DE3737837C2 - - Google Patents

Info

Publication number
DE3737837C2
DE3737837C2 DE3737837A DE3737837A DE3737837C2 DE 3737837 C2 DE3737837 C2 DE 3737837C2 DE 3737837 A DE3737837 A DE 3737837A DE 3737837 A DE3737837 A DE 3737837A DE 3737837 C2 DE3737837 C2 DE 3737837C2
Authority
DE
Germany
Prior art keywords
oil
use according
natural latex
formwork
adhesive
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired
Application number
DE3737837A
Other languages
German (de)
Other versions
DE3737837A1 (en
Inventor
Hans-Peter 7432 Metzingen De Schur
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to DE19873737837 priority Critical patent/DE3737837A1/en
Publication of DE3737837A1 publication Critical patent/DE3737837A1/en
Application granted granted Critical
Publication of DE3737837C2 publication Critical patent/DE3737837C2/de
Granted legal-status Critical Current

Description

Die Erfindung betrifft die Verwendung einer ein Schmieröl und einen Haftvermittler enthaltenden Zusammensetzung als Motorsägekettenhaftöl, Schalöl oder Tiefziehöl.The invention relates to the use of a lubricating oil and a coupling agent-containing composition as Chain saw chainshaft oil, formwork oil or thermoforming oil.

Haftöle für Motorsägeketten werden in der Bundesrepublik Deutschland in großen Mengen benötigt. Jährlich werden etwa 6 Millionen bis etwa 7 Millionen Liter Motorsägekettenhaftöl verbraucht. Im Baugewerbe werden erhebliche Mengen Haftöl als Trennmittel für Bauschalungen, insbesondere für Betonschalungen, benötigt, um nach dem Aushärten des in die Schalung eingebrachten Betons die Schaltafeln problemlos vom Beton entfernen zu können. Weiterhin sind in der Autoindustrie große Mengen an Tiefziehölen zum Einstreichen der Formteile, wie der Bleche, erforderlich.Bonding oils for chainsaw chains are in the Federal Republic Germany needed in large quantities. Annually about 6 million to about 7 million liters Power chain chain oil consumed. In the construction industry significant amounts of adhesive oil as a release agent for Building formwork, in particular for concrete formwork, required, after hardening of the introduced into the formwork Concrete easily remove the formwork panels from the concrete can. Furthermore, in the auto industry large quantities At Tiefziehölen for painting the moldings, such as Sheets, required.

Sowohl das für Motorsägeketten benötigte Haftöl, als auch das als Trennmittel für Bauschalungen dienende Schalöl und das in der Autoindustrie verwendete Tiefziehöl bleibt nach seiner Anwendung in der Natur zurück und belastet insbesondere das Wasser erheblich. Bekanntlich werden durch 1 Liter Öl etwa 1 Million Liter Wasser ungenießbar gemacht.Both the necessary for chainsaw chains adhesive oil, as well which serves as a release agent for building formwork formwork oil and the thermoforming oil used in the automotive industry remains behind its application in nature back and charged especially the water considerably. Be known through 1 liter of oil about 1 million liters of water made inedible.

Die bisher bekannten Haftöle enthalten als Haftvermittler, der beispielsweise das Anhaften des Haftöls an Motorsägeketten bewirkt, ein hochmolekulares Polymer, wie Polyethylenglykol oder Polyacrylamid mit Molekulargewichten von mehr als 1 Million. Diese Stoffe sind biologisch nicht abbaubar.The previously known adhesive oils contain as adhesion promoters, for example, the adhesion of the adhesive oil Chainsaw chains causes a high molecular weight polymer, such as  Polyethylene glycol or polyacrylamide with Molecular weights of more than 1 million. These substances are not biodegradable.

Die DE-OS 32 04 734 beschreibt Schmiermittel, die im wesentlichen aus einem aus pflanzlichen oder tierischen Produkten hergestellten Öl bestehen.DE-OS 32 04 734 describes lubricants that are in essentially one of vegetable or animal Products made of oil.

