KR100707154B1 - Liquid permeable composite sheet for disposable body fluid absorbable article and method thereof - Google Patents

Abstract

The present invention seeks to increase the hiding power of a liquid-permeable composite sheet for use in disposable body fluid absorbent articles.

The liquid-permeable composite sheet 2 used for the disposable body fluid absorbent article includes a plastic sheet layer 11 on the upper surface side and a fiber assembly layer 12 on the lower surface side, and the plastic layers 11 are parallel to each other in one direction. It consists of a plurality of rows of strip-shaped material portions 16 and thin-film-shaped material portions 17 bonded to the strip-shaped material portions 16 and covering substantially the entirety of the fiber assembly layer 12. In the thin film-shaped material portion 17, a liquid permeable aperture 19 is formed between the band-shaped material portion 16 and the band-shaped material portion 16.

Description

Liquid-permeable composite sheet of disposable bodily fluid absorbent article and its manufacturing method {LIQUID PERMEABLE COMPOSITE SHEET FOR DISPOSABLE BODY FLUID ABSORBABLE ARTICLE AND METHOD THEREOF}

1 is a partially broken perspective view of a sanitary napkin.

2 is a partially enlarged view of FIG. 1;

3 is a cross-sectional view taken along the line III-III of FIG. 2.

4 is a cross-sectional view taken along the line IV-IV of FIG. 2.

FIG. 5 is a view similar to FIG. 2 showing an example of an embodiment; FIG.

6 is a manufacturing process diagram of the composite sheet.

7 shows an example of the prior art;

8 is a perspective view of a sanitary napkin showing another example of the prior art.

<Explanation of symbols for the main parts of the drawings>

1: body fluid absorbent article (physiological napkin)

2: composite sheet (surface sheet)

11: plastic sheet layer

12: fiber assembly layer

16: strip-shaped material part                 

17: thin film material portion

19: opening

22: standing part

101: thin film (first web)

102: fiber web (second web)

103: strip (third web)

108: composite web

The present invention relates to a liquid-permeable composite sheet suitable for use in disposable body fluid absorbent articles such as disposable diapers or sanitary napkins.

7 is a perspective view of the flexible micro-opening plastic sheet 110 disclosed in Japanese Patent Laid-Open No. 62-57551. The plastic sheet is suitable for use as a surface sheet of a disposable diaper, etc., wherein a plurality of cylindrical protrusions 120 are formed on the surface of the sheet 110, and a micro-opening portion 125 is formed on the top of the protrusion 120. It is. This sheet 110 is described as being flexible and having a cloth-like texture.

8 is a perspective view of the sanitary napkin 200 disclosed in Japanese Patent Laid-Open No. 7-328061. The surface sheet 210 of the napkin 200 is composed of a nonwoven fabric 211 and a plurality of strips of strip-shaped plastic sheets 212 bonded to the upper surface of the nonwoven fabric 211, and the strip-shaped plastic sheets 212 are mutually supported. It extends in the longitudinal direction of the napkin 200 in parallel. In the napkin 200, the presence of the plastic sheet 212 can conceal contamination by menstrual blood.

One method of concealing contamination by the menstrual blood of the liquid-absorbing core located below the surface sheet by using the known micro-opening plastic sheet 110 in the surface sheet of the sanitary napkin is, for example, carbonic acid in the sheet 110. It is to fill inorganic particles, such as calcium and barium sulfate. In addition, in order to increase the hiding power, the filling amount of the particles may be increased. However, if only the filling amount is increased, the strength of the sheet decreases or the contact width of the thickness at the time of sheet production becomes large. Therefore, these problems must be solved by increasing the thickness of the sheet to be used. However, in doing so, the sheet becomes highly rigid and loses a texture similar to that of the cloth, and the cylindrical protrusions 120 may also lack flexibility.

