JP3270608B2 - How to make a sticker type striped picture - Google Patents

Description

DETAILED DESCRIPTION OF THE INVENTION

[0001]

The present invention relates to a thermoplastic emulsion type synthetic resin agent colored in various colors,
The present invention relates to a method of forming a stained glass-like three-dimensional thick film picture as a sticker-type peeling picture on a carrier surface such as a transparent glass plate or a synthetic resin plate having a smooth surface.

[0002]

2. Description of the Related Art Conventionally, a glass substrate, a synthetic resin plate, or the like, having a smooth surface, is coated with a thermoplastic emulsion-type synthetic resin agent which is colored in various colors, and the surface of the support is stained glass-like. After drawing a thick film picture and drying it, this stained glass-like three-dimensional film picture is peeled off from the surface of the carrier as a sticker-type peeling picture, and this is adhered to the smooth surface of another object. Playing was done by peeling and peeling. However, the sticker-type peeling picture made with the conventional synthetic resin agent has no special consideration for the thermoplastic emulsion type synthetic resin agent that draws a stained glass-like three-dimensional thick film picture.
Stained glass-like three-dimensional thick film paintings formed on the surface of a carrier such as a synthetic resin plate have a small thickness that does not provide sufficient thickness, and thus lack a three-dimensional effect, and if the drying on the surface of the carrier is slow, Disadvantage, furthermore, the sticker type peeling picture which peeled it from the surface of the carrier lacks elasticity and therefore lacks extensibility,
There is a defect that the sticking force is weak when sticking to a smooth surface of another object.

[0003]

SUMMARY OF THE INVENTION The present invention provides a thick-walled and highly extensible film which eliminates these disadvantages, has a fast drying on the supporting surface, and has a stained glass-like thick film on the supporting surface. Is intended to create a thick film painting with high light brightness or a color change brilliant phenomenon that adapts to light and dark when it is peeled off from the carrier and attached to another object as a sticker type peeling picture is there.

[0004]

Means for Solving the Problems On the surface of a carrier such as a transparent plate glass or a synthetic resin plate having a smooth surface, a thickener, a film forming aid, a surfactant, an emulsifier, a glycol, etc. , Ammonia as appropriate, and metal fine powder,
The outline is formed with a synthetic resin agent that is a mixture of one of a luminous agent, a luminous agent, a thermochromic dye, and a liquid crystal enclosed in a microcapsule.
A sticker type wherein the inside is painted out and dried to form a stained glass-like three-dimensional thick film picture on the surface of the carrier, and peeled off the carrier surface as an adhesive. How to make a striped picture.

[0005]

By carrying out the present invention, a sketch, a transparent plate having a smooth surface, and a synthetic resin agent of a thermoplastic emulsion type having various colors can be easily applied to a surface of a transparent plate having a smooth surface like a stained glass. It is possible to easily and quickly produce a three-dimensional film picture with a simple border. The three-dimensional stained glass-like coating picture produced by carrying out the present invention can be peeled off from the transparent plate having a smooth surface to form a sticker-type peeling picture, which is made of window glass or steel equipment. Can be attached to a desired portion of the smooth surface or can be peeled off.

[0006]

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS Hereinafter, a method for producing a thick film picture 8 composed of a three-dimensional pattern and pattern on a transparent carrier surface such as a glass plate or a synthetic resin plate having a smooth surface by using a stained glass-like synthetic resin agent according to the present invention. In addition, an embodiment of a manufacturing method in which this is peeled off from the surface of the carrier to obtain a sticker-shaped peeling picture 9 will be described with reference to the drawings. FIGS. 1 and 2 show a stained glass-like three-dimensional design or pattern coating film 8 made of a synthetic resin agent formed on a transparent support such as a glass plate or a synthetic resin plate having a smooth surface. FIG. 2 shows an example of a sticker type peeling picture 9 as well as a plan view thereof and an example of a sectional view thereof.

