CN103788824A - 一种消防管道用粉末涂料及其制备方法 - Google Patents

一种消防管道用粉末涂料及其制备方法 Download PDF

Info

Publication number
CN103788824A
CN103788824A CN201410028964.7A CN201410028964A CN103788824A CN 103788824 A CN103788824 A CN 103788824A CN 201410028964 A CN201410028964 A CN 201410028964A CN 103788824 A CN103788824 A CN 103788824A
Authority
CN
China
Prior art keywords
powder coating
parts
fire protection
protection pipeline
coating according
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201410028964.7A
Other languages
English (en)
Inventor
曹伟
葛锦妹
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nantong Haiou Lift-Saving & Protection Equipment Co Ltd
Original Assignee
Nantong Haiou Lift-Saving & Protection Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nantong Haiou Lift-Saving & Protection Equipment Co Ltd filed Critical Nantong Haiou Lift-Saving & Protection Equipment Co Ltd
Priority to CN201410028964.7A priority Critical patent/CN103788824A/zh
Publication of CN103788824A publication Critical patent/CN103788824A/zh
Withdrawn legal-status Critical Current

Abstract

本发明提供一种消防管道用粉末涂料及其制备方法，该粉末涂料按重量份计包括如下组分：环氧树脂80~110份，固化剂10~18份，助剂8~10份，填料40~60份和颜料2~5份。制备方法包括如下步骤：按配方组成精确称量物料，置于高速混合机中混合3~5min，混合物料用粉末涂料挤出机在90±2℃温度下挤出，挤出料用粉末涂料磨粉机粉碎为平均粒径为40~50μm的粉体颗粒，用180目筛网过筛，即得到合格的粉末涂料。本发明提供的一种消防管道用粉末涂料，不含对涂料生产人员和涂装人员带来健康危害的有机溶剂，安全环保；且耐候性能优异，适于室外恶劣条件下使用。