Japanese Laid-Open Patent Publication No. H7-328061 teaches that the surface sheet 210 made of a relatively flat sheet such as a nonwoven fabric can improve hiding power by employing a strip-shaped plastic sheet 212. As for the plastic sheet such as having the projection 120, the method of utilizing the strip-shaped plastic sheet is not taught at all.

The present invention has been made with reference to these prior arts to provide a soft touch and high hiding power to a liquid-permeable sheet used as a surface material of a disposable body fluid absorbent article, for example.

This invention for solving the said subject is comprised by the 1st invention regarding the liquid permeable composite sheet used for a disposable body fluid absorbent article, and the 2nd invention regarding the manufacturing method of the said composite sheet.

In the first aspect of the invention, the object of the present invention is a liquid permeable composite having a plastic sheet layer on an upper surface side, a fiber assembly layer bonded to the plastic sheet layer on a lower surface side, and used for a disposable body fluid absorbent article. It is a sheet.

In this composite sheet, the first invention is characterized in that the plastic sheet layer is joined to the strip-shaped material portion and the strip-shaped material portion having a plurality of lines extending in parallel to each other in one direction to substantially aggregate the fibers. It consists of the thin-film-shaped material part which covers the whole layer upper surface, Comprising: The said thin-film-shaped material part has many liquid permeable openings arranged intermittently in the said direction between the adjacent strip | belt-shaped material parts. .

The first invention has the following preferred embodiments.

(1) The thin film-like material portion is provided with a standing portion extending upwardly above the upper surface of the composite sheet while repeating the ups and downs along the edge of the opening.

(2) The strip-shaped material portion is bonded to the fiber assembly layer between the thin film-like material portion and the fiber assembly layer.

(3) The thin film-like material portion is bonded to the fiber assembly layer between the strip-shaped material portion and the fiber assembly layer.

(4) The said plastic sheet layer contains an inorganic filler, and content of the filler per unit area in the said strip | belt-shaped material part is higher than content of the filler per unit area in the said thin film-shaped material part.

The object of the second invention is to produce a liquid-permeable composite sheet which includes a plastic sheet layer on the upper surface side and a fiber assembly layer bonded to the plastic sheet layer on the lower surface side, and is used in disposable body fluid absorbent articles. It is a way. In this method, the second invention is characterized in that the composite sheet is produced through at least the following process.

a. Continuously supplying the fiber web to form the fiber aggregation layer in one direction,

b. Extruding the first thermoplastic plastic, which is to form part of the plastic sheet layer, into a strip of plural lines,

c. Extruding the second thermoplastic plastic to form part of the plastic sheet layer into one thin film,

d. A first composite web is obtained by bonding one of the strips and the thin film extruded to an upper surface of the fiber web, and the other of the strip and the thin film is attached to the first composite web and the upper surface of the fiber web and the Obtaining a second composite web continuously fed in the one direction by bonding to at least one of the band and the thin film,

e. A high pressure columnar water flow is injected into the second composite web from at least the fiber web side of the thin film side and the fibrous web side of the second composite web continuously supplied in the one direction, and between the adjacent bands and bands. Forming a standing portion extending in one direction on the top surface of the thin film at the edges of the plurality of openings formed by partially rupturing the film, and having a sawtooth shape, forming the standing portion extending in the one direction from the ruptured film;

The second invention has the following preferred embodiments.

(1) Before spraying the high pressure columnar water flow on the fiber web side to the second composite web, spraying columnar water flow on the film side to the second composite web causes the thin film to partially rupture, thereby forming a plurality of the openings. Embodiments which include the process of forming.

(2) A specific example in which the bonding between the plastic sheet layer and the fiber assembly layer is performed by welding between them.

With reference to the accompanying drawings, a liquid-permeable composite sheet used in a disposable body fluid absorbent article and a method for producing the same will be described in detail as follows.