Die DE-PS 36 26 376 beschreibt Haftöle aus einem Schmieröl und einem Haftvermittler, wobei das Schmieröl mindestens ein pflanzliches und/oder mindestens ein tierisches Öl und der Haftvermittler ein kolophoniumhaltiges Harz und/oder Kolophonium ist.DE-PS 36 26 376 describes adhesive oils from a lubricating oil and a bonding agent, wherein the lubricating oil is at least a vegetable and / or at least one animal oil and the adhesion promoter is a rosin-containing resin and / or Rosin is.

Die DE-OS 34 19 415 beschriebt Schmiermittel, die Ester mehrwertiger Alkohole enthalten.DE-OS 34 19 415 beschriebt lubricants, the esters polyhydric alcohols.

Die GB-PS 1 41 433 beschreibt ein Mittel, das ein Mineralöl, Glyceride und einen Pflanzenextrakt enthält.GB-PS 1 41 433 describes an agent which is a mineral oil, Glycerides and a plant extract contains.

Gegenstand der vorliegenden Erfindung ist die Verwendung einer ein Schmieröl aus mindestens einem pflanzlichen und/oder mindestens einem tierischen Öl und einem Naturlatex als Haftvermittler enthaltenden Zusammensetzung als Motorsägekettenhaftöl, Schalöl oder Tiefziehöl.The subject of the present invention is the use one a lubricating oil from at least one vegetable and / or at least one animal oil and a natural latex as a primer-containing composition as Chain saw chainshaft oil, formwork oil or thermoforming oil.

Naturlatex bzw. Naturkautschuk wird ganz vorwiegend aus dem weißen milchigen Saft gewonnen, der beim Anritzen der Stämme von Hevea brasiliensis ausfließt. Latex ist eine mikroskopisch beobachtbare Emulsion von 0,0005 bis 0,001 mit großen Kautschuktröpfchen in Wasser, wobei jeweils Eiweißstoffe als Schutzkolloide dienen. Je 100 g Latex enthält etwa 30 bis 35 g Kautschuk, Proteine, Sterine, Fette, Kohlenhydrate (zusammen 4,5 bis 5 g) und 0,5 g mineralische Bestandteile; der Rest ist Wasser (Römpps Chemie-Lexikon, 7. Aufl., S. 1737).Natural latex or natural rubber is quite predominantly won the white milky juice, which when scoring the Tribes of Hevea brasiliensis emanates. Latex is one microscopically observable emulsion from 0.0005 to 0.001 with large rubber droplets in water, each containing protein serve as protective colloids. Per 100 g of latex contains about 30 up to 35 g of rubber, proteins, sterols, fats, carbohydrates (together 4.5 to 5 g) and 0.5 g of mineral constituents; the rest is water (Rompps Chemie-Lexikon, 7th ed., p. 1737).

Ein Teil des gezapften Kautschuks wird in konzentrierter flüssiger Form als Latex verarbeitet, der größte Teil wird zu festem Kautschuk aufgearbeitet. Das durch Verdampfen gewonnene Konzentrat führt die Bezeichnung Revertex. Dabei werden pastenförmige Konzentrate mit bis zu 75% Gesamt-Festsubstanz erhalten, die gegen mechanische Beanspruchung und chemische Einflüsse äußerst stabil sind, da sie nicht nur die gesamten natürlichen Stabilisatoren und Kautschukbegleitstoffe, sondern auch die für das Verfahren notwendigen zusätzlichen Stabilisierungsstoffe enthalten. Infolge seiner Stabilität und hohen Konzentration wird Revertex hauptsächlich für Streich- und Spritzmischungen angewandt (Ullmanns Enzyklopädie der technischen Chemie, 4. Aufl., Band 13, Seite 584).Part of the tapped rubber is concentrated in liquid form as latex processed, the largest part becomes  worked up to solid rubber. That by evaporation The concentrate obtained is called Revertex. there become pasty concentrates with up to 75% Total solid substance obtained against mechanical Stress and chemical influences are extremely stable, Not only do they have all the natural stabilizers and rubber adjuncts, but also for the Procedure necessary additional stabilizing substances contain. Due to its stability and high Revertex concentrates mainly on prank and painting Spray mixtures applied (Ullmanns encyclopedia of the Technical Chemistry, 4th ed., Volume 13, page 584).