Description

一种消防管道用粉末涂料及其制备方法
技术领域
本发明涉及涂料领域，具体涉及一种消防管道用粉末涂料及其制备方法。
背景技术
普通消防用镀锌管及连接件由于其自身在防腐蚀、防结垢和抗菌性能等较差，加之消防用水的长期静止性和突发急用性等特点，因此在实际使用中存在诸多问题。首先，由于镀锌钢管防腐性能差，长期受到水的侵蚀，棺材的内表面易生锈，修曾脱落后容易堵塞喷头；其次，管材内表面结垢后，容易使棺材的内径缩小或堵塞，使输水、凄凉减少甚至无法输送，影响实际使用效果；最关键的一点是，如果在消防救灾过程中出现上述情况，延误救灾，后果将不堪设想；上述缺陷的存在使得镀锌管的使用寿命较短，一般仅为7~8年。经过改进后，人们在消防用镀锌管的内侧涂覆了粉末涂料，但其耐候性不能达到户外高耐候性的涂装要求。
发明内容
鉴于上述信息，本发明的目的之一在于提供一种耐候性能提高、成本低廉的消防管道用粉末涂料。
本发明提供一种消防管道用粉末涂料，按重量份计包括如下组分：环氧树脂80~110份，固化剂10~18份，助剂8~10份，填料40~60份和颜料2~5份。
作为优选，按重量份计包括如下组分：环氧树脂100份，固化剂15份，助剂10份，填料50份和颜料2份。
所述固化剂为TGIC。
所述助剂包括流平剂和脱气剂，二者质量比为1:1。
所述流平剂为PV88，脱气剂为聚乙烯蜡APP620F。
所述填料是空心玻璃微珠、纳米氧化硅、硫酸钡中的一种或多种。
所述颜料为氧化铁红。
本发明的另一目的在于提供一种消防管道用粉末涂料的制备方法，包括如下步骤：按配方组成精确称量物料，置于高速混合机中混合3~5min，混合物料用粉末涂料挤出机在90±2℃温度下挤出，挤出料用粉末涂料磨粉机粉碎为平均粒径为40~50μm的粉体颗粒，用180目筛网过筛，即得到合格的粉末涂料。
本发明提供的一种消防管道用粉末涂料，不含对涂料生产人员和涂装人员带来健康危害的有机溶剂，安全环保；且耐候性能优异，适于室外恶劣条件下使用。
具体实施方式
下面的实施例可使本专业技术人员更全面地理解本发明，但不以任何方式限制本发明。
实施例1
取环氧树脂80份，TGIC固化剂10份，助剂8份（PV88 4份、聚乙烯蜡APP620F 4份），空心玻璃微珠40份和氧化铁红2份，置于高速混合机中混合3~5min，混合物料用粉末涂料挤出机在90±2℃温度下挤出，挤出料用粉末涂料磨粉机粉碎为平均粒径为40~50μm的粉体颗粒，用180目筛网过筛，即得到合格的粉末涂料。
主要涂抹性能指标：
抗冲击性 ≥45kg·cm
QUV-B（480h）保光率 ≥95%。
实施例2
取环氧树脂100份，TGIC固化剂15份，助剂10份（PV88 5份、聚乙烯蜡APP620F 5份），纳米氧化硅25份，硫酸钡25份和氧化铁红2份，置于高速混合机中混合3~5min，混合物料用粉末涂料挤出机在90±2℃温度下挤出，挤出料用粉末涂料磨粉机粉碎为平均粒径为40~50μm的粉体颗粒，用180目筛网过筛，即得到合格的粉末涂料。
主要涂抹性能指标：
抗冲击性 ≥50kg·cm
QUV-B（480h）保光率 ≥95%。
实施例3
取环氧树脂110份，TGIC固化剂18份，助剂10份（PV88 5份、聚乙烯蜡APP620F 5份），纳米氧化硅40份，硫酸钡20份和氧化铁红5份，置于高速混合机中混合3~5min，混合物料用粉末涂料挤出机在90±2℃温度下挤出，挤出料用粉末涂料磨粉机粉碎为平均粒径为40~50μm的粉体颗粒，用180目筛网过筛，即得到合格的粉末涂料。
主要涂抹性能指标：
抗冲击性 ≥50kg·cm
QUV-B（480h）保光率 ≥90%。

Claims (8)

1.一种消防管道用粉末涂料，其特征在于，按重量份计包括如下组分：环氧树脂80~110份，固化剂10~18份，助剂8~10份，填料40~60份和颜料2~5份。
2.根据权利要求1所述的一种消防管道用粉末涂料，其特征在于，按重量份计包括如下组分：环氧树脂100份，固化剂15份，助剂10份，填料50份和颜料2份。
3.根据权利要求1所述的一种消防管道用粉末涂料，其特征在于，所述固化剂为TGIC。
4.根据权利要求1所述的一种消防管道用粉末涂料，其特征在于，所述助剂包括流平剂和脱气剂，二者质量比为1:1。
5.根据权利要求4所述的一种消防管道用粉末涂料，其特征在于，所述流平剂为PV88，脱气剂为聚乙烯蜡APP620F。
6.根据权利要求1所述的一种消防管道用粉末涂料，其特征在于，所述填料是空心玻璃微珠、纳米氧化硅、硫酸钡中的一种或多种。
7.根据权利要求1所述的一种消防管道用粉末涂料，其特征在于，所述颜料为氧化铁红。
8.基于权利要求1所述的一种消防管道用粉末涂料的制备方法，其特征在于，包括如下步骤：按配方组成精确称量物料，置于高速混合机中混合3~5min，混合物料用粉末涂料挤出机在90±2℃温度下挤出，挤出料用粉末涂料磨粉机粉碎为平均粒径为40~50μm的粉体颗粒，用180目筛网过筛，即得到合格的粉末涂料。
CN201410028964.7A 2014-01-22 2014-01-22 一种消防管道用粉末涂料及其制备方法 Withdrawn CN103788824A (zh)