1 is a partially broken perspective view of a sanitary napkin 1 which is an example of a disposable body fluid absorbent article. The napkin 1 consists of a liquid-permeable surface sheet 2, an impermeable backing sheet 3, and a liquid-absorbing core 4 interposed between these sheets 2, 3, and has a front and back surface sheet 2, 3) is overlapped in the part extended from the peripheral edge of the core 4, and is joined to each other by welding or adhesion in the line 6. The napkin 1 has a width extending in the X direction and a length extending in the Y direction. In this napkin 1, the composite sheet which concerns on this invention is used as the surface sheet 2. As shown in FIG.

2, 3, and 4 show a partial enlarged view of the napkin 1, a cross-sectional view taken along line III-III, and a cross-sectional view taken on line IV-IV. However, the back sheet 3 and the core 4 are shown by the virtual line. The surface sheet 2 is a composite sheet which consists of the plastic sheet layer 11 located in the upper surface side, and the nonwoven fabric layer 12 which is an aggregate of the fiber 13, and these both layers 11 and 12 are used for welding or adhesion | attachment. Are joined to each other by. The plastic sheet layer 11 is a thin film in which the upper surface of the nonwoven fabric layer 12 substantially covers the entirety of the plurality of rows of strip material portion 16 extending in the Y direction parallel to each other, and under the strip material portion 16. It includes a shape material portion 17, and both of these portions 16 and 17 are formed of thermoplastic plastic and are welded to each other at the overlapping portions. The thin film-like material portion 17 has a plurality of openings extending in the Y direction between the flat portions 18 and adjacent flat portions 18 in a practical sense, with a plurality of lines extending in the Y direction parallel to each other. (19), the bridge portion 20 extending in the X direction from the edge portions 21 facing each other in the adjacent flat portions 18 and crossing the opening 19, and the edge portions 21 of the flat portions 18. ) Has a standing portion 22 extending upwards of the figure. The standing portion 22 is a portion having a substantially sawtooth shape extending in the Y direction while repeating the irregular undulation.

The nonwoven fabric layer 12 is joined to the flat part 18 of the thin film-shaped material part 17 from the bottom of the figure, and the part of the nonwoven fabric layer 12 is exposed in the opening 19.

As the back sheet 3, a nonwoven fabric made of a thermoplastic sheet or a thermoplastic synthetic fiber, a laminate of these sheets and a nonwoven fabric, and the like are used.

As the core 4, a pulverized pulp, a mixture of pulverized pulp and a super absorbent polymer, or the like is used.

3 and 4, the strip-shaped material portion 16 is provided in the flat portion 18 of the thin film-shaped material portion 17, preferably in each of the flat portions 18, and is 0.01 to 0.3 mm. Has a thickness, and a width S ₁ of 0.1 to 4 mm. When the thickness is less than 0.01 mm, the effect of increasing the concealability of the thin film-shaped material portion 17 is insufficient, and when the thickness is more than 0.3 mm, the rigidity is increased, and the irritation to the skin may be too strong. The width S ₁ is approximately equal to or smaller than the width of the flat portion 18. However, in order to increase the concealability in the flat part 18, the width S ₁ is preferably not to be 1/3 or less of the width W ₁ of the flat part 18, and is preferably 1/2 or less. It is more preferable that it does not become. This strip-shaped material portion 16 is obtained by extruding a thermoplastic into a strip shape and supplying it on the thin film-shaped material portion 17, but the cross-sectional shape can be round, elliptical, etc. in addition to the rectangular shape as shown in the example. have.