Bringt man Rohkautschuk mit organischen Flüssigkeiten, wie Benzol, Benzin, pflanzlichen Ölen, Erdöl, Tetrachlorkohlenstoff, in Berührung, so quillt der Kautschuk erheblich, wobei eine mehr oder minder zähflüssige Kautschuklösung oder ein Gel entsteht (Ullmanns Enzyklopädie der technischen Chemie, 4. Aufl., Band 13, Seite 590).Bringing raw rubber with organic liquids, such as Benzene, gasoline, vegetable oils, petroleum, Carbon tetrachloride, in contact, so swells the Rubber considerably, with a more or less viscous rubber solution or a gel is formed (Ullmanns Enzyklopadie der technischen Chemie, 4th ed., Volume 13, page 590).

Das erfindungsgemäß verwendete Haftmittel ist biologisch vollständig abbaubar, da sowohl das pflanzliche und/oder tierische Öl als auch der Haftvermittler vollständig abbaubar sind und daher die Umwelt nicht belasten. Es hat sich überraschenderweise gezeigt, daß das erfindungsgemäß verwendete Haftmittel innerhalb von 14 Tagen vollständig abgebaut wird.The adhesive used in the invention is biologically complete degradable, as both the vegetable and / or animal oil as well as the bonding agent are completely degradable and therefore the environment is not strain. It has surprisingly been found that the Adhesive used in the invention within 14 days is completely degraded.

Der Zusatz des Naturlatex zu Schmierölen führt zu Haftmitteln mit ausgezeichneter Haftung bei Verwendung als Haftöl für Motorsägeketten, als Schalöl für Bauschalungen und als Tiefziehöl.The addition of natural latex to lubricating oils leads to Adhesives with excellent adhesion at Use as adhesive oil for chainsaw chains, as a formwork oil for Building formwork and as thermoforming oil.

Als Naturlatex kann jeder im Handel erhältliche Naturlatex verwendet werden. Vorzugsweise wird ein eingedampfter Naturlatex, der ein durch Verdampfen gewonnenes Konzentrat ist, verwendet. Ein solcher eingedampfter Naturlatex besitzt einen relativ niedrigen Wassergehalt, der im Bereich von 40 bis 25% liegt. Die im Handel erhältlichen eingedampften Naturlatices weisen beispielsweise Trockensubstanzgehalte von 62%, 68% oder 73% auf.As a natural latex, every commercially available natural latex  be used. Preferably, a vaporized Natural latex, a concentrate obtained by evaporation is used. Such a steamed natural latex has a relatively low water content in the Range of 40 to 25%. The commercially available evaporated natural latexes have, for example Dry matter contents of 62%, 68% or 73%.

Besonders bevorzugt sind Haftmittel, die als Schmieröl mindestens ein pflanzliches und/oder mindestens ein tierisches Öl und als Haftvermittler einen eingedampften Naturlatex mit einem Trockensubstanzgehalt von 73% aufweisen.Particularly preferred are adhesives used as lubricating oil at least one vegetable and / or at least one animal oil and a primer as a primer Natural latex with a dry matter content of 73% respectively.

Es ist bevorzugt, als Haftvermittler eine Kombination aus Naturlatex und Tallöl zu verwenden.It is preferred, as a primer, a combination of Natural latex and tall oil to use.

Als tierisches oder pflanzliches Öl können in den Haftmitteln z. B. Rüböl, Sonnenblumenöl, Rizinusöl, Olivenöl, Erdnußöl, Sojaöl oder Walöl enthalten sein. Unter diesen Ölen sind Rüböl, Sonnenblumenöl und/oder Rizinusöl bevorzugt. Ein Zusatz von Rizinusöl zu Rüböl und/oder Sonnenblumenöl ist aufgrund der ausgezeichneten Schmierwirkung des Rizinusöls in manchen Fällen zweckmäßig.As animal or vegetable oil can in the Adhesives z. B. rapeseed oil, sunflower oil, Castor oil, olive oil, peanut oil, soybean oil or whale oil his. Among these oils are rapeseed oil, sunflower oil and / or castor oil. An addition of castor oil too Rape oil and / or sunflower oil is due to the excellent lubricating effect of castor oil in some Cases appropriate.

