 금속분말층과 절삭층의 구성은 상기한 바와 같이 구성되어 있으나, 이에 한정하는 것은 아니며, 석재의 종류 또는 기계상태 즉, 구동모처의 회전력에 의해 혼합물의 구성 및 중량%가 달라질 수 있다.
Meanwhile, the structure of the metal powder layer and the cutting layer of the stone cutting tip according to the present invention is configured as described above, but the present invention is not limited thereto, and the shape of the stone or the mechanical state, that is, Composition and% by weight of the composition.
이와 같이 이루어진 본 발명에 따른 석재 절삭용 팁을 제조하여 절삭휠에 접합 고정시켜 사용하고자 할 경우에는 첨부된 도면 도 3에 도시된 바와 같이 먼저, 철30중량%와 구리20중량%와 주석5중량% 그리고 코발트30중량%를 혼합기를 통하여 금속합금혼합물을 제조한 후 제조된 금속합금혼합물95중량%에 인조 다이아몬드 입자5중량%를 혼합하여 절삭층용 혼합물을 제조한다.3, when a tip for cutting a stone according to the present invention is manufactured and fixed by bonding it to a cutting wheel, first, 30% by weight of iron, 20% by weight of copper and 5% by weight of tin % And 30 wt% of cobalt were mixed to prepare a metal alloy mixture, and then 5 wt% of artificial diamond particles were mixed with 95 wt% of the metal alloy mixture to prepare a mixture for cutting layer.
상기와 같이 절삭층용 혼합물이 제조되면, 철80중량%와 구리15중량% 그리고 주석5중량%를 혼합기를 통하여 금속분말층용 혼합물을 제조한다.When the mixture for cutting layer is prepared as described above, a mixture for metal powder layer is prepared by mixing 80 wt% of iron, 15 wt% of copper and 5 wt% of tin in a mixer.
이와 같이 절삭층용 혼합물와 금속분말층용 혼합물이 제조되면 성형틀에 절삭층용 혼합물와 금속분말층용 혼합물을 석재 절삭용 팁으로 제조 완료시 양측면에 절삭층이 형성되도록 교번되게 적층시킨다.When the mixture for the cutting layer and the mixture for the metal powder layer are produced as described above, the mixture for the cutting layer and the mixture for the metal powder layer are alternately laminated so as to form a cutting layer on both sides of the stone cutting tip.
상기와 같이 절삭층용 혼합물와 금속분말층용 혼합물이 성형틀에서 교번되게 적층되면, 가압장치를 통하여 50톤의 가압력으로 가압시킨다.As described above, when the mixture for the cutting layer and the mixture for the metal powder layer are alternately stacked in the mold, they are pressed at a pressure of 50 tons through the pressurizing device.
상기와 같이 가압되면 가열장치를 통하여 750℃의 가열온도로 5분 동안 가열시킨 후 냉각시키는 것에 의해 도 2에 도시된 바와 같이 양측면은 절삭층(130)이 형성되고, 상기 절삭층(130) 사이에 금속분말층(110)이 형성된 석재 절삭용 팁(100)으로 제조된다.2, the
이와 같이 제조된 석재 절삭용 팁(100)을 도 1에 도시된 바와 같이 절삭휠(10)의 외주면을 따라 복수개로 일면을 용접으로 접합 고정시킨다.As shown in Fig. 1, a
상기와 같이 외주면을 따라 복수개의 석재 절삭용 팁(100)이 접합 고정된 절삭휠을 구동모터의 구동으로 회전시켜 석재를 절삭시키게 되면, 금속분말층(110)의 양측면에 위치한 절삭층(130)에 의해 석재가 절삭되고 절삭층(130)이 아닌 금속분말층(110)은 석재를 절삭하는 것이 아니라 석재를 타격으로 탈락시켜 절단하게 되므로 구동모터의 부하가 적게 걸리게 되면서 신속하게 석재를 절삭시킬 수 있다.When cutting stone is cut by rotating a cutting wheel having a plurality of
이상의 설명은 본 발명의 기술 사상을 예시적으로 설명한 것에 불과한 것으로서, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자라면 본 발명의 본질적인 특성에서 벗어나지 않는 범위에서 다양한 수정 및 변형이 가능할 것이다. 따라서, 본 발명에 개시된 실시예들은 본 발명의 기술 사상을 한정하기 위한 것이 아니라 설명하기 위한 것이고, 이러한 실시예에 의하여 본 발명의 기술 사상의 범위가 한정되는 것은 아니다. 본 발명의 보호 범위는 아래의 청구범위에 의하여 해석되어야 하며, 그와 동등한 범위 내에 있는 모든 기술 사상은 본 발명의 권리범위에 포함되는 것으로 해석되어야 할 것이다.
The foregoing description is merely illustrative of the technical idea of the present invention and various changes and modifications may be made by those skilled in the art without departing from the essential characteristics of the present invention. Therefore, the embodiments disclosed in the present invention are intended to illustrate rather than limit the scope of the present invention, and the scope of the technical idea of the present invention is not limited by these embodiments. The scope of protection of the present invention should be construed according to the following claims, and all technical ideas within the scope of equivalents should be construed as falling within the scope of the present invention.