The strip-shaped material portion 16 is the napkin 1 of FIG. 1 so that the menstrual blood absorbed by the core 4 is not visible through the surface sheet 2, that is, to increase the concealment of the surface sheet 2. Will have to function. An inorganic filler such as titanium oxide or barium sulfate is added to the strip material portion 16, and a salt pigment or the like may be added as necessary. These addition amounts can be made large in the range which does not interfere with extrusion of the strip | belt-shaped material part 16. As shown in FIG. When the addition amount of the inorganic filler is large, the narrow and thick strip-shaped material portion 16 is easier to extrudate than the wide and thin film-shaped material portion 17, and furthermore, the strip-shaped material portion 16 ) Has a small influence on the performance of the surface sheet 2 even if the thickness varies, so using such a strip-shaped material portion 16 facilitates increasing the hiding power of the surface sheet 2. When the surface sheet 2 is viewed from above, the content of the inorganic filler per unit area of the strip-shaped material portion 16 is higher than the content of the thin film material portion 17, and preferably the former content is at least 1.3 of the latter content. It is doubled. The strip-shaped material portion 16 may contribute to the improvement of the tensile strength in the Y direction of the thin film-shaped material portion 17.

The flat portion 18 in the thin film portion 17 has a thickness of 0.001 to 0.05 mm, and a width W ₁ of 0.3 to 5 mm between the opening 19 and the opening 19. The majority of the openings 19 extend in the Y direction, and preferably have a width W ₂ of 0.03 to 5 mm and a length of at least 1.5 times the width W ₂ .

The bridge portion 20 in the thin film-shaped material portion 17 is located between the openings 19 and the openings 19 arranged in the Y direction, and arcs are formed to be convex upward from the flat portion 18 ( 20A, or similar to the flat portion 18, there is a flat 20B (see FIG. 2). The arcuate bridge portion 20A has a proximal end 25A that appears to extend from the flat portion 18 and a proximal end 25B that appears to extend from the top 27 of the standing portion 22. In some cases (see FIG. 2). The preferred bridge portion 20 has a thickness equal to or thinner than the thickness of the flat portion 18 and ranges from 0.001 to 2 mm at the narrowest portion of the width W ₃ extending in the Y direction (see FIG. 3). Is in.

The standing portion 22 of the thin film-shaped material portion 17 is formed by a large portion 22 being formed by a portion of the thin film extending from the edge portion 21 of the flat portion 18 upwards in the drawing, and the flat portion 18 ) And a free end 27 extending upwardly from the proximal end 26. The upper edge 27A of the standing portion 22 repeats the sawtooth ups and downs along the edge 21. Although the maximum value of the height from the flat part 18 to the upper edge 27A can reach about 5 mm, in order to improve the touch of the surface sheet 2, the maximum value is suppressed to about 1 mm, and It is desirable for the majority of the standing portions 22 to protrude from the top surface of the strip material portion 16. Some 22B of the standing part 22 are formed in the edge part of the bridge part 20 (refer FIG. 2).

An example of a specific example in which the upper edge 27A of the standing portion 22 repeats ups and downs is shown in FIG. 3, which includes an inclined surface 31 extending upwardly from the right, an inclined surface 32 upwardly extending from the left, and Is an irregular connection of a portion 33 having a triangular or triangular-like shape formed by a proximal end portion 26 extending between these inclined surfaces 31 and 32. The standing part 22B may also repeat ups and downs. These standing portions 22, including the standing portions 22B, have a thickness equal to or thinner than the thickness of the flat portion 18, and are softly deformed upon contact with the skin of the person so that the surface sheet 2 has a velvet effect. It can give a smooth and flexible texture. It is not easy to visually check each one of the standing portions 22, but when there are many standing portions 22, the surface of the surface sheet 2 appears to have been raised. In addition, the standing portion 22 can attenuate the surface gloss often seen in the plastic sheet by diffusely reflecting the incident light rays to the surface sheet 2.

In general, the addition of a large amount of inorganic filler to thin films, such as thin film portion 17, makes the manufacture of thin films difficult. Therefore, in this surface sheet 2, a high concealing force with respect to the core contaminated by the thin film-like material portion 17 is not obtained, but the concealing force is obtained by the strip-shaped material portion 16, and thus the thin film-shaped material portion 17 is obtained. Both parts 16 and 17 are distinguished and used so as to improve the appearance and the feel of the silver surface sheet 2.