Das erfindungsgemäß verwendete Haftmittel weist eine ausgezeichnete Haltbarkeit auf, so daß ein Zusatz eines haltbarmachenden Mittels nicht erforderlich ist.The adhesive used in the invention has an excellent Shelf life, so that an addition of a durable By means of not required.

Das erfindungsgemäß verwendete Haftmittel enthält vorzugsweise 99,9 bis 90,0 Gew.-% Schmieröl und 0,1 bis 10,0 Gew.-% Haftvermittler. Besonders bevorzugt enthält das Haftmittel 99,0 bis 95,0 Gew.-% Schmieröl und 1,0 bis 5,0 Gew.-% Haftvermittler. The adhesive used in the invention preferably contains 99.9 to 90.0% by weight of lubricating oil and 0.1 to 10.0% by weight Adhesion promoters. Most preferably, the adhesive contains 99.0 to 95.0% by weight of lubricating oil and 1.0 to 5.0% by weight Adhesion promoters.  

Bei Verwendung als Motorsägekettenhaftöl weist das Haftmittel den weiteren Vorteil auf, daß ihm keine Verschleiß- und keine Korrosionsschutz-Inhibitoren zugesetzt werden brauchen. Es hat sich nämlich gezeigt, daß der Haftvermittler gegen Verschleiß und Korrosion schützende Eigenschaften aufweist.When used as chainsaw chain oil that has Adhesive has the further advantage that him no wear and no Corrosion inhibitors need to be added. It has shown that the Adhesive against wear and corrosion protective Features.

Das erfindungsgemäß verwendete Haftmittel eignet sich als Motorsägekettenhaftöl, als Trennmittel für Bauschalungen, wie Betonschalungen, und zwar in gleicher Weise für sogenannte saugende als auch nicht saugende Schalungen, und als Tiefziehöl für die Autoindustrie.The adhesive used in the invention is suitable as chainsaw chain oil, as release agent for building formwork, such as concrete formwork, and in same way for so-called sucking as well as not absorbent formwork, and as thermoforming oil for the Auto industry.

Die Herstellung des Haftmittels erfolgt in einfacher Weise durch Vermischen des Schmieröls mit dem Haftvermittler. Üblicherweise wird in einem Mischer das Schmieröl vorgelegt und der Haftvermittler zugesetzt. Das Vermischen geht problemlos bei Raumtemperatur vonstatten. Bei Verwendung eines 1000 l fassenden Mischers und einem Volumen der Mischung aus Schmieröl und Haftvermittler von etwa 900 l ist bei üblichen Mischgeschwindigkeiten und bei Raumtemperatur nach etwa 10minütiger Mischdauer ein homogenes Haftöl entstanden, das sich auch nach langem Stehen nicht entmischt.The preparation of the adhesive takes place in a simple manner by mixing the lubricating oil with the Adhesion promoters. Usually in a mixer the Submitted lubricating oil and added to the primer. The Mixing is easy at room temperature. When using a 1000 liter mixer and a volume of the mixture of lubricating oil and Primer of about 900 l is at usual Mixing speeds and at room temperature after about 10 minutes mixing time a homogeneous adhesive oil emerged that does not separate even after standing for a long time.

Nachfolgend werden als Beispiele besonders bevorzugte Zusammensetzungen erfindungsgemäß verwendeter Haftmittel angegeben:Hereinafter, examples which are particularly preferred Compositions of adhesives used according to the invention indicated:

Beispiel 1example 1 MotorsägekettenhaftölChainsaw chain oil

Es wurde folgender Naturlatex verwendet: The following natural latex was used:  

Trockensubstanzgehalt|ca. 73%Dry matter content | approx. 73% KOH-GehaltKOH content ca. 1,0 Gew.-%about 1.0% by weight pH-WertPH value ca. 11,4about 11.4 VFA-ZahlVFA number max. 0,1Max. 0.1 Koagelgehalt, auf Latex naßKoagelgehalt, wet on latex max. 0,05 Gew.-%Max. 0.05% by weight Viskosität (Brookfield LVT 4/60, 30°C)Viscosity (Brookfield LVT 4/60, 30 ° C) ca. 6000 mPasabout 6000 mPas Mechanische StabilitätMechanical stability 1500 sek. min1500 sec. min

2 Gew.-% dieses Latex wurden mit 98 Gew.-% Rüböl in einem Schnellmischer bei 1200 bis 200 U/min bei Raumtemperatur gemischt.2% by weight of this latex was mixed with 98% by weight of rapeseed oil in one Fast mixer at 1200 to 200 rpm at room temperature mixed.