10 ; 절삭휠
100 ; 석재 절삭용 팁
110 ; 금속분말층
130 ; 절삭층10; Cutting wheel
100; Stone cutting tips
110; Metal powder layer
130; Cutting layer
Claims (4)
상기 절삭휠(10)의 회전시 석재를 타격시키는 것에 의해 석재를 탈락시켜 절단가능하도록 구비되는 금속분말층(110)과;
상기 금속분말층(110) 양면에 위치되어 상기 절삭휠(10)이 구동모터에 의해 회전시 석재를 절삭가능하도록 인조 다이아몬드 입자가 혼합되어 구비되는 절삭층(130)을 포함하되,
상기 석재 절삭용 팁(100)은 석재 절삭시 구동모터의 부하를 줄이면서 절삭성능을 향상시킬 수 있도록 절삭층(130)과 금속분말층(110)이 교번으로 3~7층으로 구성되고, 상기 석재 절삭용 팁(100)의 양측면을 형성하는 절삭층(130)의 최 외측면은 석재 절삭시 절삭용 팁의 양측면이 석재와 접촉 면적이 최소화되도록 하여 구동모터의 부하를 줄이면서 절삭 속도를 향상시킬 수 있도록 단차부(130a,130b)가 형성되어 구비된 것을 특징으로 하는 석재 절삭용 팁.A stone cutting tip (100) for cutting a stone according to rotation of a cutting wheel (10) by driving and driving a driving motor, wherein a plurality of one side are welded and fixed along an outer peripheral surface of a cutting wheel (10)
A metal powder layer (110) provided on the cutting wheel (10) so as to be able to cut off the stone by striking the stone during rotation of the cutting wheel (10);
And a cutting layer (130) located on both sides of the metal powder layer (110) and having artificial diamond particles mixed so that the cutting wheel (10) can cut stone when it is rotated by a drive motor,
The cutting stone 130 and the metal powder layer 110 are alternately formed in 3 to 7 layers so as to improve the cutting performance while reducing the load of the driving motor when cutting the stone, The outermost sides of the cutting layer 130 forming both side surfaces of the stone cutting tip 100 are formed such that both side surfaces of the cutting tip at the time of stone cutting minimize the contact area with the stone and thereby improve the cutting speed while reducing the load of the driving motor (130a, 130b) are formed on the surface of the stone for cutting.
절삭휠의 외주면을 따라 복수개로 일면이 용접에 의해 접합 고정되어 절삭휠이 회전됨에 따른 석재를 절삭할 수 있도록 절삭층용 혼합물을 제조하는 단계(S210)와,
절삭휠의 회전시 석재를 타격시키는 것에 의해 석재를 탈락시켜 절단가능하도록 금속분말층용 혼합물을 제조하는 단계(S220)와,
상기 단계(S210, S220)에 의해 각각 제조된 절삭층용 혼합물과 금속분말층용 혼합물을 성형틀에 교번되게 적층시키는 단계(S230)와,
상기 단계(S230)에 의해 성형틀내에서 교번으로 적층된 절삭층용 혼합물과 금속분말층용 혼합물을 가압장치를 통하여 가압하는 단계(S240)와,
상기 단계(S240)에 의해 가압된 절삭층용 혼합물과 금속분말층용 혼합물을 가열장치를 통하여 가열시키는 단계(S250)를 포함하되,
상기 절삭층용 혼합물 제조단계(S210)는 석재의 절삭능력을 향상시키면서 절삭용 팁을 저가로 제조할 수 있도록 금속합금혼합물을 제조하는 단계(S211)와, 상기 단계(S211)에 의해 제조된 금속합금혼합물에 인조 다이아몬드 입자를 혼합하는 단계(S212)로 이루어지고,
상기 가압장치를 통하여 교번으로 적층된 절삭층용 혼합물과 금속분말층용 혼합물을 가압하는 단계(S240)에서 절삭층용 혼합물의 최 양외측면에 석재 절삭시 절삭용 팁의 양측면이 석재와 접촉 면적이 최소화되도록 하여 구동모터의 부하를 줄이면서 절삭 속도를 향상시킬 수 있도록 단차부(130a,130b)가 형성되도록 하는 것을 특징으로 하는 석재 절삭용 팁의 제조방법.A method of manufacturing a stone cutting tip,
A step (S210) of preparing a mixture for a cutting layer so that a plurality of pieces are welded and fixed along a circumferential surface of the cutting wheel to cut the stone according to the rotation of the cutting wheel,
(S220) of preparing a mixture for a metal powder layer so as to be able to cut off stones by striking the stone during rotation of the cutting wheel,
A step (S230) of alternately laminating the mixture for cutting layer and the metal powder layer produced in the steps (S210, S220)
A step S240 of pressing the mixture for the cutting layer and the metal powder layer alternately stacked in the mold by the above step S230 through a pressurizing device,
(S250) heating the mixture for the cutting layer and the metal powder layer by the heating device by the step S240,
The step S210 of preparing the mixture for cutting layer may include a step S211 of manufacturing a metal alloy mixture to improve the cutting ability of the stone and a cutting tip at a low cost, Mixing the artificial diamond particles with the mixture (S212)
In the step S240 of pressing the mixture for the cutting layer and the metal powder layer alternately stacked through the pressing device, both sides of the cutting tip at the time of cutting the stone at the outermost side of the mixture for the cutting layer are minimized in contact area with the stone Wherein stepped portions (130a, 130b) are formed so as to increase the cutting speed while reducing the load of the drive motor.