The nonwoven layer 12 may contain at least 70% by weight of thermoplastic synthetic fibers, and may contain up to 30% by weight of hydrophilic natural fibers such as rayon fibers and hydrophilic natural fibers such as cotton and pulp fibers. An example of a preferred nonwoven layer 12 consists of a thermoplastic synthetic fiber having a fineness of 0.5 to 15 d and a basis weight of 5 to 50 g / m 2, including spunbond nonwoven fabric, point bond nonwoven fabric, and air-through. In addition to thermal bond nonwoven fabrics such as nonwoven fabrics, there are melt blown nonwoven fabrics, spunlace nonwoven fabrics, and the like.                     

When such a surface sheet 2 is used for the sanitary napkin 1, the menstrual blood is absorbed from the opening 19 via the nonwoven fabric layer 12 to the core 4. The core 4 and the nonwoven fabric layer 12, which are soiled with menstrual blood, are covered with a highly concealed band-like material portion 16, a standing portion 22 that diffusely reflects light rays, and the contamination is inconspicuous.

5 is a view similar to FIG. 4 showing an example of an embodiment of the invention. In this surface sheet 2, the strip | belt-shaped material part 16 is located between the nonwoven fabric layer 12 and the flat part 18 of the thin film material part 17. As shown in FIG. The lower surface of the strip-shaped material portion 16 is bonded to the nonwoven fabric layer 12 by welding or bonding, and the upper surface is bonded to the flat portion 18 by welding or bonding. The thin film material portion 17 is joined to the strip-shaped material portion 16 and the nonwoven fabric layer 12 by welding or bonding. In the sanitary napkin 1 employing such a surface sheet 2, since the strip-shaped material portion 16 is not exposed unlike in FIG. 1, the standing portion 22 and the strip on the upper surface of the surface sheet 2 are not exposed. There is no fear that menstrual blood will stay between the shaped material portions 16 or irritate the skin of the napkin wearer with the edge of the band shaped material portion 16.

FIG. 6 is a diagram showing a process of continuously producing a composite sheet 108 used as the surface sheet 2 of FIG. On the left side of the figure, the second web 102, which is a fiber assembly which is to be the nonwoven layer 12 of FIG. 2, is continuously fed. On the upper surface 102A of the second web 102, one first web made of the first thermoplastic plastic discharged from the first extruder 121 and intended to be the thin film portion 17 of the surface sheet 2 is formed. In the state where 101 is softened by heat, it overlaps and is supplied between a pair of compression rolls 173, and both webs 101 and 102 are welded and it becomes the 1st composite web 104. FIG.

In the first composite web 104, a plurality of strips of band 116 made of a second thermoplastic plastic discharged from the second extruder 122 on the first web 101 and spaced in a predetermined dimension in parallel to each other. The third web 103 is supplied in a state of being softened by heat, and the first web 101 and the third web 103 are welded between the pair of compression rolls 174, and the second composite web 106 is disposed. Is formed. The strip 116 of the third web 103 is to be the strip material portion 16 of the surface sheet 2.

The second composite web 106 proceeds to the first treatment section 123, and the high pressure columnar water flow flows from the row 123A of the plurality of nozzles arranged at a predetermined pitch in the width direction of the second composite web 106. It is sprayed toward the upper surface 101A of 101 to obtain the third composite web 107. The first web 101 is selectively ruptured between the strip 116 and the strip 116 by the columnar water flow, and the first web 101 is intermittently arranged in the advancing direction of the third composite web 107. Opening rows are formed, and the openings are arranged in parallel with each other in the width direction of the third composite web 107. In the first processing section 123, in order to form a plurality of rows of open holes, in addition to the nozzle row 123A, columnar water flow is also performed in the rows of the second and third nozzle rows 123B and 123C as shown. Can be sprayed. It is preferable that these nozzle rows 123A, 123B, and 123C substantially match the positions of the nozzles in the width direction of the third composite web 107 so that the trajectories of the water jets overlap. In the lower portion of the first treatment section 123, a suction mechanism 124 for sucking the injected water is provided.                     