The materials and tools used in the present invention are:
It is as follows. That is, a sketch 2 in which a predetermined pattern or pattern 1 of animals, flowers, landscapes, and the like is drawn, and an emulsion type thermoplastic synthetic resin having a predetermined color necessary for drawing the outline of the pattern 1 in the sketch 2 Agent 3 and several types of emulsion-type synthetic resin agents 5, 5... Used to color the interior of the contour 4 drawn by the synthetic resin agent 3 into a desired color. These synthetic resin agents are referred to as “synthetic resin agents” hereinafter), and these synthetic resin agents 3, 5,... Are used to carry two types of patterns or a transparent synthetic resin plate or a sheet glass having a smooth surface on which to draw patterns. It is.

FIGS. 3 to 6 show a method of carrying out the present invention to draw a three-dimensional sticker type thick pattern pattern coating picture 8 of a synthetic resin agent using the above materials and tools. It is. First, the maker selects a desired one from a plurality of sketches 2 and lays the sketch 2 on the lower surface of a transparent plate 6 having a smooth surface (see FIG. 3). A contour line 4 of a ridge is formed of the synthetic resin agent 3 along the contour of the design or pattern 1 of the above-mentioned underlay 2 (FIG.
reference). In the present invention, the carrier 6 which is a transparent plate is used.
The predetermined design 1 such as an animal, a floral design, a landscape or other design, or a design to be applied and drawn on the top is determined by the design 1 of the base design 2 drawn in advance, but the base design 2 is not necessarily used. Of course.

The synthetic resin agent 3 for drawing the contour line 4 is
It is desirable to use a low-brightness color such as black or brown so that the outline 4 can be clearly defined. The use of such a color such as black or brown also has the effect of resembling the outline of stained glass. Needless to say, the color of the synthetic resin agent 3 can be appropriately selected according to the purpose of how to form the three-dimensional sticker type thick film picture 8 to be drawn. This contour line 4
The inside of each part of the outline 4 drawn by the above is painted with a synthetic resin agent 5 having various colors (see FIG. 5). As a result, a three-dimensional thick film picture 8 is formed in a stained glass manner on the surface of the carrier having a smooth surface.

Further, in this embodiment, the synthetic resin agents 3 and 5 for drawing the outline 4 or painting the inside of the outline 4 are used.
In order to easily draw the outline 4 on the surface of the transparent plate carrier 6 and to easily fill the inside of the outline 4, a tube 7 having a tapered end is used. A synthetic resin agent filled in a tube as a container can be poured out from the mouth 7a, and the tube as the container is formed into a writing instrument type with a flexible material.

Finally, after drawing a desired pattern or pattern by the above-described procedure, the synthetic resin agents 3 and 5 used for the drawing are dried. After this drying, the carrier 6 which is a transparent plate
On the surface, a stained glass-like three-dimensional film picture 8 made of the synthetic resin agent is formed in a sticker-type thick strip picture 9 that retains elasticity in a peelable state. When the stained glass-like three-dimensional thick film picture is peeled off from the carrier 6 which is a transparent plate, a sticker-type thick peel picture as shown in FIG. 1 is completed (see FIG. 6).

As shown in FIG. 1, the sticker type three-dimensional thick strip picture 9 produced as described above is formed into a stained glass-like three-dimensional thick film picture 8 using only the synthetic resin agents 3 and 5. To form. The sticker-shaped three-dimensional thick strip picture 9 produced by the above means retains elasticity even after the used synthetic resin agents 3 and 5 are dried as the three-dimensional thick film picture 8 and stretches. Since it is formed as a material having a high degree of flexibility, it can be stuck as a sticker to a flat surface such as a window glass or a steel instrument, and this is not an adhesive. It is easy to peel off because it is an adhesive that utilizes elasticity and extensibility.

As the synthetic resin agent for carrying out the present invention, a chemical composition of a synthetic resin adhesive is used, but in a container such as a tube, it is held as a thermoplastic synthetic resin agent having viscosity of an emulsion type. It was poured out of the container, exposed to the outside air, dried over time, and prepared as a thick leather having a soft leather-like shape.