Beispiel 2Example 2 Schalöl für BauschalungenScarf oil for building formwork

4 Gew.-% des in Beispiel 1 angegebenen Naturlatex wurden mit 96 Gew.-% Rüböl wie in Beispiel 1 angegeben gemischt.4 wt .-% of the natural latex indicated in Example 1 were mixed with 96 wt .-% rapeseed oil as indicated in Example 1.

Beispiel 3Example 3 Tiefziehöl für die AutoindustrieDeep-drawing oil for the auto industry

3 Gew.-% des in Beispiel 1 angegebenen Naturlatex wurden mit 97 Gew.-% Rüböl wie in Beispiel 1 angegeben gemischt.3 wt .-% of the natural latex indicated in Example 1 were mixed with 97 wt .-% of rapeseed oil as indicated in Example 1.

Claims (8)

1. Verwendung einer ein Schmieröl aus mindestens einem pflanzlichen und/oder mindestens einem tierischen Öl und einen Naturlatex als Haftvermittler enthaltenden Zusammensetzung als Motorsägekettenhaftöl, Schalöl oder Tiefziehöl.1. Use of a lubricating oil from at least one vegetable and / or at least one animal oil and one Natural latex containing as a primer composition as Chain saw chainshaft oil, formwork oil or thermoforming oil. 2. Verwendung nach Anspruch 1, dadurch gekennzeichnet, daß der Haftvermittler weiterhin Tallöl enthält.2. Use according to claim 1, characterized in that the Adhesion agents continue to contain tall oil. 3. Verwendung nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß das Verhältnis von Schmieröl zu Haftvermittler 99,9 bis 90,0 Gew.-% zu 0,1 bis 10,0 Gew.-% beträgt.3. Use according to claim 1 or 2, characterized that the ratio of lubricating oil to adhesion promoter 99.9 to 90.0 wt .-% to 0.1 to 10.0 wt .-% is. 4. Verwendung nach Anspruch 1 oder 2, dadurch gekennzeichnet, daß das Verhältnis von Schmieröl zu Haftvermittler 99,0 bis 95,0 Gew.-% zu 1,0 bis 5,0 Gew.-% beträgt.4. Use according to claim 1 or 2, characterized that the ratio of lubricating oil to adhesion promoter 99.0 to 95.0 wt .-% to 1.0 to 5.0 wt .-% is. 5. Verwendung nach einem der Ansprüche 1 bis 4, dadurch gekennzeichnet, daß der Naturlatex ein Konzentrat ist.5. Use according to one of claims 1 to 4, characterized characterized in that the natural latex is a concentrate. 6. Verwendung nach Anspruch 5, dadurch gekennzeichnet, daß der Naturlatex einen Wassergehalt von 40-25% besitzt. 6. Use according to claim 5, characterized in that the Natural latex has a water content of 40-25%.   7. Verwendung nach Anspruch 5, dadurch gekennzeichnet, daß der Naturlatex Revertex ist.7. Use according to claim 5, characterized in that the Natural Latex Revertex is. 8. Verwendung nach einem der Ansprüche 1 bis 7, dadurch gekennzeichnet, daß das pflanzliche Öl Rüböl, Sonnenblumenöl und/oder Rizinusöl ist.8. Use according to one of claims 1 to 7, characterized characterized in that the vegetable oil is rapeseed oil, sunflower oil and / or castor oil.
DE19873737837 1987-11-06 1987-11-06 Adherent composition and its use as power saw chain oil, forming oil and deep-drawing oil Granted DE3737837A1 (en)