The third composite web 107 proceeds to the second processing section 127. In the second processing section 127, nozzle rows 127A, 127B, and 127C forming rows in the width direction of the third composite web 107 and the suction mechanism 128 are provided. Here, the high pressure columnar water flow is injected to the lower surface 102B of the second web 102 forming the third composite web 107, and then dried to form the composite sheet 108. In the composite sheet 108, the portion of the first web 101 that has already been ruptured in the first processing section 123 is deformed to conform to the direction of the columnar water flow in the second processing section 127 so that the first web 101 can be used. Extends in the direction from the lower surface 101B toward the upper surface 101A. The trajectory of the jet streams by the nozzle rows 127A, 127B, and 127C in the second processing section 127 does not necessarily have to match the trajectory by the nozzle rows 123A, 123B and 123C in the first processing section 123. However, if they are roughly coincident with each other, a long opening in which the first web 101 is ruptured extensively is formed, and most of the ruptured portion extends above the upper surface 101A of the first web 101. According to the manufacturing method according to the present invention, a plurality of rows of opening rows in which a predetermined portion in the width direction of the first web 108 is selectively ruptured and extends in parallel to each other in the longitudinal direction are easily formed.

In the composite sheet 108, the first and second webs 101 and 102 joined to each other become the plastic layer 17 of the surface sheet 2, and the openings formed in the first web 101 are opened. The ruptured portion of the first web 101 becomes the standing portion 22. In the opening row arranged in the feeding direction of the first web 101, the portion not broken by the high pressure columnar water flow between the opening portion and the opening portion becomes the bridge portion 20.                     

In Fig. 6, the diameters of the nozzles in the nozzle rows 123A to 123C and 127A to 127C are 0.05 to 0.15 mm, the pitch of the adjacent nozzles in each nozzle row is 0.1 to 0.5 mm, and the water pressure of the columnar water flow is 30 to 200 kg. / Cm 2, and the suction pressure is preferably 200 to 1000 mmH ₂ O. In the first and second processing sections 123 and 127, the web to be processed is loaded on the supports 131 and 132 such as a mesh screen and moved in a predetermined direction.

When the first web 101, the second web 102, and the third web 103 are supplied at room temperature, these webs are welded between a pair of heated rolls, or bonded with a hot melt adhesive or the like. Can be bonded.

If necessary, the first web 101, the second web 102, and the third web 103 may be subjected to water repellent treatment or other surface treatment at an appropriate position in the illustrated process. When the 1st web 101 is a film uniaxially stretched along a supply direction, formation of the opening by columnar water flow may become easy. A thickness of 0.001 to 0.05 mm is used for the first web 101, and a thickness of 0.01 to 0.3 mm and a width of 0.1 to 4 mm is used for the third web 103. The second web 102 has a basis weight of 5-50 g / m 2. In the process of FIG. 6, the first treatment section 123 is omitted, and the high pressure columnar water flow is injected only in the second treatment section 127, thereby making the first composite web 106 without making the second composite web 107. The composite sheet 108 can also be manufactured from. However, in this manufacturing method, since the columnar water flow is difficult to directly act on the first web 101, a narrow opening and many bridge portions are easily formed in the first web 101. The composite web 108 is suitably dried before it is wound up. In addition, in the process of FIG. 6, it is also possible to extract the 2nd composite web 107 from the process of illustration, and to use this composite web 107 as the surface sheet 2. As shown in FIG. In the surface sheet 2 in this case, the standing portion 22 is hardly formed in the edge portion 21 of the opening 19.