Further, this synthetic resin agent for carrying out the present invention eliminates the above-mentioned conventional disadvantages caused by the stained glass-like three-dimensional thick film formed on the surface of the carrier 6, and In order to enhance the swelling of the contour line 4 constituting the thick film painting formed on the body surface, the inside of the contour line 4 is painted in parallel, and a three-dimensional pattern integrated with the contour line 4 is formed in a stained glass style. Regarding the synthetic resin agent on which the thick coating picture is drawn, in order to prevent the thick coating picture from losing its shape until the synthetic resin agent dries, the thick coating picture is rich in elasticity and stretched. A thick resin film that has the property of being able to be stretched as a thick film, and forms a thick film in order to accelerate the drying speed; a thickener, a film forming aid, a surfactant, and an emulsifier. , Glycol, ammo An appropriate amount formulated ya.

Further, in order to make the stained glass-like three-dimensional thick film picture completed on the smooth surface of the carrier into a film picture having a metallic sensation with luster, ultrafine metal powder is mixed into a synthetic resin agent. Alternatively, a luminous agent and a luminous agent encapsulated in microcapsules are mixed in order to obtain a film picture having a color tone change depending on the lightness and darkness, and further a film picture having a color tone change corresponding to a temperature change. For this purpose, thermochromic dye liquid crystals encapsulated in microcapsules are mixed.

Using the synthetic resin agent thus prepared,
The film picture produced by the above means is a film picture with an improved taste that is not available in conventional film pictures.

[0017]

As described above, the sticker-type three-dimensional thick film made of a stained glass-like synthetic resin obtained by carrying out the present invention has a smooth surface as described above on the surface of a carrier such as a plate glass or a synthetic resin plate. The three-dimensional thick film picture thus completed is constructed as a thick film picture which is rich in flexibility and elasticity and extensible, since it is configured to be peelable by the synthetic resin agent prepared as described above. Therefore, it can be played by peeling it off from the surface of the carrier and using it as a sticker on a window glass, pen case, or other smooth surface of an article or peeling it off. Furthermore, this three-dimensional thick film picture made of this stained glass type synthetic resin is produced on the entire surface of the window glass,
If this is left attached, an atmosphere like real stained glass can be created in the room, and the present invention can be used not only as a toy but also for interior purposes.

[Brief description of the drawings]

FIG. 1 is a plan view of a sticker type peeling picture.

FIG. 2 is a sectional view taken along line AA of FIG. 1;

FIG. 3 is a diagram showing a sketch under a transparent plate.

FIG. 4 is a state diagram of drawing a contour of a desired pattern on a transparent plate;

FIG. 5 is a diagram showing a state in which an outline to be drawn on a transparent plate is painted.

FIG. 6 is a diagram showing a state in which a peeling picture drawn from a transparent plate is peeled off;

[Explanation of symbols]

 2 Underlay 6 Transparent plate 8 Film painting 9 Sticker-type peeling picture

──────────────────────────────────────────────────続 き Continued on front page (58) Field surveyed (Int. Cl. ⁷ , DB name) B44C 5/00 G09F 3/04

Claims (1)

(57) [Claims] 1. A thickening agent, such as a pattern or a pattern shown in the figure below, on a surface of a carrier such as a transparent plate glass or a synthetic resin plate having a smooth surface.
A film forming aid, a surfactant, an emulsifier, glycol, and ammonia are appropriately compounded, and the contour is made of a synthetic resin agent that is a mixture of one of metal ultrafine powder, a luminous agent, a luminous agent, a thermochromic dye, and a liquid crystal encapsulated in microcapsules. And coating the inside thereof, drying it to form a stained glass-like three-dimensional thick film picture on the surface of the carrier, and peeling this as a sticking material from the carrier surface. Manufacturing method of sticker type striped picture.