The order in the process of FIG. 6 is changed, and the strip | belt 116 of multiple shape is discharged from the 1st extruder 121 as the 1st web 101, and this is bonded to the fiber assembly which is 2nd web 102. As shown in FIG. The first composite web 104 can be obtained. The second composite web 106 is formed by discharging the third web 103, which is a thin film, from the second extruder 122 and joining the first and second webs 101 and 102 forming the first composite web 104. Get) This second composite web 106 is processed in the first and second processing sections 123 and 127 to become a composite sheet 108 having the cross-sectional structure of FIG. This composite sheet 108 can also be used as the surface sheet 2.

Since the composite sheet according to the present invention is formed of a plurality of strips of band-like material portion and a thin film-like material portion bonded thereto, when the composite sheet is used as a surface sheet of a disposable diaper or sanitary napkin, both portions overlap. Contamination of the core can be reliably concealed at the site where it becomes. The strip material portion also helps to improve the tensile strength of the thin film material portion in the direction in which it extends.

According to the manufacturing method of the composite sheet which concerns on this invention, a predetermined part in the width direction of the web which should form a thin-film-shaped material part is selectively ruptured, and the permeable opening and the standing part which makes a touch soft are easy. You can get it.

Claims (8)

A liquid-permeable composite sheet comprising a plastic sheet layer on an upper surface side and a fiber aggregation layer bonded to the plastic sheet layer on a lower surface side, and used in disposable body fluid absorbent articles, The plastic sheet layer is joined to the strip-shaped material portion having a plurality of lines extending parallel to each other in one direction, and substantially covers the entire upper surface of the fiber assembly layer, and is thicker than the strip-shaped material portion. The composite sheet comprising a thin film-like material portion, wherein the thin film-like material portion is formed with a plurality of liquid permeable apertures intermittently arranged in the one direction between the adjacent strip-shaped material portions. . The composite sheet according to claim 1, wherein the thin film-like material portion is formed with a standing portion extending upwardly above the upper surface of the composite sheet while repeating the ups and downs along the edge of the opening. The composite sheet according to claim 1 or 2, wherein the strip-shaped material portion is bonded to the fiber assembly layer between the thin film-like material portion and the fiber assembly layer. The composite sheet according to claim 1 or 2, wherein the thin film-like material portion is bonded to the fiber assembly layer between the band-shaped material portion and the fiber assembly layer. The said plastic sheet layer contains an inorganic filler, and content of the said filler per unit area in the said strip | belt-shaped material part is higher than content in the said thin-film-shaped material part of Claim 1 or 2 characterized by the above-mentioned. Composite sheet made with. A method for producing a liquid-permeable composite sheet comprising a plastic sheet layer on an upper surface side and a fiber aggregation layer bonded to the plastic sheet layer on a lower surface side, and used for a disposable body fluid absorbent article, wherein the composite sheet includes at least A process for producing a liquid-permeable composite sheet, which is produced through a process. a. Continuously supplying the fiber web to form the fiber aggregation layer in one direction, b. Extruding the first thermoplastic plastic, which is to form part of the plastic sheet layer, into a strip of plural lines, c. Extruding the second thermoplastic plastic to form part of the plastic sheet layer into one thin film, d. A first composite web is obtained by bonding one of the strips and the thin film extruded to an upper surface of the fiber web, and the other of the strip and the thin film is attached to the first composite web and the upper surface of the fiber web and the Obtaining a second composite web continuously fed in the one direction by bonding to at least one of a band and the thin film, e. Injecting a high pressure columnar stream into the second composite web from at least the fibrous web side of the thin film side and the fibrous web side of the second composite web continuously supplied in one direction, between adjacent bands and bands. Forming a standing portion extending in the one direction in the direction of the upper surface of the thin film, and forming a standing portion extending in one direction at the edges of the plurality of openings formed by partially rupturing the thin film. 7. The method of claim 6, wherein the high pressure columnar water flow is injected from the thin film side to the second composite web by spraying the high pressure columnar water flow from the thin film side to partially rupture the thin film. The manufacturing method characterized by including the process of forming the said opening of the. The method according to claim 6 or 7, wherein the bonding between the plastic sheet layer and the fiber assembly layer is made by welding between them.